CN103639579A - Device and method for welding micro-beam plasma high-frequency solderless high-purity gold and sliver - Google Patents
Device and method for welding micro-beam plasma high-frequency solderless high-purity gold and sliver Download PDFInfo
- Publication number
- CN103639579A CN103639579A CN201310750331.2A CN201310750331A CN103639579A CN 103639579 A CN103639579 A CN 103639579A CN 201310750331 A CN201310750331 A CN 201310750331A CN 103639579 A CN103639579 A CN 103639579A
- Authority
- CN
- China
- Prior art keywords
- cavity
- sleeve
- welding
- power supply
- supply circuit
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to the technical field of noble metal welding and provides a micro-beam plasma high-frequency solderless high-purity gold and sliver. The device consists of an insulating sleeve, a conductive gas guide sleeve, a conductive clamping sleeve, an insulated arc-concentrating sleeve, a tungsten electrode, a direct-current power supply circuit and a high-frequency power supply circuit, wherein a gas guide hole is formed in the conductive clamping sleeve; an oval pumping chamber is arranged at a welding nozzle on the insulated arc-concentrating sleeve. The high-frequency power supply circuit and the direct-current power supply circuit provide current and voltage for the whole device, so that the whole device forms constant-temperature and stable cylindrical plasma arcs; the plastic arcs are used for directly welding butt-joint parts of welded workpieces together without any other welding flux, so that the welded butt-joint parts do not have problems of discoloring and welding point dropping; moreover, purity of noble metals such as gold and sliver is ensured.
Description
Technical field
The invention belongs to precious metal welding technology field, relate in particular to a kind of microplasma high frequency open high-purity gold and silver welder and method.
Background technology
Tungsten electrode plasma gun is conventional welding equipment, it is to utilize high-frequency oscillating circuits to produce electric arc between rifle head and tip, under the high temperature of electric arc, the argon gas of flowing through between tip inner surface and tungsten electrode is ionized and conducting, and then, under the effect of dc source, electric arc is introduced in weldment surface, electric arc is compressed, current density in electric arc, brightness increasing and concentration of energy, form the good ion arc of straight and upright property therefrom, and two materials to be welded are integrally welded.
In the production of gold and silver ornaments, comprise that some style is comparatively complicated or have the ornaments of special process requirement, in process, also need a large amount of use welding procedures, at present, the complementary scolder (comprising filler and welding agent) of the general use of welding of the precious metal such as gold, silver carries out auxiliary welding, to guarantee the firm of two weldments, but adopt this welding manner but to have following defect:
(1), in welding process, impurity inevitably incorporates in the precious metals such as gold or silver, causes the purity of the precious metals such as gold and silver to reduce, and does not reach corresponding standard-required;
(2), adopt the ornaments of the precious metals such as the gold of welding agent technique welding or silver in long-term wearing in process, there is variable color in pad place, comes off, of bad quality and cause wearing the problems such as irritated;
(3), the general power supply that adopts larger electric current of traditional welding, be not suitable for the small gold of welding work pieces type or silver ornaments.
Summary of the invention
The object of the present invention is to provide a kind of microplasma high frequency open high-purity gold and silver welder, when being intended to solve the complementary scolder of use of the prior art the precious metal ornaments such as bullion and silver being carried out to auxiliary welding, existing such as purity reduce, the problem such as the easy variable color of pad comes off.
The present invention is achieved in that a kind of microplasma high frequency open high-purity gold and silver welder, and described device comprises:
Be arranged on and be welded and fixed on frame, with the insulation sleeve that described fixed mount insulation arranges, described insulation sleeve is provided with the first cavity and the second cavity being communicated with up and down, and the aperture of described the first cavity is greater than the aperture of described the second cavity;
Be arranged on the tubular conduction guide sleeve in the first cavity of described insulation sleeve, described tubular conduction guide sleeve upper end is provided with for import the gas port of inert gas to described the first cavity and the second cavity;
Be arranged on the poly-arc cover of insulation that described insulation sleeve bottom is fixedly connected with described insulation sleeve, inner the 3rd cavity adapting with described the second cavity that is provided with of the poly-arc cover of described insulation, the lower end of described the 3rd cavity is provided with elliptoid pumping chamber near the position of tip, and described pumping chamber is used for compressing plasma arc and forms cylindrical arc;
In described tubular conduction guide sleeve, be provided with the tungsten electrode of needle bar shape, described tungsten electrode from described tubular conduction guide sleeve along the second cavity, extend to the bottom, pumping chamber of described the 3rd cavity, described tungsten electrode and described tip are provided with certain distance;
Described tungsten electrode fixes to clamp by conduction gripping sleeve, and the cross section of described conduction gripping sleeve is T-shaped, and the medial surface of described conduction gripping sleeve and described cylindric conduction guide sleeve forms cavity for enter inert gas circulation from described gas port;
Described tungsten electrode one end is connected with high-frequency power supply circuit with DC power supply circuit respectively by wire, and described DC power supply circuit is connected with welded part with after high-frequency power supply circuit parallel connection;
Wherein, described conduction gripping sleeve forms with the medial surface of described cylindric conduction guide sleeve cavity, the second cavity and the 3rd cavity form inert gas passage until tip is communicated with in the lump.
