CN103664100A - 一种微膨胀无机保温砂浆 - Google Patents
一种微膨胀无机保温砂浆 Download PDFInfo
- Publication number
- CN103664100A CN103664100A CN201310606522.1A CN201310606522A CN103664100A CN 103664100 A CN103664100 A CN 103664100A CN 201310606522 A CN201310606522 A CN 201310606522A CN 103664100 A CN103664100 A CN 103664100A
- Authority
- CN
- China
- Prior art keywords
- parts
- insulation mortar
- raw material
- micro
- thermal insulation
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种微膨胀无机保温砂浆,它是由下述重量份的原料组成的:普通硅酸盐水泥700-800、脱硫灰100-200、无水氯化钙30-40、三辛酸丁基锡0.6-1、聚四氟乙烯纤维4-6、硅烷基粉末SHP-501-2、聚丙烯酰胺1-2、十二烷基苯磺酸钠6-10、聚-4-甲基-1-戊烯3-5、改性助剂20-30、水适量;本发明生产的保温砂浆具有燃烧性低、耐火等级高、遇高温不会散发挥发性气体和有毒有害气体的优点,还具有很好的抗折强度和抗裂性。
Description
技术领域
本发明主要涉及一种砂浆,尤其涉及一种微膨胀无机保温砂浆。
背景技术
保温砂浆是以各种轻质材料为骨料,以水泥为胶凝料,掺和一些改性添加剂,经生产企业搅拌混合而制成的一种预拌干粉砂浆。主要用于建筑外墙保温,具有施工方便、耐久性好等优点。
发明内容
本发明目的就是提供一种微膨胀无机保温砂浆。
本发明是通过以下技术方案实现的:
一种微膨胀无机保温砂浆,其特征在于它是由下述重量份的原料组成的:
普通硅酸盐水泥700-800、脱硫灰100-200、无水氯化钙30-40、三辛酸丁基锡0.6-1、聚四氟乙烯纤维4-6、硅烷基粉末SHP-50 1-2、聚丙烯酰胺1-2、十二烷基苯磺酸钠6-10、聚-4-甲基-1-戊烯3-5、改性助剂20-30、水适量;
所述的改性助剂是由下述重量份的原料组成的:
红土40-65、骨粉2-4、蜂胶3-5、磷酸二氢铝3-4、可再分散乳胶粉20-30、聚乙烯吡咯烷酮2-3、硅烷偶联剂KH560 1-2、羟丙基甲基纤维素醚1-2、聚乙二醇400 2-3;
所述的改性助剂的制备方法包括以下步骤:
将上述红土在700-800℃下煅烧2-3小时,冷却至室温,加6-10%的氢氧化钠溶液研磨1-2小时,再加入10-15%的盐酸,调节PH为中性,在搅拌调节下依次加入蜂胶、磷酸二氢铝、可再分散乳胶粉、聚乙烯吡咯烷酮、聚乙二醇400,加入完毕后在60-80℃下保温搅拌10-16分钟,再加入剩余各原料,800-1000转/分搅拌分散3-5分钟,即得所述改性助剂。
一种\微膨胀无机保温砂浆的制备方法,包括以下步骤:
将上述普通硅酸盐水泥、脱硫灰、无水氯化钙、三辛酸丁基锡、聚四氟乙烯纤维、硅烷基粉末SHP-50混合,加入混合料重量70-85%的水,搅拌均匀;将十二烷基苯磺酸钠加入到20-25倍水中,搅拌均匀;将聚-4-甲基-1-戊烯与聚丙烯酰胺混合,80-100℃下加热搅拌3-5分钟,冷却至常温;将上述处理后的各原料与剩余各原料混合,搅拌均匀,浆浇注或喷射入模具中,即得所述微膨胀无机保温砂浆。
