CN103643371A - 一种牛奶冰丝布料的制作工艺 - Google Patents
一种牛奶冰丝布料的制作工艺 Download PDFInfo
- Publication number
- CN103643371A CN103643371A CN201310583506.5A CN201310583506A CN103643371A CN 103643371 A CN103643371 A CN 103643371A CN 201310583506 A CN201310583506 A CN 201310583506A CN 103643371 A CN103643371 A CN 103643371A
- Authority
- CN
- China
- Prior art keywords
- milk
- meryl
- fabric
- mentioned
- ice silk
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开了一种牛奶冰丝布料的制作工艺,包括以下工艺步骤:(1)将棉短绒和木材作为原料提取出纯净的浆粕,(2)将上述浆粕放入氢氧化钠水溶液中,得到粘稠的纺丝原液,(3)将液状牛奶进行脱水脱脂处理,得到牛奶蛋白质,(4)将上述牛奶蛋白质加上柔和剂制成牛奶浆液,(5)将上述牛奶浆液通过湿纺工艺,纺制成牛奶蛋白纤维,(6)将上述(2)中的纺丝原液和上述(5)中的牛奶蛋白纤维相结合经过过滤、熟成、脱泡后,进行湿法纺丝,(7)将上述湿法纺丝进行编织而成牛奶冰丝布料。通过上述方式,本发明牛奶冰丝布料的制作工艺操作简单,操作过程易于控制,牛奶冰丝的出纤率很高,制作而成的牛奶冰丝布料具有棉的本质,丝的品质,是地道的生态纤维,源于天然而优于天然。
Description
技术领域
本发明涉及功能布料领域,特别是涉及一种牛奶冰丝布料的制作工艺。
背景技术
进入21世纪以来,人们更加注重服饰的舒适性、保健性、高档化和时尚化。牛奶冰丝布料作为一种新型的布料,含湿率最符合人体皮肤的生理需要,具有棉的本质,丝的品质,地道的生态纤维,源于天然而优于天然,具有光滑凉爽、透气、抗静电、色彩绚丽等特点。
发明内容
本发明主要解决的技术问题是提供一种操作简单,操作过程易于控制、牛奶冰丝的出纤率高的牛奶冰丝布料的制作工艺。
为解决上述技术问题,本发明提供一种牛奶冰丝布料的制作工艺,包括以下工艺步骤:
(1)将棉短绒和木材作为原料提取出纯净的浆粕,
(2)将上述浆粕放入氢氧化钠水溶液中,得到粘稠的纺丝原液,
(3)将液状牛奶进行脱水脱脂处理,得到牛奶蛋白质,
(4)将上述牛奶蛋白质加上柔和剂制成牛奶浆液,
(5)将上述牛奶浆液通过湿纺工艺,纺制成牛奶蛋白纤维,
(6)将上述(2)中的纺丝原液和上述(5)中的牛奶蛋白纤维相结合经过过滤、熟成、脱泡后,进行湿法纺丝,
(7)讲上述湿法纺丝进行编织而成牛奶冰丝布料。
在本发明一个较佳实施例中,所述浆粕放入氢氧化钠水溶液浓度为15%-20%。
在本发明一个较佳实施例中,所述脱水脱脂处理中脂肪含量低于0.3%,所述含量为重量的百分比。
在本发明一个较佳实施例中,所述纺丝原液和牛奶蛋白纤维相结合的体积比例为1:2。
在本发明一个较佳实施例中,所述熟成是指在18-25度的环境下放置20-30小时,以降低纤维素黄原酸酯的酯化数。
