CN103664055A - 一种聚合物砂浆及其调配方法 - Google Patents

一种聚合物砂浆及其调配方法 Download PDF

Info

Publication number
CN103664055A
CN103664055A CN201210340806.6A CN201210340806A CN103664055A CN 103664055 A CN103664055 A CN 103664055A CN 201210340806 A CN201210340806 A CN 201210340806A CN 103664055 A CN103664055 A CN 103664055A
Authority
CN
China
Prior art keywords
polymer mortar
water
thickening
water reducer
quartz sand
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210340806.6A
Other languages
English (en)
Inventor
张翮
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
NANJING HULIAN NEW BUILDING MATERIAL CO Ltd
Original Assignee
NANJING HULIAN NEW BUILDING MATERIAL CO Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by NANJING HULIAN NEW BUILDING MATERIAL CO Ltd filed Critical NANJING HULIAN NEW BUILDING MATERIAL CO Ltd
Priority to CN201210340806.6A priority Critical patent/CN103664055A/zh
Publication of CN103664055A publication Critical patent/CN103664055A/zh
Pending legal-status Critical Current

Abstract

一种聚合物砂浆，以质量百分数计原料包括以下组分：粉煤灰5.0～10.0%、硅粉0.3～0.8%、可再分散乳胶粉0.5～0.8%、增稠保水剂0.2～0.3%、减水剂0.8～1.2%、促凝剂0.1～0.3%、抗裂纤维0.1～0.2%、木纤维0.1～0.2%、石英砂45.0～50.0%以及水泥40.0～45.0%。公开了聚合物砂浆的调配方法，首先将粉煤灰、增稠保水剂、减水剂、促凝剂、抗裂纤维、木纤维、可再分散乳胶粉以及硅粉按比例搅拌混合，得搅拌均匀的混合物；然后将上述混合物、水泥以及石英砂按照比例称量、混合、搅拌均匀，得到聚合物砂浆。应用本发明的技术方案，聚合物砂浆的性能指标参数如下：劈裂抗拉强度为7.2MPa、抗压强度为58.8MPa、抗折强度为12.2Mpa以及正拉粘结强度为2.5MPa。

