CN103818179A - Process for manufacturing glass enamel picture - Google Patents
Process for manufacturing glass enamel picture Download PDFInfo
- Publication number
- CN103818179A CN103818179A CN201410044538.2A CN201410044538A CN103818179A CN 103818179 A CN103818179 A CN 103818179A CN 201410044538 A CN201410044538 A CN 201410044538A CN 103818179 A CN103818179 A CN 103818179A
- Authority
- CN
- China
- Prior art keywords
- glass
- glaze
- picture
- crystal
- glue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a process for manufacturing a glass enamel picture. The process comprises the following steps: firstly, using a piece of tempered glass which is 8-10mm in thickness as a main material; polishing the sides into arc shapes according to different models; spraying sand to the surface of the glass to be in a dull state; subsequently putting a designed fine brushwork line pattern of the same size as a drawing below the glass; sufficiently penetrating the fine brushwork lines on the right surface of the glass through the transparency of the glass so as to inlay wires; adhering the metal wires by using shadowless super glue; solidly integrating the metal wires with the glass; blending pure natural cloisonn glaze and a glue solution; enabling parts with formed patterns to be filled with glaze of different colors; flatting filling other empty parts by using crystal, wherein as the glaze is aqueous glue, the glaze needs to be baked, the baking temperature is within 38-41 DEG C, and preferably the temperature is kept constant for 26-28 hours; finally embedding the glass enamel picture into a metal frame. The process has the advantage that the glass enamel picture is rich and natural in color, can be permanently preserved, and is high in three-dimensional feeling, solid without crushing, good in visual effect.
Description
Technical field
The present invention relates to a kind of method of craft articles, the manufacture craft that specifically glass method thinkling sound draws.
Background technology
In prior art, the word on handicraft or pattern be generally adopt carve, directly write, shell carving or carve and make with feather.Engraving or shell carving complex process, time-consuming, paste feather cost is higher, look also very beautiful although directly write, lack stereoeffect.
Summary of the invention
The manufacture craft that the object of the present invention is to provide a kind of glass method thinkling sound to draw, this manufacture craft is to use the theory of Modern Industry Products development and Design, should adapt to modern way of life and Social Culture in line with Traditional Handcraft Industry, the requirement following the laws of the market economy, utilize modern high tech method and in conjunction with traditional technology, form method thinkling sound's painting making technology flow process a set of novelty, ripe, artistic value, enjoying value, memorial value, place value, the practical value of drawing from truly improving glass method thinkling sound.
The technical scheme adopting is:
The manufacture craft that glass method thinkling sound draws, comprises following process steps:
1, selecting the safety glass that 8-10mm is thick is main material.
2, become circular-arc according to different size edging.
3, glass surface sandblast is to sub-light state.
4, design is completed etc. the Chinese realistic painting line image of large drawing be placed on below glass, utilize the transparency of glass, fully Chinese realistic painting lines thoroughly in glass front, so that the use of wiring inlay.
5, adopt and be stained with alloy threads without shadow seccotine, make wire and glass firm in one.
6, select pure natural cloisonne enamel glaze and liquid glue to be in harmonious proportion, the part that forms pattern is dosed to the glaze of different colours, all the other vacant lots are filled and led up with crystal.
7, fill out glaze property of water-bearing glue, therefore need baking, baking temperature, between 38-41 degree Celsius, keeps constant temperature to be advisable at 26~28 hours.
8, select 7336A type crystal resin and ethyl ketone and two stars pair to plug with molten metal the blending ratio by 1: 0.01: 0.03, fully stir and make it to be coated in glass surface after fusion, be covered with again the sub-light film of import, on film, push away away bubble levelling with rolling son, after crystal liquid forms solid, carry out again polishing grinding.
Crystal processing is all carried out by program like this in the back side of 9, drawing.
10, two faces of glass like this have formed the dim artistic effect of glass of the clear wash rice of picture.
11, framework selects 2: the gold-plated pipe of stainless steel of 3cm, by picture specification, carries out seamless sub-arc welding, makes it surface, the back side, smooth-sided compression candles without breakpoint.
12, glass enamel is drawn and is embedded in metal framework, with the neutral copper silicon weather proofing sealant of N-39 type, frame and picture are sealed to be stained with and consolidate.
13, can erect and form glass enamel double-faced picture until within 24 hours, being stained with after closing.
The present invention has the following advantages:
(1) color is enriched nature: it is to be made up of the color of the versicolor glaze of occurring in nature itself that glass method thinkling sound draws, and color and luster is soft, natural, true, original.Picture color transition nature, just like the picture effect as photo.
(2) persistence: through special crystal frosted technical finesse, this picture decades, upper a century also can not fade, year picture is still aobvious outmoded for a long time, and there is acid and alkali-resistance, antiultraviolet, the feature such as can clean.
(3) picture smooth: after special exclusive refrigeration technique is processed, picture is as crystal, like glittering and translucent amber.There is extremely strong innervation, third dimension.