本发明的有益效果是:本发明牛奶冰丝布料的制作工艺操作简单、操作过程易于控制、牛奶冰丝的出纤率高,制作而成的牛奶冰丝布料具有棉的本质,丝的品质,地道的生态纤维,源于自然而优于自然,含有7种氨基酸和多种天然抗菌素,其抗菌率高于85%,因此牛奶冰丝面料具有保健作用,同时牛奶冰丝面料的吸湿性强、透气性好、抗静电、色彩绚丽。
具体实施方式
下面将对本发明实施例中的技术方案进行清楚、完整地描述,显然,所描述的实施例仅是本发明的一部分实施例,而不是全部的实施例。基于本发明中的实施例,本领域普通技术人员在没有做出创造性劳动前提下所获得的所有其它实施例,都属于本发明保护的范围。
本发明实施例包括:
一种牛奶冰丝布料的制作工艺,包括以下工艺:
(1)将棉短绒和木材作为原料提取出纯净的浆粕,
(2)将上述浆粕放入氢氧化钠水溶液中,得到粘稠的纺丝原液,
(3)将液状牛奶进行脱水脱脂处理,得到牛奶蛋白质,
(4)将上述牛奶蛋白质加上柔和剂制成牛奶浆液,
(5)将上述牛奶浆液通过湿纺工艺,纺制成牛奶蛋白纤维,
(6)将上述(2)中的纺丝原液和上述(5)中的牛奶蛋白纤维相结合经过过滤、熟成、脱泡后,进行湿法纺丝,
(7)讲上述湿法纺丝进行编织而成牛奶冰丝布料。
另外,所述浆粕放入氢氧化钠水溶液浓度为15%-20%。
另外,所述脱水脱脂处理中脂肪含量低于0.3%,所述含量为重量的百分比。
另外,所述纺丝原液和牛奶蛋白纤维相结合的体积比例为1:2。
另外,所述熟成是指在18-25度的环境下放置20-30小时,以降低纤维素黄原酸酯的酯化数。
本发明牛奶冰丝布料的制作工艺操作简单、操作过程易于控制、牛奶冰丝的出纤率高,制作而成的牛奶冰丝布料具有棉的本质,丝的品质,地道的生态纤维,源于自然而优于自然,含有7种氨基酸和多种天然抗菌素,其抗菌率高于85%,因此牛奶冰丝面料具有保健作用,同时牛奶冰丝面料的吸湿性强、透气性好、抗静电、色彩绚丽。
以上所述仅为本发明的实施例,并非因此限制本发明的专利范围,凡是利用本发明说明书内容所作的等效结构或等效流程变换,或直接或间接运用在其它相关的技术领域,均同理包括在本发明的专利保护范围内。
Claims (5)
1.一种牛奶冰丝布料的制作工艺,其特征在于,包括以下工艺步骤:
(1)将棉短绒和木材作为原料提取出纯净的浆粕,
(2)将上述浆粕放入氢氧化钠水溶液中,得到粘稠的纺丝原液,
(3)将液状牛奶进行脱水脱脂处理,得到牛奶蛋白质,
(4)将上述牛奶蛋白质加上柔和剂制成牛奶浆液,
(5)将上述牛奶浆液通过湿纺工艺,纺制成牛奶蛋白纤维,
(6)将上述(2)中的纺丝原液和上述(5)中的牛奶蛋白纤维相结合经过过滤、熟成、脱泡后,进行湿法纺丝,
(7)将上述湿法纺丝进行编织而成牛奶冰丝布料。
2.根据权利要求1所述的牛奶冰丝布料的制作工艺,其特征在于,所述浆粕放入氢氧化钠水溶液浓度为15%-20%。
3.根据权利要求1所述的牛奶冰丝布料的制作工艺,其特征在于,所述脱水脱脂处理中脂肪含量低于0.3%,所述含量为重量的百分比。
4.根据权利要求1所述的牛奶冰丝布料的制作工艺,其特征在于,所述纺丝原液和牛奶蛋白纤维相结合的体检比例为1:2。
5.根据权利要求1所述的牛奶冰丝布料的制作工艺,其特征在于,所述熟成是指在18-25度的环境下放置20-30小时,以降低纤维素黄原酸酯的酯化数。