CN103757992A - Unbroken glass paperboard with width of 10m and thickness of 0.3mm sawn and drilled by metal - Google Patents
Unbroken glass paperboard with width of 10m and thickness of 0.3mm sawn and drilled by metal Download PDFInfo
- Publication number
- CN103757992A CN103757992A CN201210032748.0A CN201210032748A CN103757992A CN 103757992 A CN103757992 A CN 103757992A CN 201210032748 A CN201210032748 A CN 201210032748A CN 103757992 A CN103757992 A CN 103757992A
- Authority
- CN
- China
- Prior art keywords
- glass
- dust slurry
- glass dust
- plate
- metal
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an unbroken glass paperboard with width of 10m and thickness of 0.3mm sawn and drilled by metal. The glass paperboards are produced by glass power slurry in batches at room temperature, so that production difficulty can be reduced, energy consumption can be reduced, and cost can be reduced. Glass cloths are rich in elasticity, glass thin slices are elastic, and the tension of glass fibers is higher than that of metal fibers by several times, so that the glass board bear impact force tensile property and steel plate weight; the glass board can be used in acid-base fields; the glass plate is about 2g/cu. cm in specific gravity, 1mm in thickness, and 100m of glass plate is 2200kg weight, so that the weight is lighter than the steel plate by about 3 times; the glass cloth which is 0.2mm thick is worthy of 1 Yuan/sq. m, so that the price of the glass plate can be reduced in multiples, and the economic benefit is high; the glass cloths are made by silicon sand, the technology is simpler than steelmaking, and placer is abundant and is more than iron mine by millions and millions times; a steel plate does not have the characteristics, and a metal plate is replaced by the glass plate, so that the glass plate is equally dominant in preparing carriages, cabins, furniture, building workshops and the like. If the unbroken glass paperboard is prepared, the economic benefit is promoted by several times.
Description
Glass, is not afraid of soda acid worm ant, but be afraid of to clash into, one touch broken; If without shock, it's thousand pasts the life-span, makes metallic plate self-induction be not so good as.
< < that this technology proposes is wide to be surpassed 10 meters and is as thin as 0.3 millimeter and substitutes metal and can saw brill and beat not rotten glass cardboard > >, be called for short and break not rotten glass cardboard, can solve glass and be afraid of Impact Problems.
< < is wide to be surpassed 10 meters and is as thin as 0.3 millimeter and substitutes metal and can saw to bore and beat not rotten glass cardboard > >, its beneficial effect is, replace metal material, reducing fire occurs, extend working time, weight reduction, reduces costs.
< < is wide to be surpassed 10 meters and is as thin as 0.3 millimeter and substitutes metal and can saw to bore and beat not rotten glass cardboard > >, the technical scheme that its technical solution problem adopts is, by the bonding glass cloth of glass (1) (2), formed, with facility, glass dust slurry is placed in high temperature resistant template, glass cloth is placed on glass dust slurry, use again glass dust slurry cover glass cloth, strike off unnecessary glass dust slurry, after dry, sending into kiln fires, the cooling rear demoulding obtains breaks not rotten glass cardboard (3), thereby make widely to surpass 10 meters and be as thin as 0.3 millimeter and substitute metal and can saw to bore and break not rotten glass cardboard and moved, it is manufactured with 3 kinds:
1), with facility, glass dust slurry is placed in high temperature resistant template, glass cloth is placed on glass dust slurry, use again glass dust slurry cover glass cloth, strike off unnecessary glass dust slurry, after dry, send into kiln and fire, the cooling rear demoulding obtains and is as thin as 0.3 millimeter and replaces metal can saw brill playing not rotten glassine paper;
2), with facility, glass dust slurry is placed in high temperature resistant template; glass cloth is placed on glass dust slurry; use again glass dust slurry cover glass cloth; strike off unnecessary glass dust slurry; from multiple repeatedly becoming, widely can super several meters become thick in several centimeters of glass powder paste flitch; after dry, send into kiln and fire, the cooling rear demoulding obtains and widely surpasses 10 meters and thickly to several centimeters, replace metals can saw brill beating not rotten glass plate.As Fig. 1
Glass dust slurry, the technical scheme that its technical solution problem adopts is, glass is smashed and regrinded into young fine powder, can add adhesive to make glass dust slurry.
