CN103773155A - 一种抗菌绝热反射涂料及其制备方法 - Google Patents
一种抗菌绝热反射涂料及其制备方法 Download PDFInfo
- Publication number
- CN103773155A CN103773155A CN201410031302.5A CN201410031302A CN103773155A CN 103773155 A CN103773155 A CN 103773155A CN 201410031302 A CN201410031302 A CN 201410031302A CN 103773155 A CN103773155 A CN 103773155A
- Authority
- CN
- China
- Prior art keywords
- parts
- reflective coating
- antibacterial
- preparation
- heat insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
本发明涉及一种抗菌绝热反射涂料及其制备方法,属于涂料技术领域。该涂料包括按照重量份数计的如下组分:硅丙乳液40~55份、纳米二氧化钛2~4份、纳米氧化锌1~2份、吡啶硫酮锌1~3份、蛭石6~9份、海泡石5~12份、有机膨润土4~7份、分散剂0.5~1份、消泡剂0.5~2份、水18~30份。本发明制备方法简单,制得的抗菌绝热反射涂料柔韧性好,附着力强,热反射率高,绝热效果好,具有良好的抗菌效果;同时,本发明产品应用范围较广,不仅可以用于救生衣等救生设备上,还可以用于其他纺织品以及管道、船舶等。
Description
技术领域
本发明属于涂料技术领域,具体涉及一种抗菌绝热反射涂料及其制备方法。
背景技术
个人救生设备,如救生衣,一般采用泡沫塑料或软木等制成,穿在身上具有足够浮力,使落水者头部能露出水面。但是,在冰冷的水里,人体温度下降极快,因此,急需研制如何使救生衣的保温效果更好。
目前市场上大部分的保温涂料应用于建筑工程技术领域,这类涂料的柔韧性、致密性和附着力一般较差,不宜涂在纺织品表面上,而且比较单一,不具有抗菌作用。因此如何克服现有技术的不足是目前涂料技术领域亟待解决的问题。
发明内容
本发明的目的是为了解决现有技术的不足,提供一种抗菌绝热反射涂料及其制备方法。本发明产品柔韧性好,附着力强,热反射率高,绝热效果好,具有良好的抗菌效果。
本发明采用的技术方案如下:
一种抗菌绝热反射涂料,包括按照重量份数计的如下组分:硅丙乳液40~55份、纳米二氧化钛2~4份、纳米氧化锌1~2份、吡啶硫酮锌1~3份、蛭石6~9份、海泡石5~12份、有机膨润土4~7份、分散剂0.5~1份、消泡剂0.5~2份、水18~30份。
所述的分散剂为分散剂5040。
所述的消泡剂为矿物油类消泡剂。
本发明还提供一种抗菌绝热反射涂料的制备方法,包括如下步骤:
步骤(1):将蛭石、海泡石和有机膨润土研磨至120~200目;
步骤(2):将硅丙乳液加入水中,然后向其中加入分散剂和消泡剂,搅拌至混合均匀后,再加入步骤(1)研磨好的蛭石、海泡石和有机膨润土,继续搅拌,得到浆料;
步骤(3):将纳米二氧化钛、纳米氧化锌和吡啶硫酮锌加入到步骤(2)的浆料中,继续搅拌至混合均匀,即得到本发明的抗菌绝热反射涂料。
本涂料的施工方法与一般的涂料的施工方法相似,可采用等离子喷涂、静电喷涂、刷涂、浸渍涂敷、滚辊涂敷等,可以根据不同的涂装方法,调节涂料黏度。
本发明与现有技术相比,其有益效果为:本发明制备方法简单,制得的抗菌绝热反射涂料柔韧性好,附着力强,热反射率高,绝热效果好,具有良好的抗菌效果;同时,本发明产品应用范围较广,不仅可以用于救生衣等救生设备上,还可以用于其他纺织品以及管道、船舶等。
具体实施例
下面结合实施例对本发明作进一步的详细描述。
实施例1
一种抗菌绝热反射涂料,包括按照重量份数计的如下组分:硅丙乳液40份、纳米二氧化钛2份、纳米氧化锌1份、吡啶硫酮锌1份、蛭石6份、海泡石5份、有机膨润土4份、分散剂5040 0.5份、矿物油类消泡剂0.5份、水18份。
本实施例抗菌绝热反射涂料的制备方法,包括如下步骤:
步骤(1):将蛭石、海泡石和有机膨润土研磨至120~200目;
步骤(2):将硅丙乳液加入水中,然后向其中加入分散剂5040和矿物油类消泡剂,搅拌至混合均匀后,再加入步骤(1)研磨好的蛭石、海泡石和有机膨润土,继续搅拌,得到浆料;
步骤(3):将纳米二氧化钛、纳米氧化锌和吡啶硫酮锌加入到步骤(2)的浆料中,继续搅拌至混合均匀,即得到本实施例的抗菌绝热反射涂料。
实施例2
一种抗菌绝热反射涂料,包括按照重量份数计的如下组分:硅丙乳液55份、纳米二氧化钛4份、纳米氧化锌2份、吡啶硫酮锌3份、蛭石9份、海泡石12份、有机膨润土7份、分散剂5040 1份、矿物油类消泡剂2份、水30份。
本实施例抗菌绝热反射涂料的制备方法与实施例1的制备方法相同。
实施例3
一种抗菌绝热反射涂料,包括按照重量份数计的如下组分:硅丙乳液48份、纳米二氧化钛3.1份、纳米氧化锌1.6份、吡啶硫酮锌2份、蛭石8份、海泡石9份、有机膨润土5份、分散剂5040 0.9份、矿物油类消泡剂1.2份、水26份。
本实施例抗菌绝热反射涂料的制备方法与实施例1的制备方法相同。
性能检测
对本发明实施例1~3所得产品的性能测试,结果如表1所示。
表1 本发明实施例1~3产品性能测试数据
同时,对实施例1~3产品的杀菌率进行检测,检测结果如表2所示。
表2 实施例1~3产品的杀菌率检测结果
Claims (4)
1.一种抗菌绝热反射涂料,其特征在于包括按照重量份数计的如下组分:硅丙乳液40~55份、纳米二氧化钛2~4份、纳米氧化锌1~2份、吡啶硫酮锌1~3份、蛭石6~9份、海泡石5~12份、有机膨润土4~7份、分散剂0.5~1份、消泡剂0.5~2份、水18~30份。
2.根据权利要求1所述的抗菌绝热反射涂料,其特征在于所述的分散剂为分散剂5040。
3.根据权利要求1所述的抗菌绝热反射涂料,其特征在于所述的消泡剂为矿物油类消泡剂。
4.权利要求1所述的抗菌绝热反射涂料的制备方法,其特征在于包括如下步骤:
步骤(1):将蛭石、海泡石和有机膨润土研磨至120~200目;
步骤(2):将硅丙乳液加入水中,然后向其中加入分散剂和消泡剂,搅拌至混合均匀后,再加入步骤(1)研磨好的蛭石、海泡石和有机膨润土,继续搅拌,得到浆料;
步骤(3):将纳米二氧化钛、纳米氧化锌和吡啶硫酮锌加入到步骤(2)的浆料中,继续搅拌至混合均匀,即得到本发明的抗菌绝热反射涂料。