CN103756551A - Pet薄膜高附着力uv涂料 - Google Patents
Pet薄膜高附着力uv涂料 Download PDFInfo
- Publication number
- CN103756551A CN103756551A CN201410022989.6A CN201410022989A CN103756551A CN 103756551 A CN103756551 A CN 103756551A CN 201410022989 A CN201410022989 A CN 201410022989A CN 103756551 A CN103756551 A CN 103756551A
- Authority
- CN
- China
- Prior art keywords
- acrylate
- weight
- coating
- pet
- content
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明主要介绍了一种含环状的丙烯酸酯的PET的UV涂料,环状的丙烯酸酯可以减少涂层的体积收缩,进而减少涂层与基材的应力,从而达到提高PET附着力的效果。该方法操作过程施工容易、易于控制、步骤简单,成本低廉。
Description
技术领域
本发明涉及一种PET薄膜高附着力UV涂料。
背景技术
PET塑料承印材料属于非极性高分子材料,具有较高结晶性,化学性能稳定,表面张力小,低于UV光固化油墨的张力,对油墨附着能力差。固化过程中UV光固化树脂的应力大。固化过程中的应力则来自两个方面。一方面,在固化过程中涂料层体积收缩,造成与底材的在变形上的差异,在涂层与底材之间的界面上产生应力。另一方面,UV的固化为快速反应,材料在短时间内剧烈防热,这种反应会造成涂层材料本身的结构不均匀性,造成涂层本身的内应力。这些弱点在多孔的基材上,如木材或纸张,表现不出来。但在PET、PP、PE等平滑塑料材料反应明显。目前常用的提高PET附着力的方法为电晕、火焰处理、底涂处理等。电晕处理过的材料表面张力稳定性差,随着时间的推移,电晕效果会逐渐减弱。尤其在湿度较大的环境下储存,电晕效果减弱更快。火焰处理一般适用于不规则形状的材料或於耐高温的塑料制品表面处理中,但通常不用于塑料材料的处理中。
本发明采用的是加入环状的丙烯酸酯,减少涂层的体积收缩,进而减少涂层与基材的应力,从而达到提高PET附着力的效果。
发明内容
本发明涉及一种含有环状丙烯酸酯的提高PET薄膜附着力的UV涂料。
本发明提供的涂料含有环状丙烯酸酯、主体树脂、稀释剂和光引发剂,含或者不含助剂。
具体实施方式
按照本发明提供的涂料,所述环状丙烯酸酯、主体树脂、稀释剂、光引发剂和助剂的含量为UV涂料中这些组分的常规含量。以涂料的总量为基准,环状丙烯酸酯的含量为10-50重量%,优选为20-30重量%,主体树脂含量为30-80重量%,优选40-60重量%,稀释剂10-50重量%,优选20-40重量%,光引发剂含量为1-5重量%,优选2-3重量%,助剂含量为0-10重量%,优选2-5%。
所述的主体树脂为现有UV涂料常用的主体树脂中的环氧丙烯酸酯、聚氨酯丙烯酸酯和聚酯丙烯酸酯中的一种或是几种。其中优选环氧丙烯酸酯、聚酯丙烯酸酯或是两者混合物。
所述稀释剂为UV涂料常用的丙烯酸酯单体,为本领域技术人员所公知。例如,单官能度丙烯酸酯可以选用丙烯酸羟乙酯(HEA)、甲基丙烯酸羟乙酯(HEMA)、甲基丙烯酸缩水甘油酯、丙烯酸己内酯、丙烯酸异葵酯、2-苯氧基乙基丙烯酸酯中的一种。双官能度丙烯酸酯可以选用1,6-己二醇二丙烯酸酯、聚乙二醇(400)二甲基丙烯酸酯、1,6-己二醇二甲基丙烯酸酯、2(2-乙氧基乙氧基)乙基丙烯酸酯、聚乙二醇(200)二丙烯酸酯、二丙二醇二丙烯酸酯、二缩三乙二醇二甲基丙烯酸酯、三缩四乙二醇二甲基丙烯酸酯。三官能度丙烯酸酯可以选用丙氧化三羟甲基丙烷三丙烯酸酯、3-丙氧化丙三醇三丙烯酸酯、三羟甲基丙烷三丙烯酸酯、季戊四醇三丙烯酸酯或3-乙氧化三羟甲基丙烷三丙烯酸酯。高官能度可以选用二季戊四醇五/六丙烯酸酯。
所述的光引发剂种类和用量为本领域技术人员所公知,例如BP、651、907、ITX、1173、184、2959、369、TPO、819、CQ、784。国内公司如北京英力、华钛等,国外如瑞士汽巴,其牌号为本领域技术人员所公知。
