CN103773638A - Cleaning agent for solar panel - Google Patents
Cleaning agent for solar panel Download PDFInfo
- Publication number
- CN103773638A CN103773638A CN201410023991.5A CN201410023991A CN103773638A CN 103773638 A CN103773638 A CN 103773638A CN 201410023991 A CN201410023991 A CN 201410023991A CN 103773638 A CN103773638 A CN 103773638A
- Authority
- CN
- China
- Prior art keywords
- cleaning agent
- solar cell
- cell board
- board cleaning
- component
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a cleaning agent for a solar panel. The cleaning agent comprises the following components by mass percent: 10 to 30 percent of surface active agent, 10 to 30 percent of solvent, 0.5 to 5 percent of electrostatic resisting agent, 10 to 30 percent of antifreezing agent, 2 to 5 percent of softening agent and 5 to 20 percent of oil removing agent. The solar panel is conventionally cleaned manually and rinsed mechanically at present, and the traditional way for cleaning the solar panel has the weaknesses such as high labor cost, large workload, high risk, complexity in operation, halfway cleaning, short washing period and the like. The cleaning agent for the solar panel is strong in decontamination capacity, anti-electrostatic, wide in environmental applicability, good in stability, low-foam, nondestructive for the glass surface, free from peculiar smell, toxic-free, corrosiveless, inflammable, unexplosive and free from polluting the environment.
Description
Technical field
The present invention relates to clean-out system, refer to particularly a kind of solar cell board cleaning agent.
Background technology
As the cleaning new energy of a kind of green, environmental protection, photovoltaic generation is widely used at present, and has development space widely.Solar panel is the core in photovoltaic generating system, and surface protection is carried out by one deck toughened glass in its surface, and the clean-up performance of glass surface directly determines cell panel generating efficiency simultaneously.Because the glass surface of cell panel and air friction produce static electric charge, can be in its surface adsorption the dirt such as dust, sand and dust, birds droppings, shellac, greasy dirt.After glass surface is covered by dirt, can reduce the photoirradiation amount that assembly receives, affect system efficiency, reduce generated energy; Part is covered and can be caused hot spot effect, causes generated energy loss, affects the life-span of assembly, causes the problems such as potential safety hazard simultaneously.Therefore,, in order to guarantee daily regulation generated energy and component safety, should at any time the surface of battery component be cleaned, be safeguarded.
It is reported, the technology of the clean aspect of current each photo-voltaic power generation station solar panel is seriously deficient, reply market is required does not also have efficiently solution of specialty, the battery component that causes whole photo-voltaic power generation station in hysteretic state, has hindered the optimum regime of photo-voltaic power generation station cell panel generating aspect generating efficiency, cleaning.
What Vehicles Collected from Market adopted is artificial clean and machinery rinses, the subject matter of existence has that cost of labor is high, workload large, dangerous high, complicated operation, clean not thoroughly, the shortcoming such as cleaning interval interval is short.Clean at present the main ortho-water that uses as cleaning medium, the poor effect of cleaning: 1, ortho-water cannot effectively be removed the electric charge of gathering on glass, only can wash out the floating dust of glass surface.For superfine little dust, cannot wash due to the adsorption of electric charge.2, ortho-water cannot dissolve birds droppings, shellac, greasy dirt, more difficult cleaning.3, in ortho-water, contain several mineral materials ion (water body overall content of mineral substances in the Northwest's is higher), cleaning later can be in the residual spot of glass surface, causes transmittance to decline, thereby affects generating efficiency.
Summary of the invention
The object of the invention is to overcome the weak point of above-mentioned existing background technology, and a kind of solar cell board cleaning agent is provided, for cleaning of photo-voltaic power generation station solar cell sheet glass.
The object of the invention is to reach by following technical solution: solar cell board cleaning agent, it comprises the component of following mass percent: tensio-active agent 10-30%; Solvent 10-30%; Static inhibitor 0.5-5%; Frostproofer 10-30%; Tenderizer 2-5%; Removers 5-20%.
The preferred technical scheme of the present invention: solar cell board cleaning agent, it comprises the component of following mass percent: tensio-active agent 15-20%; Solvent 20-30%; Static inhibitor 2-5%; Frostproofer 15-25%; Tenderizer 2-5%; Removers 15-20%.
The good technical scheme of the present invention: solar cell board cleaning agent, it comprises the component of following mass percent: surface active agent 15-20%; Solvent 20-25%; Static inhibitor 2-3%; Frostproofer 20-25%; Tenderizer 3-5%; Removers 15-20%.
The better technical scheme of the present invention: solar cell board cleaning agent, it comprises the component of following mass percent: tensio-active agent 20%; Solvent 30%; Static inhibitor 2%; Frostproofer 20%; Tenderizer 3%; Removers 15%.
