CN103709597A - 一种改性脲甲醛树脂的配方 - Google Patents

一种改性脲甲醛树脂的配方 Download PDF

Info

Publication number
CN103709597A
CN103709597A CN201310720475.3A CN201310720475A CN103709597A CN 103709597 A CN103709597 A CN 103709597A CN 201310720475 A CN201310720475 A CN 201310720475A CN 103709597 A CN103709597 A CN 103709597A
Authority
CN
China
Prior art keywords
formaldehyde resin
agent
formula
urea
parts
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310720475.3A
Other languages
English (en)
Other versions
CN103709597B (zh
Inventor
孙明东
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SUZHOU HUADONG RUBBER Co Ltd
Original Assignee
SUZHOU HUADONG RUBBER Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SUZHOU HUADONG RUBBER Co Ltd filed Critical SUZHOU HUADONG RUBBER Co Ltd
Priority to CN201310720475.3A priority Critical patent/CN103709597B/zh
Publication of CN103709597A publication Critical patent/CN103709597A/zh
Application granted granted Critical
Publication of CN103709597B publication Critical patent/CN103709597B/zh
Expired - Fee Related legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明揭示了一种改性脲甲醛树脂的配方，包括脲甲醛树脂以及添加剂，所述的添加剂包括耐腐蚀剂、耐候剂、抗静电剂、抗氧化剂以及交联剂，所述各成分的重量份数为：所述的脲甲醛树脂800份、耐腐蚀剂30-60份、耐候剂120-150份、抗静电剂80-110份、抗氧化剂70-100份以及交联剂20-50份。通过添加添加剂使得脲甲醛树脂耐酸碱、耐气候、抗静电、抗氧化，通过交联剂调节脲甲醛树脂以及添加剂的性能混乱，使得混合物能够保持原有性能。

