CN103724742A - 一种羧基丁腈胶耐油手套的制备方法 - Google Patents

一种羧基丁腈胶耐油手套的制备方法 Download PDF

Info

Publication number
CN103724742A
CN103724742A CN201210391248.6A CN201210391248A CN103724742A CN 103724742 A CN103724742 A CN 103724742A CN 201210391248 A CN201210391248 A CN 201210391248A CN 103724742 A CN103724742 A CN 103724742A
Authority
CN
China
Prior art keywords
oil
preparation
latex
parts
resistant glove
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210391248.6A
Other languages
English (en)
Inventor
李建东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
WUXI XINYA SAFETY PRODUCTS CO Ltd
Original Assignee
WUXI XINYA SAFETY PRODUCTS CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by WUXI XINYA SAFETY PRODUCTS CO Ltd filed Critical WUXI XINYA SAFETY PRODUCTS CO Ltd
Priority to CN201210391248.6A priority Critical patent/CN103724742A/zh
Publication of CN103724742A publication Critical patent/CN103724742A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种羧基丁腈胶耐油手套的制备方法，该耐油手套以重量份计由下列组份组成：羧基丁腈胶乳100.00，稳定剂0.5-0.7，硫化剂1.3-1.7，促进剂0.6-0.8，防老剂1.1-1.3，六亚甲基四胺0.6-0.8，活性剂2.0-2.4以及适量凝固剂；其中羧基丁腈胶乳具有如下性能：粘度85-95mPa·s，表面张力36-40mN/m，结构凝胶≤35％；所述制备方法包括配料、浸渍胶乳和浸凝固剂、定型、沥滤、半成品干燥、脱模、硫化、烘干和冷却脱模工序，其中半成品干燥的温度为86-90℃，干燥时间为70-80分钟；硫化温度为116-120℃。

