CN103820787B - A kind of antirust agent containing PERFORMANCE OF MODIFIED VERMICULITE powder - Google Patents
A kind of antirust agent containing PERFORMANCE OF MODIFIED VERMICULITE powder Download PDFInfo
- Publication number
- CN103820787B CN103820787B CN201410057002.4A CN201410057002A CN103820787B CN 103820787 B CN103820787 B CN 103820787B CN 201410057002 A CN201410057002 A CN 201410057002A CN 103820787 B CN103820787 B CN 103820787B
- Authority
- CN
- China
- Prior art keywords
- parts
- vermiculite powder
- modified vermiculite
- film
- performance
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of antirust agent containing PERFORMANCE OF MODIFIED VERMICULITE powder, it is prepared by the raw materials in: Oleum Ricini 80 100 parts, barium mahogany sulfonate 58 parts, ferrocene 13 parts, polyisobutylene 0.8 1.0 parts, Bitertanol 0.5 1.0 parts, ammonium benzoate 12 parts, fatty acid amide 58 parts, aluminium stearate 8 10 parts, 2 aminoethyl 17 alkenyl imidazolines 0.8 1.2 parts, decyl primary amine 12 parts, alkyl zinc dithiophosphate 13 parts, sodium citrate 58 parts, phosphoric acid 8 10 parts, dodecylbenzene sodium sulfonate 24 parts, Polyethylene Glycol 23 parts, film-forming resin 56 parts, lanoline 35 parts, 1, 3 1,3-propanedicarboxylic acid morpholines 35 parts, 58 parts of PERFORMANCE OF MODIFIED VERMICULITE powder.The present invention, by adding PERFORMANCE OF MODIFIED VERMICULITE powder, adjusts formula, prepares a kind of antirust agent with good volatile rust prevention effect, and the antirust agent of the present invention has superior rustless property, easy to use, and production technology is simple.
Description
Technical field
The present invention relates to metal rust preventing technical field, particularly relate to a kind of antirust agent containing PERFORMANCE OF MODIFIED VERMICULITE powder.
Background technology
Metal processing piece is during production and processing and transport, it is easy to get rusty, and needs to use antirust oil at gold
Metal surface forms thin film, prevents the chemicals of corrosion of metal.Machinery run and storage in be difficult to not with sky
Oxygen, dampness or the contact of other Korrosionsmedium in gas, these materials will occur electrochemical corrosion in metal surface
And get rusty, corrosion to be prevented must stop above material to contact with metal.Antirust agent belongs to the one of antirust product.
But, some workpiece has the aperture of elongate curved, or has narrow thin blind hole, and often oiling is also difficult to antirust,
If just can complete rust preventing easily with vapor phase inhibitor.In fact, vapor phase inhibitor is a kind of active
Rush-resisting material, as long as sealed environment is permitted, antirust agent also exists, antirust state just can be continued by he, he
Being not desired to antirust oil and coating, breakdown of coating antirust function just loses.Therefore, its corrosion protection phase is very
For a long time, in military affairs conventional it to make weapon antirust, the longest rust-proof life is up to 12-20.Its use is protected and goes
Except very convenient, as long as workpiece is put together with it, add the sealings such as plastic bag and just complete corrosion protection,
Open sealing bag during removal, take out and just can use.The purposes of vapor phase inhibitor and consumption will be increasing, can
With it is envisioned that in the near future, one of vapor phase inhibitor main rush-resisting material that can become iron and steel.
Summary of the invention
It is an object of the invention to overcome the deficiencies in the prior art, it is provided that one have good volatile rust prevention effect,
Superior rustless property, the antirust agent that easy to use, production technology simply contains PERFORMANCE OF MODIFIED VERMICULITE powder.
The present invention adopts the following technical scheme that to achieve these goals
A kind of antirust agent containing PERFORMANCE OF MODIFIED VERMICULITE powder, is prepared by the raw materials in: Oleum Ricini 80-100
Part, barium mahogany sulfonate 5-8 part, ferrocene 1-3 part, polyisobutylene 0.8-1.0 part, Bitertanol 0.5-1.0
Part, ammonium benzoate 1-2 part, fatty acid amide 5-8 part, aluminium stearate 8-10 part, 2-aminoethyl 17 alkene
Base imidazoline 0.8-1.2 part, decyl primary amine 1-2 part, alkyl zinc dithiophosphate 1-3 part, sodium citrate
5-8 part, phosphoric acid 8-10 part, dodecylbenzene sodium sulfonate 2-4 part, Polyethylene Glycol 2-3 part, film-forming resin
5-6 part, lanoline 3-5 part, 1,3-1,3-propanedicarboxylic acid morpholine 3-5 part, PERFORMANCE OF MODIFIED VERMICULITE powder 5-8 part；
Described film-forming resin is prepared from by the raw material of following weight portion: Colophonium 5-8 part, carbamide 2-5 part,
Zinc powder 1-2 part, dimethicone 3-5 part, liquefied petrolatum 15-18 part, 3-aminopropyl trimethoxysilane
3-5 part, acetyl tributyl citrate three ester 10-15 part, epoxidized linseed oil 10-13 part, dimethylbenzene 10-15 part, poly-
Vinyl alcohol 5-8 part.
