CN103922034B - A kind of compound package material structure having an X-rayed multi-layer co-extruded colors changing hue film - Google Patents
A kind of compound package material structure having an X-rayed multi-layer co-extruded colors changing hue film Download PDFInfo
- Publication number
- CN103922034B CN103922034B CN201410184889.3A CN201410184889A CN103922034B CN 103922034 B CN103922034 B CN 103922034B CN 201410184889 A CN201410184889 A CN 201410184889A CN 103922034 B CN103922034 B CN 103922034B
- Authority
- CN
- China
- Prior art keywords
- layer
- film
- extruded
- rayed
- changing hue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The present invention relates to printed apcksging material and packing container technical field, specifically a kind of producing novel composite packing material structure having an X-rayed multi-layer co-extruded colors changing hue film, this structure includes five-layer structure, it is base material by ground floor, the second layer is can anti-high light metal level, third layer is at least include the lower ink layer of chalk, 4th layer for can have an X-rayed multi-layer co-extruded colors changing hue film, layer 5 is the layer of ink composition that oils, it is provided with through compound on the surface of base material, what evaporation or transfering process were made can the metal level of anti-Gao Guang, the surface of metal level of anti-Gao Guang can be covered with the lower ink layer at least including chalk, it is covered with on the lower ink layer at least including chalk and can have an X-rayed multi-layer co-extruded colors changing hue film, the layer of ink that oils is printed having an X-rayed on multi-layer co-extruded colors changing hue film.Present invention have the advantages that the position that this structure existing metallochrome on the packaging is prominent, the position that colored change is prominent again, under the premise that cost is constant, prominent commodity are personalized, have antifalse effect.
Description
[technical field]
The present invention relates to printed apcksging material and packing container technical field, specifically a kind of producing novel composite packing material structure having an X-rayed multi-layer co-extruded colors changing hue film.
[background technology]
At present in printed apcksging material field, require also more and more higher in the diversity simultaneously for packaging meeting attractive packages.In order to seek the diversity of packaging, packaging material gradually from single art post paperboard, transparent membrane is to the various holographic laser film (laser rainbow holographic film, laser film) of silver foil, color and can have an X-rayed multi-layer co-extruded colors changing hue film (rainbow film, colorful film).The metal-like of silver foil, the color-changing anti-counterfeit of holographic laser film, the change chromaticity that can have an X-rayed multi-layer co-extruded colors changing hue film are all the major reasons attracting consumer eyeball.
The application of the existing printed apcksging material technical elements combined with change color by metal-like see: patent name " composite plastic package bag " (patent No.: 200820231062), patent name " Thickened packaging bag " (patent No.: 200720307102.3).The structure of a kind of Anti-counterfeit packing bag of above-mentioned two patent disclosure and characteristic, they are the surface recombination holographic laser films at bag, the bag being covered with aluminium lamination, wherein at the inner surface of holographic laser film or/and outer surface is covered with ink layer.Laser holographic aluminized film and laser hologram hyaline membrane broadly fall into holographic laser film.This packaging bag being covered with aluminium lamination, when the inner surface printing-ink of laser holographic aluminized film, the aluminium coated of laser hologram can cover the color of bottom ink completely, also just meaningful at the bottom printing-ink of laser holographic aluminized film;When the outer surface printing-ink of laser holographic aluminized film, the color of upper strata printing-ink only cannot cover in the change color of laser holographic aluminized film in local, but only expose metallic luster, be therefore unable to reach on surface of package and only reach the needs of design with printing cash the characteristic of change color or metal at the position specified.It addition, when the inner surface printing-ink of laser hologram hyaline membrane, the change color of laser hologram hyaline membrane can be strengthened by the aluminium lamination of bottom, but the packaging material product simply using laser hologram hyaline membrane does not just exhibit metal-like;When the outer surface printing-ink of laser hologram hyaline membrane, the color of ink itself can cover again the change color of laser hologram hyaline membrane, also just loses meaning at packaging bag overlying laser hologram hyaline membrane equally.
