CN103696295A - Preparation method of terylene-polyamide interwoven fabric - Google Patents
Preparation method of terylene-polyamide interwoven fabric Download PDFInfo
- Publication number
- CN103696295A CN103696295A CN201310652135.1A CN201310652135A CN103696295A CN 103696295 A CN103696295 A CN 103696295A CN 201310652135 A CN201310652135 A CN 201310652135A CN 103696295 A CN103696295 A CN 103696295A
- Authority
- CN
- China
- Prior art keywords
- hours
- dyeing
- terylene
- polyamide
- bath
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a preparation method of a terylene-polyamide interwoven fabric. The method comprises the following steps: (1) desizing with an oxidizing agent; (2) repeatedly refining and splitting in a jar, adding 2-3g/L sodium carbonate, 5-6g/L sodium tripolyphosphate and 3-4g/L albafluid, and refining at 115 DEG C for 3 hours; (3) fixing the color of polyamide yarns, adding a 3g/L acid color fixing agent and 4g/L glacial acetic acid, and fixing color at 95 DEG C for 1 hour; (4) dyeing terylene under the condition that the pH value of dye bath is 3.5 and the bath ratio is 2:15, heating to 120 DEG C at the speed of 5 DEG C per minute, preserving heat for 2 hours, cooling to 30 DEG C at the speed of 4 DEG C per minute, draining water and cleaning; (5) washing at the water temperature of 65 DEG C for 40 minutes; (6) dyeing polyamide yarns under the condition that the pH value of dye bath is 4 and the bath ratio is 2:15, heating to 90 DEG C at the speed of 3 DEG C per minute, preserving heat for 2 hours, cooling to 30 DEG C at the speed of 5 DEG C per minute, draining water and cleaning; (7) soaping at the 60 DEG C for 40 minutes; (8) fully washing with water, and fixing color at 65 DEG C for 1 hour; and (9) sizing. The terylene-polyamide interwoven fabric prepared with the method has the advantages of high air permeability, extremely high drapability, smoothness, wear resistance and wrinkle resistance.
Description
Technical field
The present invention relates to wash the manufacture method of bright and beautiful interwoven fabric.
Background technology
Wash fabric production technical difficulty that brocade interweaves mainly in the control of feel, wash the two-color effect of brocade dyeing, in the problems such as COLOR FASTNESS of POLYAMIDE YARNS, because use and the technique of interwoven fabric dyestuff is all not quite similar, so need step by step meticulously in design technology, guarantee the COLOR FASTNESS quality of bi-material.
Summary of the invention
The object of the present invention is to provide a kind of manufacture method of washing bright and beautiful interwoven fabric, its manufacture wash bright and beautiful interwoven fabric good permeability, have fabulous drapability, slipping, wear-resisting crease-resistant, and adopt advanced cool feeling to arrange, higher wearing comfort is provided.
For achieving the above object, technical scheme of the present invention is a kind of manufacture method of washing bright and beautiful interwoven fabric of design, comprises the steps:
1) oxidant destarch;
2) adopt machine cylinder freshening to open fibre, add 2-3g/L soda ash, 5-6g/L sodium phosphate trimer, 3-4g/L Ah white and moist, in 115 ℃ of freshenings 3 hours;
3) POLYAMIDE YARNS fixation, adds 3g/L acidic color fixing agent, and 4g/L glacial acetic acid, in 95 ℃ of fixation 1 hour;
4) dyeing terylene, dyeing bath pH value 3.5, bath raio 2:15, is heated to 120 ℃ with 5 ℃/min, is incubated 2 hours, with 4 ℃/min, is cooled to 30 ℃, and draining is cleaned;
5) under 65 ℃ of water temperature conditions, wash 40 minutes;
6) POLYAMIDE YARNS dyeing; Dyeing bath pH value 4, bath raio 2:15, is heated to 90 ℃ with 3 ℃/min, is incubated 2 hours, and with 5 ℃/min but to 30 ℃, draining is cleaned;
7) at 60 ℃, soap 40 minutes;
8) fully washing, 65 ℃ of fixation 1 hour;
9) sizing.
Advantage of the present invention and beneficial effect are: a kind of manufacture method of washing bright and beautiful interwoven fabric is provided, its manufacture wash bright and beautiful interwoven fabric good permeability, there are fabulous drapability, slipping, wear-resisting crease-resistant, and adopt advanced cool feeling to arrange, higher wearing comfort is provided.
