CN103668387A - Practical nickel-free sealing agent for aluminum alloy anodic oxidation - Google Patents
Practical nickel-free sealing agent for aluminum alloy anodic oxidation Download PDFInfo
- Publication number
- CN103668387A CN103668387A CN201210325304.6A CN201210325304A CN103668387A CN 103668387 A CN103668387 A CN 103668387A CN 201210325304 A CN201210325304 A CN 201210325304A CN 103668387 A CN103668387 A CN 103668387A
- Authority
- CN
- China
- Prior art keywords
- sealing agent
- hole sealing
- agent
- practical
- hole
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a practical nickel-free sealing agent for aluminum alloy anodic oxidation, which is prepared by compounding primary salt sodium acetate, secondary salt cobalt acetate and a penetrant sorbitol in combination with an assistant. The physical state is powder or water. The practical nickel-free sealing agent for aluminum alloy anodic oxidation, provided by the invention, is affordable and non-toxic to the ecological environment, and realizes an equivalent effect as nickel salt sealing; the sealing effect on an organic dyed film (red or yellow) is better than that of a nickel salt sealing agent.
Description
Technical field
The present invention relates to aluminium alloy anode oxide without nickel hole sealing technology field, be specifically related to a kind of aluminium alloy anode oxide practical without nickel hole sealing agent.
Background technology
Since nickel salt hole sealing agent is born, nickeliferous hole sealing agent occupies the inundatory market share in aluminium alloy anode oxide sealing always, it is relatively low that reason is that nickeliferous hole sealing agent possesses sealing of hole leaching (redness or yellow dyes exception), energy consumption fast, simple to operate, that can effectively prevent dyeing film dyestuff when sealing of hole, through sealing of hole anodic oxidation aluminum products properties out, all can reach relevant criterion.Nickel salt hole sealing agent is many to aluminium processing development contribution, but metallic nickel is undisputable fact to the pollution of environment.In addition, nickeliferous liquor of hole-sealing tank is containing a large amount of nickel ions, workers with long time is exposed under this environment, with workpiece Long Term Contact, supersensitivity contact dermatitis, even carcinogenic risk, for this reason use of the multinational nickeliferous hole sealing agent of keeping under strict control of European Union are brought out in existence, and put into effect specially relevant limit standard, as BSEN12472:2005.No matter, from current environmental requirement angle or from social sustainable development angle, nickeliferous hole sealing agent is banned without nickel hole sealing agent will be the firm fact.At present about a lot of without the relevant report of nickel hole sealing technology, but comparative maturity is also successfully realized the few of industrialization practice, as Henkel KGaA is approved in European market without nickel hole sealing agent, this hole sealing agent is to take cobalt salt as main component, but because cobalt salt is expensive and such hole sealing agent energy consumption is high, the overall cost of its industrial application is higher, so unsatisfactory in Chinese Industrialization application.Therefore, developing practical is current and long-range direction without nickel hole sealing technology.
Summary of the invention
For practicality without nickel hole sealing technology blank at home, the object of the present invention is to provide a kind of price material benefit, to ecotope toxicological harmless effect, suitable with nickel salt sealing of hole effect, the aluminium alloy anode oxide that the sealing effect of organic dyeing film (red or yellow) is better than to nickel salt hole sealing agent is practical without nickel hole sealing agent.
Alloy anode of the present invention oxidation is practical without nickel hole sealing agent, take sodium-acetate as main salt, and Cobaltous diacetate is auxiliary salt, and sorbyl alcohol is permeate agent, then is equipped with additive compound and forms.
The described physical condition without nickel hole sealing agent can be pulvis or aqua.
Preferably,
Its composition is configured to by weight percentage: described sodium-acetate 20~30%, described Cobaltous diacetate 0.3~1.0%, described sorbyl alcohol 3~8%, described auxiliary agent 15~20%, water surplus.
During preparation, sodium-acetate, Cobaltous diacetate, sorbyl alcohol, auxiliary agent is water-soluble, stir.