For the problem only using the packaging of silver foil and lack riot of color color, part dealer can use the holographic laser film of aluminium lamination to be used as packaging material, but this way make packaging material colour generation cannot only part highlight metallochrome while part highlight the problem of change color of holographic laser film.There is for this people to abandon holographic laser film, directly one colorful film and transparent multilaminar co-extrusion colors changing hue film direct combination are being packed on base material, be used for increasing the gorgeous color of packaging material.But packaging entirety can present the change color of beautiful colorful film and have the counter productive covering color originally when being typically in common substrate direct combination colorful film, ultimately result in this packaging obtained at substrate surface direct combination colorful film and decorative product seems unification in effect.Therefore develop a kind of on top grade is packed the existing position highlighting metal-like highlight again the function of concordance change color in appointed part simultaneously so that the printed apcksging material that packaging presents diversity has very important meaning.
[summary of the invention]
It is an object of the present invention to provide a kind of producing novel composite packing material structure innovation having an X-rayed multi-layer co-extruded colors changing hue film, solve use silver foil, the holographic laser film existed in prior art and multi-layer co-extruded colors changing hue film can be had an X-rayed and cause that packaging product cannot highlight concordance colors changing hue while highlighting metal-like or cannot highlight metal-like while highlighting concordance colors changing hue and cause the packaging monistic problem of product, can also reach false proof purpose simultaneously.
The technical scheme is that a kind of producing novel composite packing material structure having an X-rayed multi-layer co-extruded colors changing hue film, this structure includes five-layer structure, it is base material by ground floor, the second layer is can anti-high light metal level, third layer is at least include the lower ink layer of chalk, 4th layer is multi-layer co-extruded colors changing hue film, layer 5 is the layer of ink composition that oils, it is provided with through compound on the surface of base material, what evaporation or the operation such as transfer were made can the metal level of anti-Gao Guang, the surface of metal level of anti-Gao Guang can be covered with the lower ink layer at least including chalk, it is covered with on the lower ink layer at least including chalk and can have an X-rayed multi-layer co-extruded colors changing hue film, transparent multilaminar co-extrusion colors changing hue film does not only have optical grating construction and color not easily to be weakened by other clear dopes, one layer of layer of ink that oils of printing on multi-layer co-extruded colors changing hue film can had an X-rayed, employing can be had an X-rayed the producing novel composite packing material structure of multi-layer co-extruded colors changing hue film and is applied on packaging product and both had the position that metallochrome is prominent, there is again the position that concordance colors changing hue is prominent, base material is made to present various packaging after composite transparent multi-layer co-extruded colors changing hue film, the personalization of ornament materials.
Base material includes composite or the thin film of paper or paperboard or plastics or above-mentioned material.
Anti-high light metal layer material can adopt gold or aluminum or copper or ag material or other metal materials.
Multi-layer co-extruded colors changing hue film can be had an X-rayed include adopting colorful film or rainbow film, rainbow film no-raster structure, not easily be weakened by other clear dopes.
The surface of metal level of anti-Gao Guang can be covered with lower ink layer, lower ink layer includes at least lower chalk layer, chalk has not only hidden the reflective of following metal level and has more improved the chroma that can have an X-rayed multi-layer co-extruded colors changing hue film so that the appointed part only having lower chalk on packaging material can present prominent change color.
One layer of layer of ink that oils of printing on multi-layer co-extruded colors changing hue film can had an X-rayed.
This package material structure is applied in article of everyday use, food, tobacco and wine, cosmetics, sample, label and packing and decorating, under the premise that cost is basically unchanged, it is possible to attract the eyeball of more consumer, the packing instructions that prominent commodity are personalized, has antifalse effect.