Described tensio-active agent is selected from following component: the ethylene oxide adduct of alpha-sulfo monocarboxylic acid, Sodium dodecylbenzene sulfonate, branch-alkylbenzene sulfonate, sodium alkyl benzene sulfonate, alkylphenol polyoxyethylene, high-carbon fatty alcohol polyoxyethylene ether, polyoxyethylene carboxylate, fatty acid methyl ester ethoxylate, polypropylene glycol, the ionogenic surfactant of polyoxyethylene.Wherein, described tensio-active agent comprises anion surfactant and nonionogenic tenside, both by a certain percentage mixed tensio-active agent there is good penetrating quality and synergy, solar components glass surface dust granule is had to stronger seepage force, dispersion force.
Described solvent is selected from following component: ethanol, methyl alcohol, diethanolamine, trolamine, deionized water.Described solvent is mainly used in improving the intermiscibility of each compatibility component, and birds droppings, shellac are had to solvency action.
Described static inhibitor is selected from following component: glycerol, fatty acid methyl ester sulfonate.Described static inhibitor is mainly used in reducing glass surface resistance, prevents accumulation of static electricity.
Described frostproofer is selected from following component: ethylene glycol, propylene glycol, diethylene glycol monobutyl ether, diethylene glycol dimethyl ether.Described frostproofer is mainly used in preventing under low temperature environment, and scavenging solution freezes.
Described tenderizer is selected from following component: sodium phosphate, EDTA-4Na, ethylenediamine tetraacetic acid (EDTA).Described tenderizer energy and alkalimetal ion etc. form stable water soluble complex, prevent water tank and cleaning means fouling.
Described removers is selected from following component: Virahol, acetone, butanone.Described removers is strong to the solvency power of lipophilicity substance, can remove the greasy dirt on glass surface.
In such scheme, material component all can be obtained by market.
The invention has the advantages that: this clean-out system is added in water and can obtain stronger soil removability, can effectively remove fast the dirts such as the dust, sand and dust, birds droppings, shellac, greasy dirt of solar components glass; The glass surface that utilizes this clean-out system to clean has certain antistatic effect, can reduce the gathering of static electric charge, thereby reduces the absorption to dust; This clean-out system has wide in range thermal adaptability, can under low temperature environment, use, and can prevent that glass surface and cleaning means from freezing, and can round-the-clockly operate, thereby increase work efficiency greatly; This scavenging solution contains tenderizer, can form stable water soluble complex with mineral ion etc., prevents water tank and cleaning means fouling, can extend the work-ing life of water tank and cleaning means, thereby reduce production costs; This scavenging solution steady chemical structure, nonirritant, can long-term storage never degenerate.Overcome adopt artificial clean and cost of labor is high when machinery rinses, workload large, dangerous high, complicated operation, clean not thoroughly, the shortcoming such as cleaning interval interval is short, also improved using ortho-water as cleaning medium the problem of the poor effect of cleaning.
Embodiment
Below in conjunction with specific embodiment, the present invention is described in further detail:
Divide A, B group to carry out simultaneous test below, wherein A group, using ortho-water as cleaning medium, is carried out the cleaning of solar panel, and B group is that this solar cell board cleaning agent is added in water, carry out the cleaning of solar panel, A group contrasts in table 1 with the cleaning performance of B group:
The cleaning performance contrast table of table 1 solar panel
As shown in Table 1:
A group is with using ortho-water as cleaning medium, and the poor effect of cleaning: 1, ortho-water cannot effectively be removed the electric charge of gathering on glass, only can wash out the floating dust of glass surface.For superfine little dust, cannot wash due to the adsorption of electric charge.2, ortho-water cannot dissolve birds droppings, shellac, greasy dirt, more difficult cleaning.3, in ortho-water, contain several mineral materials ion (water body overall content of mineral substances in the Northwest's is higher), cleaning later can be in the residual spot of glass surface, causes transmittance to decline, thereby affects generating efficiency.
B group is that this clean-out system is added in water, can obtain stronger soil removability, can effectively remove fast the dirts such as the dust, sand and dust, birds droppings, shellac, greasy dirt of solar components glass; The glass surface that utilizes this clean-out system to clean has certain antistatic effect, can reduce the gathering of static electric charge, thereby reduces the absorption to dust; This clean-out system has wide in range thermal adaptability, can under low temperature environment, use, and can prevent that glass surface and cleaning means from freezing, and can round-the-clockly operate, thereby increase work efficiency greatly; This scavenging solution contains tenderizer, can form stable water soluble complex with mineral ion etc., prevents water tank and cleaning means fouling, can extend the work-ing life of water tank and cleaning means, thereby reduce production costs; This scavenging solution steady chemical structure, nonirritant, can long-term storage never degenerate.