Described auxiliary agent comprises and presses down grey agent, promotor, tensio-active agent, steady toner.
But described grey agent is dextrin.
Described promotor is one or both in boric acid, citric acid.
Described tensio-active agent is one or more in AES (being polyoxyethylenated alcohol sodium sulfate), trolamine and triethanolamine salt.
Described steady toner is one or both in peach gum, balsam.
Described sodium-acetate is one or both in crystal water sodium-acetate, sodium acetate, anhydrous.
Described hole sealing agent work bath parameters is: concentration 10g/L, pH:5.5~6.0, time: 1.0um/min, temperature: 85~90 ℃.
Not only price material benefit of the present invention, to ecotope toxicological harmless effect, suitable with nickel salt sealing of hole effect, and can substantially improve its sealing of hole net effect, make the sealing effect of organic dyeing film (red or yellow) be better than nickel salt hole sealing agent.
Embodiment
The present invention design is: hole sealing agent can be take sodium-acetate as main salt, and Cobaltous diacetate is auxiliary salt, and sorbyl alcohol is permeate agent, then is equipped with auxiliary agent and carries out that science is composite to be formed.Wherein take sodium-acetate as main salt, and it is according to being: sodium-acetate relative low price, and the source of goods is stable; Sodium-acetate is nontoxic, can not destroy ecotope; Sodium-acetate occurs with auxiliary salt identity, and has confirmed to possess certain sealing of hole effect in nickel salt hole sealing agent.Then adding Cobaltous diacetate is auxiliary salt, and sorbyl alcohol is permeate agent, is equipped with auxiliary agent (containing pressing down grey agent, promotor, tensio-active agent, steady toner), further substantially improves its sealing of hole net effect.
The present invention design realizes by following embodiment, aluminum usedly in operating process is same specification 6063 section bars.By specific embodiments of the invention given below, can further understand the present invention, but they not limitation of the invention.Some nonessential improvement and adjustment of for those skilled in the art, according to foregoing invention content, doing, be also considered as dropping in protection scope of the present invention.
In addition, unless stated otherwise, the per-cent adopting in the present invention is all weight percentage.
Embodiment 1
Pre-treatment: acid deoiling → twice washing → alkaline etching → twice washing → bright dipping → twice washing
Anodic oxidation: sulfuric acid concentration 160~180g/L, current density 1.45A/dm
2, 20 ℃ of temperature,
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.5, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (sodium-acetate 20%, Cobaltous diacetate 0.3%, sorbyl alcohol 3%, auxiliary agent 15%, water surplus)
Embodiment 2
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.8, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 1)
Embodiment 3
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:6.0, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 1)
Embodiment 4
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.5, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 1)
Embodiment 5
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.8, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 1)
Embodiment 6
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:6.0, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 1)
Embodiment 7
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.5, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (sodium-acetate 20%, Cobaltous diacetate 1.0%, sorbyl alcohol 8%, auxiliary agent 20%, water surplus)
Embodiment 8
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.8, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 7)
Embodiment 9
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:6.0, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 7)
Embodiment 10
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.5, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 7)
Embodiment 11
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.8, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 7)
Embodiment 12
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:6.0, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 7)
Embodiment 13
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.5, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (sodium-acetate 25%, Cobaltous diacetate 0.6%, sorbyl alcohol 5%, auxiliary agent 18%, water surplus)
Embodiment 14
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.8, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 13)
Embodiment 15