Description

一种羧基丁腈胶耐油手套的制备方法
技术领域
本发明涉及安全防护技术领域，尤其涉及一种羧基丁腈胶耐油手套的制备方法。
背景技术
目前工业上所使用的耐油手套，有橡胶耐油手套、塑料耐油手套和乳胶耐油手套等几种类型。其中橡胶耐油手套的手形板直、质地发硬、穿戴别手、十分不便；塑料耐油手套具有塑料制品的弱点：冬天硬而脆、夏天软绵绵、易老化、寿命短，而且价格较高；乳胶手套的质地柔软、穿戴舒适，特别是羧基丁腈胶耐油手套比天然胶乳手套和氯丁胶乳手套更具有良好的耐油性、耐酸碱性、耐磨性和耐穿刺性，是一种现代工业中质量较好、深受操作使用人员喜欢的耐油手套产品。生产羧基丁腈胶耐油手套的主要原料是羧基丁腈胶乳，其性能直接决定了丁腈胶耐油手套的耐油性能，羧基丁腈胶乳采用乳液聚合的方法生产。单体体系除丁二烯、丙烯腈外，改性用的不饱和酸有一元不饱和酸，如丙烯酸等。也有用不饱和二元酸，如马来酸等。乳化体系多用阴离子乳化剂和非离子乳化剂，如日本的Zeon公司用油酸钾、十烷基硫酸钠、聚氧乙烯醚等。该乳化体系要具有反应过程稳定、浸渍时易于破乳成膜的特点。引发体系有用过硫酸盐，如过硫酸铵的高温体系，也有过氧化异丙苯-还原剂的低温体系。加料方式有一次性投料的间歇式反应、有分批加入单体的半连续方式，也有连续加料的生产方式。胶除残余单体有物理方式，如减压闪蒸汽提法、减压闪蒸N2提取法，也有物理法与化学法并用的方法。总之，单体体系，乳化体系，引发体系，进料方式，工艺条件构成制备羧基丁腈胶的技术要点。
发明内容
本发明的目的在于提出一种羧基丁腈胶耐油手套的制备方法，该制备方法通过选择适宜的羧基丁腈胶乳，选择合适的粘结性和成膜性，从而利用制备出耐油性能极佳的羧基丁腈胶耐油手套。
为达此目的，本发明采用以下技术方案：
一种羧基丁腈胶耐油手套的制备方法，该耐油手套以重量份计由下列组份组成：羧基丁腈胶乳100.00，稳定剂0.5-0.7，硫化剂1.3-1.7，促进剂0.6-0.8，防老剂1.1-1.3，六亚甲基四胺0.6-0.8，活性剂2.0-2.4以及适量凝固剂；其中羧基丁腈胶乳具有如下性能：粘度85-95mPa·s，表面张力36-40mN/m，结构凝胶≤35％；所述制备方法包括配料、浸渍胶乳和浸凝固剂、定型、沥滤、半成品干燥、脱模、硫化、烘干和冷却脱模工序，其中半成品干燥的温度为86-90℃，干燥时间为70-80分钟；硫化温度为116-120℃。
本发明具有如下有益效果
1）通过选择适宜的羧基丁腈胶乳，提高羧基丁腈胶耐油手套的性能。
2）该耐油手套具有优良的耐油性能和耐酸、耐碱、耐溶剂以及耐磨、耐穿刺等性能，广泛应用于石油化工、油田炼油、油脂加工、水产加工、矿山机械等工业部门及家庭卫生用品。
3）该耐油手套与橡胶耐油手套和塑料耐油手套相比，具有质地柔软、穿戴舒适、冬季保暖、夏季吸汗、美观大方等特点，是一种深受用户欢迎的劳动保护用品。
具体实施方式
实施例一
一种羧基丁腈胶耐油手套的制备方法，该耐油手套以重量份计由下列组份组成：羧基丁腈胶乳100.00，稳定剂0.5，硫化剂1.7，促进剂0.6，防老剂1.3，六亚甲基四胺0.6，活性剂2.4以及适量凝固剂；其中羧基丁腈胶乳具有如下性能：粘度85-95mPa·s，表面张力36-40mN/m，结构凝胶≤35％；所述制备方法包括配料、浸渍胶乳和浸凝固剂、定型、沥滤、半成品干燥、脱模、硫化、烘干和冷却脱模工序，其中半成品干燥的温度为86℃，干燥时间为80分钟；硫化温度为116℃。
实施例二
一种羧基丁腈胶耐油手套的制备方法，该耐油手套以重量份计由下列组份组成：羧基丁腈胶乳100.00，稳定剂0.7，硫化剂1.3，促进剂0.8，防老剂1.1，六亚甲基四胺0.8，活性剂2.0以及适量凝固剂；其中羧基丁腈胶乳具有如下性能：粘度85-95mPa·s，表面张力36-40mN/m，结构凝胶≤35％；所述制备方法包括配料、浸渍胶乳和浸凝固剂、定型、沥滤、半成品干燥、脱模、硫化、烘干和冷却脱模工序，其中半成品干燥的温度为90℃，干燥时间为70分钟；硫化温度为120℃。
实施例三
一种羧基丁腈胶耐油手套的制备方法，该耐油手套以重量份计由下列组份组成：羧基丁腈胶乳100.00，稳定剂0.6，硫化剂1.5，促进剂0.7，防老剂1.2，六亚甲基四胺0.7，活性剂2.2以及适量凝固剂；其中羧基丁腈胶乳具有如下性能：粘度85-95mPa·s，表面张力36-40mN/m，结构凝胶≤35％；所述制备方法包括配料、浸渍胶乳和浸凝固剂、定型、沥滤、半成品干燥、脱模、硫化、烘干和冷却脱模工序，其中半成品干燥的温度为88℃，干燥时间为75分钟；硫化温度为118℃。

Claims (1)

1.一种羧基丁腈胶耐油手套的制备方法，其特征在于，该耐油手套以重量份计由下列组份组成：羧基丁腈胶乳100.00，稳定剂0.5-0.7，硫化剂1.3-1.7，促进剂0.6-0.8，防老剂1.1-1.3，六亚甲基四胺0.6-0.8，活性剂2.0-2.4以及适量凝固剂；其中羧基丁腈胶乳具有如下性能：粘度85-95mPa·s，表面张力36-40mN/m，结构凝胶≤35％；所述制备方法包括配料、浸渍胶乳和浸凝固剂、定型、沥滤、半成品干燥、脱模、硫化、烘干和冷却脱模工序，其中半成品干燥的温度为86-90℃，干燥时间为70-80分钟；硫化温度为116-120℃。
CN201210391248.6A 2012-10-15 2012-10-15 一种羧基丁腈胶耐油手套的制备方法 Pending CN103724742A (zh)