CN103628207A - Method for manufacturing colored spun yarn - Google Patents
Method for manufacturing colored spun yarn Download PDFInfo
- Publication number
- CN103628207A CN103628207A CN201310650259.6A CN201310650259A CN103628207A CN 103628207 A CN103628207 A CN 103628207A CN 201310650259 A CN201310650259 A CN 201310650259A CN 103628207 A CN103628207 A CN 103628207A
- Authority
- CN
- China
- Prior art keywords
- consumption
- temperature
- dyeing
- minutes
- time
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a method for manufacturing a colored spun yarn. The method comprises the following steps of (1) dyeing with dischargeable dye, performing enzyme treatment and soaping, wherein conditions of the enzyme treatment are shown as follows: the dosage of scouring enzyme is 4-6g/L, the consumption of sodium carbonate is 1-2g/L, the temperature is 65 DEG C, and the time is 40 minutes; indexes of the soaping are shown as follows: the consumption of a soaping agent is 8g/L, the time is 45 minutes, and the temperature is 80 DEG C; indexes of dyeing liquor are shown as follows: dye strength is 18 percent, the consumption of sodium chloride is 50g/L, the consumption of the sodium carbonate is 35g/L, the temperature is 65 DEG C, and the time is 40 minutes; (2) spinning dyed cotton slivers and other dyed cotton slivers, wherein the weight of dyed fibers accounts for 45 percent of the total weight of fibers; (3) performing singeing and reeling; (4) performing mercerization at the temperature of 70 DEG C for 5 seconds. According to the method for manufacturing the colored spun yarn, disclosed by the invention, a yarn dyed fabric produced by the colored spun yarn is dischargeable, so that the colored spun yarn double-mercerized yarn dyed fabric is special in discharge style.
Description
Technical field
The present invention relates to the manufacture method of fiber dyed yarn.
Background technology
Look spinning is generally to mix by two or more different color and luster fibers the yarn being spun into, and the fabric that look spinning is made into has a kind of dim natural stylistic effects, very popular.Colored fibre in look spinning mostly in the market is cotton bulk fibre and adopts K type or the reactive dyeing of KN type, bright in colour, chromatogram is complete, can form multiple style, but alkaline-resisting mercerising fastness is very poor, after concentrated base mercerising, fades serious, color and luster withers secretly, after processing, must carry out complementary color, strengthen the loss of human and material resources, energy aspect, production efficiency is low; Colored fibre in a kind of look spinning in addition adopts high temperature dyeing, and dyestuff mostly is s-triazine structure REACTIVE DYES, ability highly basic mercerising, but discharge performance is not good.To sum up, alkaline-resisting can not the pulling out of look spinning, can pull out not alkaline-resisting shortcoming and seriously hinder further developing and applying of look spinning.
Summary of the invention
The object of the present invention is to provide a kind of manufacture method of fiber dyed yarn, its yarn-dyed fabric of producing through this fiber dyed yarn has discharge, makes the photochromic fabric of look spinning mariages have special discharge style.
For achieving the above object, technical scheme of the present invention is the manufacture method of a kind of fiber dyed yarn of design, comprises the steps:
1) dyeing, with dyeing that can discharge, and carry out enzyme processing, the step of soaping; Enzyme treatment conditions are: scouring enzyme consumption 4-6g/L, soda ash consumption 1-2g/L, and temperature is 65 ℃, the time is 40 minutes; Described index of soaping is: soaping agent consumption 8g/L, and 45 minutes time, temperature is 80 ℃; The index of described dyeing liquor is: dye strength is 18%, sodium chloride consumption 50g/L, soda ash consumption 35g/L, and temperature is 65 ℃, the time is 40 minutes;
2) dyeing sliver and other dyeing slivers are spinned, coloured fibre weight accounts for 45% of total weight of fiber;
3) singe, reeling;
4) mercerization finish, temperature is 70 ℃, the processing time is 5 seconds.
Advantage of the present invention and beneficial effect are: a kind of manufacture method of fiber dyed yarn is provided, and its yarn-dyed fabric of producing through this fiber dyed yarn has discharge, make the photochromic fabric of look spinning mariages have special discharge style.
