CN103665683A - High-strength wear-resistant engineering plastic - Google Patents
High-strength wear-resistant engineering plastic Download PDFInfo
- Publication number
- CN103665683A CN103665683A CN201310579873.8A CN201310579873A CN103665683A CN 103665683 A CN103665683 A CN 103665683A CN 201310579873 A CN201310579873 A CN 201310579873A CN 103665683 A CN103665683 A CN 103665683A
- Authority
- CN
- China
- Prior art keywords
- parts
- engineering plastic
- asbestos
- mica
- silicon carbide
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a high-strength wear-resistant engineering plastic. The invention is characterized in that the engineering plastic is prepared from the following raw materials in parts by weight: 10-20 parts of polytetrafluoroethylene, 5-8 parts of toughener, 3-6 parts of high-aluminum aggregate, 4-8 parts of mica, 6-8 parts of silicone oil, 3-6 parts of silicon carbide, 2-5 parts of asbestos, 3-6 parts of plasticizer and 8-14 parts of internal molding lubricant. The engineering plastic has excellent electrical properties and favorable appearance, changes the situation that the user can only select either properties or appearance when designing the product, and satisfies all environmental requirements; the properties are similar to those of imported like materials, but the price is only one-third to one half of that of the imported like materials; and the engineering plastic is convenient to produce and purchase.
Description
Technical field
The present invention relates to plastics field, particularly relate to a kind of high-strength abrasion-proof engineering plastics.
Background technology
The development of high temperature resistant nylon changes into as possibility the more microminiaturized lightweight of industrial or agricultural and civilian installation and powerful.Resistance to plastics can bring higher heat resistance for some parts, or simply having substituted raw material metal produces these parts.The device of novel appts and assembly equally also useful resistance to plastics replace the trend of metal and thermosetting material.These all will strengthen the demand to resistance to plastic material, thereby drive the market requirement.But, the develop rapidly of present society technology, make rapid progress, product innovation new invention pours out, for picture, relating to requirement can have very big width to reduce frictional coefficient, extremely strong component of starting material self wear resistance simultaneously, the plurality of advantages of common plastics allows designer favor very much, but but the shortcoming of self wear resistance deficiency allows people's headache very much.
Summary of the invention
For the deficiencies in the prior art, technical problem to be solved by this invention is, a kind of possess fabulous self lubricity and wear resistance are provided, and when producing product the high-strength abrasion-proof engineering plastics of the demoulding voluntarily.
For solving the problems of the technologies described above, the technical solution used in the present invention is: a kind of high-strength abrasion-proof engineering plastics, it is characterized in that, and by the raw material of following weight part, made: tetrafluoroethylene 10-20 part, toughner 5-8 part, bauxites aggregate 3-6 part, mica 4-8 part, silicone oil 6-8 part, silicon carbide 3-6 part, asbestos 2-5 part, softening agent 3-6 part, inner pattern releasing agent applicable 8-14 part.
Above-mentioned high-strength abrasion-proof engineering plastics, is characterized in that, by the raw material of following weight part, are made: 15 parts of tetrafluoroethylene, 6 parts of toughner, 5 parts of bauxites aggregates, 6 parts, mica, 7 parts of silicone oil, 5 parts, silicon carbide, 3 parts, asbestos, 4 parts, softening agent, 11 parts of inner pattern releasing agent applicables.
The advantage of high-strength abrasion-proof engineering plastics of the present invention is: have excellent electrical characteristic and good outward appearance, while having changed user's deisgn product performance and outward appearance the two can only select the situation of one, also meet all environmental requirements simultaneously, and performance and import same type of material are similar, price is but only equivalent to the same type of material 1/3rd of import between half, and production procurement is convenient.
Embodiment
Below in conjunction with embodiment, the invention will be further described.
High-strength abrasion-proof engineering plastics, is characterized in that, by the raw material of following weight part, are made: tetrafluoroethylene 10-20 part, toughner 5-8 part, bauxites aggregate 3-6 part, mica 4-8 part, silicone oil 6-8 part, silicon carbide 3-6 part, asbestos 2-5 part, softening agent 3-6 part, inner pattern releasing agent applicable 8-14 part.
The preferred embodiment of the present invention is: a kind of high-strength abrasion-proof engineering plastics, by the raw material of following weight part, made: 15 parts of tetrafluoroethylene, 6 parts of toughner, 5 parts of bauxites aggregates, 6 parts, mica, 7 parts of silicone oil, 5 parts, silicon carbide, 3 parts, asbestos, 4 parts, softening agent, 11 parts of inner pattern releasing agent applicables.
Certainly, above-mentioned explanation is not limitation of the present invention, and the present invention is also not limited to above-mentioned giving an example; those skilled in the art; in essential scope of the present invention, the variation of making, change, interpolation or replacement, all should belong to protection scope of the present invention.
Claims (2)
1. high-strength abrasion-proof engineering plastics, is characterized in that, by the raw material of following weight part, are made: tetrafluoroethylene 10-20 part, toughner 5-8 part, bauxites aggregate 3-6 part, mica 4-8 part, silicone oil 6-8 part, silicon carbide 3-6 part, asbestos 2-5 part, softening agent 3-6 part, inner pattern releasing agent applicable 8-14 part.
2. high-strength abrasion-proof engineering plastics according to claim 1, is characterized in that, by the raw material of following weight part, are made: 15 parts of tetrafluoroethylene, 6 parts of toughner, 5 parts of bauxites aggregates, 6 parts, mica, 7 parts of silicone oil, 5 parts, silicon carbide, 3 parts, asbestos, 4 parts, softening agent, 11 parts of inner pattern releasing agent applicables.