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:6.0, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 13)
Embodiment 16
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.5, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 13)
Embodiment 17
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.8, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 13)
Embodiment 18
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:6.0, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 13)
Embodiment 19
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.5, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (sodium-acetate 30%, Cobaltous diacetate 0.3%, sorbyl alcohol 3%, auxiliary agent 15%, water surplus)
Embodiment 20
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.8, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 19)
Embodiment 21
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:6.0, temperature: 85 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 19)
Embodiment 22
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.5, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 19)
Embodiment 23
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:5.8, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 19)
Embodiment 24
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Sealing of hole: hole sealing agent concentration 10g/L, pH:6.0, temperature: 90 ℃, time 1.0um/min,
Hole sealing agent stoste forms (consistent with embodiment 19)
Embodiment 25
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Dyeing: wild organic dye difficult to understand is red
Sealing of hole: embodiment 1~embodiment 24 randomly draws 8
Hole sealing agent stoste forms (embodiment 1~embodiment 24 randomly draws)
Embodiment 26
Pre-treatment: condition is consistent with embodiment 1
Anodic oxidation: operating parameters is consistent with embodiment 1
Dyeing: wild organic dye difficult to understand is yellow
Sealing of hole: embodiment 1~embodiment 24 randomly draws 8
Hole sealing agent stoste forms (embodiment 1~embodiment 24 randomly draws)
Embodiment result:
1, from embodiment 1~embodiment 6, hole sealing agent stoste used forms: sodium-acetate 20%, Cobaltous diacetate 0.3%, sorbyl alcohol 3%, auxiliary agent 15%, water surplus; In embodiment 7~embodiment 12, hole sealing agent stoste used forms: sodium-acetate 20%, Cobaltous diacetate 1.0%, sorbyl alcohol 8%, auxiliary agent 20%, water surplus; In embodiment 13~embodiment 18, hole sealing agent stoste used forms: sodium-acetate 25%, Cobaltous diacetate 0.6%, sorbyl alcohol 5%, auxiliary agent 18%, water surplus; In embodiment 19~embodiment 24, hole sealing agent stoste used forms: sodium-acetate 30%, Cobaltous diacetate 0.3%, sorbyl alcohol 3%, auxiliary agent 15%, water surplus, above embodiment sealing of hole is respond well.
2, pH=5.5 in embodiment 1,7,13,19; PH=5.8 in embodiment 2,8,14,20; PH=6.0 in embodiment 3,9,15,21, above embodiment sealing of hole is respond well.
3, under equal conditions, 90 ℃ of 85 ℃ of embodiment 1 working temperatures and embodiment 4 working temperatures; 90 ℃ of 85 ℃ of embodiment 2 working temperatures and embodiment 5 working temperatures; 90 ℃ of 85 ℃ of embodiment 3 working temperatures and embodiment 6 working temperatures; 90 ℃ of 85 ℃ of embodiment 7 working temperatures and embodiment 10 working temperatures; 90 ℃ of 85 ℃ of embodiment 8 working temperatures and embodiment 11 working temperatures; 90 ℃ of 85 ℃ of embodiment 9 working temperatures and embodiment 12 working temperatures; 90 ℃ of 85 ℃ of embodiment 13 working temperatures and embodiment 16 working temperatures; 90 ℃ of 85 ℃ of embodiment 14 working temperatures and embodiment 17 working temperatures; 90 ℃ of 85 ℃ of embodiment 15 working temperatures and embodiment 18 working temperatures; 90 ℃ of 85 ℃ of embodiment 19 working temperatures and embodiment 22 working temperatures; 90 ℃ of 85 ℃ of embodiment 20 working temperatures and embodiment 23 working temperatures; 90 ℃ of 85 ℃ of embodiment 21 working temperatures and embodiment 24 working temperatures, above group of row contrast, 90 ℃ of the latter's working temperatures are higher than the sealing of hole speed of 85 ℃ of the former working temperatures, and above embodiment sealing of hole is respond well.
4, hole sealing agent stoste used in embodiment 1~embodiment 6, embodiment 19~embodiment 24, auxiliary agent accounts for 15%; Hole sealing agent stoste used in embodiment 13~embodiment 18, auxiliary agent accounts for 18%; Hole sealing agent stoste used in embodiment 7~embodiment 12, auxiliary agent accounts for 20%, and above embodiment sealing of hole is respond well, and auxiliary agent accounts for anodic oxidation product appearance that 20% embodiment seals out, and obviously than auxiliary agent, to account for 15% embodiment smooth.
