CN103737938B - A kind of preparation method of novel anticorrosion composite pressure pipe material - Google Patents
A kind of preparation method of novel anticorrosion composite pressure pipe material Download PDFInfo
- Publication number
- CN103737938B CN103737938B CN201310645101.XA CN201310645101A CN103737938B CN 103737938 B CN103737938 B CN 103737938B CN 201310645101 A CN201310645101 A CN 201310645101A CN 103737938 B CN103737938 B CN 103737938B
- Authority
- CN
- China
- Prior art keywords
- parts
- steel pipe
- layer
- preparation
- ultra
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the preparation method of a kind of novel anticorrosion composite pressure pipe material, belong to tubing technical field.The method of the invention uniformly coats one layer of Vinylidene Chloride bonding agent owing to using at outer surface of steel tube, the method of one layer of ultra-high molecular weight polyethylene layer of extrusion cladding outside steel pipe the most again, ultra-high molecular weight polyethylene and steel pipe are combined closely, thus do not have skidding peeling, substantially prolongs the service life of tubing.The composite pipe that described method is prepared have wear-resisting, be not easily stripped the characteristics such as high with impact strength.
Description
Technical field
The present invention relates to the preparation method of a kind of composite pipe, belong to tubing technical field.
Background technology
Carrying roller used by numerous domestic conveying machinery industry has steel pipe, nylon tube, steel to be cladded with rubber tube, steel sleeve PE at present
The kinds such as pipe, simple use steel pipe do carrying roller exist easily get rusty, frictional resistance big and to defects such as conveyer belt serious wear;And make
Making carrying roller with nylon tube, producing length can only be within 500mm, once lengthen, can not carry bigger load;Steel pipe is cladded with
Although rubber is elastic preferably, but equally exists the defect that frictional resistance is big;And use steel pipe overcoat polyvinyl piping materials, although at dress
Timing can use interference fit to make minimizing gap between steel pipe and the polyethylene tube of overcoat, but rubs owing to passing through in running
Can produce certain heat after wiping, and polyethylene cannula external diameter after being heated expands, thus skidding occur, service life is subject to
To certain impact.
Summary of the invention
It is an object of the invention to overcome defect of the prior art, it is provided that the system of a kind of novel anticorrosion composite pressure pipe material
Preparation Method, tubing prepared by described method have wear-resisting, be not easily stripped the characteristics such as high with impact strength.
The present invention is achieved by the following technical programs.
The preparation method of a kind of novel anticorrosion composite pressure pipe material, preparation method is as follows: first carried out by outer surface of steel tube
Derusting by sandblasting, by clean for outer surface of steel tube cleaning, then is heated to 300 DEG C at steel pipe by steel pipe rotary in heating furnace, and insulation 2 is little
Time, it is heated to 400 DEG C, is incubated 1 hour, steel pipe is cooled down 4 hours under room temperature state, uniformly coats one at outer surface of steel tube
Layer anti-corrosion resin, is then dried at room temperature for the steel pipe of coated anti-corrosion resin 20-30 minute, then is inserted by steel pipe in mould,
Open extruder at one layer of ultra-high molecular weight polyethylene layer of steel pipe outer cladding, each district heating-up temperature of extruder be followed successively by 165 DEG C,
170 DEG C, 170 DEG C, 175 DEG C, 180 DEG C, 190 DEG C, die temperature is 185-190 DEG C, and extruder engine speed is 400-450r/
Min, after cool down through water tank;Anti-corrosion resin following ingredients forms, by weight,
Epoxy resin 30-40 part
Amino resins 10-20 part
Almag thin slice 10-25 part
Modified bisphenol epoxy tree 20-25 part
Novolac epoxy resin 15-20 part
Polyethylene Glycol 0.5 part
Silicon dioxide thin slice 2-5 part
Zinc oxide thin slice 4-5 parts
Vinyl chloride 30-40 part
Pulvis Talci 20-30 part
Solvent 45-60 part.