Description

一种聚合物砂浆及其调配方法
技术领域
本发明及建筑材料领域，尤其涉及一种高性能高强度结构加固型聚合物砂浆及其调配方法。
背景技术
砂浆在日常生活中的运用非常的广泛。
目前采用的一般性聚合物水泥砂浆存在以下的不足：（1）普遍抗压强度比较低，抗震性能不好；（2）抗压强度高的抗折性能又低, 抗震性能不好；（3）而环氧砂浆虽然性能较好，但是价格偏高。
现有的抹面砂浆抗压强度在20～30Mpa，抗折强度在4～6Mpa；地坪砂浆抗压强度在50～60Mpa，但是没有粘结力，不能抹墙。
发明内容
本发明的第一目的是提供一种高性能高强度结构加固型聚合物砂浆，具体的技术方案如下：
一种聚合物砂浆，以质量百分数计原料包括以下组分：
粉煤灰5.0～10.0%       硅粉0.3～0.8%       可再分散乳胶粉0.5～0.8%
增稠保水剂0.2～0.3%    减水剂0.8～1.2%     促凝剂0.1～0.3%
抗裂纤维0.1～0.2%      木纤维0.1～0.2%     石英砂45.0～50.0%
52.5级普通硅酸盐水泥40.0～45.0%。
优选的，以质量百分数计原料包括以下组分：
粉煤灰5.0%        硅粉0.6%       可再分散乳胶粉0.6%
增稠保水剂0.3%    减水剂1.0%     促凝剂0.25%
抗裂纤维0.15%     木纤维0.1%     石英砂47.0%
52.5级普通硅酸盐水泥45.0%。
优选的，所述增稠保水剂为羟丙基甲基纤维素醚。
优选的，所述减水剂为奈系减水剂。
优选的，所述促凝剂为硫铝酸盐水泥。
本发明聚合物砂浆中采用增稠保水剂提高其施工时间和施工性；采用减水剂减少水量，提高其强度；采用抗裂纤维、木纤维提高其抗裂性；采用抗裂纤维、硅粉提高其抗折性能；采用促凝剂提高其早期强度。运用本发明的技术方案，聚合物砂浆的性能指标参数如下：
劈裂抗拉强度/28d        7.2MPa
抗压强度/28d            58.8MPa
抗折强度/28d            12.2MPa
正拉粘结强度/28d        2.5MPa。
    本发明的第二目的是提供如上所述聚合物砂浆的调配方法，具体如下：
第一步：首先将粉煤灰、增稠保水剂、减水剂、促凝剂、抗裂纤维、木纤维、可再分散乳胶粉以及硅粉按比例搅拌混合，得到搅拌均匀的混合物；
第二步：然后将搅拌均匀的混合物、52.5级普通硅酸盐水泥以及石英砂按照比例称量、混合、搅拌均匀，得到聚合物砂浆。
本工艺方法简单，容易操作，适合大量生产应用。
具体实施方式
下面将结合具体实施例来详细说明本发明，在此本发明的示意性实施例以及说明用来解释本发明，但并不作为对本发明的限定。
实施例1：
一种聚合物砂浆，以质量百分数计原料包括以下组分：
粉煤灰5.0～10.0%       硅粉0.3～0.8%       可再分散乳胶粉0.5～0.8%
增稠保水剂0.2～0.3%    减水剂0.8～1.2%     促凝剂0.1～0.3%
抗裂纤维0.1～0.2%      木纤维0.1～0.2%     石英砂45.0～50.0%
52.5级普通硅酸盐水泥40.0～45.0%。
其中，所述增稠保水剂为羟丙基甲基纤维素醚，所述减水剂为奈系减水剂，所述促凝剂为硫铝酸盐水泥。
本发明聚合物砂浆中采用增稠保水剂提高其施工时间和施工性；采用减水剂减少水量，提高其强度；采用抗裂纤维、木纤维提高其抗裂性；采用抗裂纤维、硅粉提高其抗折性能；采用促凝剂提高其早期强度。
本发明聚合物砂浆的调配方法，具体如下：
第一步：首先将粉煤灰、增稠保水剂、减水剂、促凝剂、抗裂纤维、木纤维、可再分散乳胶粉以及硅粉按比例搅拌混合，得到搅拌均匀的混合物；
第二步：然后将搅拌均匀的混合物、52.5级普通硅酸盐水泥以及石英砂按照比例称量、混合、搅拌均匀，得到聚合物砂浆。
本工艺方法简单，容易操作，适合大量生产应用。
实施例2：
一种聚合物砂浆，以质量百分数计原料包括以下组分：
粉煤灰5.0%        硅粉0.6%       可再分散乳胶粉0.6%
增稠保水剂0.3%    减水剂1.0%     促凝剂0.25%
抗裂纤维0.15%     木纤维0.1%     石英砂47.0%
52.5级普通硅酸盐水泥45.0%。
其中，所述增稠保水剂为羟丙基甲基纤维素醚，所述减水剂为奈系减水剂，所述促凝剂为硫铝酸盐水泥。
本发明聚合物砂浆中采用增稠保水剂提高其施工时间和施工性；采用减水剂减少水量，提高其强度；采用抗裂纤维、木纤维提高其抗裂性；采用抗裂纤维、硅粉提高其抗折性能；采用促凝剂提高其早期强度。本发明聚合物砂浆的抗压强度、抗折强度、劈裂抗拉强度、正拉粘结强度都高，聚合物砂浆具体的性能指标参数如下：
劈裂抗拉强度/28d        7.2MPa
抗压强度/28d            58.8MPa
抗折强度/28d            12.2MPa
正拉粘结强度/28d             2.5MPa。
本发明聚合物砂浆可以广泛应用于建筑材料中，例如抹墙、制作支撑柱等等。
本发明聚合物砂浆的调配方法，具体如下：
第一步：首先将粉煤灰、增稠保水剂、减水剂、促凝剂、抗裂纤维、木纤维、可再分散乳胶粉以及硅粉按比例搅拌混合，得到搅拌均匀的混合物；
第二步：然后将搅拌均匀的混合物、52.5级普通硅酸盐水泥以及石英砂按照比例称量、混合、搅拌均匀，得到聚合物砂浆。
本工艺方法简单，容易操作，适合大量生产应用。
以上对本发明实施例所提供的技术方案进行了详细介绍，本文中应用了具体个例对本发明实施例的原理以及实施方式进行了阐述，以上实施例的说明只适用于帮助理解本发明实施例的原理；同时，对于本领域的一般技术人员，依据本发明实施例，在具体实施方式以及应用范围上均会有改变之处，综上所述，本说明书内容不应理解为对本发明的限制。

Claims (6)

1.一种聚合物砂浆，其特征在于：以质量百分数计原料包括以下组分：
粉煤灰5.0～10.0%       硅粉0.3～0.8%       可再分散乳胶粉0.5～0.8%
增稠保水剂0.2～0.3%    减水剂0.8～1.2%     促凝剂0.1～0.3%
抗裂纤维0.1～0.2%      木纤维0.1～0.2%     石英砂45.0～50.0%
52.5级普通硅酸盐水泥40.0～45.0%。
2.根据权利要求1所述聚合物砂浆，其特征在于：以质量百分数计原料包括以下组分：
粉煤灰5.0%        硅粉0.6%       可再分散乳胶粉0.6%
增稠保水剂0.3%    减水剂1.0%     促凝剂0.25%
抗裂纤维0.15%     木纤维0.1%     石英砂47.0%
52.5级普通硅酸盐水泥45.0%。
3.根据权利要求1或者2所述聚合物砂浆，其特征在于所述增稠保水剂为羟丙基甲基纤维素醚。
4.根据权利要求1或者2所述聚合物砂浆，其特征在于所述减水剂为奈系减水剂。
5.根据权利要求1或者2所述聚合物砂浆，其特征在于所述促凝剂为硫铝酸盐水泥。
6.一种如权利要求1或者2所述聚合物砂浆的调配方法，其特征在于：包括以下步骤：
（1）首先将粉煤灰、增稠保水剂、减水剂、促凝剂、抗裂纤维、木纤维、可再分散乳胶粉以及硅粉按比例搅拌混合，得到搅拌均匀的混合物；
（2）然后将搅拌均匀的混合物、52.5级普通硅酸盐水泥以及石英砂按照比例称量、混合、搅拌均匀，得到聚合物砂浆。
CN201210340806.6A 2012-09-15 2012-09-15 一种聚合物砂浆及其调配方法 Pending CN103664055A (zh)