CN103779585B - Water filling magnesium alloy battery - Google Patents
Water filling magnesium alloy battery Download PDFInfo
- Publication number
- CN103779585B CN103779585B CN201210424688.7A CN201210424688A CN103779585B CN 103779585 B CN103779585 B CN 103779585B CN 201210424688 A CN201210424688 A CN 201210424688A CN 103779585 B CN103779585 B CN 103779585B
- Authority
- CN
- China
- Prior art keywords
- magnesium alloy
- addition
- magnesium
- water filling
- battery
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of water filling magnesium alloy battery, comprises anode, catalyst and outer protection box hat that magnesium alloy is made.In this magnesium alloy, the addition of aluminium element is 0.2-10.0wt%, and the addition of Zn-ef ficiency is 0.2-3.0wt%, and the addition of manganese element is 0.1-3.0wt%, and all the other are magnesium elements.Under the condition of storage that water filling magnesium alloy battery of the present invention seals in drying, the storage life can reach more than 20 years.
Description
Technical field
The present invention relates to cell art, specifically a kind of water filling magnesium alloy battery.
Background technology
Magnesium alloy electrode potential compared with kirsite is lower, electrochemical equivalent is less and conductivity is better, is more preferably battery anode material.But, because magnesium alloy electrochemical properties is too active, therefore series of negative effect (such as: voltage delay and the perishable perforation of housing etc.) can be produced when being used as battery anode material.In most of electrolyte solution, magnesium alloy dissolution velocity is very fast, produces a large amount of hydrogen, causes anode faradic efficiency to reduce.In addition, the existence of impurity element in magnesium alloy, accelerates magnesium alloy from corrosion reaction speed, generates and has certain thickness Mg (OH)
2passivating film, seriously inhibits magnesium alloy anode active dissolution.Therefore, the utilance improving magnesium-alloy anode material is focus and the difficult point of current magnesium alloy battery research, and its key problem in technology solves the contradictory relation between magnesium alloy anode activation and passivation.
Summary of the invention
An object of the present invention is to provide a kind of water filling magnesium alloy battery anode material, by measures such as material alloys modification and battery structure rational Design on Plane, solve the technical bottleneck of the water filling perishable perforation of magnesium alloy battery anode and voltage delay.
Water filling magnesium alloy battery of the present invention, comprises anode, catalyst and outer protection box hat that magnesium alloy is made.In described magnesium alloy, the addition of aluminium element is 0.2-10.0wt%, and the addition of Zn-ef ficiency is 0.2-3.0wt%, and the addition of manganese element is 0.1-3.0wt%, and all the other are magnesium elements.
Described catalyst is Powdered, is selected from magnesium chloride, magnesium nitrate, activation electrolytic manganese dioxide, water-absorbing resin, one or more in active carbon and sodium chloride.
A kind of preferred catalyst, comprise 1-10wt% magnesium chloride, 1-10wt% magnesium nitrate, 1-15wt% activation electrolytic manganese dioxide, 1-15wt% water-absorbing resin, 5-25wt% sodium chloride, all the other are active carbon.
The beneficial effect that technical solution of the present invention realizes:
Water filling magnesium alloy battery of the present invention has excellent storge quality, and under the condition of drying sealing, the storage life can reach more than 20 years.
Embodiment
Below describe technical scheme of the present invention in detail.
Embodiment 1
As the embodiment of battery of the present invention; comprise anode, catalyst, outer protection box hat, the material of described anode is magnesium alloy, and in described magnesium alloy, the addition of aluminium element is 3.0wt%; the addition of Zn-ef ficiency is 0.8wt%, and the addition of manganese element is 0.3wt%.
In the present embodiment, in described catalyst, content of magnesium chloride is 5wt%, and magnesium nitrate content is 5wt%, and activation electrolytic manganese dioxide content is 5wt%, and water-absorbing resin content is 5wt%, and sodium chloride content is 10wt%, and all the other 70wt% are active carbon.
Battery storage is after 12 months, and the discharge capacity of battery of the present invention, in average discharge times, is not less than 98% of initial period discharge capacity.
Embodiment 2
As the embodiment of battery of the present invention; comprise anode, catalyst, outer protection box hat, the material of described anode is magnesium alloy, and in described magnesium alloy, the addition of aluminium element is 0.5wt%; the addition of Zn-ef ficiency is 0.5wt%, and the addition of manganese element is 2.0wt%.
In the present embodiment, in described catalyst, content of magnesium chloride is 10wt%, and magnesium nitrate content is 10wt%, and activation electrolytic manganese dioxide content is 5wt%, and water-absorbing resin content is 10wt%, and sodium chloride content is 15wt%, and all the other 50wt% are active carbon.
Battery storage is after 12 months, and the discharge capacity of battery of the present invention, in average discharge times, is not less than 98% of initial period discharge capacity.
Embodiment 3
As the embodiment of battery of the present invention; comprise anode, catalyst, outer protection box hat, the material of described anode is magnesium alloy, and in described magnesium alloy, the addition of aluminium element is 6.5wt%; the addition of Zn-ef ficiency is 2.0wt%, and the addition of manganese element is 0.3wt%.
In the present embodiment, in described catalyst, content of magnesium chloride is 5wt%, and magnesium nitrate content is 5wt%, and activation electrolytic manganese dioxide content is 10wt%, and water-absorbing resin content is 5wt%, and sodium chloride content is 10wt%, and all the other 65wt% are active carbon.
Battery storage is after 12 months, and the discharge capacity of battery of the present invention, in average discharge times, is not less than 98% of initial period discharge capacity.
Claims (2)
1. a water filling magnesium alloy battery, comprise anode, catalyst and outer protection box hat that magnesium alloy is made, it is characterized in that the addition of aluminium element in described magnesium alloy is 0.2-10.0wt%, the addition of Zn-ef ficiency is 0.2-3.0wt%, the addition of manganese element is 0.1-3.0wt%, and all the other are magnesium elements;
Described catalyst comprises 1-10wt% magnesium chloride, 1-10wt% magnesium nitrate, 1-15wt% activation electrolytic manganese dioxide, 1-15wt% water-absorbing resin and 5-25wt% sodium chloride.
2. water filling magnesium alloy battery according to claim 1, is characterized in that described catalyst is Powdered.