本发明的优点是:
本发明生产的保温砂浆具有燃烧性低、耐火等级高、遇高温不会散发挥发性气体和有毒有害气体的优点,还具有很好的抗折强度和抗裂性。
具体实施方式
实施例1
一种微膨胀无机保温砂浆,它是由下述重量份的原料组成的:
普通硅酸盐水泥800、脱硫灰200、无水氯化钙40、三辛酸丁基锡0.6、聚四氟乙烯纤维4、硅烷基粉末SHP-50 2、聚丙烯酰胺1、十二烷基苯磺酸钠10、聚-4-甲基-1-戊烯3-5、改性助剂30、水适量;
所述的改性助剂是由下述重量份的原料组成的:
红土45、骨粉3、蜂胶3、磷酸二氢铝3、可再分散乳胶粉30、聚乙烯吡咯烷酮2、硅烷偶联剂KH560 2、羟丙基甲基纤维素醚1-2、聚乙二醇400 3;
所述的改性助剂的制备方法包括以下步骤:
将上述红土在800℃下煅烧3小时,冷却至室温,加6-10%的氢氧化钠溶液研磨1小时,再加入15%的盐酸,调节PH为中性,在搅拌调节下依次加入蜂胶、磷酸二氢铝、可再分散乳胶粉、聚乙烯吡咯烷酮、聚乙二醇400,加入完毕后在60℃下保温搅拌16分钟,再加入剩余各原料,1000转/分搅拌分散5分钟,即得所述改性助剂。
一种\微膨胀无机保温砂浆的制备方法,包括以下步骤:
将上述普通硅酸盐水泥、脱硫灰、无水氯化钙、三辛酸丁基锡、聚四氟乙烯纤维、硅烷基粉末SHP-50混合,加入混合料重量75%的水,搅拌均匀;将十二烷基苯磺酸钠加入到25倍水中,搅拌均匀;将聚-4-甲基-1-戊烯与聚丙烯酰胺混合,100℃下加热搅拌5分钟,冷却至常温;将上述处理后的各原料与剩余各原料混合,搅拌均匀,浆浇注或喷射入模具中,即得所述微膨胀无机保温砂浆。
性能测试:
28d抗折强度:0.45MPa;
28d抗压强度≥0.6Mpa。
Claims (2)
1.一种微膨胀无机保温砂浆,其特征在于它是由下述重量份的原料组成的:
普通硅酸盐水泥700-800、脱硫灰100-200、无水氯化钙30-40、三辛酸丁基锡0.6-1、聚四氟乙烯纤维4-6、硅烷基粉末SHP-50 1-2、聚丙烯酰胺1-2、十二烷基苯磺酸钠6-10、聚-4-甲基-1-戊烯3-5、改性助剂20-30、水适量;
所述的改性助剂是由下述重量份的原料组成的:
红土40-65、骨粉2-4、蜂胶3-5、磷酸二氢铝3-4、可再分散乳胶粉20-30、聚乙烯吡咯烷酮2-3、硅烷偶联剂KH560 1-2、羟丙基甲基纤维素醚1-2、聚乙二醇400 2-3;
所述的改性助剂的制备方法包括以下步骤:
将上述红土在700-800℃下煅烧2-3小时,冷却至室温,加6-10%的氢氧化钠溶液研磨1-2小时,再加入10-15%的盐酸,调节PH为中性,在搅拌调节下依次加入蜂胶、磷酸二氢铝、可再分散乳胶粉、聚乙烯吡咯烷酮、聚乙二醇400,加入完毕后在60-80℃下保温搅拌10-16分钟,再加入剩余各原料,800-1000转/分搅拌分散3-5分钟,即得所述改性助剂。
2.一种如权利要求1所述的微膨胀无机保温砂浆的制备方法,其特征在于包括以下步骤:
将上述普通硅酸盐水泥、脱硫灰、无水氯化钙、三辛酸丁基锡、聚四氟乙烯纤维、硅烷基粉末SHP-50混合,加入混合料重量70-85%的水,搅拌均匀;将十二烷基苯磺酸钠加入到20-25倍水中,搅拌均匀;将聚-4-甲基-1-戊烯与聚丙烯酰胺混合,80-100℃下加热搅拌3-5分钟,冷却至常温;将上述处理后的各原料与剩余各原料混合,搅拌均匀,浆浇注或喷射入模具中,即得所述微膨胀无机保温砂浆。