CN103626442A - 粉煤灰蒸压砖砌筑专用砂浆及制备方法 - Google Patents

粉煤灰蒸压砖砌筑专用砂浆及制备方法 Download PDF

Info

Publication number
CN103626442A
CN103626442A CN201210302053.XA CN201210302053A CN103626442A CN 103626442 A CN103626442 A CN 103626442A CN 201210302053 A CN201210302053 A CN 201210302053A CN 103626442 A CN103626442 A CN 103626442A
Authority
CN
China
Prior art keywords
mortar
fly ash
cement
coal ash
water
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201210302053.XA
Other languages
English (en)
Inventor
王明飞
程立国
刘晓美
陈功富
刘鑫
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
SHUANGLIAO GUOFENG CEMENT PRODUCT Co Ltd
Original Assignee
SHUANGLIAO GUOFENG CEMENT PRODUCT Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by SHUANGLIAO GUOFENG CEMENT PRODUCT Co Ltd filed Critical SHUANGLIAO GUOFENG CEMENT PRODUCT Co Ltd
Priority to CN201210302053.XA priority Critical patent/CN103626442A/zh
Publication of CN103626442A publication Critical patent/CN103626442A/zh
Pending legal-status Critical Current

Abstract

本发明适用粉煤灰蒸压砖砌筑专用砂浆，该专用砂浆是由以下重量配比的原料制成：天然砂1350～1550kg；水泥183～337kg；粉煤灰32～60kg；粉煤灰蒸压砖砌筑专用砂浆专用外加剂2.15～7.15Kg；水215～250kg。其制作方法包括以下步骤：①将天然砂、水泥、粉煤灰、外加剂、水按重量比通过通过机械均匀混合；②将步骤①混合好的砂浆用机械搅拌3min。本发明制备工艺简单，有效降低普通砌筑砂浆的用水量，改善和易性，提高密实性，且后期强度增长较快，还有效提高了其抗掺抗冻性能和耐久性能。蒸压粉煤灰砖表面光洁不易与砂浆粘结，本发明中掺入一定比例的粉煤灰及外加剂不但有效改善砂浆性能，降低造价，还会提高砂浆与砖的粘结力。

