CN103881415A - 一种造纸用荧光增白剂组合物及其制备方法 - Google Patents
一种造纸用荧光增白剂组合物及其制备方法 Download PDFInfo
- Publication number
- CN103881415A CN103881415A CN201410085799.9A CN201410085799A CN103881415A CN 103881415 A CN103881415 A CN 103881415A CN 201410085799 A CN201410085799 A CN 201410085799A CN 103881415 A CN103881415 A CN 103881415A
- Authority
- CN
- China
- Prior art keywords
- compositions
- stock
- fluorescent whitening
- whitening agents
- fluorescent brightener
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明涉及一种造纸用荧光增白剂组合物及其制备方法,造纸用荧光增白剂组合物由以下成分按照重量份组成:荧光增白剂JD-3为0.5~1.0份、湿强剂为0.6~1.0份、分散蓝RD为0.02~0.1份、硫酸钠为0.003~0.02份、水为90~100份。造纸用荧光增白剂组合物的制备方法步骤为物理搅拌,制备得到的造纸用荧光增白剂组合物对纸类的白度值提升高,纸类增白达到相同的白度要求时,可降低荧光增白剂用量,节约成本。
Description
技术领域
本发明涉及荧光增白剂,更具体是涉及一种造纸用荧光增白剂组合物及其制备方法。
背景技术
荧光增白剂俗称白色染料,是一种无色并在紫外光照射下能激发出荧光的有机化合物,它能提高物质的白度和光泽。复配后的荧光增白剂具有降低荧光增白剂的使用量、增强使用后的增白效果等显著优点。
荧光增白剂主要通过化学复配和物理复配这两种方法来达到效果。其中化学复配是将几种结构相似的化合物按一定比较混合后形成复合增白剂;物理复配分为三种:不同荧光增白剂的复配、荧光增白剂与塑料添加剂的复配、荧光增白剂与增感染料的复配。专利CN 102898870 A公开了一种棉布用荧光增白剂,由荧光增白剂BA、分散紫2RL、分散艳蓝E-4R、元明粉混合组成。选择合适的增感染料与荧光增白剂组合,可以提高荧光增白剂的使用效果,达到提高白度、降低荧光增白剂用量的目的。
为了提高纸类的白度值,有必要制造出一种专用于纸类的荧光增白剂组合物。
发明内容
要解决的技术问题:常规的荧光增白剂增白效果差,使用量大的问题。
技术方案:本发明公开了一种造纸用荧光增白剂组合物,由以下成分按照重量份组成:荧光增白剂JD-3为0.5~1.0份、湿强剂为0.6~1.0份、分散蓝RD为0.02~0.1份、硫酸钠为0.003~0.02份、水为90~100份。
造纸用荧光增白剂组合物的制备方法,包括如下步骤将荧光增白剂JD-3为0.5~1.0份、湿强剂为0.6~1.0份、分散蓝RD为0.02~0.1份、硫酸钠为0.003~0.02份、水为90~100份,进行搅拌,搅拌转速为60~90rpm,搅拌时间为0.5~1h,反应温度为室温。搅拌结束后所得溶液即为所需产品。
一种造纸用荧光增白剂组合物,荧光增白剂JD-3优选为0.8份。
一种造纸用荧光增白剂组合物,湿强剂优选为0.8份。
一种造纸用荧光增白剂组合物,所述湿强剂为聚酰胺环氧氯丙烷。
有益效果:本发明制备得到的造纸用荧光增白剂组合物增白效果好,相较于同类增白剂达到相同白度下使用量减少,成本降低。
具体实施方式
实施例1
造纸用荧光增白剂组合物及其制备方法,包括如下步骤:向反应釜中加入荧光增白剂JD-3 0.8kg、湿强剂0.8kg、分散蓝RD0.02kg、硫酸钠0.01kg、水98kg进行搅拌,搅拌转速为60~90rpm时间为0.5~1h,反应温度为室温。搅拌结束后所得溶液即为所需产品。
实施例2
造纸用荧光增白剂组合物及其制备方法,包括如下步骤:向反应釜中加入荧光增白剂JD-3 0.5kg、湿强剂1.0kg、分散蓝RD0.1kg、硫酸钠0.003kg、水90kg进行搅拌,搅拌转速为60~90rpm时间为0.5~1h,反应温度为室温。搅拌结束后所得溶液即为所需产品。
实施例3
造纸用荧光增白剂组合物及其制备方法,包括如下步骤:向反应釜中加入荧光增白剂JD-3 1.0kg、湿强剂0.6kg、分散蓝RD0.02kg、硫酸钠0.02kg、水100kg进行搅拌,搅拌转速为60~90rpm时间为0.5~1h,反应温度为室温。搅拌结束后所得溶液即为所需产品。
将实施例1、实施例2、实施例3制备的造纸用荧光增白剂组合物,用浸染法在2‰(owf)染色深度、浴比1:40的条件下,80℃浸染30分钟,与荧光增白剂JD-3染纸的结果如下表所示。
荧光增白剂JD-3 | 实施例1 | 实施例2 | 实施例3 | |
CIE白度值 | 125.6 | 143.8 | 139.2 | 141.3 |
从上表可知,本发明的造纸用荧光增白剂组合物对纸类的白度值提升高,使用效果优于荧光增白剂JD-3。
Claims (5)
1.一种造纸用荧光增白剂组合物,其特征在于由以下成分按照重量份组成:荧光增白剂JD-3为0.5~1.0份、湿强剂为0.6~1.0份、分散蓝RD为0.02~0.1份、硫酸钠为0.003~0.02份、水为90~100份。
2.造纸用荧光增白剂组合物的制备方法,其特征在于包括如下步骤:将荧光增白剂JD-3 0.5~1.0份、湿强剂0.6~1.0份、分散蓝RD0.02~0.1份、硫酸钠0.003~0.02份、水90~100份加入反应釜进行搅拌,搅拌转速为60~90rpm时间为0.5~1h,反应温度为室温,搅拌结束后所得溶液即为所需产品。
3.根据权利要求1所述的一种造纸用荧光增白剂组合物,其特征在于荧光增白剂JD-3为0.8份。
4.根据权利要求1所述的一种造纸用荧光增白剂组合物,其特征在于湿强剂为0.8份。
5.根据权利要求1所述的一种造纸用荧光增白剂组合物,其特征在于所述湿强剂为聚酰胺环氧氯丙烷。