CN103849304A - 一种含没食子酸的烘漆及其制备方法 - Google Patents
一种含没食子酸的烘漆及其制备方法 Download PDFInfo
- Publication number
- CN103849304A CN103849304A CN201210520199.1A CN201210520199A CN103849304A CN 103849304 A CN103849304 A CN 103849304A CN 201210520199 A CN201210520199 A CN 201210520199A CN 103849304 A CN103849304 A CN 103849304A
- Authority
- CN
- China
- Prior art keywords
- paint
- baking
- gallic acid
- drying
- preparation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种含没食子酸的烘漆及其制备方法,它主要包括。苯甲酸改性蓖麻油醇酸树脂和白色氨基快干烘漆。该漆用于自行车、汽车、仪器仪表,机电设备等表面,于120℃烘烤1小时,干燥可得到满意漆膜。漆膜只需在100℃烘烤10分钟之内完全干燥,光泽可达95%以上,漆膜丰满平滑,光亮坚硬,该产品具有良好的理化性能、装饰性能和储存稳定性。因此是有发展前途的新品种。
Description
技术领域
本发明属于防腐涂料技术领域,涉及一种含没食子酸的烘漆及其制备方法。
背景技术
防腐涂料是现代工业、交通、能源、海洋工程等部门应用极为广泛的一种涂料。按其涂料膜层的耐腐蚀程度和使用要求,通常将防腐蚀涂料分为通用型和重防腐型两类。根据使用环境腐蚀介质的情况选用不同类型的防腐蚀涂料。在一般大气环境的腐蚀条件下,如机床、汽车、铁路车辆、工程机械等行业,常采用通用型防腐蚀涂料,此时还要求涂层具有较高的装饰功能;在工业或海洋性大气腐蚀环境条件下,如化工、石油化工、冶金、海洋工程等行业,多采用重防腐蚀涂料。防腐涂料在我国涂料工业中占有重要地位,在涂料工业中所占的比例已经位居前列。近年来,我国在建筑、交通运输、石化、水电以及海洋工程等众多领域,都出现了飞速增长,进而带动了相关配套产品需求的快速增长,我国防腐涂料市场也出现了喜人的局面,市场规模已经仅次于建筑涂料而位居第二位。
氨基醇酸树脂涂料应用始于1940年。用氨基树脂与不干性醇酸树脂相配合,制得的氨基醇酸涂料,具有良好的综合性能。漆膜外观平整、光滑、丰满度好,在轻工、机械、汽车、仪器、仪表、五金工具等涂装中占有重要的比例,而且价格适中。传统的氨基醇酸烘漆需在120℃/2小时的条件下干燥成膜,因此氨基烘漆用户成了耗能之大户;且烘烤温度高,时间长,导致漆膜泛黄表面产生针孔等弊病。目前涂料工业正在开发低温烘烤体系如低温快干氨基烘漆,它能降低烘烤温度,从120℃/2小时降到100戈/20分钟,可节约能源50%左右。因此是有发展前途的新品种。
发明内容
一种含没食子酸的烘漆,其特征在于它是有下述重量份数的原料组成:
1)、苯甲酸改性蓖麻油醇酸树脂:
2)、白色氨基快干烘漆:
本发明优选含没食子酸的烘漆,其特征在于它是有下述重量份数的原料组成:
1)、苯甲酸改性蓖麻油醇酸树脂:
2)、白色氨基快干烘漆:
该漆用于自行车、汽车、仪器仪表,机电设备等表面,于120℃烘烤1小时,干燥可得到满意漆膜。
该漆在G B 1727-79规定的条件下,漆膜只需在100℃烘烤10分钟之内完全干燥,光泽可达95%以上,漆膜丰满平滑,光亮坚硬,该产品具有良好的理化性能、装饰性能和储存稳定性。
本发明公开的含没食子酸的烘漆技术要求指标:
1漆膜颜色及外观 符合标准及色差范围,平整光滑
2粘度(涂-4杯),S调合漆:120-160/磁漆:80-120
3细度,um≤调合漆35
磁漆20
4遮盖力 符合国家标准
5干燥时间,h≤表干 调合漆:8/磁漆:8
实干 调合漆:24/磁漆:15
6光泽,%≥调合漆:80/磁漆:85
7硬度,≥调合漆:0.2/磁漆:0.25
8附着力,级≤2
9柔韧性,mm 1
10 VOC含量(按GB18581-2001)≤400(GB18581-2001标准为≤550)
2、防腐漆的技术指标
项目 | 指标 |
基料 | 特种合成树脂 |
颜色 | 灰色、棕色、淡色、蓝色等 |
细度 | 25um |
黏度(斯托默黏度计) | ≥60KU |
喷涂黏度(涂-4杯/23℃) | 20-30秒 |
淋涂黏度(涂-4杯/23℃) | 30-40秒 |
稀释剂 | 石油二甲苯 |
理论消耗量 | 淋涂湿膜110-125g/m2 |
干膜厚度 | 40um |
干燥 | 板温130℃烘3-4分钟 |
闪点(GB/T 5208-1985) | 23.7℃以上 |
密度(GB/T 6705-1986) | 1.5g±0.1/ml,20℃ |
固体含量(GB/T 1725-19**) | 70±2% |
交货包装 | 250KG/铁桶 |
贮存 | 室温下12个月 |
具体实施方式
下面结合实施例,对本发明进一步说明,下述实施例是说明性的,不是限定性的,不能以下述实施例来限定本发明的保护范围。以下实施例中的“份”指的是公斤或克,根据实际生产的情况加以选择。其中所用到的原料均有市售。
实施例1
1)、苯甲酸改性蓖麻油醇酸树脂:
2)、白色氨基快干烘漆:
该漆用于自行车、汽车、仪器仪表,机电设备等表面,于120℃烘烤1小时,干燥可得到满意漆膜。
实施例2
1)、苯甲酸改性蓖麻油醇酸树脂:
2)、白色氨基快干烘漆:
该漆用于自行车、汽车、仪器仪表,机电设备等表面,于120℃烘烤1小时,干燥可得到满意漆膜。
Claims (2)