CN103756753B - 一种稀***掺杂纳米TiO2润滑材料的制备方法 - Google Patents
一种稀***掺杂纳米TiO2润滑材料的制备方法 Download PDFInfo
- Publication number
- CN103756753B CN103756753B CN201310493463.1A CN201310493463A CN103756753B CN 103756753 B CN103756753 B CN 103756753B CN 201310493463 A CN201310493463 A CN 201310493463A CN 103756753 B CN103756753 B CN 103756753B
- Authority
- CN
- China
- Prior art keywords
- rare earth
- solution
- doped nano
- obtained solution
- take
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种稀***掺杂纳米<b>TiO2</b>润滑材料的制备方法，包括以下具体步骤：a、称取第一种稀土氧化物，将其溶于浓硝酸中，加入无水乙醇和去离子水，制得溶液A；b、称取第二种稀土氧化物，将其溶于浓硝酸中，加入无水乙醇和去离子水，制得溶液B；c、将溶液A和溶液B混合，制得溶液C；d、称取钛醇盐或钛的无机盐，加入无水乙醇中，并加入控制剂，制得溶液D；e、将溶液C滴加到溶液D中，形成溶胶；f、将步骤e中的溶胶放置得到凝胶，蒸发，再煅烧得到稀***掺杂纳米<b>TiO2</b>。通过上述方式，本发明步骤简单，采用该制备方法制得的稀***掺杂纳米<b>TiO2</b>，具有较好的抗磨减摩性能，是一种性能优良的、环境友好型润滑添加剂。
Description
技术领域
本发明涉及纳米材料改性技术领域，特别是涉及一种稀***掺杂纳米TiO 2 润滑材料的制备方法。
背景技术
随着各种机械装置向高速重载化方向发展及人们环保意识的不断提高，迫切要求使用环保型的润滑油添加剂来代替含硫、磷、氯的润滑油添加剂，传统润滑剂的更新换代已迫在眉睫，各国研究人员进行了大量的研究工作。近年来，将纳米材料作为添加剂应用于润滑材料以改善其润滑性能，获得了一定的效果，成为润滑剂材料研究领域的主要研究方向之一。本申请致力于研发一种稀***掺杂纳米TiO 2 润滑材料的制备方法。
发明内容
本发明主要解决的技术问题是提供一种稀***掺杂纳米TiO 2 润滑材料的制备方法，步骤简单，采用该制备方法制得的稀***掺杂纳米TiO 2 ，具有较好的抗磨减摩性能，是一种性能优良的、环境友好型润滑添加剂。
为解决上述技术问题，本发明采用的一个技术方案是：提供一种稀***掺杂纳米TiO 2 润滑材料的制备方法，包括以下具体步骤：
a、称取第一种稀土氧化物，将其溶于浓硝酸中，加入无水乙醇和去离子水，充分搅拌40~50分钟，制得溶液A；
b、称取第二种稀土氧化物，将其溶于浓硝酸中，加入无水乙醇和去离子水，充分搅拌40~50分钟，制得溶液B；
c、将溶液A和溶液B混合，再充分搅拌10~20分钟，制得溶液C；
d、称取钛醇盐或钛的无机盐，加入无水乙醇中，并加入控制剂，持续搅拌40~50分钟，制得溶液D；
e、在室温条件下，将溶液C滴加到溶液D中，在滴加过程中，要持续搅拌，滴加完成后，再继续搅拌5~6个小时，形成溶胶；
f、将步骤e中的溶胶放置10~24个小时缩聚得到凝胶，其中含有大量液相，通过蒸发除去液体介质，最后再煅烧得到稀***掺杂纳米TiO 2 。
在本发明一个较佳实施例中，所述步骤f中的煅烧温度为800℃，煅烧时间为8个小时。
本发明的有益效果是：本发明一种稀***掺杂纳米TiO 2 润滑材料的制备方法，步骤简单，采用该制备方法制得的稀***掺杂纳米TiO 2 ，具有较好的抗磨减摩性能，是一种性能优良的、环境友好型润滑添加剂。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述，显然，所描述的实施例仅是本发明的一部分实施例，而不是全部的实施例。基于本发明中的实施例，本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例，都属于本发明保护的范围。
本发明实施例包括：
一种稀***掺杂纳米TiO 2 润滑材料的制备方法，包括以下具体步骤：
a、称取第一种稀土氧化物，将其溶于浓硝酸中，加入无水乙醇和去离子水，充分搅拌40~50分钟，制得溶液A；
b、称取第二种稀土氧化物，将其溶于浓硝酸中，加入无水乙醇和去离子水，充分搅拌40~50分钟，制得溶液B；
c、将溶液A和溶液B混合，再充分搅拌10~20分钟，制得溶液C；
d、称取钛醇盐或钛的无机盐，加入无水乙醇中，并加入控制剂，持续搅拌40~50分钟，制得溶液D；
e、在室温条件下，将溶液C滴加到溶液D中，在滴加过程中，要持续搅拌，滴加完成后，再继续搅拌5~6个小时，形成溶胶；
f、将步骤e中的溶胶放置10~24个小时缩聚得到凝胶，其中含有大量液相，通过蒸发除去液体介质，最后再煅烧得到稀***掺杂纳米TiO 2 ，煅烧温度为800℃，煅烧时间为8个小时。
本发明一种稀***掺杂纳米TiO 2 润滑材料的制备方法，步骤简单，采用该制备方法制得的稀***掺杂纳米TiO 2 ，具有较好的抗磨减摩性能，是一种性能优良的、环境友好型润滑添加剂。
以上所述仅为本发明的实施例，并非因此限制本发明的专利范围，凡是利用本发明说明书内容所作的等效结构或等效流程变换，或直接或间接运用在其它相关的技术领域，均同理包括在本发明的专利保护范围内。
Claims (1)
1.一种稀***掺杂纳米TiO 2 润滑材料的制备方法，其特征在于，包括以下具体步骤：
a、称取第一种稀土氧化物，将其溶于浓硝酸中，加入无水乙醇和去离子水，充分搅拌40~50分钟，制得溶液A；
b、称取第二种稀土氧化物，将其溶于浓硝酸中，加入无水乙醇和去离子水，充分搅拌40~50分钟，制得溶液B；
c、将溶液A和溶液B混合，再充分搅拌10~20分钟，制得溶液C；
d、称取钛醇盐或钛的无机盐，加入无水乙醇中，并加入控制剂，持续搅拌40~50分钟，制得溶液D；
e、在室温条件下，将溶液C滴加到溶液D中，在滴加过程中，要持续搅拌，滴加完成后，再继续搅拌5~6个小时，形成溶胶；
f、将步骤e中的溶胶放置10~24个小时缩聚得到凝胶，其中含有大量液相，通过蒸发除去液体介质，最后再煅烧得到稀***掺杂纳米TiO 2 ，煅烧温度为800℃，煅烧时间为8个小时。