Description

一种改性脲甲醛树脂的配方
技术领域
本发明涉及一种塑料配方，具体涉及一种改性脲甲醛树脂的配方。
背景技术
塑料为合成的高分子化合物，是利用单体原料以合成或缩合反应聚合而成的材料，由合成树脂及填料、增塑剂、稳定剂、润滑剂、色料等添加剂组成的。大多数塑料具有质轻、化学性稳定、不会锈蚀、耐冲击性好、绝缘性好等优点，因此，塑料广泛应用于文具制品、餐饮用品、包装用品等领域。
脲甲醛树脂广泛应用于各种塑料、橡胶、陶瓷、耐火材料等产品，因此，需要有优良的机械强度、硬度、阻燃等性能，现如今所用的脲甲醛树脂机械强度、阻燃、耐高温等性能都一般，在制造成产品后往往会因为承受的力量过大或温度过高而导致损坏，无法满足使用的要求。
发明内容
本发明的目的在于提供一种耐腐蚀、耐气候、抗静电、抗氧化、性能稳定的改性脲甲醛树脂的配方。
本发明的技术方案是，一种改性脲甲醛树脂的配方，包括脲甲醛树脂以及添加剂，所述的添加剂包括耐腐蚀剂、耐候剂、抗静电剂、抗氧化剂以及交联剂，所述各成分的重量份数为：所述的脲甲醛树脂800份、耐腐蚀剂30-60份、耐候剂120-150份、抗静电剂80-110份、抗氧化剂70-100份以及交联剂20-50份。
在本发明一个较佳实施例中，所述的耐腐蚀剂为增韧三氧化二铝。
在本发明一个较佳实施例中，所述的耐候剂为2-羟基-4-甲氧基二苯甲酮。
在本发明一个较佳实施例中，所述的抗静电剂为聚氧乙烯硬脂酸酯。  
在本发明一个较佳实施例中，所述的抗氧化剂为特丁基苯二酚。
在本发明一个较佳实施例中，所述的交联剂为2-异丙基咪唑、六氢邻苯二甲酸酐以及三亚乙基四胺的一种或一种以上的混合物。
本发明所述为一种改性脲甲醛树脂的配方，通过添加耐腐蚀剂可以使得脲甲醛树脂耐酸碱，不易被腐蚀，耐候剂可以使得脲甲醛树脂耐气候，使脲甲醛树脂不易被破坏，抗静电剂可以提高脲甲醛树脂的抗静电能力，制成的产品不容易发生静电现象，抗氧化剂可以改善脲甲醛树脂的性能，不易被氧化，交联剂可以调节脲甲醛树脂以及添加剂的性能混乱，使得混合物能够保持原有性能。
具体实施方式
下面对本发明的较佳实施例进行详细阐述，以使本发明的优点和特征能更易于被本领域技术人员理解，从而对本发明的保护范围做出更为清楚明确的界定。
本发明所述为一种改性脲甲醛树脂的配方，包括脲甲醛树脂以及添加剂，所述的添加剂包括耐腐蚀剂、耐候剂、抗静电剂、抗氧化剂以及交联剂，所述各成分的重量份数为：所述的脲甲醛树脂800份、耐腐蚀剂30-60份、耐候剂120-150份、抗静电剂80-110份、抗氧化剂70-100份以及交联剂20-50份。
进一步地，所述的耐腐蚀剂为增韧三氧化二铝。
进一步地，所述的耐候剂为2-羟基-4-甲氧基二苯甲酮。
进一步地，所述的抗静电剂为聚氧乙烯硬脂酸酯。  
进一步地，所述的抗氧化剂为特丁基苯二酚。
进一步地，所述的交联剂为2-异丙基咪唑、六氢邻苯二甲酸酐以及三亚乙基四胺的一种或一种以上的混合物。
实施例1：所述的改性脲甲醛树脂的配方各成分的重量份数为：脲甲醛树脂800份；耐腐蚀剂45份；耐候剂135份；抗静电剂90份；抗氧化剂80份；交联剂30份。
本发明所述为一种改性脲甲醛树脂的配方，通过添加耐腐蚀剂可以使得脲甲醛树脂耐酸碱，不易被腐蚀，耐候剂可以使得脲甲醛树脂耐气候，使脲甲醛树脂不易被破坏，抗静电剂可以提高脲甲醛树脂的抗静电能力，制成的产品不容易发生静电现象，抗氧化剂可以改善脲甲醛树脂的性能，不易被氧化，交联剂可以调节脲甲醛树脂以及添加剂的性能混乱，使得混合物能够保持原有性能。
以上所述仅为本发明的具体实施方式，但本发明的保护范围并不局限于此，任何熟悉本领域的技术人员在本发明所揭露的技术范围内，可不经过创造性劳动想到的变化或替换，都应涵盖在本发明的保护范围之内。因此，本发明的保护范围应该以权利要求书所限定的保护范围为准。

Claims (6)

1.一种改性脲甲醛树脂的配方，包括脲甲醛树脂以及添加剂，其特征在于：所述的添加剂包括耐腐蚀剂、耐候剂、抗静电剂、抗氧化剂以及交联剂，所述各成分的重量份数为：所述的脲甲醛树脂800份、耐腐蚀剂30-60份、耐候剂120-150份、抗静电剂80-110份、抗氧化剂70-100份以及交联剂20-50份。
2.根据权利要求1所述的改性脲甲醛树脂的配方，其特征在于：所述的耐腐蚀剂为增韧三氧化二铝。
3.根据权利要求1所述的改性脲甲醛树脂的配方，其特征在于：所述的耐候剂为2-羟基-4-甲氧基二苯甲酮。
4.根据权利要求1所述的改性脲甲醛树脂的配方，其特征在于：所述的抗静电剂为聚氧乙烯硬脂酸酯。
5.根据权利要求1所述的改性脲甲醛树脂的配方，其特征在于：所述的抗氧化剂为特丁基苯二酚。
6.根据权利要求1所述的改性脲甲醛树脂的配方，其特征在于：所述的交联剂为2-异丙基咪唑、六氢邻苯二甲酸酐以及三亚乙基四胺的一种或一种以上的混合物。
CN201310720475.3A 2013-12-24 2013-12-24 一种改性脲甲醛树脂的配方 Expired - Fee Related CN103709597B (zh)