CN103657446B - 聚偏氟乙烯中空纤维膜 - Google Patents
聚偏氟乙烯中空纤维膜 Download PDFInfo
- Publication number
- CN103657446B CN103657446B CN201310688685.9A CN201310688685A CN103657446B CN 103657446 B CN103657446 B CN 103657446B CN 201310688685 A CN201310688685 A CN 201310688685A CN 103657446 B CN103657446 B CN 103657446B
- Authority
- CN
- China
- Prior art keywords
- mass parts
- hollow fiber
- fiber membrane
- average grain
- microporous hollow
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明公开了一种聚偏氟乙烯中空纤维膜，由如下原料制成：100-120质量份聚偏氟乙烯，2质量份十二烷基硫酸钠，1质量份乙二醇单硬脂酸酯，2质量份平均粒径为9nm二氧化硅，5质量份二甲基亚砜，15质量份聚乙烯吡咯烷酮，35质量份磷酸三乙基，2质量份平均粒径为20nm碳酸钙，3质量份十二烷基苯磺酸钠，5质量份聚乙二醇，15质量份二甲基乙酰胺，2质量份十二烷基氨基丙酸钠，5质量份去离子水，3质量份聚乙烯醇，2质量份甲基纤维素，25质量份二甲基甲酰胺，3质量份十六烷基三甲基溴化铵，1质量份脂肪胺聚氧乙烯醚，8质量份聚氧乙烯。本发明聚偏氟乙烯中空纤维膜，其具有较高的抗压及抗拉强度，高通量，且具有良好的柔软性。
Description
技术领域
本发明涉及聚偏氟乙烯中空纤维膜。
背景技术
现有聚偏氟乙烯中空纤维膜，其抗压、抗拉强度、通量、柔软性都不是很理想。
发明内容
本发明的目的在于提供一种聚偏氟乙烯中空纤维膜，其具有较高的抗压及抗拉强度，高通量，且具有良好的柔软性。
为实现上述目的，本发明的技术方案是设计一种聚偏氟乙烯中空纤维膜，由如下原料制成：
100-120质量份聚偏氟乙烯，
2质量份十二烷基硫酸钠，
1质量份乙二醇单硬脂酸酯，
2质量份平均粒径为9nm二氧化硅，
5质量份二甲基亚砜，
15质量份聚乙烯吡咯烷酮，
35质量份磷酸三乙基，
2质量份平均粒径为20nm碳酸钙，
3质量份十二烷基苯磺酸钠，
5质量份聚乙二醇，
15质量份二甲基乙酰胺，
2质量份十二烷基氨基丙酸钠，
5质量份去离子水，
3质量份聚乙烯醇，
2质量份甲基纤维素，
25质量份二甲基甲酰胺，
3质量份十六烷基三甲基溴化铵，
1质量份脂肪胺聚氧乙烯醚，
8质量份聚氧乙烯。
本发明的优点和有益效果在于：提供一种聚偏氟乙烯中空纤维膜，其具有较高的抗压及抗拉强度，高通量，且具有良好的柔软性。
具体实施方式
下面结合实施例，对本发明的具体实施方式作进一步描述。以下实施例仅用于更加清楚地说明本发明的技术方案，而不能以此来限制本发明的保护范围。
本发明具体实施的技术方案是：
实施例1
一种聚偏氟乙烯中空纤维膜，由如下原料制成：
110质量份聚偏氟乙烯，
2质量份十二烷基硫酸钠，
1质量份乙二醇单硬脂酸酯，
2质量份平均粒径为9nm二氧化硅，
5质量份二甲基亚砜，
15质量份聚乙烯吡咯烷酮，
35质量份磷酸三乙基，
2质量份平均粒径为20nm碳酸钙，
3质量份十二烷基苯磺酸钠，
5质量份聚乙二醇，
15质量份二甲基乙酰胺，
2质量份十二烷基氨基丙酸钠，
5质量份去离子水，
3质量份聚乙烯醇，
2质量份甲基纤维素，
25质量份二甲基甲酰胺，
3质量份十六烷基三甲基溴化铵，
1质量份脂肪胺聚氧乙烯醚，
8质量份聚氧乙烯。
实施例2
一种聚偏氟乙烯中空纤维膜，由如下原料制成：
120质量份聚偏氟乙烯，
2质量份十二烷基硫酸钠，
1质量份乙二醇单硬脂酸酯，
2质量份平均粒径为9nm二氧化硅，
5质量份二甲基亚砜，
15质量份聚乙烯吡咯烷酮，
35质量份磷酸三乙基，
2质量份平均粒径为20nm碳酸钙，
3质量份十二烷基苯磺酸钠，
5质量份聚乙二醇，
15质量份二甲基乙酰胺，
2质量份十二烷基氨基丙酸钠，
5质量份去离子水，
3质量份聚乙烯醇，
2质量份甲基纤维素，
25质量份二甲基甲酰胺，
3质量份十六烷基三甲基溴化铵，
1质量份脂肪胺聚氧乙烯醚，
8质量份聚氧乙烯。
实施例3
一种聚偏氟乙烯中空纤维膜，由如下原料制成：
100质量份聚偏氟乙烯，
2质量份十二烷基硫酸钠，
1质量份乙二醇单硬脂酸酯，
2质量份平均粒径为9nm二氧化硅，
5质量份二甲基亚砜，
15质量份聚乙烯吡咯烷酮，
35质量份磷酸三乙基，
2质量份平均粒径为20nm碳酸钙，
3质量份十二烷基苯磺酸钠，
5质量份聚乙二醇，
15质量份二甲基乙酰胺，
2质量份十二烷基氨基丙酸钠，
5质量份去离子水，
3质量份聚乙烯醇，
2质量份甲基纤维素，
25质量份二甲基甲酰胺，
3质量份十六烷基三甲基溴化铵，
1质量份脂肪胺聚氧乙烯醚，
8质量份聚氧乙烯。
以上所述仅是本发明的优选实施方式，应当指出，对于本技术领域的普通技术人员来说，在不脱离本发明技术原理的前提下，还可以做出若干改进和润饰，这些改进和润饰也应视为本发明的保护范围。
Claims (1)
1.聚偏氟乙烯中空纤维膜，其特征在于，由如下原料制成：
100-120质量份聚偏氟乙烯，
2质量份十二烷基硫酸钠，
1质量份乙二醇单硬脂酸酯，
2质量份平均粒径为9nm二氧化硅，
5质量份二甲基亚砜，
15质量份聚乙烯吡咯烷酮，
35质量份磷酸三乙基，
2质量份平均粒径为20nm碳酸钙，
3质量份十二烷基苯磺酸钠，
5质量份聚乙二醇，
15质量份二甲基乙酰胺，
2质量份十二烷基氨基丙酸钠，
5质量份去离子水，
3质量份聚乙烯醇，
2质量份甲基纤维素，
25质量份二甲基甲酰胺，
3质量份十六烷基三甲基溴化铵，
1质量份脂肪胺聚氧乙烯醚，
8质量份聚氧乙烯。