CN103666156A - 一种耐紫外线铜雕塑用丙烯酸树脂油漆 - Google Patents

一种耐紫外线铜雕塑用丙烯酸树脂油漆 Download PDF

Info

Publication number
CN103666156A
CN103666156A CN201310676008.5A CN201310676008A CN103666156A CN 103666156 A CN103666156 A CN 103666156A CN 201310676008 A CN201310676008 A CN 201310676008A CN 103666156 A CN103666156 A CN 103666156A
Authority
CN
China
Prior art keywords
parts
acrylic resin
paint
glycidyl ether
hour
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
CN201310676008.5A
Other languages
English (en)
Other versions
CN103666156B (zh
Inventor
郑东平
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
TONGLING XINJIUDING COPPER CULTURE INDUSTRY Co Ltd
Original Assignee
TONGLING XINJIUDING COPPER CULTURE INDUSTRY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by TONGLING XINJIUDING COPPER CULTURE INDUSTRY Co Ltd filed Critical TONGLING XINJIUDING COPPER CULTURE INDUSTRY Co Ltd
Priority to CN201310676008.5A priority Critical patent/CN103666156B/zh
Publication of CN103666156A publication Critical patent/CN103666156A/zh
Application granted granted Critical
Publication of CN103666156B publication Critical patent/CN103666156B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明涉及一种油漆，具体涉及一种耐紫外线铜雕塑用丙烯酸树脂油漆，本发明油漆由以下重量份的原料制成：纳米二氧化铈2-3、硅酸钾3-4、硅酸锂1-2、丙烯酸树脂30-34、柠檬酸铜1-2、2-氨乙基十七烯基咪唑啉1-2、二缩三丙二醇二丙烯酸酯10-12、苯基缩水甘油醚1-2、丙烯基缩水甘油醚4-7、乙烯基三乙氧基硅烷2-3、促进剂Na-220.5-1.2、钛酸四丁酯2-3、异佛尔酮二胺1-2、三羟甲基丙烷三丙烯酸酯10-12、过氧化二异丙苯1-2、二甲胺基丙胺4-6、助剂5-6、二甲苯10-12、乙酸丁酯10-12；本发明油漆含有纳米二氧化铈，再结合其他原料，制备的油漆硬度高，光学性能好，耐紫外辐照老化，耐环境腐蚀，性质稳定，使用寿命长。

Description

一种耐紫外线铜雕塑用丙烯酸树脂油漆
技术领域
本发明涉及一种油漆，具体涉及一种耐紫外线铜雕塑用丙烯酸树脂油漆及其制备工艺。
背景技术
铜雕塑是日常生活中常见的一类工艺品，具有较高的艺术价值和欣赏价值，然而，铜雕塑艺术品由于其本身材质性质及摆放环境的特点，容易出现氧化腐蚀等问题，影响美观和使用寿命，为了保护铜器，往往需要在雕塑外面涂上油漆，并且对铜雕塑用漆有一定的要求，比如附着力、耐候老化、耐日光暴晒、耐温等等，因此，需要改进油漆配方，配制出适合不同使用场合的油漆，增加其艺术价值。
发明内容
本发明的目的在于，提供一种耐紫外线铜雕塑用丙烯酸树脂油漆，以保护雕塑品，为了实现上述目的，本发明采用的技术方案如下：
一种耐紫外线铜雕塑用丙烯酸树脂油漆，其特征在于，本发明材料由以下重量份的原料制成：纳米二氧化铈2-3、硅酸钾3-4、硅酸锂1-2、丙烯酸树脂30-34、柠檬酸铜1-2、2-氨乙基十七烯基咪唑啉1-2、二缩三丙二醇二丙烯酸酯10-12、苯基缩水甘油醚1-2、丙烯基缩水甘油醚4-7、乙烯基三乙氧基硅烷2-3、促进剂Na-220.5-1.2、钛酸四丁酯2-3、异佛尔酮二胺1-2、三羟甲基丙烷三丙烯酸酯10-12、过氧化二异丙苯1-2、二甲胺基丙胺4-6、助剂5-6、二甲苯10-12、乙酸丁酯10-12。
所述的助剂由以下重量份的原料制成：粘土10-12、硅藻土3-4、玉石2-3、海泡石2-3、促进剂DTDM1-2、交联剂TAC2-3、癸二酸钠1-2、烷基酚聚氧乙烯醚4-5、三聚磷酸钠1-2、甘油三醋酸酯35-40、二硼化钒1-2、没食子酸丙酯1-2、薏仁油2-3、表儿茶素1-2；其制备方法是将粘土、硅藻土、玉石、海泡石送入煅烧炉中在700-720℃下煅烧2-3小时，然后取出，送入10-15%的盐酸溶液中浸泡2-3小时，过滤，得滤渣，用清水洗净，烘干、研磨成400-600目粉体；所得粉体与其它剩余成分混合，加热至60-70℃，搅拌反应40-50分钟，冷却，研磨成浆料，即得。
所述的一种耐紫外线铜雕塑用丙烯酸树脂油漆，其制备工艺为：
（1）将纳米二氧化铈、二缩三丙二醇二丙烯酸酯、钛酸四丁酯、三羟甲基丙烷三丙烯酸酯、助剂混合，加入到二甲苯、乙酸丁酯溶剂中，加热至120-130℃，反应3-4小时；
（2）将步骤（1）的物料冷却至70-85℃，加入苯基缩水甘油醚、丙烯基缩水甘油醚、乙烯基三乙氧基硅烷、过氧化二异丙苯，搅拌反应3-4小时；
（3）将步骤（2）的物料降温至50-65℃，加入其它剩余物料，搅拌反应40-60分钟后，冷却至室温，研磨成20-60μm浆料，即得。
与现有技术相比，本发明提供的铜雕塑用油漆具备以下优点：特别添加了纳米二氧化铈原料，再结合其他原料，有效的改善了传统丙烯酸树脂材料的性能，制得的油漆硬度高，光学性能好，耐紫外辐照老化，耐环境腐蚀，性质稳定，使用时间长，且生产工艺相对简单，可以广泛用于各类青铜工艺品。
具体实施方式
实施例
本实施例油漆由以下重量份原料制成：纳米二氧化铈3、硅酸钾4、硅酸锂2、丙烯酸树脂34、柠檬酸铜2、2-氨乙基十七烯基咪唑啉2、二缩三丙二醇二丙烯酸酯12、苯基缩水甘油醚2、丙烯基缩水甘油醚6、乙烯基三乙氧基硅烷3、促进剂Na-221、钛酸四丁酯3、异佛尔酮二胺2、三羟甲基丙烷三丙烯酸酯12、过氧化二异丙苯2、二甲胺基丙胺6、助剂6、二甲苯12、乙酸丁酯12。
所述的助剂由以下重量份的原料制成：粘土12、硅藻土4、玉石3、海泡石3、促进剂DTDM2、交联剂TAC3、癸二酸钠2、烷基酚聚氧乙烯醚5、三聚磷酸钠2、甘油三醋酸酯40、二硼化钒2、没食子酸丙酯2、薏仁油3、表儿茶素2；其制备方法是将粘土、硅藻土、玉石、海泡石送入煅烧炉中在700-720℃下煅烧3小时，然后，取出，送入15%的盐酸溶液中浸泡3小时，过滤，得滤渣，用清水洗净，烘干、研磨成500目粉体；所得粉体与其它剩余成分混合，加热至60-70℃，搅拌反应50分钟，冷却，研磨成浆料，即得。
所述的一种耐紫外线铜雕塑用丙烯酸树脂油漆，其制备工艺为：
（1）将纳米二氧化铈、二缩三丙二醇二丙烯酸酯、钛酸四丁酯、三羟甲基丙烷三丙烯酸酯、助剂混合，加入到二甲苯、乙酸丁酯溶剂中，加热至120-130℃，反应4小时；
（2）将步骤（1）的物料冷却至70-85℃，加入苯基缩水甘油醚、丙烯基缩水甘油醚、乙烯基三乙氧基硅烷、过氧化二异丙苯，搅拌反应4小时；
（3）将步骤（2）的物料降温至50-65℃，加入其它剩余物料，搅拌反应50分钟后，冷却至室温，研磨成40μm浆料，即得。
本发明油漆的性能测试结果为：
Figure BDA0000434902970000031
上述测试均遵循相关标准进行。