As a kind of improved plan, described DC power supply circuit provides weak current, and current values scope is 0.1A-10A.
As a kind of improved plan, described high-frequency power supply circuit provides the voltage of 250kHz/25000V.
As a kind of improved plan, the aperture of described tip is 0.5mm-1.0mm.
As a kind of improved plan, described tip is 3mm-4mm to the distance of welded part place plane.
As a kind of improved plan, described conduction gripping sleeve and described tubular conduction guide sleeve are made by the high copper product of conductance.
As a kind of improved plan, described insulation sleeve is made by high temperature ceramic material.
As a kind of improved plan, the poly-arc cover of described insulation is made by high-temperature insulation nonmetallic materials.
Another object of the embodiment of the present invention is to provide a kind of welding method based on microplasma high frequency open high-purity gold and silver welder, and described method comprises the steps:
The position docking that the first welding work pieces and the second welding work pieces need to be welded, wherein, described the first welding work pieces or the second welding work pieces are provided with body filler;
Opening inert gas valve makes inert gas enter by gas port, along inert gas passage, circulate, connect successively high-frequency power supply circuit and DC power supply circuit simultaneously, make tungsten electrode in pumping chamber, form electric arc, described plasma arc forms the stable plasma arc of cylindrical constant temperature through the air cooling effect of the poly-arc cover of insulation and tip oral area;
Described plasma arc carries out preheating to the docking site of described the first welding work pieces, the second welding work pieces and described body filler, then according to technological requirement, the body filler after described fusing is filled up to the corresponding docking site at described the first welding work pieces and described the second welding work pieces;
Follow-up polishing and matting are carried out in relevant position to the corresponding docking site of described the first welding work pieces and described the second welding work pieces and described body filler.
As a kind of improved plan, described the first welding work pieces, the docking site of the second welding work pieces and the distance of described tip are 3mm-4mm.
Because microplasma high frequency open high-purity gold and silver welder is by insulation sleeve, conduction guide sleeve, conduction gripping sleeve, the poly-arc cover of insulation and tungsten electrode form, wherein, in conduction, clamp to put and be provided with gas port, the tip place putting at the poly-arc of insulation is provided with elliptoid pumping chamber, whole device provides current/voltage by high-frequency power supply circuit and DC power supply circuit, this device forms the stable columniform plasma arc of constant temperature, and this plasma arc directly by the docking site molten solder of welding work pieces together, do not need other any scolders, the docking site of welding there will not be fades, the problem that solder joint comes off, and guaranteed the high-purity of the noble metals such as bullion and silver.
Because DC power supply circuit provides 0.1A-10A weak current, can guarantee electric arc smooth combustion under the effect of this electric current, energy consumption is less simultaneously, the energy-conservation energy.
Because high-frequency power supply circuit provides the voltage of 250kHz/25000V, ionized air, fast and stable striking, effect is better.
Because the aperture of tip is set to 0.5mm-1.0mm, guarantee from pumping chamber the better performances such as temperature, intensity, arc length and outspoken nature of plasma arc out, to improve speed of welding and welding quality.
Because tip is 3mm-4mm to the distance of welded part place plane, under this distance, plasma arc is better to the pre-heat effect of the docking site of welding work pieces, and speed of welding is very fast, and welding quality is higher.
