CN103897542A - 一种车用中涂层涂漆 - Google Patents
一种车用中涂层涂漆 Download PDFInfo
- Publication number
- CN103897542A CN103897542A CN201210574452.1A CN201210574452A CN103897542A CN 103897542 A CN103897542 A CN 103897542A CN 201210574452 A CN201210574452 A CN 201210574452A CN 103897542 A CN103897542 A CN 103897542A
- Authority
- CN
- China
- Prior art keywords
- painting
- japanning
- automobile
- vehicle middle
- agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及化工技术领域,具体地说是一种车用中涂层涂漆。该涂漆由以下组分按重量百分比分:颜填料50-60%,无油醇酸树脂7-9%,环氧树脂溶液8-10%,聚酯树脂5-7%,氨基树脂10-12%,催化剂0.2-0.5%,流平剂0.2-0.5%,消泡剂0.2-0.5%,防沉剂0.2-0.5%。将上述组分通过混合、均匀分散及过滤即制成涂漆产品。本发明的目的是提供一种成本低、使用效果好的车用中涂层涂漆。
Description
技术领域
本发明涉及化工技术领域,具体地说是一种车用中涂层涂漆。
背景技术
中涂层是一种介于底漆涂层和面漆涂层之间的涂层,它不仅可以调整电泳漆表面的缺陷,并且在汽车快速行驶过程中受到外界各种因素对汽车表面所形成的碰撞时,能保护底漆涂层和基材免遭损伤,从而提高底漆涂膜的耐久性。中涂涂料则要求既于底漆、面漆牢固结合、又具有附着力好、硬度高、丰满度好、光度高、耐高温性好、泛黄性小、保光保色性好、与底漆间不咬底、与面漆间不出现浮色,因此使用单一的树脂漆很难达到如此高的要求,而且成本也是高居不下。
发明内容
本发明的目的是提供一种成本低、使用效果好的车用中涂层涂漆。
本发明采用的技术方案是,一种车用中涂层涂漆,由以下组分按重量百分比分:颜填料50-60%,无油醇酸树脂7-9%,环氧树脂溶液8-10%,聚酯树脂5-7%,氨基树脂10-12%,催化剂0.2-0.5%,流平剂0.2-0.5%,消泡剂0.2-0.5%,防沉剂0.2-0.5%。
进一步地说,上述组分通过混合、均匀分散及过滤即制成涂漆产品。
本发明的优点:
1、使产品具备良好的打磨性,光泽高,抗紫外线,流动性,弹性好及耐候性,且有优良的抗石击性能;
2、节约生产成本
具体实施方式
本发明结合以下实施例作进一步描述。
实施例1,一种车用中涂层涂漆,由以下组分按重量百分比分:颜填料50%,无油醇酸树脂7%,环氧树脂溶液8%,聚酯树脂5%,氨基树脂10%,催化剂0.2%,流平剂0.2%,消泡剂0.2%,防沉剂0.2%。上述组分通过混合、均匀分散及过滤即制成涂漆产品。
实施例2,一种车用中涂层涂漆,由以下组分按重量百分比分:颜填料55%,无油醇酸树脂8%,环氧树脂溶液9%,聚酯树脂6%,氨基树脂11%,催化剂0.35%,流平剂0.35%,消泡剂0.35%,防沉剂0.35%。上述组分通过混合、均匀分散及过滤即制成涂漆产品。
实施例3,一种车用中涂层涂漆,其特征在于,由以下组分按重量百分比分:颜填料60%,无油醇酸树脂9%,环氧树脂溶液10%,聚酯树脂7%,氨基树脂12%,催化剂0.5%,流平剂0.5%,消泡剂0.5%,防沉剂0.5%。上述组分通过混合、均匀分散及过滤即制成涂漆产品。
应理解,该实施例仅用于说明本发明而不用于限制本发明的范围。此外,应理解,在阅读了本发明讲授的内容之后,本领域技术人员可以对本发明作各种改动或修改,这些等价形式同样落于本申请所附权利要求书所限定的保护范围之内。
Claims (2)
1.一种车用中涂层涂漆,其特征在于,由以下组分按重量百分比分:颜填料50-60%,无油醇酸树脂7-9%,环氧树脂溶液8-10%,聚酯树脂5-7%,氨基树脂10-12%,催化剂0.2-0.5%,流平剂0.2-0.5%,消泡剂0.2-0.5%,防沉剂0.2-0.5%。
2.根据权利要求1所述的一种车用中涂层涂漆,其特征在于,上述组分通过混合、均匀分散及过滤即制成涂漆产品。