Compared with the contrast patent in background technology, present invention differs in that following some:
1. the present invention can have an X-rayed the compound package material of multi-layer co-extruded colors changing hue film mainly by base material, metal level, lower ink layer, multi-layer co-extruded colors changing hue film can be had an X-rayed and oil what layer of ink was constituted, wherein used in the present invention have an X-rayed multi-layer co-extruded colors changing hue film and there is no optical grating construction, and the layer of ink that oils of the present invention at least includes chalk.
2. the present invention covers the lower ink layer having at least chalk can have an X-rayed below multi-layer co-extruded colors changing hue film, and chalk exactly can had an X-rayed multi-layer co-extruded colors changing hue film and be different at the action effect under holographic laser film.Chalk is covered having an X-rayed below multi-layer co-extruded colors changing hue film, cover in the reflection of the aluminium lamination of bottom due to the strong covering power of chalk, at this moment present the effect of colors changing hue in the place having chalk just strong than the colors changing hue effect that place without chalk under can having an X-rayed multi-layer co-extruded colors changing hue film presents.Therefore, chalk actually rises to be the effect strengthening change color under can having an X-rayed multi-layer co-extruded colors changing hue film, and when covering chalk below holographic laser film, have the place of chalk to present the effect of colors changing hue and have metal level than under laser hologram hyaline membrane but local color effect without chalk is weak.Therefore, chalk is actual under laser hologram hyaline membrane not to be affected colors changing hue, and if when using laser holographic aluminized film, aluminizing of holographic film will hide the effect of lower section ink comprehensively, so also just it is unnecessary for using chalk.
3. the present invention is after can having an X-rayed on multi-layer co-extruded colors changing hue film to carry out end face printing and protection glazing or pad pasting, the effect of colors changing hue will not be reduced, and background technology patent uses laser holographic aluminized film, after the printing of its end face and protection glazing or pad pasting, cannot present only metallochrome and without the effect of illusion-colour, and after the use transparent glazing film of laser hologram carries out end face printing and protection glazing or pad pasting, structure (including nearly 1000 small peak valleys in lmm length to rise and fall) due to the transparent glazing film of laser hologram itself, printing-ink can be filled and led up small peak valley and rise and fall, thus having eliminated the effect of colors changing hue, even if such as this patent, on the base material of metal cladding, print includes the lower ink layer of chalk, it is covered with laser holographic aluminized film again, it finally also can offset down the effect of ink layer because of covering of aluminium lamination comprehensively.
The invention has the beneficial effects as follows that this employing can be had an X-rayed the producing novel composite packing material structure of multi-layer co-extruded colors changing hue film and is applied in the appointed part of packaging product and need to can not present then through manufacturing procedures such as alignment cut and both had the position that metallochrome is prominent, there is again the position that concordance colors changing hue is prominent, make base material present the personalization of various packaging, ornament materials after composite transparent multi-layer co-extruded colors changing hue film;Under the premise that cost is basically unchanged, the eyeball of more consumer can be attracted, it is suitable for being used in the needs printings such as front cover, sales promotion, packaging and integrating the colour of metallic luster texture and concordance variable color and don't lose the package design of the locally product of individual requirement, the packing instructions that prominent commodity are personalized, there is antifalse effect, improve product power of influence, promote enterprise economic growth.
[accompanying drawing explanation]
Fig. 1 is the structural representation of the present invention;
Fig. 2 is the structural representation of another embodiment of the present invention;
Fig. 3 is the structural representation of further embodiment of this invention;
Fig. 4 is the structural representation of yet another embodiment of the invention;
Fig. 5 is the structural representation of the another another embodiment of the present invention;
Referring to Fig. 1 to Fig. 5:
1,21,31,41,51 base materials (paper, plastics, composite or thin film);
2,22,32,42,52 can the metal level (metal level such as gold, aluminum, copper) of anti-Gao Guang;
3,23,33,43,53 times chalks;
4,24,34,44,54 multi-layer co-extruded colors changing hue film (colorful film, rainbow film) can be had an X-rayed;
5,25,35,45,55 oil layer of ink (upper yellow layer of ink, upper red rete, blueing layer of ink);
Chalk on 46;
57 times ink layeies (lower blue layer of ink);
Specify Fig. 1 as the Figure of abstract of the present invention.