The preparation method of above-mentioned novel anticorrosion composite pressure pipe material, wherein, the thickness of described ultra-high molecular weight polyethylene layer
Degree is 8-12mm.
The method of the invention uniformly coats one layer of anti-corrosion resin at outer surface of steel tube, then outside steel pipe again owing to using
The method of extrusion one layer of ultra-high molecular weight polyethylene layer of cladding so that ultra-high molecular weight polyethylene and steel pipe are combined closely, thus
Do not have skidding peeling, substantially prolongs the service life of tubing.The composite pipe that described method is prepared has resistance to
Mill, it is not easily stripped the characteristics such as high with impact strength, and makes tubing possess higher bearing capacity;And this anti-corrosion resin has
Preferably antiseptic property, thus, substantially increase the service life of this tubing.
Detailed description of the invention
Below by way of specific embodiment, the present invention is further detailed explanation.
Embodiment 1
The preparation method of a kind of composite pipe, preparation method is as follows: first outer surface of steel tube is carried out derusting by sandblasting, by steel
Tube outer surface cleaning is clean, then at steel pipe, steel pipe rotary is heated in heating furnace 300 DEG C, is incubated 2 hours, is heated to
400 DEG C, it is incubated 1 hour, steel pipe is cooled down 4 hours under room temperature state, uniformly coat one layer of anti-corrosion resin at outer surface of steel tube,
Then the steel pipe of coated anti-corrosion resin is dried at room temperature for 20-30 minute, then steel pipe is inserted in mould, open extruder
At one layer of ultra-high molecular weight polyethylene layer of steel pipe outer cladding, each district heating-up temperature of extruder be followed successively by 165 DEG C, 170 DEG C, 170
DEG C, 175 DEG C, 180 DEG C, 190 DEG C, die temperature is 185-190 DEG C, and extruder engine speed is 400r/min, after through water tank
Cool down;Anti-corrosion resin is by epoxy resin 30 parts, amino resins 10-part, almag thin slice 10 parts, modified bisphenol epoxy tree
20 parts, novolac epoxy resin 15 parts, Polyethylene Glycol 0.5 part, silicon dioxide thin slice 2 parts, zinc oxide thin slice 4 parts, 30 parts of vinyl chloride,
Pulvis Talci 20 parts, solvent 45 parts composition, by weight, solvent is made up of ethyl acetate and n-butyl alcohol, ethyl acetate: n-butyl alcohol
For 2:1, by weight.The thickness of ultra-high molecular weight polyethylene layer is 8mm.
Embodiment 2
The preparation method of a kind of composite pipe, preparation method is as follows: first outer surface of steel tube is carried out derusting by sandblasting, by steel
Tube outer surface cleaning is clean, then at steel pipe, steel pipe rotary is heated in heating furnace 300 DEG C, is incubated 2 hours, is heated to
400 DEG C, it is incubated 1 hour, steel pipe is cooled down 4 hours under room temperature state, uniformly coat one layer of anti-corrosion resin at outer surface of steel tube,
Then the steel pipe of coated anti-corrosion resin is dried at room temperature for 20-30 minute, then steel pipe is inserted in mould, open extruder
At one layer of ultra-high molecular weight polyethylene layer of steel pipe outer cladding, each district heating-up temperature of extruder be followed successively by 165 DEG C, 170 DEG C, 170
DEG C, 175 DEG C, 180 DEG C, 190 DEG C, die temperature is 185-190 DEG C, and extruder engine speed is 430r/min, after through water tank
Cool down;Anti-corrosion resin is by epoxy resin 35 parts, 15 parts of amino resins, almag thin slice 20 parts, modified bisphenol epoxy tree
22 parts, novolac epoxy resin 15 parts, Polyethylene Glycol 0.5 part, silicon dioxide thin slice 5 parts, zinc oxide thin slice 4 parts, 35 parts of vinyl chloride,
Pulvis Talci 25 parts, solvent 50 parts composition, by weight, solvent is made up of ethyl acetate and n-butyl alcohol, ethyl acetate: n-butyl alcohol
For 2:1, by weight, the thickness of ultra-high molecular weight polyethylene layer is 10mm.
