CN103920263A - Domestic fire blanket - Google Patents
Domestic fire blanket Download PDFInfo
- Publication number
- CN103920263A CN103920263A CN201410142035.9A CN201410142035A CN103920263A CN 103920263 A CN103920263 A CN 103920263A CN 201410142035 A CN201410142035 A CN 201410142035A CN 103920263 A CN103920263 A CN 103920263A
- Authority
- CN
- China
- Prior art keywords
- heat treatment
- warming
- temperature heat
- low temperature
- carbon fiber
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a domestic fire blanket. The domestic fire blanket comprises a carbonized fiber blanket body, wherein hand side pockets are arranged at two to four corners of the carbonized fiber blanket body; when carbonized fibers are carbonized, the temperature of a low-temperature heat treatment furnace is raised from 163 DEG C; the temperature is raised by 2-6 DEG C each minute and is raised to 300-320 DEG C; the temperature is kept for 9-25 minutes and then is raised to 330-350 DEG C; then the low-temperature heat treatment furnace is cooled until the temperature is lower than 80 DEG C; nitrogen gas is added at an inlet and an outlet of the low-temperature heat treatment furnace to carry out gas sealing. The domestic fire blanket is reasonable in structure, is very convenient to use and has a good fire extinguishment effect.
Description
Technical field
The present invention relates to a kind of firing fighting apparatus.
Background technology
A lot of family fires are because the improper use of kitchen kitchen range causes, and occur to burn once there is the positions such as kitchen kitchen range, often can not technology put out, and particularly the fire such as oil cauldron is all the more so.
Summary of the invention
The object of the present invention is to provide a kind of rational in infrastructure, the Household fire blanket that fire extinguishing is convenient, effective.
Technical solution of the present invention is:
A Household fire blanket, is characterized in that: comprise carbon fiber blanket body, 2 ~ 4 angles of carbon fiber blanket body arrange hand slash pocket; When carbon fiber charing is processed, Low Temperature Heat Treatment stove is since 163 ℃ of intensifications, intensification 2-6 ℃ per minute, be warming up to 300-320 ℃, then after constant temperature 9-25 minute, be warming up to 330-350 ℃ again, be then cooled to temperature lower than 80 ℃, the import and export of Low Temperature Heat Treatment stove add nitrogen sealing gland.
Hand slash pocket is triangle, and leg-of-mutton two limits overlap with two limits of blanket body; When carbon fiber charing is processed, Low Temperature Heat Treatment stove is since 163 ℃ of intensifications, 3 ℃ of intensifications per minute, be warming up to 301 ℃, then constant temperature is warming up to 340 ℃ again after 9 minutes, is then cooled to temperature lower than 80 ℃, and the import and export of Low Temperature Heat Treatment stove add nitrogen sealing gland.
In the upper strata bag of hand slash pocket, weight block is set; When carbon fiber charing is processed, Low Temperature Heat Treatment stove is since 163 ℃ of intensifications, 4 ℃ of intensifications per minute, be warming up to 302 ℃, then constant temperature is warming up to 350 ℃ again after 25 minutes, is then cooled to temperature lower than 80 ℃, and the import and export of Low Temperature Heat Treatment stove add nitrogen sealing gland.
The present invention is rational in infrastructure, use very convenient, good extinguishing effect.
Below in conjunction with embodiment, the invention will be further described.
The specific embodiment
A Household fire blanket, comprises carbon fiber blanket body, and 2 ~ 4 angles of carbon fiber blanket body arrange hand slash pocket; When carbon fiber charing is processed, Low Temperature Heat Treatment stove is since 163 ℃ of intensifications, intensification 2-6 ℃ per minute, be warming up to 300-320 ℃, then after constant temperature 9-25 minute, be warming up to 330-350 ℃ again, be then cooled to temperature lower than 80 ℃, the import and export of Low Temperature Heat Treatment stove add nitrogen sealing gland.
Hand slash pocket is triangle, and leg-of-mutton two limits overlap with two limits of blanket body; When carbon fiber charing is processed, Low Temperature Heat Treatment stove is since 163 ℃ of intensifications, 3 ℃ of intensifications per minute, be warming up to 301 ℃, then constant temperature is warming up to 340 ℃ again after 9 minutes, is then cooled to temperature lower than 80 ℃, and the import and export of Low Temperature Heat Treatment stove add nitrogen sealing gland.
In the upper strata bag of hand slash pocket, weight block is set; When carbon fiber charing is processed, Low Temperature Heat Treatment stove is since 163 ℃ of intensifications, 4 ℃ of intensifications per minute, be warming up to 302 ℃, then constant temperature is warming up to 350 ℃ again after 25 minutes, is then cooled to temperature lower than 80 ℃, and the import and export of Low Temperature Heat Treatment stove add nitrogen sealing gland.
Claims (3)
1. a Household fire blanket, is characterized in that: comprise carbon fiber blanket body, 2 ~ 4 angles of carbon fiber blanket body arrange hand slash pocket; When carbon fiber charing is processed, Low Temperature Heat Treatment stove is since 163 ℃ of intensifications, intensification 2-6 ℃ per minute, be warming up to 300-320 ℃, then after constant temperature 9-25 minute, be warming up to 330-350 ℃ again, be then cooled to temperature lower than 80 ℃, the import and export of Low Temperature Heat Treatment stove add nitrogen sealing gland.
2. Household fire blanket according to claim 1, is characterized in that: hand slash pocket is triangle, and leg-of-mutton two limits overlap with two limits of blanket body; When carbon fiber charing is processed, Low Temperature Heat Treatment stove is since 163 ℃ of intensifications, 3 ℃ of intensifications per minute, be warming up to 301 ℃, then constant temperature is warming up to 340 ℃ again after 9 minutes, is then cooled to temperature lower than 80 ℃, and the import and export of Low Temperature Heat Treatment stove add nitrogen sealing gland.
3. Household fire blanket according to claim 1, is characterized in that: in the upper strata bag of hand slash pocket, weight block is set; When carbon fiber charing is processed, Low Temperature Heat Treatment stove is since 163 ℃ of intensifications, 4 ℃ of intensifications per minute, be warming up to 302 ℃, then constant temperature is warming up to 350 ℃ again after 25 minutes, is then cooled to temperature lower than 80 ℃, and the import and export of Low Temperature Heat Treatment stove add nitrogen sealing gland.