CN103724884B - A kind of nonpoisonous and tasteless wet motor epr cable compound - Google Patents
A kind of nonpoisonous and tasteless wet motor epr cable compound Download PDFInfo
- Publication number
- CN103724884B CN103724884B CN201410013217.6A CN201410013217A CN103724884B CN 103724884 B CN103724884 B CN 103724884B CN 201410013217 A CN201410013217 A CN 201410013217A CN 103724884 B CN103724884 B CN 103724884B
- Authority
- CN
- China
- Prior art keywords
- tasteless
- nonpoisonous
- raw material
- modified filler
- wet motor
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses a kind of nonpoisonous and tasteless wet motor epr cable compound, it is obtained by the raw material of following weight parts: SG-5PVC resin 70-80, terpolymer EP rubber 20-30, potter's clay 4-6, talcum powder 1-2, calcium stearate 2.5-3, paraffin oil 1-2, zinc oxide 1-3, chlorinatedpolyethylene 4-8, clorafin 2-4, stearic acid 1-2, epoxidation tri-glyceride 1.5-3, modified filler 50-60.
Description
Technical field
The present invention relates to CABLE MATERIALS field, is exactly a kind of nonpoisonous and tasteless wet motor epr cable compound.
Background technology
Electric wire is resin dedicated comprises cable insulating material and cable jacket material, raw materials usedly mainly contains polyethylene and polyvinyl chloride.
The quality of polyvinyl chloride cable material and PVC cable material quality is fundamentally to be filled a prescription by PVC cable material and selected raw material decides.Along with the various auxiliary agent of PVC and the continuous renewal of weighting material and development, the formula of PVC cable material is also made constantly to improve and improve.
Summary of the invention
The object of the present invention is to provide a kind of nonpoisonous and tasteless wet motor epr cable compound.
Above-mentioned purpose is realized by following scheme:
A kind of nonpoisonous and tasteless wet motor epr cable compound, is characterized in that: it is obtained by the raw material of following weight parts:
SG-5PVC resin 70-80, terpolymer EP rubber 20-30, potter's clay 4-6, talcum powder 1-2, calcium stearate 2.5-3, paraffin oil 1-2, zinc oxide 1-3, chlorinatedpolyethylene 4-8, clorafin 2-4, stearic acid 1-2, epoxidation tri-glyceride 1.5-3, modified filler 50-60;
Modified filler is made up of the raw material of following weight part:
Attapulgite 15-18, wilkinite 10-12, aluminium nitride 1.5-3.5, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 2-3, aluminium hydroxide 7-9, magnesium oxide 1-2, silane coupling agent KH5801.4-2.8;
Attapulgite dodges to burn 7-9 second by the preparation method of modified filler at 800-850 DEG C in sudden strain of a muscle firing, take out, add in suitable quantity of water and grind, adding 10-15% hydrochloric acid soln adjusts PH to be 4-5, and after ground slurry to 600-800 order, repeated hydrogenation sodium oxide is adjusted to neutrality, spraying dry, powder, gained powder mixes with other remaining component, and ground and mixed is evenly and get final product.
The nonpoisonous and tasteless wet motor epr cable compound of described one, is characterized in that:
Preparation method is:
(1) get SG-5PVC resin, potter's clay, chlorinatedpolyethylene, calcium stearate mix by weight, in forcing machine at 150-160 DEG C mixing completely after, take out cooling;
(2) by the cooled material of step (1) gained and each raw material blending of residue, mixing in twin screw extruder, granulation, control temperature, at 140-155 DEG C, obtains finished product.
Beneficial effect of the present invention is:
The present invention has good mechanical property, also has excellent water tolerance, the performance such as nontoxic, tasteless, meets the requirement that Europe relates to drinking water pollution KTW certification.
Embodiment
A kind of nonpoisonous and tasteless wet motor epr cable compound, it is obtained by the raw material of following weight parts (kg):
SG-5PVC resin 80, terpolymer EP rubber 25, potter's clay 5, talcum powder 2, calcium stearate 2.7, paraffin oil 1.5, zinc oxide 2, chlorinatedpolyethylene 5, clorafin 4, stearic acid 1, epoxidation tri-glyceride 1.7, modified filler 60;
Modified filler is made up of the raw material of following weight part:
Attapulgite 18, wilkinite 12, aluminium nitride 3.2, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 3, aluminium hydroxide 9, magnesium oxide 1, silane coupling agent KH5801.7;
Attapulgite is dodged burning 9 seconds by the preparation method of modified filler at 850 DEG C in sudden strain of a muscle firing, take out, add in suitable quantity of water and grind, adding 15% hydrochloric acid soln adjusts PH to be 5, and after ground slurry to 800 order, repeated hydrogenation sodium oxide is adjusted to neutrality, spraying dry, powder, gained powder mixes with other remaining component, and ground and mixed is evenly and get final product.
The nonpoisonous and tasteless wet motor epr cable compound of described one, preparation method is:
(1) get SG-5PVC resin, potter's clay, chlorinatedpolyethylene, calcium stearate mix by weight, in forcing machine at 150 DEG C mixing completely after, take out cooling;
(2) by the cooled material of step (1) gained and each raw material blending of residue, mixing in twin screw extruder, granulation, control temperature, at 155 DEG C, obtains finished product.
The present embodiment is carried out performance test, and the data obtained is as follows:
From the present embodiment test result, product of the present invention is through the aging of 100 DEG C × 168h and 80 DEG C × 6h Apparatus for Pressure at high-temp, the change of its mechanical and physical performance meets corresponding mark requirement, has good physical and mechanical properties, meets the demand of differing temps environmental change.
Claims (2)
1. a nonpoisonous and tasteless wet motor epr cable compound, it is characterized in that: it is obtained by the raw material of following weight parts: SG-5PVC resin 70-80, terpolymer EP rubber 20-30, potter's clay 4-6, talcum powder 1-2, calcium stearate 2.5-3, paraffin oil 1-2, zinc oxide 1-3, chlorinatedpolyethylene 4-8, clorafin 2-4, stearic acid 1-2, epoxidation tri-glyceride 1.5-3, modified filler 50-60; Modified filler is made up of the raw material of following weight part: attapulgite 15-18, wilkinite 10-12, aluminium nitride 1.5-3.5, sec.-propyl three (dioctylphyrophosphoric acid acyloxy) titanic acid ester 2-3, aluminium hydroxide 7-9, magnesium oxide 1-2, silane coupling agent KH5801.4-2.8; Attapulgite dodges to burn 7-9 second by the preparation method of modified filler at 800-850 DEG C in sudden strain of a muscle firing, take out, add in suitable quantity of water and grind, adding 10-15% hydrochloric acid soln adjusts pH to be 4-5, and after ground slurry to 600-800 order, repeated hydrogenation sodium oxide is adjusted to neutrality, spraying dry, powder, gained powder mixes with other remaining component, and ground and mixed is evenly and get final product.
2. the nonpoisonous and tasteless wet motor epr cable compound of one according to claim 1, it is characterized in that: preparation method is: (1) gets SG-5PVC resin, potter's clay, chlorinatedpolyethylene, calcium stearate mix by weight, in forcing machine at 150-160 DEG C mixing completely after, take out cooling; (2) by the cooled material of step (1) gained and each raw material blending of residue, mixing in twin screw extruder, granulation, control temperature, at 140-155 DEG C, obtains finished product.