In embodiments of the present invention, when the welder that adopts above-mentioned microplasma high frequency open high-purity gold and silver welder welds the first welding work pieces and the second welding work pieces, on the first welding work pieces or the second welding work pieces, body filler is set, the stable plasma arc of constant temperature forming by pumping chamber carries out preheating to the docking site of two workpiece and body filler, then melt away described body condiment and be filled in docking site, the first welding work pieces and the second welding work pieces are welded together, its logical too little current, the quality that pumping chamber and middle cold-working are welded with the plasma arc forming is higher, there will not be and fade, the problem that solder joint comes off, simultaneously, speed of welding is very fast, be applicable to the welding of the precious metals such as bullion and silver.
Accompanying drawing explanation
Fig. 1 is the structural representation of the microplasma high frequency open high-purity gold and silver welder that provides of the embodiment of the present invention;
Fig. 2 is the realization flow figure of the microplasma high frequency open high-purity gold and silver welding method that provides of the embodiment of the present invention;
Fig. 3 is the welding schematic diagram based on microplasma high frequency open high-purity gold and silver welder that the embodiment of the present invention provides;
Wherein, 1-insulation sleeve, 11-the first cavity, 12-the second cavity, 2-tubular conduction guide sleeve, 21-gas port, the poly-arc cover of 3-insulation, 31-the 3rd cavity, 32-tip, 33-pumping chamber, 4-tungsten electrode, 5-conducts electricity gripping sleeve, 6-DC power supply circuit, 7-high-frequency power supply circuit, 8-welded part, 9-body filler.
The specific embodiment
In order to make object of the present invention, technical scheme and advantage clearer, below in conjunction with drawings and Examples, the present invention is further elaborated.Should be appreciated that specific embodiment described herein, only in order to explain the present invention, is not intended to limit the present invention.
Fig. 1 shows the structural representation of the microplasma high frequency open high-purity gold and silver welder that the embodiment of the present invention provides, and for convenience of explanation, has only provided the part relevant to the embodiment of the present invention in figure.
The microplasma high frequency open high-purity gold and silver welder that the embodiment of the present invention provides is based on the welding requirements of the highly purified precious metals such as bullion and silver is designed, described device is mainly comprised of insulation sleeve 1, tubular conduction guide sleeve 2, the poly-arc cover 3 of insulation, tungsten electrode 4, conduction gripping sleeve 5 and DC power supply circuit 6 and high-frequency power supply circuit 7, it complements each other to form the stable plasma arc of constant temperature, for the welding to high purity noble metal such as small bullion and silvers, its concrete structure is as described below:
Be arranged on that to be welded and fixed frame (in figure for providing) upper, with the insulation sleeve 1 that described fixed mount insulation arranges, described insulation sleeve 1 is provided with the first cavity 11 and the second cavity 12 being communicated with up and down, and the aperture of described the first cavity 11 is greater than the aperture of described the second cavity 12;
Be arranged on the tubular conduction guide sleeve 2 in the first cavity 11 of described insulation sleeve 1, described tubular conduction guide sleeve 2 upper ends are provided with for import the gas port 21 of inert gases to described the first cavity 11 and the second cavity 12;
Be arranged on the poly-arc cover 3 of insulation that described insulation sleeve 1 bottom is fixedly connected with described insulation sleeve 1, the poly-arc of described insulation overlaps 3 inside and is provided with the 3rd cavity 31 adapting with described the second cavity 12, the lower end of described the 3rd cavity 31 is provided with elliptoid pumping chamber 33 near the position of tip 32, and described pumping chamber 33 forms cylindrical arc for compressing plasma arc;
In described tubular conduction guide sleeve 2, be provided with the tungsten electrode 4 of needle bar shape, described tungsten electrode 4 extends to 33 bottoms, pumping chamber of described the 3rd cavity 31 from described tubular conduction guide sleeve 2 is interior along the second cavity 12, and described tungsten electrode 4 is provided with certain distance with described tip 32;
Described tungsten electrode 4 fixes to clamp by conduction gripping sleeve 5, and the cross section of described conduction gripping sleeve 5 is T-shaped, and described conduction gripping sleeve 5 forms cavity for enter inert gas circulation from described gas port 21 with the medial surface of described cylindric conduction guide sleeve 2;
Described tungsten electrode 4 one end are connected with high-frequency power supply circuit 7 with DC power supply circuit 6 respectively by wire, after described DC power supply circuit 6 is in parallel with high-frequency power supply circuit 7, are connected with welded part 8;
Wherein, conduction gripping sleeve 5 forms with the medial surface of described cylindric conduction guide sleeve 2 cavity, the second cavity 12 and the 3rd cavity 31 form inert gas passage until tip 32 is communicated with in the lump.