5, embodiment 25~26 (randomly draws 8 sealing of hole experiments of doing yellow, red staining film from embodiment 1~embodiment 24, and compare with general nickeliferous hole sealing agent), in test, yellow, the decolouring phenomenon of red staining film in nickeliferous liquor of hole-sealing tank are relatively serious.
Interpretation of result:
1, from embodiment 1~embodiment 24, show that the practical hole sealing agent of this aluminium alloy anode oxide forms tolerable limit and is: sodium-acetate 20~30%, Cobaltous diacetate 0.3%~1.0%, sorbyl alcohol 3~8%, auxiliary agent 15~20%;
2, from embodiment 1~embodiment 3, embodiment 7~embodiment 9, embodiment 13~embodiment 15, embodiment 19~embodiment 21 draws, its work tank liquor pH value tolerable limit is 5.5~6.0;
3, from embodiment 1 and embodiment 4, embodiment 2 and embodiment 5, embodiment 3 and embodiment 6, embodiment 7 and embodiment 10, embodiment 8 and embodiment 11, embodiment 9 and embodiment 12, embodiment 13 and embodiment 16, embodiment 14 and embodiment 17, embodiment 15 and embodiment 18, embodiment 19 and embodiment 22, embodiment 20 and embodiment 23, embodiment 21 and embodiment 24, draw, with the variation of tank liquor operation interval (85~90 ℃), the practical sealing of hole ability without nickel hole sealing agent of aluminium alloy anode oxide is in rising trend.
4, from embodiment 1 and embodiment 7, draw, in assistant concentration constant interval (15~20%), along with assistant concentration ratio increases, more smooth through sealing of hole anodic oxidation goods out.
5, through embodiment 25,26, show that aluminium alloy anode oxide is practical, without nickel hole sealing agent, the sealing effect of organic dyeing film (red or yellow) is better than to nickel salt hole sealing agent.
Claims (10)
1. aluminium alloy anode oxide is practical without a nickel hole sealing agent, it is characterized in that: take sodium-acetate as main salt, Cobaltous diacetate is auxiliary salt, and sorbyl alcohol is permeate agent, then is equipped with additive compound and forms.
2. aluminium alloy anode oxide as claimed in claim 1 is practical without nickel hole sealing agent, it is characterized in that: the described physical condition without nickel hole sealing agent is pulvis or aqua.
3. aluminium alloy anode oxide as claimed in claim 1 is practical without nickel hole sealing agent, it is characterized in that: its composition is configured to by weight percentage: described sodium-acetate 20~30%, described Cobaltous diacetate 0.3~1.0%, described sorbyl alcohol 3~8%, described auxiliary agent 15~20%, water surplus.
4. aluminium alloy anode oxide as claimed in claim 3 is practical without nickel hole sealing agent, it is characterized in that: described auxiliary agent comprises and presses down grey agent, promotor, tensio-active agent, steady toner.
5. aluminium alloy anode oxide as claimed in claim 4 is practical without nickel hole sealing agent, it is characterized in that: but described grey agent is dextrin.
6. aluminium alloy anode oxide as claimed in claim 4 is practical without nickel hole sealing agent, it is characterized in that: described promotor is one or both in boric acid, citric acid.
7. aluminium alloy anode oxide as claimed in claim 4 is practical without nickel hole sealing agent, it is characterized in that: described tensio-active agent is one or more in AES, trolamine and triethanolamine salt.
8. aluminium alloy anode oxide as claimed in claim 4 is practical without nickel hole sealing agent, it is characterized in that: described steady toner is one or both in peach gum, balsam.
9. aluminium alloy anode oxide as claimed in claim 4 is practical without nickel hole sealing agent, it is characterized in that: described sodium-acetate is one or both in crystal water sodium-acetate, sodium acetate, anhydrous.
10. aluminium alloy anode oxide as claimed in claim 4 is practical without nickel hole sealing agent, it is characterized in that: its work bath parameters is: concentration 10g/L, pH:5.5~6.0, time: 1.0um/min, temperature: 85~90 ℃.