The preparation method of described PERFORMANCE OF MODIFIED VERMICULITE powder is: by Vermiculitum at 400-500 DEG C after roasting 3-4 hour,
Clay into power, with 10-15% hydrogen peroxide dipping 3-5 hour, deionized water wash, dry, add wherein
Be equivalent to the chlorination stone of the sodium laurylsulfate of its weight 1-2%, the ethyl α-cyanoacrylate of 2-3%, 1-2%
Wax, the cross-linking agent TAC of 1-2%, high speed 4500-4800 rev/min stirs 20-30 minute, dries and pulverized
200-400 mesh sieve,.
The preparation method of the described antirust agent containing PERFORMANCE OF MODIFIED VERMICULITE powder, including following preparation process:
(1) be prepared as film resin: by dimethicone, liquefied petrolatum, 3-aminopropyl trimethoxysilane,
Acetyl tributyl citrate three ester, epoxy soybean oil, dimethylbenzene, polyvinyl alcohol add rustless steel by above-mentioned weight ratio
Reactor, is warming up to 100-115 DEG C, stirring, adds remaining raw material being prepared as film resin, mixing, then
With the ramp of 30-40 DEG C/h to 200-220 DEG C, after 1-2 hour, stop heating, put to dilution still,
It is cooled to 60-75 DEG C, obtains film-forming resin；
(2) film-forming resin and other each raw materials of step (1) being prepared are mixed by above-mentioned weight ratio,
Stir at 80-100 DEG C 30-40 minute, after being then incubated 1-2 hour, cooling,.
Compared with the prior art, beneficial effects of the present invention is as follows:
The present invention, by adding PERFORMANCE OF MODIFIED VERMICULITE powder, adjusts formula, and preparation one has good volatile rust prevention effect
Antirust agent, the antirust agent of the present invention has superior rustless property, easy to use, and production technology is simple.
Detailed description of the invention
Below in conjunction with embodiment, the invention will be further described.
Embodiment:
A kind of antirust agent containing PERFORMANCE OF MODIFIED VERMICULITE powder, is prepared by the raw materials in: Oleum Ricini 100 parts,
Barium mahogany sulfonate 6 parts, ferrocene 2 parts, polyisobutylene 0.8 part, Bitertanol 0.7 part, ammonium benzoate
2 parts, fatty acid amide 7 parts, aluminium stearate 8 parts, 2-aminoethyl 17 alkenyl imidazoline 0.9 part, decane
Base primary amine 2 parts, alkyl zinc dithiophosphate 2 parts, sodium citrate 6 parts, phosphatase 11 0 part, detergent alkylate
Sodium sulfonate 3 parts, Polyethylene Glycol 3 parts, film-forming resin 5 parts, lanoline 3 parts, 1,3-1,3-propanedicarboxylic acid morpholine 5
Part, 6 parts of PERFORMANCE OF MODIFIED VERMICULITE powder；
Described film-forming resin is prepared from by the raw material of following weight portion: Colophonium 6 parts, 3 parts of carbamide, zinc powder
2 parts, dimethicone 4 parts, liquefied petrolatum 16 parts, 3-aminopropyl trimethoxysilane 4 parts, acetyl lemon
Lemon acid three ester 10 parts, epoxy soybean oil 10 parts, dimethylbenzene 12 parts, polyvinyl alcohol 6 parts.
The preparation method of described PERFORMANCE OF MODIFIED VERMICULITE powder is: by Vermiculitum at 500 DEG C after roasting 3 hours, grinds
End, with 15% hydrogen peroxide dipping 4 hours, deionized water wash, dries, and adds wherein and is equivalent to its weight
The sodium laurylsulfate of 2%, the ethyl α-cyanoacrylate of 2%, the chlorinated paraffin of 1%, the cross-linking agent TAC of 2%,
4500 revs/min are stirred 30 minutes at a high speed, dry and pulverize 200 mesh sieves,.