所述环状丙烯酸酯为本领域技术人员所公知的美国沙多玛的产品:四氢呋喃丙烯酸酯(SR285)、烷氧化四氢呋喃丙烯酸酯(CD611)、丙烯酸异冰片酯(SR506)、四氢呋喃甲基丙烯酸酯(SR203)、甲基丙烯酸异冰片酯(SR423)、三环葵烷二甲醇二丙烯酸酯(SR833S),和台湾长兴公司的3,3,5-三甲基环已基丙烯酸酯(EM2104)、四氢化糠基丙烯酸酯(EM214)。
所述助剂为UV涂料常用的流平剂、消泡剂、分散剂。其中流平剂为本领域技术人员所公知的BYK公司的BYK333、BYK366、BYK307,德国迪高公司的DEGO410、DEGO432、DEGO435。消泡剂为本领域技术人员所公知的BYK公司的BYK357、BYK354、BYK352。分散剂为本领域技术人员所公知的美国Kerper公司的Kerper-602,Kerper-605,Kerper-630。
本发明提供的UV涂料的制备方法为将主体树脂、稀释剂、环状丙烯酸酯和光引发剂,加入或者不加助剂,混合均匀。以涂料的总量为基准,环状丙烯酸酯的含量为10-50重量%,优选为20-30重量%,主体树脂含量为30-80重量%,优选40-60重量%,稀释剂10-50重量%,优选20-40重量%,光引发剂含量为1-5重量%,优选2-3重量%,助剂含量为0-10重量%,优选2-5%。
本发明提供的PET高附着UV涂料适合各种PET薄膜的面漆。所述PET高附着UV涂料适合涂膜厚度为15-25微米的应用。
实施例子进一步说明
举例1
环氧丙烯酸酯80g,三羟甲基丙烷三丙烯酸酯10g,四氢呋喃丙烯酸酯(SR285)10g,引发剂184为1g,40摄氏度溶解后分散均匀。
举例2
聚酯丙烯酸酯30g,1,6-己二醇二丙烯酸酯20g,丙烯酸异冰片酯(SR506)50g,BYK357为2g,引发剂TPO为1g,40摄氏度溶解后分散均匀。
举例3
聚氨酯丙烯酸酯60g,二缩三乙二醇二甲基丙烯酸酯20g,3,3,5-三甲基环已基丙烯酸酯(EM2104)20g,引发剂BP为1g,40摄氏度溶解后分散均匀。
举例4
环氧丙烯酸酯20g,聚酯丙烯酸酯20g,丙烯酸羟乙酯40g,烷氧化四氢呋喃丙烯酸酯(CD611)15g,BYK354为5g,引发剂1173为2g,40摄氏度溶解后分散均匀。
举例5
聚酯丙烯酸酯12g,聚乙二醇(200)二丙烯酸酯50g,三环葵烷二甲醇二丙烯酸酯(SR833S)30g,引发剂651为5g,BYK333为2g,40摄氏度溶解后分散均匀。
举例6
环氧丙烯酸酯27g,季戊四醇三丙烯酸酯30g,四氢化糠基丙烯酸酯(EM214)30g,引发剂907为3g,DEGO410为10g,40摄氏度溶解后分散均匀。
举例7
环氧丙烯酸酯19g,聚氨酯丙烯酸酯20g,二季戊四醇五/六丙烯酸酯5g,四氢呋喃甲基丙烯酸酯(SR203)50g,引发剂2959为1g,Kerper-602为2g,BYK307为3g。40摄氏度溶解后分散均匀。
举例8
环氧丙烯酸酯10g,聚酯丙烯酸酯29g,2(2-乙氧基乙氧基)乙基丙烯酸酯5g,甲基丙烯酸异冰片酯(SR423)50g,引发剂369为1g,Kerper-630为2g,DEGO432为3g。40摄氏度溶解后分散均匀。
Claims (3)
1.本发明提供的涂料,该涂料包括环状丙烯酸酯、主体树脂、稀释剂、光引发剂和助剂,其特征在于该涂料含有环状丙烯酸酯,以涂料总量为基准,含量为10-50重量%,优选为20-30重量%。
2.根据权利要求1所述的涂料,其特征在于以涂料的总量为基准,环状丙烯酸酯的含量为10-50重量%,优选为20-30重量%,主体树脂含量为30-80重量%,优选40-60重量%,稀释剂10-50重量%,优选20-40重量%,光引发剂含量为1-5重量%,优选2-3重量%,助剂含量为0-10重量%,优选2-5%。
3.根据权利要求1所述的涂料,其环状丙烯酸酯为四氢呋喃丙烯酸酯(SR285)、烷氧化四氢呋喃丙烯酸酯(CD611)、丙烯酸异冰片酯(SR506)、四氢呋喃甲基丙烯酸酯(SR203)、甲基丙烯酸异冰片酯(SR423)、三环葵烷二甲醇二丙烯酸酯(SR833S),和台湾长兴公司的3,3,5-三甲基环已基丙烯酸酯(EM2104)、四氢化糠基丙烯酸酯(EM214)。