CN103665900A - High-performance anti-solarization wood-plastic composite material - Google Patents
High-performance anti-solarization wood-plastic composite material Download PDFInfo
- Publication number
- CN103665900A CN103665900A CN201310532708.7A CN201310532708A CN103665900A CN 103665900 A CN103665900 A CN 103665900A CN 201310532708 A CN201310532708 A CN 201310532708A CN 103665900 A CN103665900 A CN 103665900A
- Authority
- CN
- China
- Prior art keywords
- parts
- wood
- plastic composite
- performance
- solarization
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-performance anti-solarization wood-plastic composite material which is composed of the following raw materials in parts by weight: 50-60 parts of polyethylene resin particle, 70-80 parts of wood fiber, 6-8 parts of nano bauxite, 3-4 parts of tributyl citrate, 2-4 parts of methyl isothiazolinone, 1-2 parts of zinc naphthenate, 2-3 parts of pentaerythritol, 1-2 parts of cetyl trimethyl ammonium bromide, 1-2 parts of aminopropyltriethoxysilane and 6-10 parts of binding assistant. According to the invention, the wood-plastic composite material has excellent performance such as weather resistance, chemical corrosion resistance, compression resistance, stretching resistance, aging resistance and the like, has high mechanical strength, high dimensional stability, favorable high and low temperature resistance and high anti-solarization performance, and can be used as an outdoor construction material.
Description
Technical field
The present invention relates generally to a kind of matrix material, relates in particular to the anti-Japanese solarization wood plastic composite of a kind of high-performance.
Background technology
Wood plastic composite is the class advanced composite material being in recent years surging forward both at home and abroad, refer to utilize polyethylene, polypropylene and polyvinyl chloride etc., replace common resin adhesive, be mixed into new wood materials with useless vegetable fibres such as surpassing more than 50% wood powder, rice husk, stalk, again through the plastic processings such as extruding, mold pressing, injection molding, the sheet material of producing or section bar.Be mainly used in the industries such as building materials, furniture, logistics packaging.Plastics and wooden powder are mixed to the sheet material by hot extrusion molding by a certain percentage, be referred to as to push wood-plastic composite panel.
Summary of the invention
The object of the invention is just to provide the anti-Japanese solarization wood plastic composite of a kind of high-performance.
The present invention is achieved by the following technical solutions:
The anti-Japanese solarization wood plastic composite of high-performance, it is comprised of the raw material of following weight parts:
Waste and old polystyrene plastics reclaims pellet 62-70, wood fibre 70-80, sodium polyacrylate 2-4, dioctyl phthalate (DOP) 2-3, magnesium hydroxide 2-3, wilkinite 5-6, mineral wool fibre 1-2, sorbyl alcohol 2-3, urea groups propyl-triethoxysilicane 1-2, Octabenzone 0.8-1, antioxidant 1010 1-2, adhesive aid 5-10;
Described adhesive aid is comprised of the raw material of following weight parts:
Polyvinyl alcohol 15-20, hexamethoxymethyl melamine resin 3-4, polyamide wax micropowder 2-3, dialdehyde starch 4-5, Jojoba oil 1-2, anilinomethyl triethoxysilane 1-2;
Above-mentioned polyvinyl alcohol is joined in reactor, be heated to 70-80 ℃, add polyamide wax micropowder, insulation reaction 4-5 minute, reduction temperature is 50-60 ℃, adds hexamethoxymethyl melamine resin, anilinomethyl triethoxysilane, 600-700 rev/min of dispersed with stirring 10-15 minute, be cooled to normal temperature, add each raw material of residue, fully mixing obtains described adhesive aid.
A preparation method for the anti-Japanese solarization wood plastic composite of high-performance, comprises the following steps:
Above-mentioned waste and old polystyrene plastics recovery pellet, dioctyl phthalate (DOP) are mixed with urea groups propyl-triethoxysilicane, 200-300 rev/min of dispersed with stirring 10-15 minute, joins in homogenizer, adds wood fibre, wilkinite, mineral wool fibre, high-speed stirring 20-30 minute at 80-100 ℃, reduce temperature to normal temperature, add each raw material of residue, fully mix, send into twin screw extruder, extrusion moulding, cooling and shaping, obtains the anti-Japanese solarization wood plastic composite of described high-performance.