The preparation method of the described antirust agent containing PERFORMANCE OF MODIFIED VERMICULITE powder, including following preparation process:
(1) be prepared as film resin: by dimethicone, liquefied petrolatum, 3-aminopropyl trimethoxysilane,
Acetyl tributyl citrate three ester, epoxy soybean oil, dimethylbenzene, polyvinyl alcohol add rustless steel by above-mentioned weight ratio
Reactor, is warming up to 100 DEG C, stirring, adds remaining raw material being prepared as film resin, and mixing, then with 30
DEG C/h ramp to 220 DEG C, after 2 hours stop heating, put to dilution still, be cooled to 70 DEG C,
Obtain film-forming resin；
(2) film-forming resin and other each raw materials of step (1) being prepared are mixed by above-mentioned weight ratio, and 100
Stir at DEG C 30 minutes, after being then incubated 2 hours, cooling,.
Test example:
The performance test of antirust agent of the present invention:
Static state does not contact accelerated test
Respectively the present embodiment of 5ml and 10ml is placed in small beaker, by metal testing plate (50mm × 25mm
× 2mm) method that specifies by GB/T4879-1999 processes and is placed on directly over beaker, then will contain
HCO3 -1000mg/L、SO4 2-2500mg/L、Cl-The electrolyte solution of 1500mg/L is put in a large beaker,
Electrolyte solution remains 40 DEG C, is placed in large beaker by the small beaker being placed with the present embodiment, by large beaker and
The metal testing plate of small beaker and surface is all placed in a sealing device, and device upper end arranges an air-vent,
Observe each material under room temperature and the time of corrosion occurs.It addition, do not put antirust agent as blank test.Test knot
Fruit is such as table 1 below:
Table 1 static state does not contact accelerated test result
The antirust agent rust-proof effect of the present invention is obvious as shown in Table 1, all has good to steel class and pyrite
Rust-proof effect.
Claims (1)
1. the antirust agent containing PERFORMANCE OF MODIFIED VERMICULITE powder, it is characterised in that: it is prepared by the raw materials in:
Oleum Ricini 80-100 part, barium mahogany sulfonate 5-8 part, ferrocene 1-3 part, polyisobutylene 0.8-1.0 part,
Bitertanol 0.5-1.0 part, ammonium benzoate 1-2 part, fatty acid amide 5-8 part, aluminium stearate 8-10
Part, 2-aminoethyl 17 alkenyl imidazoline 0.8-1.2 part, decyl primary amine 1-2 part, alkyl dithiophosphoric acid
Zinc 1-3 part, sodium citrate 5-8 part, phosphoric acid 8-10 part, dodecylbenzene sodium sulfonate 2-4 part, poly-second two
Alcohol 2-3 part, film-forming resin 5-6 part, lanoline 3-5 part, 1,3-1,3-propanedicarboxylic acid morpholine 3-5 part, PERFORMANCE OF MODIFIED VERMICULITE
Powder 5-8 part；
Described film-forming resin is prepared from by the raw material of following weight portion: Colophonium 5-8 part, carbamide 2-5 part,
Zinc powder 1-2 part, dimethicone 3-5 part, liquefied petrolatum 15-18 part, 3-aminopropyl trimethoxysilane
3-5 part, acetyl tributyl citrate three ester 10-15 part, epoxidized linseed oil 10-13 part, dimethylbenzene 10-15 part, poly-
Vinyl alcohol 5-8 part；
The preparation method of the described antirust agent containing PERFORMANCE OF MODIFIED VERMICULITE powder, including following preparation process:
(1) be prepared as film resin: by dimethicone, liquefied petrolatum, 3-aminopropyl trimethoxysilane,
Acetyl tributyl citrate three ester, epoxy soybean oil, dimethylbenzene, polyvinyl alcohol add rustless steel by above-mentioned weight ratio
Reactor, is warming up to 100-115 DEG C, stirring, adds remaining raw material being prepared as film resin, mixing, then
With the ramp of 30-40 DEG C/h to 200-220 DEG C, after 1-2 hour, stop heating, put to dilution still,
It is cooled to 60-75 DEG C, obtains film-forming resin；
(2) film-forming resin and other each raw materials of step (1) being prepared are mixed by above-mentioned weight ratio,
Stir at 80-100 DEG C 30-40 minute, after being then incubated 1-2 hour, cooling,；
The preparation method of described PERFORMANCE OF MODIFIED VERMICULITE powder is: by Vermiculitum at 400-500 DEG C after roasting 3-4 hour,
Clay into power, with 10-15% hydrogen peroxide dipping 3-5 hour, deionized water wash, dry, add wherein
Be equivalent to the chlorination stone of the sodium laurylsulfate of its weight 1-2%, the ethyl α-cyanoacrylate of 2-3%, 1-2%
Wax, the cross-linking agent TAC of 1-2%, high speed 4500-4800 rev/min stirs 20-30 minute, dries and pulverized
200-400 mesh sieve,.