Wherein, as can be seen from Figure, gas port 21 is from external tracheae enters the first cavity 11, the position of its connection is concrete as in figure, from conduction gripping sleeve 5 and the medial surface of described cylindric conduction guide sleeve 2, form cavity extension down, wherein, this conduction gripping sleeve 5 forms with the medial surface of described cylindric conduction guide sleeve 2 cylinder type that cavity is upper end closed, its this cylinder type cavity is a part for the first cavity 11, then the inert gas entering from gas port 21 enters the second cavity 12 along this cylinder type cavity, then continue to come downwards to the 3rd cavity 31, then enter pumping chamber 33, end formation electric arc by tungsten electrode 4 finally forms plasma arc, its Plasma Arc length etc. are from tungsten electrode 4 ends, extend past tip 32 always, then extend until the outside certain distance of tip 32.
In figure, insulation sleeve 1 is fixedly connected with the poly-arc cover 3 of insulation with conduction gripping sleeve 2, insulation sleeve 1, between its coupling assembling, adopts encapsulant, makes the inner cavity sealing forming better.
In embodiments of the present invention, whole device provides current/voltage by high-frequency power supply circuit and DC power supply circuit, this device forms the stable columniform plasma arc of constant temperature, and this plasma arc directly by the docking site molten solder of welding work pieces together, do not need other any scolders, the docking site of welding there will not be fade, problem that solder joint comes off, and guaranteed the purity of the noble metals such as bullion and silver.
In embodiments of the present invention, DC power supply circuit 6 provides weak current (relative), current values scope is 0.1A-10A, the formed plasma arc of its small and weak electric current is stablized constant temperature equally, and its temperature, density and straight and upright property meet the requirement of the high purity noble metal such as welding bullion and silver equally.
In embodiments of the present invention, high-frequency power supply circuit 7 provides the voltage of 250kHz/25000V, when this high frequency voltage is worked for this welder, at tungsten electrode 4 ends, produce striking, be that high-frequency power supply circuit 7 provides this high voltage to be coupled on tungsten electrode 4, ionized air, thus form plasma arc.
Wherein, above-mentioned DC power supply circuit 6 and high-frequency power supply circuit 7 inside also comprise other components, and loops such as rectification, filtering, protection, does not repeat them here, but not in order to limit the present invention.
In embodiments of the present invention, for the raising further welding quality to high purity noble metal such as gold platinum, can carry out following concrete setting to the relative dimensions of tip:
(1) aperture of tip 32 can be set as 0.5mm-1.0mm;
(2) tip 32 is 3mm-4mm to the distance of welded part 8 place planes;
(3) tungsten electrode 4 end-to-end distances are certain from the distance of tip 32, set certain distance, for example 4mm.
Certainly, also can adopt other rational size design, not repeat them here, but not in order to limit the present invention.
In embodiments of the present invention, each part of above-mentioned microplasma high frequency open high-purity gold and silver welder can have following concrete setting:
(1) tungsten electrode 4 can adopt conventional material, and in pure tungsten batching, adding mass fraction is the cerium oxide of 1.8%-2.2% and the electrode of impurity≤0.1%, can certainly adopt other recipe ratios, at this only in order to explain the present invention;
Wherein, the end of tungsten electrode 4 in pumping chamber 33 can adopt back taper, like this easy arc striking.
(2) tubular conduction guide sleeve 2 is made by the high copper product of conductance, and it is mainly used in conduction and extraneous compressed inert is imported to inert gas passage by gas port 21, thereby forms melting tank, carries out welding operation;
(3) insulation sleeve 1 is made by high temperature ceramic material, and it plays and grips welder core component, and insulate with fixed mount, high temperature resistant;
(4) the poly-arc cover 3 of insulation is made by high-temperature insulation nonmetallic materials, and it is mainly used in article on plasma arc and converges, and produces air cooling effect, forms the plasma arc of columniform arc surface-stable, for welding work pieces and body filler 9 are welded to fusion;
(5) conduction gripping sleeve 2 plays and clamps tungsten electrode 4, and connects dc source 6 and high-frequency power supply circuit 7, and it is made by the higher copper product of conductance.
In this embodiment, the material of each part mentioned above also can adopt to possess the other materials of equivalent effect and effect type, does not repeat them here, but is not used in restriction the present invention.