The specific embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A manufacture method of washing bright and beautiful interwoven fabric, comprises the steps:
1) oxidant destarch;
2) adopt machine cylinder freshening to open fibre, add 2g/L soda ash, 5g/L sodium phosphate trimer, 3g/L Ah white and moist, in 115 ℃ of freshenings 3 hours;
3) POLYAMIDE YARNS fixation, adds 3g/L acidic color fixing agent, and 4g/L glacial acetic acid, in 95 ℃ of fixation 1 hour;
4) dyeing terylene, dyeing bath pH value 3.5, bath raio 2:15, is heated to 120 ℃ with 5 ℃/min, is incubated 2 hours, with 4 ℃/min, is cooled to 30 ℃, and draining is cleaned;
5) under 65 ℃ of water temperature conditions, wash 40 minutes;
6) POLYAMIDE YARNS dyeing; Dyeing bath pH value 4, bath raio 2:15, is heated to 90 ℃ with 3 ℃/min, is incubated 2 hours, and with 5 ℃/min but to 30 ℃, draining is cleaned;
7) at 60 ℃, soap 40 minutes;
8) fully washing, 65 ℃ of fixation 1 hour;
9) sizing.
Embodiment 2
A manufacture method of washing bright and beautiful interwoven fabric, comprises the steps:
1) oxidant destarch;
2) adopt machine cylinder freshening to open fibre, add 3g/L soda ash, 6g/L sodium phosphate trimer, 4g/L Ah white and moist, in 115 ℃ of freshenings 3 hours;
3) POLYAMIDE YARNS fixation, adds 3g/L acidic color fixing agent, and 4g/L glacial acetic acid, in 95 ℃ of fixation 1 hour;
4) dyeing terylene, dyeing bath pH value 3.5, bath raio 2:15, is heated to 120 ℃ with 5 ℃/min, is incubated 2 hours, with 4 ℃/min, is cooled to 30 ℃, and draining is cleaned;
5) under 65 ℃ of water temperature conditions, wash 40 minutes;
6) POLYAMIDE YARNS dyeing; Dyeing bath pH value 4, bath raio 2:15, is heated to 90 ℃ with 3 ℃/min, is incubated 2 hours, and with 5 ℃/min but to 30 ℃, draining is cleaned;
7) at 60 ℃, soap 40 minutes;
8) fully washing, 65 ℃ of fixation 1 hour;
9) sizing.
Embodiment 3
A manufacture method of washing bright and beautiful interwoven fabric, comprises the steps:
1) oxidant destarch;
2) adopt machine cylinder freshening to open fibre, add 2.3g/L soda ash, 5.6g/L sodium phosphate trimer, 3.4g/L Ah white and moist, in 115 ℃ of freshenings 3 hours;
3) POLYAMIDE YARNS fixation, adds 3g/L acidic color fixing agent, and 4g/L glacial acetic acid, in 95 ℃ of fixation 1 hour;
4) dyeing terylene, dyeing bath pH value 3.5, bath raio 2:15, is heated to 120 ℃ with 5 ℃/min, is incubated 2 hours, with 4 ℃/min, is cooled to 30 ℃, and draining is cleaned;
5) under 65 ℃ of water temperature conditions, wash 40 minutes;
6) POLYAMIDE YARNS dyeing; Dyeing bath pH value 4, bath raio 2:15, is heated to 90 ℃ with 3 ℃/min, is incubated 2 hours, and with 5 ℃/min but to 30 ℃, draining is cleaned;
7) at 60 ℃, soap 40 minutes;
8) fully washing, 65 ℃ of fixation 1 hour;
9) sizing.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. the manufacture method of washing bright and beautiful interwoven fabric, is characterized in that, comprises the steps:
1) oxidant destarch;
2) adopt machine cylinder freshening to open fibre, add 2-3g/L soda ash, 5-6g/L sodium phosphate trimer, 3-4g/L Ah white and moist, in 115 ℃ of freshenings 3 hours;
3) POLYAMIDE YARNS fixation, adds 3g/L acidic color fixing agent, and 4g/L glacial acetic acid, in 95 ℃ of fixation 1 hour;
4) dyeing terylene, dyeing bath pH value 3.5, bath raio 2:15, is heated to 120 ℃ with 5 ℃/min, is incubated 2 hours, with 4 ℃/min, is cooled to 30 ℃, and draining is cleaned;
5) under 65 ℃ of water temperature conditions, wash 40 minutes;
6) POLYAMIDE YARNS dyeing; Dyeing bath pH value 4, bath raio 2:15, is heated to 90 ℃ with 3 ℃/min, is incubated 2 hours, and with 5 ℃/min but to 30 ℃, draining is cleaned;
7) at 60 ℃, soap 40 minutes;
8) fully washing, 65 ℃ of fixation 1 hour;
9) sizing.