Advantage of the present invention is:
Wood plastic composite weather resisteant of the present invention, resistance to chemical attack, resistance to compression, stretch-proof, the superior performance such as anti-aging, physical strength is high, and dimensional stability is strong, and resistant of high or low temperature is good, and anti-insolation performance is strong, can be for outdoor building material.
Embodiment
Embodiment 1
The anti-Japanese solarization wood plastic composite of high-performance, it by following weight parts (kilogram) raw material form:
Waste and old polystyrene plastics reclaims pellet 70, wood fibre 80, sodium polyacrylate 4, dioctyl phthalate (DOP) 2, magnesium hydroxide 2, wilkinite 6, mineral wool fibre 1, sorbyl alcohol 2, urea groups propyl-triethoxysilicane 1, Octabenzone 0.8, antioxidant 1010 1, adhesive aid 10;
Described adhesive aid is comprised of the raw material of following weight parts:
Polyvinyl alcohol 20, hexamethoxymethyl melamine resin 3, polyamide wax micropowder 3, dialdehyde starch 4, Jojoba oil 2, anilinomethyl triethoxysilane 1;
Above-mentioned polyvinyl alcohol is joined in reactor, be heated to 80 ℃, add polyamide wax micropowder, insulation reaction 4 minutes, reducing temperature is 60 ℃, adds hexamethoxymethyl melamine resin, anilinomethyl triethoxysilane, 700 revs/min of dispersed with stirring 15 minutes, be cooled to normal temperature, add each raw material of residue, fully mixing obtains described adhesive aid.
A preparation method for the anti-Japanese solarization wood plastic composite of high-performance, comprises the following steps:
Above-mentioned waste and old polystyrene plastics recovery pellet, dioctyl phthalate (DOP) are mixed with urea groups propyl-triethoxysilicane, 300 revs/min of dispersed with stirring 15 minutes, join in homogenizer, add wood fibre, wilkinite, mineral wool fibre, at 100 ℃, high-speed stirring is 30 minutes, reduce temperature to normal temperature, add each raw material of residue, fully mix, send into twin screw extruder, extrusion moulding, cooling and shaping, obtains the anti-Japanese solarization wood plastic composite of described high-performance.
Performance test:
Flexural strength is 58.71MPa;
Modulus in flexure is 3.55GPa.
Claims (2)
1. the anti-Japanese solarization wood plastic composite of high-performance, is characterized in that it is comprised of the raw material of following weight parts:
Waste and old polystyrene plastics reclaims pellet 62-70, wood fibre 70-80, sodium polyacrylate 2-4, dioctyl phthalate (DOP) 2-3, magnesium hydroxide 2-3, wilkinite 5-6, mineral wool fibre 1-2, sorbyl alcohol 2-3, urea groups propyl-triethoxysilicane 1-2, Octabenzone 0.8-1, antioxidant 1010 1-2, adhesive aid 5-10;
Described adhesive aid is comprised of the raw material of following weight parts:
Polyvinyl alcohol 15-20, hexamethoxymethyl melamine resin 3-4, polyamide wax micropowder 2-3, dialdehyde starch 4-5, Jojoba oil 1-2, anilinomethyl triethoxysilane 1-2;
Above-mentioned polyvinyl alcohol is joined in reactor, be heated to 70-80 ℃, add polyamide wax micropowder, insulation reaction 4-5 minute, reduction temperature is 50-60 ℃, adds hexamethoxymethyl melamine resin, anilinomethyl triethoxysilane, 600-700 rev/min of dispersed with stirring 10-15 minute, be cooled to normal temperature, add each raw material of residue, fully mixing obtains described adhesive aid.
2. a preparation method for the anti-Japanese solarization wood plastic composite of high-performance as claimed in claim 1, is characterized in that comprising the following steps:
Above-mentioned waste and old polystyrene plastics recovery pellet, dioctyl phthalate (DOP) are mixed with urea groups propyl-triethoxysilicane, 200-300 rev/min of dispersed with stirring 10-15 minute, joins in homogenizer, adds wood fibre, wilkinite, mineral wool fibre, high-speed stirring 20-30 minute at 80-100 ℃, reduce temperature to normal temperature, add each raw material of residue, fully mix, send into twin screw extruder, extrusion moulding, cooling and shaping, obtains the anti-Japanese solarization wood plastic composite of described high-performance.