In embodiments of the present invention, above-mentioned microplasma high frequency open high-purity gold and silver welder is also provided with other parts, control section for example, its control section is mainly to coordinate Current Control, air guide control and other controls, such as when switching on, when gas transmission etc., do not repeat them here, but not in order to limit the present invention.
In embodiments of the present invention, above-mentioned mentioned inert gas comprises argon gas, the argon arc welding of namely saying on ordinary meaning, at this not in order to limit the present invention.
In embodiments of the present invention, because plasma-arc has higher energy density, (energy density can reach 10000 to 100000w/ square centimeter for temperature and outspoken nature, more than the central temperature of cylindrical plasma arc can reach 18000-24000K, more than flame Flow Velocity can reach 300m/s), therefore, compare with general arc welding, the formed plasma-arc of microplasma high frequency open high-purity gold and silver welder that the embodiment of the present invention provides has following advantages:
(1) energy density is large, electric arc high directivity, and the ability of melting is strong, and Plasma Welding speed is faster;
(2) weldquality is insensitive to the variation of arc length, adopt special welding electrode, make the form subcylindrical of plasma arc, the angle of divergence very little (approximately 5 degree), and straight and upright property is good, arc length changes very little to the area effect of heating dot, therefore easily obtains uniform weld shape, all very useful to guaranteeing appearance of weld and even weld;
(3) tungsten electrode contracting, at the poly-arc cover of 4 insulation, can not contact with workpiece, therefore, can effectively avoid weld metal to produce tungsten inclusion phenomenon, and in addition, electric arc stirring property is good, and bath temperature is high, is conducive to the release of molten pool gas;
(4) plasma-arc due to pinch effect and thermal ionization degree higher, electric current is hour still very stable, the electronic power supply that adapted is novel, welding current may diminish to 0.1A, so little electric current also can reach arc stability burning, is therefore particularly suitable for welding the small high purity noble metal ornaments such as bullion and silver;
(5) welding cost is low, compares with water Welding, can power saving 1/3-1/2, economize gas 1/2-2/3, and in the situation that throat thickness is less, without silk filling.
Fig. 2 shows the welding method of the microplasma high frequency open high-purity gold and silver welder based on shown in above-mentioned Fig. 1 that the embodiment of the present invention provides, and its concrete step is as described below:
In step S101, the position docking that the first welding work pieces and the second welding work pieces need to be welded, wherein, described the first welding work pieces or the second welding work pieces are provided with body filler.
In step S102, opening inert gas valve makes inert gas enter by gas port, along inert gas passage, circulate, connect successively high-frequency power supply circuit and DC power supply circuit simultaneously, make tungsten electrode in pumping chamber, form electric arc, described plasma arc forms the stable plasma arc of cylindrical constant temperature through the air cooling effect of the poly-arc cover of insulation and tip oral area.
In step S103, described plasma arc carries out preheating to the docking site of described the first welding work pieces, the second welding work pieces and described body filler, then according to technological requirement, the body filler after described fusing is filled up to the corresponding docking site at described the first welding work pieces and described the second welding work pieces.
In step S104, follow-up polishing and matting are carried out in the relevant position of the corresponding docking site of described the first welding work pieces and described the second welding work pieces and described body filler.
In conjunction with shown in Fig. 3, the welding method of this device is understood, wherein simultaneously, in the present embodiment, in welding process, the temperature reaching when related relevant preheating time, weld interval, welding and the uniformity of welding etc., do not repeat them here, but not in order to limit the present invention.
In embodiments of the present invention, described the first welding work pieces, the docking site of the second welding work pieces and the distance of described tip are 3mm-4mm.
In embodiments of the present invention, above-mentioned body filler is the weld filler that utilizes workpiece self structure partly to form, and is filled in the docking site between workpiece, in weld seam after its fusing.
Wherein, after having welded, follow-up polishing and the operation of cleaning, substantially identical with the operation of prior art, do not repeat them here.
In embodiments of the present invention, plasma high-frequency welding manner is applied to the welding of the high purity noble metal such as bullion and silver, it is different from common Plasma Welding technology, the welding that this welder and welding manner provide, when guaranteeing weldment bonding strength and quality, guarantee the purity of precious metal, but also reduced loss, saved material.
The foregoing is only preferred embodiment of the present invention, not in order to limit the present invention, all any modifications of doing within the spirit and principles in the present invention, be equal to and replace and improvement etc., within all should being included in protection scope of the present invention.