Embodiment 3
The preparation method of a kind of composite pipe, preparation method is as follows: first outer surface of steel tube is carried out derusting by sandblasting, by steel
Tube outer surface cleaning is clean, then at steel pipe, steel pipe rotary is heated in heating furnace 300 DEG C, is incubated 2 hours, is heated to
400 DEG C, it is incubated 1 hour, steel pipe is cooled down 4 hours under room temperature state, uniformly coat one layer of anti-corrosion resin at outer surface of steel tube,
Then the steel pipe of coated anti-corrosion resin is dried at room temperature for 20-30 minute, then steel pipe is inserted in mould, open extruder
At one layer of ultra-high molecular weight polyethylene layer of steel pipe outer cladding, each district heating-up temperature of extruder be followed successively by 165 DEG C, 170 DEG C, 170
DEG C, 175 DEG C, 180 DEG C, 190 DEG C, die temperature is 185-190 DEG C, and extruder engine speed is 450r/min, after through water tank
Cool down;Anti-corrosion resin is by epoxy resin 40 parts, 20 parts of amino resins, almag thin slice 25 parts, modified bisphenol epoxy tree
25 parts, novolac epoxy resin 20 parts, Polyethylene Glycol 0.5 part, silicon dioxide thin slice 5 parts, zinc oxide thin slice 4 parts, 40 parts of vinyl chloride,
By weight, solvent is made up of ethyl acetate and n-butyl alcohol, ethyl acetate for Pulvis Talci 30 parts, solvent 60 parts: n-butyl alcohol is 2:
1, by weight.The thickness of ultra-high molecular weight polyethylene layer is 12mm.
The a length of 4um of silicon dioxide thin slice, zinc oxide thin slice and almag thin slice, width is 2um, and thickness is 1um.
The performance indications of composite pipe prepared by the method for the invention are as follows:
16 hours surface abrasion rates < 0.17%
Peel strength during room temperature > 45MPa
Peel strength when 80 DEG C > 36MPa
Cantilever beam impact strength >=20KJ/m2
Here description of the invention and application is illustrative, is not wishing to limit the scope of the invention to above-described embodiment
In, therefore, the present invention is not limited by the present embodiment, and any technical scheme using equivalence replacement to obtain all is protected in the present invention
In the range of.
Claims (1)
1. the preparation method of a composite pipe, it is characterised in that preparation method is as follows: first outer surface of steel tube is carried out sandblasting
Rust cleaning, by clean for outer surface of steel tube cleaning, then is heated to 300 DEG C at steel pipe in heating furnace by steel pipe rotary, is incubated 2 hours,
It is heated to 400 DEG C, is incubated 1 hour, steel pipe is cooled down 4 hours under room temperature state, uniformly coats one layer at outer surface of steel tube
Anti-corrosion resin, is then dried at room temperature for the steel pipe of coated anti-corrosion resin 20-30 minute, then is inserted by steel pipe in mould, opens
Open extruder at one layer of ultra-high molecular weight polyethylene layer of steel pipe outer cladding, each district heating-up temperature of extruder be followed successively by 165 DEG C,
170 DEG C, 170 DEG C, 175 DEG C, 180 DEG C, 190 DEG C, die temperature is 185-190 DEG C, and extruder engine speed is 400r/min,
Cool down through water tank after;Anti-corrosion resin is by epoxy resin 30 parts, amino resins 10-part, almag thin slice 10 parts, modification
20 parts of bisphenol epoxies tree, novolac epoxy resin 15 parts, Polyethylene Glycol 0.5 part, silicon dioxide thin slice 2 parts, zinc oxide thin slice 4 parts,
30 parts of vinyl chloride, Pulvis Talci 20 parts, solvent 45 parts composition, by weight, solvent is made up of ethyl acetate and n-butyl alcohol, acetic acid
Ethyl ester: n-butyl alcohol is 2:1, by weight;The thickness of ultra-high molecular weight polyethylene layer is 8mm.