The specific embodiment
Below in conjunction with embodiment, the specific embodiment of the present invention is further described.Following examples are only for technical scheme of the present invention is more clearly described, and can not limit the scope of the invention with this.
The concrete technical scheme of implementing of the present invention is:
Embodiment 1
A manufacture method for fiber dyed yarn, comprises the steps:
1) dyeing, with dyeing that can discharge, and carry out enzyme processing, the step of soaping; Enzyme treatment conditions are: scouring enzyme consumption 4g/L, soda ash consumption 1g/L, and temperature is 65 ℃, the time is 40 minutes; Described index of soaping is: soaping agent consumption 8g/L, and 45 minutes time, temperature is 80 ℃; The index of described dyeing liquor is: dye strength is 18%, sodium chloride consumption 50g/L, soda ash consumption 35g/L, and temperature is 65 ℃, the time is 40 minutes;
2) dyeing sliver and other dyeing slivers are spinned, coloured fibre weight accounts for 45% of total weight of fiber;
3) singe, reeling;
4) mercerization finish, temperature is 70 ℃, the processing time is 5 seconds.
Embodiment 2
A manufacture method for fiber dyed yarn, comprises the steps:
1) dyeing, with dyeing that can discharge, and carry out enzyme processing, the step of soaping; Enzyme treatment conditions are: scouring enzyme consumption 6g/L, soda ash consumption 2g/L, and temperature is 65 ℃, the time is 40 minutes; Described index of soaping is: soaping agent consumption 8g/L, and 45 minutes time, temperature is 80 ℃; The index of described dyeing liquor is: dye strength is 18%, sodium chloride consumption 50g/L, soda ash consumption 35g/L, and temperature is 65 ℃, the time is 40 minutes;
2) dyeing sliver and other dyeing slivers are spinned, coloured fibre weight accounts for 45% of total weight of fiber;
3) singe, reeling;
4) mercerization finish, temperature is 70 ℃, the processing time is 5 seconds.
Embodiment 3
A manufacture method for fiber dyed yarn, comprises the steps:
1) dyeing, with dyeing that can discharge, and carry out enzyme processing, the step of soaping; Enzyme treatment conditions are: scouring enzyme consumption 5g/L, soda ash consumption 1.2g/L, and temperature is 65 ℃, the time is 40 minutes; Described index of soaping is: soaping agent consumption 8g/L, and 45 minutes time, temperature is 80 ℃; The index of described dyeing liquor is: dye strength is 18%, sodium chloride consumption 50g/L, soda ash consumption 35g/L, and temperature is 65 ℃, the time is 40 minutes;
2) dyeing sliver and other dyeing slivers are spinned, coloured fibre weight accounts for 45% of total weight of fiber;
3) singe, reeling;
4) mercerization finish, temperature is 70 ℃, the processing time is 5 seconds.
The above is only the preferred embodiment of the present invention; it should be pointed out that for those skilled in the art, do not departing under the prerequisite of the technology of the present invention principle; can also make some improvements and modifications, these improvements and modifications also should be considered as protection scope of the present invention.
Claims (1)
1. the manufacture method of fiber dyed yarn, is characterized in that, comprises the steps:
1) dyeing, with dyeing that can discharge, and carry out enzyme processing, the step of soaping; Enzyme treatment conditions are: scouring enzyme consumption 4-6g/L, soda ash consumption 1-2g/L, and temperature is 65 ℃, the time is 40 minutes; Described index of soaping is: soaping agent consumption 8g/L, and 45 minutes time, temperature is 80 ℃; The index of described dyeing liquor is: dye strength is 18%, sodium chloride consumption 50g/L, soda ash consumption 35g/L, and temperature is 65 ℃, the time is 40 minutes;
2) dyeing sliver and other dyeing slivers are spinned, coloured fibre weight accounts for 45% of total weight of fiber;
3) singe, reeling;
4) mercerization finish, temperature is 70 ℃, the processing time is 5 seconds.