[detailed description of the invention]
Below in conjunction with accompanying drawing, the invention will be further described, the printing manufacturing technology of this packing container for the people of this specialty it is quite clear that.
Referring to Fig. 1, a kind of producing novel composite packing material structure having an X-rayed multi-layer co-extruded colors changing hue film, its structure is formed by with lower part, base material, can anti-Gao Guang metal level, have at least chalk lower ink layer, multi-layer co-extruded colors changing hue film can be had an X-rayed, oil layer of ink.Wherein, be provided with on the surface of base material 1 through different operation such as compound or evaporation or transfer etc. make can the metal level 2 of anti-Gao Guang.Base material includes paper, paperboard, plastics, composite or thin film;The metal level of anti-Gao Guang can include the metal materials such as gold, silver, aluminum, copper, zinc, chromium;Described complex technique refers to the operation that a kind of material is fitted with another kind of material again through coating adhesive, metal material is vaporized the postadhesion a kind of operation on cylinder material by described evaporation when vacuum high-temperature, and described transfer refers to and is stripped on base material on thin film together with binding agent after binding agent with the laminating of another base material by the metal material layer on thin film originally again.The surface printing of metal level 2 of anti-Gao Guang can at least include the lower ink layer 3 of chalk;What be coated with fantasy coloured effect on the lower ink layer 3 at least including chalk has an X-rayed multi-layer co-extruded colors changing hue film 4.Multi-layer co-extruded colors changing hue film adopts the colors changing hue composite membrane that plural layers are combined by multi-layer co-extruded complex technique, can have an X-rayed multi-layer co-extruded color transformed film and include colorful film, rainbow film.Can having an X-rayed by utilizing typography printing to oil layer of ink 5 on multi-layer co-extruded colors changing hue film, described product can be made into the products such as packing box, label, publicity picture album, packaging bag.
This package material structure is applied in article of everyday use, food, tobacco and wine, cosmetics, sample, label and packing and decorating, under the premise that cost is basically unchanged, it is possible to attract the eyeball of more consumer, the packing instructions that prominent commodity are personalized, has antifalse effect.
Embodiment 1:
As in figure 2 it is shown, in the paperboard 21 of aluminizer 22 printing chalk 23, then at printing surface overlying colorful film 24, finally process yellow ink 25 on colorful film 24.When light be irradiated to lower chalk local time, owing to the covering power of chalk is very strong, it can stop the reflective degree of aluminium foil, so mainly presenting illusion-colour color at the local packaging material having lower chalk.When light is radiated at the place not playing chalk, what packaging material almost all presented is silver color.Chalk under nothing and the place of yellow layer of ink on having, what packaging material presented is the yellow having silver-like effect.Finally give with the yellow of silver-like effect, metal-like structure prominent, the unanimously prominent packaging of effect of change color, decorative product.
Embodiment 2:
As it is shown on figure 3, in the transfer paperboard 31 of transfer aluminum plated layer 32 printing chalk 33, then at printing surface overlying colorful film 34, then on the colorful film having lower chalk printing indigo plant ink 35.When light is irradiated to the lower chalk place without blueing layer of ink, main body presents the change color of colorful film.Being irradiated to lower chalk at light and have the place of blueing layer of ink, packaging material mainly present the blueness with fantasy coloured effect.Not only chalk is not played but also either with or without the region of upper chalk, what packaging material almost all presented is the silver color of aluminium foil when light is irradiated to.Finally give and above blueness, have the structure that illusion-colour, metal-like are prominent, concordance color highlights the packaging of effect, decorative product.