Not rotten glass cardboard is broken in existing combination principle introduction:
It is reported, the pulling force of glass fibre is several times of metal fibre pulling force, glass cloth high resilience.
This technology organically combines whippy glass cloth and hard glass bi-material, makes product be rich in brand-new advantage.
This technology is smashed glass to regrind into young fine powder, add adhesive to make glass dust slurry, solve glass and need to be heated into glass paste ability adhesive glass cloth problem, make glass cardboard energy first in ambient operation, and reduction manufacture difficulty improves making progress, cold of the glass cardboard of making is in batch put in batch kiln into again and is fired, reduce energy consumption, reduce costs.
It is reported, glass just becomes glass paste through more than 800 degree high-temperature heatings; Resistance to 1000 degree of glass cloth that this technology is taken, like this, when the powder of high temp glass more than 800 has become glass paste parcel glass cloth, the glass fibre of glass cloth is not damaged, and glass cloth still keeps original pulling force, still keeps original elasticity; Utilize the mutual viscosity of glass paste, make multiple glassine papers stick into glass plate.
The glass thread that glass cloth is comprised of many glass fibres is woven into, so glass cloth high resilience.When glass plate is subject to impacting, glass is passed to glass cloth by impulsive force, and whippy glass cloth just absorbs impulsive force.Glass is used as adhesive, so glass can be as thin as 0.02 millimeter, makes glass flake also flexible; And along with the glass cloth number of plies increases, the impulsive force that glass plate bears constantly strengthens, until and steel plate trial of strength.
Because the pulling force of glass fibre is several times of metal fibre pulling force, so, the tensile property of glass plate, also can with steel plate trial of strength.
Glass plate includes the whippy glass cloth of multilayer, makes its high resilience; Glass plate is not afraid of soda acid; Beat the not rotten about 2g/cm of glass plate proportion
3, thick 1 millimeter 100 meters
2glass plate 200kg, light nearly 3 times of weight ratio steel plate; 1 yuan/meter of thick 0.2 millimeter of glass cloth less than
2, make glass plate price reduce at double, economic benefit is high; Glass, glass cloth is to make of silica sand, and technique is simple more a lot of than steel-making, and placer is abundant, than the many thousands of times of iron ore; These characteristics are that steel plate is unexistent, with glass plate, replacing metallic plate, make compartment, cabin, and furniture, the large factory building of bedding, exterior wall finishings etc. all account for and have great advantage.If be made into, beat not rotten foam glass board, economic benefit promotes several times
Figure of description explanation
Fig. 1: break not rotten glass cardboard
1 glass, 2 glass cloth, 3 glass cardboards.
Claims (2)
1. < < is wide surpasses 10 meters and is as thin as 0.3 millimeter and substitutes metal and can saw to bore and beat not rotten glass cardboard > >, it is characterized in that, by bonding glass glass cloth, formed, with facility, glass dust slurry is placed in high temperature resistant template, glass cloth is placed on glass dust slurry, use again glass dust slurry cover glass cloth, strike off unnecessary glass dust slurry, after dry, sending into kiln fires, the cooling rear demoulding obtains breaks not rotten glass cardboard, thereby make widely to surpass 10 meters and be as thin as 0.3 millimeter and substitute metal and can saw to bore and break not rotten glass cardboard and moved, it is manufactured with 2 kinds:
1), with facility, glass dust slurry is placed in high temperature resistant template, glass cloth is placed on glass dust slurry, use again glass dust slurry cover glass cloth, strike off unnecessary glass dust slurry, after dry, send into kiln and fire, the cooling rear demoulding obtains and is as thin as 0.3 millimeter and replaces metal can saw brill playing not rotten glassine paper;
2), with facility, glass dust slurry is placed in high temperature resistant template; glass cloth is placed on glass dust slurry; use again glass dust slurry cover glass cloth; strike off unnecessary glass dust slurry; from multiple repeatedly becoming, widely can super several meters become thick in several centimeters of glass powder paste flitch; after dry, send into kiln and fire, the cooling rear demoulding obtains and widely surpasses 10 meters and thickly to several centimeters, replace metals can saw brill beating not rotten glass plate.
2. glass dust slurry according to claim 1, is characterized in that, glass is smashed and regrinded into young fine powder, can add adhesive to make glass dust slurry.