Claims (10)
1. a microplasma high frequency open high-purity gold and silver welder, is characterized in that, described device comprises:
Be arranged on and be welded and fixed on frame, with the insulation sleeve that described fixed mount insulation arranges, described insulation sleeve is provided with the first cavity and the second cavity being communicated with up and down, and the aperture of described the first cavity is greater than the aperture of described the second cavity;
Be arranged on the tubular conduction guide sleeve in the first cavity of described insulation sleeve, described tubular conduction guide sleeve upper end is provided with for import the gas port of inert gas to described the first cavity and the second cavity;
Be arranged on the poly-arc cover of insulation that described insulation sleeve bottom is fixedly connected with described insulation sleeve, inner the 3rd cavity adapting with described the second cavity that is provided with of the poly-arc cover of described insulation, the lower end of described the 3rd cavity is provided with elliptoid pumping chamber near the position of tip, and described pumping chamber is used for compressing plasma arc and forms cylindrical arc;
In described tubular conduction guide sleeve, be provided with tungsten electrode, described tungsten electrode from described tubular conduction guide sleeve along the second cavity, extend to the bottom, pumping chamber of described the 3rd cavity, described tungsten electrode and described tip are provided with certain distance;
Described tungsten electrode fixes to clamp by conduction gripping sleeve, and the cross section of described conduction gripping sleeve is T-shaped, and the medial surface of described conduction gripping sleeve and described cylindric conduction guide sleeve forms cavity for enter inert gas circulation from described gas port;
Described tungsten electrode one end is connected with high-frequency power supply circuit with DC power supply circuit respectively by wire, and described DC power supply circuit is connected with welded part with after high-frequency power supply circuit parallel connection;
Wherein, described conduction gripping sleeve forms with the medial surface of described cylindric conduction guide sleeve cavity, the second cavity and the 3rd cavity form inert gas passage until tip is communicated with in the lump.
2. microplasma high frequency open high-purity gold and silver welder according to claim 1, is characterized in that, described DC power supply circuit provides weak current, and current values scope is 0.1A-10A.
3. microplasma high frequency open high-purity gold and silver welder according to claim 1, is characterized in that, described high-frequency power supply circuit provides the voltage of 250kHz/25000V.
4. microplasma high frequency open high-purity gold and silver welder according to claim 1, is characterized in that, the aperture of described tip is 0.5mm-1.0mm.
5. according to the microplasma high frequency open high-purity gold and silver welder described in claim 1 or 4, it is characterized in that, described tip is 3mm-4mm to the distance of welded part place plane.
6. microplasma high frequency open high-purity gold and silver welder according to claim 1, is characterized in that, described conduction gripping sleeve and described tubular conduction guide sleeve are made by the high copper product of conductance.
7. microplasma high frequency open high-purity gold and silver welder according to claim 1, is characterized in that, described insulation sleeve is made by high temperature ceramic material.
8. microplasma high frequency open high-purity gold and silver welder according to claim 1, is characterized in that, the poly-arc cover of described insulation is made by high-temperature insulation nonmetallic materials.
9. the welding method based on microplasma high frequency open high-purity gold and silver welder claimed in claim 1, is characterized in that, described method comprises the steps:
The position docking that the first welding work pieces and the second welding work pieces need to be welded, wherein, described the first welding work pieces or the second welding work pieces are provided with body filler;
Opening inert gas valve makes inert gas enter by gas port, along inert gas passage, circulate, connect successively high-frequency power supply circuit and DC power supply circuit simultaneously, make tungsten electrode in pumping chamber, form electric arc, described plasma arc forms the stable plasma arc of cylindrical constant temperature through the air cooling effect of the poly-arc cover of insulation and tip oral area;
Described plasma arc carries out preheating to the docking site of described the first welding work pieces, the second welding work pieces and described body filler, then according to technological requirement, the body filler after described fusing is filled up to the corresponding docking site at described the first welding work pieces and described the second welding work pieces;
Follow-up polishing and matting are carried out in relevant position to the corresponding docking site of described the first welding work pieces and described the second welding work pieces and described body filler.
10. microplasma high frequency open high-purity gold and silver welding method according to claim 9, is characterized in that, described the first welding work pieces, the docking site of the second welding work pieces and the distance of described tip are 3mm-4mm.