(4) solid not broken: product adopts special tire plate and moulding bed and unique fork-join technology, glaze and wire are organically synthesized together by the infiltration of special crystal liquid, strengthened integral hardness, picture core can not rupture and can not occur the phenomenon of fracture yet, is applicable to transporting for long-distance.
(5) be not water funkly afraid of humidity: be that one is synthetic owing to drawing core and tire plate, directly to be contained in picture frame, to make finished product and draw, with air insulated, do not need mounting glass, unique material and technique make picture core not water funk, be not afraid of humidity, be applicable to very much the special occasions such as luxurious bath center, Saunas clinic, Household bathroom and decorate.
(6) good visual effect: smooth wire lines, rough natural colored glaze, naturally abundant color, mixes various patterns, and every width picture all makes people stop to look around, noticeable, has extraordinary visual effect.
(7) expressive force is strong: it is in extensive range that product is got figure, relates to works modelled after an antique, famous person's calligraphy and painting, as the works of the various styles such as oil painting, traditional Chinese Painting, photo, Chinese realistic painting, freehand brushwork.
The specific embodiment
The manufacture craft that glass method thinkling sound draws, specifically comprises following process steps:
1, selecting the safety glass that 9mm is thick is main material.
2, become circular-arc according to different size edging.
3, glass surface sandblast is to sub-light state.
4, design is completed etc. the Chinese realistic painting line image of large drawing be placed on below glass, utilize the transparency of glass, fully Chinese realistic painting lines thoroughly in glass front, so that the use of wiring inlay.
5, adopt and be stained with and close aluminum oxide wire without shadow seccotine, make aluminum oxide wire and glass firm in one, the specification of aluminum oxide wire is 1.0 × 0.5mm.
6, select pure natural cloisonne enamel glaze and liquid glue to be in harmonious proportion, the part that forms pattern is dosed to the glaze as shown in the figure of different colours, all the other vacant lots are filled and led up with crystal.(fill and lead up technique and see the 8th article)
7, fill out glaze property of water-bearing glue, therefore need baking, baking temperature is set as 40 degrees Celsius, keeps constant temperature 27 hours.
8, select 7336A type crystal resin and ethyl ketone and two stars pair to plug with molten metal the blending ratio by 1: 0.01: 0.03, fully stir and make it to be coated in glass surface after fusion, be covered with the sub-light film of import again, on film, push away away bubble levelling with rolling son, after 1 hour, crystal liquid forms solid and carries out polishing grinding again.
Crystal processing is all carried out by program like this in the back side of 9, drawing.
10, two faces of glass like this have formed the dim artistic effect of glass of the clear wash rice of picture.
11, framework selects 2: the gold-plated pipe of stainless steel of 3cm, by picture specification, carries out seamless sub-arc welding, makes it surface, the back side, smooth-sided compression candles without breakpoint.
12, glass enamel is drawn and is embedded in metal framework, with the neutral copper silicon weather proofing sealant of N-39 type, frame and picture are sealed to be stained with and consolidate.
13, can erect and form glass enamel double-faced picture until within 24 hours, being stained with after closing.(office building screen used is drawn for this most applicable hotel of technique, hotel.The 25th floors little banquet hall collections in Wanda residence, the present Tianjin of finished product).
Claims (1)
1. the manufacture craft that glass method thinkling sound draws, is characterized in that comprising following processing step:
A, to select the safety glass that 8-10mm is thick be main material;
B, become circular-arc according to different size edging;
C, glass surface sandblast are to sub-light state;
D, design is completed etc. the Chinese realistic painting line image of large drawing be placed on below glass, utilize the transparency of glass, fully Chinese realistic painting lines thoroughly in glass front, so that the use of wiring inlay;
E, employing are stained with alloy threads without shadow seccotine, make wire and glass firm in one;
F, select pure natural cloisonne enamel glaze and liquid glue to be in harmonious proportion, the part of formation pattern is dosed to the glaze of different colours, all the other vacant lots are filled and led up with crystal;
G, the glaze property of water-bearing glue of filling out, therefore need baking, baking temperature, between 38-41 degree Celsius, keeps constant temperature to be advisable at 26~28 hours;
H, select 7336A type crystal resin and ethyl ketone and two stars are two plugs with molten metal the blending ratio by 1: 0.01: 0.03, fully stir and make it to be coated in glass surface after fusion, be covered with again the sub-light film of import, on film, push away away bubble levelling with rolling son, after crystal liquid forms solid, carry out again polishing grinding;
Crystal processing is all carried out by program like this in the back side of I, picture;
Two faces of J, glass like this have formed the dim artistic effect of glass of the clear wash rice of picture;
K, framework select 2: the gold-plated pipe of stainless steel of 3cm, by picture specification, carries out seamless sub-arc welding, makes it surface, the back side, smooth-sided compression candles without breakpoint;
L, glass enamel is drawn and is embedded in metal framework, with the neutral copper silicon weather proofing sealant of N-39 type, frame and picture are sealed to be stained with and consolidate;
M, can erect and form the manufacture craft that glass enamel is drawn until within 24 hours, being stained with after closing.