Embodiment 3:
As shown in Figure 4, the paperboard 41 of aluminizer 42 prints part chalk 43, then at printing surface overlying rainbow film 44, then on rainbow film 44, print part chalk 46, on chalk 46, finally print red black 45.Chalk is had up and down and without the place of the red ink in upper strata, the white that packaging material present when light is irradiated to;Having chalk when light is irradiated to levels and has the place of the red ink in upper strata, what mainly present is red effect;Be radiated at the supreme chalk of lower chalk and the place of the red layer of ink of supreme printing when light, what packaging material mainly presented is change color;When light is radiated at up and down all without the place of chalk, what packaging material almost all presented is the silver color of aluminium foil.Finally give red effect, metal-like is prominent, concordance colors changing hue is prominent and the structure of the packaging of white effect, decorative product.
Embodiment 4:
As it is shown in figure 5, in the transfer paperboard 51 of transfer aluminum plated layer 52 printing chalk 53, printing indigo plant ink 57 on lower chalk 53, overall on blue ink 57 cover rainbow film 54, finally printing indigo plant ink 55 on colorful film 54.When light is irradiated to lower chalk and lower blue layer of ink and without the place of blueing layer of ink, what packaging material presented is have blue ribbon change color effect;When light is irradiated to lower chalk and without lower blue layer of ink and the place without blueing layer of ink, what packaging material presented is the change color of very strong rainbow film;When light is irradiated to lower blue layer of ink and without lower chalk and without the place of blueing layer of ink, packaging material present partially blue silver-like effect;When light is irradiated to upper strata Lan Moer without lower floor's chalk and without the place of lower floor indigo plant ink, packaging material also present the blueness having silver-like effect, but the blueness in this place can be stronger;When light is irradiated to without lower chalk, without lower blue layer of ink and the place without blueing layer of ink, packaging material almost all present silver color.Finally give structure prominent with the blueness in various degree of silver-like effect, metal-like, the prominent packaging of effect of concordance change color, decorative product.
Claims (4)
1. the compound package material structure that can have an X-rayed multi-layer co-extruded colors changing hue film, it is characterized in that this structure includes five-layer structure, it is base material (1) by ground floor, the second layer is can anti-high light metal level (2), third layer is the lower ink layer (3) being made up of chalk, 4th layer for having an X-rayed multi-layer co-extruded colored change film (4), layer 5 forms for the layer of ink that oils (5), it is provided with through compound on the surface of base material (1), what evaporation or transfering process were made can the metal level (2) of anti-Gao Guang, the surface of metal level (2) of anti-Gao Guang can be covered with the lower ink layer (3) being made up of chalk, the reflection of the aluminium lamination of bottom is covered in due to the strong covering power of chalk, at this moment the effect of colors changing hue is presented in the place having chalk just strong than the colors changing hue effect that place without chalk under can having an X-rayed multi-layer co-extruded colors changing hue film presents, it is covered with on the lower ink layer (3) being made up of chalk and can have an X-rayed multi-layer co-extruded colors changing hue film (4), multi-layer co-extruded colors changing hue film (4) one layer of layer of ink that oils (5) of upper printing can had an X-rayed, transparent multilaminar co-extrusion colors changing hue film does not only have optical grating construction and color not easily to be weakened by other clear dopes, multi-layer co-extruded colors changing hue film is the colors changing hue composite membrane adopting multi-layer co-extruded complex technique to be combined by plural layers.
2. a kind of compound package material structure having an X-rayed multi-layer co-extruded colors changing hue film as claimed in claim 1, it is characterised in that base material (1) includes composite or the thin film of paper or paperboard or plastics or above-mentioned material.
3. a kind of compound package material structure having an X-rayed multi-layer co-extruded colors changing hue film as claimed in claim 1, it is characterised in that metal level (2) material of anti-Gao Guang can adopt gold or aluminum or copper or ag material or other metal materials
4. a kind of compound package material structure having an X-rayed multi-layer co-extruded colors changing hue film as claimed in claim 1, it is characterised in that transparent multi-layer co-extruded colors changing hue film (4) includes adopting colorful film or rainbow film.