Claims (2)

1.一种耐紫外线铜雕塑用丙烯酸树脂油漆，其特征在于，该油漆由以下重量份的原料制成：纳米二氧化铈2-3、硅酸钾3-4、硅酸锂1-2、丙烯酸树脂30-34、柠檬酸铜1-2、2-氨乙基十七烯基咪唑啉1-2、二缩三丙二醇二丙烯酸酯10-12、苯基缩水甘油醚1-2、丙烯基缩水甘油醚4-7、乙烯基三乙氧基硅烷2-3、促进剂Na-22 0.5-1.2、钛酸四丁酯2-3、异佛尔酮二胺1-2、三羟甲基丙烷三丙烯酸酯10-12、过氧化二异丙苯1-2、二甲胺基丙胺4-6、助剂5-6、二甲苯10-12、乙酸丁酯10-12；
所述的助剂由以下重量份的原料制成：粘土10-12、硅藻土3-4、玉石2-3、海泡石2-3、促进剂DTDM 1-2、交联剂 TAC 2-3、癸二酸钠1-2、烷基酚聚氧乙烯醚4-5、三聚磷酸钠1-2、甘油三醋酸酯35-40、二硼化钒1-2、没食子酸丙酯1-2、薏仁油2-3、表儿茶素1-2；其制备方法是将粘土、硅藻土、玉石、海泡石送入煅烧炉中在700-720℃下煅烧2-3小时，然后取出，送入10-15%的盐酸溶液中浸泡2-3小时，过滤，得滤渣，用清水洗净，烘干、研磨成400-600目粉体；所得粉体与其它剩余成分混合，加热至60-70℃，搅拌反应40-50分钟，冷却，研磨成浆料，即得。
2.如权利要求1所述的一种耐紫外线铜雕塑用丙烯酸树脂油漆，其制作工艺为：
（1）将纳米二氧化铈、二缩三丙二醇二丙烯酸酯、钛酸四丁酯、三羟甲基丙烷三丙烯酸酯、助剂混合，加入到二甲苯、乙酸丁酯溶剂中，加热至120-130℃，反应3-4小时；
（2）将步骤（1）的物料冷却至70-85℃，加入苯基缩水甘油醚、丙烯基缩水甘油醚、乙烯基三乙氧基硅烷、过氧化二异丙苯，搅拌反应3-4小时；
（3）将步骤（2）的物料降温至50-65℃，加入其它剩余物料，搅拌反应40-60分钟后，冷却至室温，研磨成20-60μm浆料，即得。
CN201310676008.5A 2013-12-07 2013-12-07 一种耐紫外线铜雕塑用丙烯酸树脂油漆 Active CN103666156B (zh)