The specific embodiment of the invention is as follows:
Embodiment 1: solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
Strong, the low bubble of this solar cell board cleaning agent soil removability, to glass surface not damaged, free from extraneous odour, nontoxic, non-corrosiveness.
Embodiment 2: solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, to glass surface not damaged, free from extraneous odour, nontoxic, non-corrosiveness.
Embodiment 3:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
Stronger, the low bubble of this solar cell board cleaning agent soil removability, to glass surface not damaged, free from extraneous odour, nontoxic, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 4:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, there is broader environmental compatibility, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 5:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, there is broader environmental compatibility, satisfactory stability, do not fire not quick-fried, free from environmental pollution.
Embodiment 6:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, there is broader environmental compatibility, do not fire not quick-fried, free from environmental pollution.
Embodiment 7:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, have broader environmental compatibility, satisfactory stability, free from extraneous odour, nontoxic, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 8:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, there is broader environmental compatibility, satisfactory stability, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 9:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, nontoxic, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 10:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, free from extraneous odour, nontoxic, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 11:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, free from extraneous odour, nontoxic, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 12:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, nontoxic, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 13:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, have broader environmental compatibility, satisfactory stability.
Embodiment 14:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, it is not quick-fried, free from environmental pollution not fire.Embodiment 15:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, have broader environmental compatibility.
Embodiment 16:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, free from extraneous odour, nontoxic, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 17:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, free from extraneous odour, nontoxic, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 18:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, have broader environmental compatibility, free from extraneous odour, nontoxic, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
Embodiment 19:
Solar cell board cleaning agent comprises the component of following mass percent:
This solar cell board cleaning agent is added in water, carry out the cleaning of solar panel.
This solar cell board cleaning agent soil removability is strong, antistatic, have broader environmental compatibility, free from extraneous odour, nontoxic, non-corrosiveness, do not fire not quick-fried, free from environmental pollution.
The content not being described in detail in this specification sheets belongs to the known prior art of professional and technical personnel in the field.
Claims (10)
1. a solar cell board cleaning agent, it comprises the component of following mass percent: tensio-active agent 10-30%; Solvent 10-30%; Static inhibitor 0.5-5%; Frostproofer 10-30%; Tenderizer 2-5%; Removers 5-20%.
2. solar cell board cleaning agent according to claim 1, is characterized in that: it comprises the component of following mass percent: tensio-active agent 15-20%; Solvent 20-30%; Static inhibitor 2-5%; Frostproofer 15-25%; Tenderizer 2-5%; Removers 15-20%.
3. solar cell board cleaning agent according to claim 1, is characterized in that: it comprises the component of following mass percent: tensio-active agent 15-20%; Solvent 20-25%; Static inhibitor 2-3%; Frostproofer 20-25%; Tenderizer 3-5%; Removers 15-20%.
4. solar cell board cleaning agent according to claim 1, is characterized in that: it comprises the component of following mass percent: tensio-active agent 20%; Solvent 30%; Static inhibitor 2%; Frostproofer 20%; Tenderizer 3%; Removers 15%.
5. according to the solar cell board cleaning agent described in claim 1～4 any one, it is characterized in that: described tensio-active agent is selected from following component: the ethylene oxide adduct of alpha-sulfo monocarboxylic acid, Sodium dodecylbenzene sulfonate, branch-alkylbenzene sulfonate, sodium alkyl benzene sulfonate, alkylphenol polyoxyethylene, high-carbon fatty alcohol polyoxyethylene ether, polyoxyethylene carboxylate, fatty acid methyl ester ethoxylate, polypropylene glycol, the ionogenic surfactant of polyoxyethylene.
6. according to the solar cell board cleaning agent described in claim 1～4 any one, it is characterized in that: described solvent is selected from following component: ethanol, methyl alcohol, diethanolamine, trolamine, deionized water.
7. according to the solar cell board cleaning agent described in claim 1～4 any one, it is characterized in that: described static inhibitor is selected from following component: glycerol, fatty acid methyl ester sulfonate.
8. according to the solar cell board cleaning agent described in claim 1～4 any one, it is characterized in that: described frostproofer is selected from following component: ethylene glycol, propylene glycol, diethylene glycol monobutyl ether, diethylene glycol dimethyl ether.
9. according to the solar cell board cleaning agent described in claim 1～4 any one, it is characterized in that: described tenderizer is selected from following component: sodium phosphate, EDTA-4Na, ethylenediamine tetraacetic acid (EDTA).
10. according to the solar cell board cleaning agent described in claim 1～4 any one, it is characterized in that: described removers is selected from following component: Virahol, acetone, butanone.