Description

粉煤灰蒸压砖砌筑专用砂浆及制备方法
技术领域
本发明属于建筑材料领域，具体涉及粉煤灰蒸压砖砌筑专用砂浆及制备方法。
背景技术
随着社会的进步，城市的需要，红砖已逐步被取替，取而代之的蒸压粉煤灰砖和许多新型墙体材料砌体已开始流向市场，而现场搅拌的砂浆和一般普通砂浆也不能满足蒸压粉煤灰砖等新型墙体材料砌体的需求。
很多施工人员对砂浆的了解还局现在加点水泥再加点砂子就可以了，其实我们研制砂浆的同时还需要深入了解原材料的性能。例如，水泥在别人的眼中是灰色的粉末，而在研发人员的眼中，应该是硅酸三钙、硅酸二钙、铝酸三钙、铁铝酸三钙、石膏和填料的混合物，我们不是在简单的和泥，我们不是简单的工匠。砂浆领域，是一个未被充分认识的领域，好多的反应机理由于过于复杂，还没有被研究。预拌砂浆属于聚合物水泥砂浆的领域，聚合物与水泥相互作用形成了最终的固化体，其中深入的机理，还需要投入大量的精力去研究。
现场拌制的砂浆，配合比不稳定、污染严重一直是砌筑工程难以解决的一大弊端，成为影响现场拌制砂浆应用效果的主要因素。而预拌砂浆的应用恰恰解决了这一问题。近几年来，随着预拌砂浆生产的规模化，生产成本的进一步降低，再加上其质量稳定、提高工效和文明环保的优点，越来越广泛地被应用于砌筑工程。预拌砂浆因为掺加了粉煤灰和外加剂，并且砌体灰缝减小到3-5mm，从而大大降低了灰缝的冷桥效应，有效提高了墙体的节能效果。
发明内容
本发明所要解决的技术问题是提供一种粉煤灰蒸压砖砌筑专用砂浆及制备方法，该砂浆由水泥，砂子，粉煤灰，粉煤灰蒸压砖砌筑专用砂浆外加剂和水制成，以粉煤灰按比例取代水泥用量、降低成本，降低砌筑砂浆的用水量，改善和易性，提高密实性，提高后期强度增长，改善抗掺抗冻性能和耐久性能并降低造价，以外加剂改善其新拌性能和抗渗抗冻抗裂，并提高混凝土强度的性能。
本发明的技术方案：
一种粉煤灰蒸压砖砌筑专用砂浆，其原料配方是：天然砂1350～1550 Kg；水泥183～337Kg；粉煤灰32～60Kg；粉煤灰蒸压砖砌筑专用砂浆外加剂(KDH-L型）2.15～7.15kg；水215～250 Kg（使砂浆稠度达到70～90mm的用水量）。
所述天然砂细度模数为中砂且应符合《普通混凝土用砂、石质量及检验方法标准》JGJ52的要求，所述水泥为强度等级是32.5级的复合硅酸盐水泥或强度等级是32.5级矿渣硅酸盐水泥或普通硅酸盐水泥，所述粉煤灰为Ⅰ级或Ⅱ级粉煤灰，所述外加剂为粉煤灰蒸压砖砌筑专用砂浆外加剂(山西凯迪建材公司生产KDH-L型)，所述水为符合《混凝土用水标准》JGJ63要求用水。
一种粉煤灰蒸压砖砌筑专用砂浆的制备方法，它包括以下步骤：①将天然砂1350～1550 Kg；水泥183～337Kg；粉煤灰32～60Kg；外加剂2.15kg～7.15Kg；水215～250 Kg按重量比通过机械均匀混合；②将步骤①混合好的砂浆用机械搅拌3min。
本发明与现有技术相比所改善的效果有以下几点：①有效降低普通砌筑砂浆的用水量，改善和易性，提高密实性；②后期强度增长较快，还有效提高其抗掺抗冻性能和耐久性能；③提高砂浆与砖的粘结力，改善砂浆性能，降低造价。
主要性能指标见下表
具体实施方式
砂含水大于0.5%时要扣去砂中含水。
实施例1：
按配比称取原材料（原材料为干材料），砂子1550kg，水泥183 kg，粉煤灰32 kg，外加剂2.15 kg，水215 kg。
所述砂子为堆积密度1550 kg /m3的河砂中砂，所述水泥为强度等级是32.5级的复合硅酸盐水泥，所述粉煤灰为Ⅰ级粉煤灰，所述外加剂为粉煤灰蒸压砖砌筑专用砂浆外加剂(山西凯迪建材公司生产KDH-L型)，所述水为饮用水。
制备方法是：①将砂子1550kg，水泥183 kg，粉煤灰32 kg，外加剂2.15 kg，水215 kg按重量比通过机械均匀混合；②将步骤①混合好的砂浆用机械搅拌3min。
实施例2：
按配比称取原材料（原材料为干材料），砂子1500 kg，水泥208 kg，粉煤灰37 kg，外加剂2.94 kg，水220 kg。
所述砂子为堆积密度1500 Kg/m3的河砂中砂，所述水泥为强度等级是32.5级的复合硅酸盐水泥，所述粉煤灰为Ⅰ级粉煤灰，所述外加剂为粉煤灰蒸压砖砌筑专用砂浆外加剂(山西凯迪建材公司生产KDH-L型)，所述水为饮用水。
制备方法同实施例1。
实施例3：
按配比称取原材料（原材料为干材料），砂子1450 kg，水泥234 kg，粉煤灰41 kg，外加剂3.85 kg，水230 kg。
所述砂子为堆积密度1450 Kg/m3的河砂中砂，所述水泥为强度等级是32.5级的复合硅酸盐水泥，所述粉煤灰为Ⅰ级粉煤灰，所述外加剂为粉煤灰蒸压砖砌筑专用砂浆外加剂(山西凯迪建材公司生产KDH-L型)，所述水为饮用水。
制备方法同实施例1。
实施例4：
按配比称取原材料（原材料为干材料），砂子1400 kg，水泥286 kg，粉煤灰50 kg，外加剂5.38kg，水240 kg。
所述砂子为堆积密度1400 Kg/m3的河砂中砂，所述水泥为强度等级是32.5级的复合硅酸盐水泥，所述粉煤灰为Ⅰ级粉煤灰，所述外加剂为粉煤灰蒸压砖砌筑专用砂浆外加剂(山西凯迪建材公司生产KDH-L型)，所述水为饮用水。
制备方法同实施例1。
实施例5：
按配比称取原材料（原材料为干材料），砂子1350 kg，水泥337kg，粉煤灰60 kg，外加剂7.15kg，水250kg。
所述砂子为堆积密度1350 Kg/m3的河砂中砂，所述水泥为强度等级是32.5级的复合硅酸盐水泥，所述粉煤灰为Ⅰ级粉煤灰，所述外加剂为粉煤灰蒸压砖砌筑专用砂浆外加剂(山西凯迪建材公司生产KDH-L型)，所述水为饮用水。
制备方法同实施例1。

Claims (6)

1. 一种粉煤灰蒸压砖砌筑专用砂浆，其特征在于：该专用砂浆是由以下重量配比的原料制成：天然砂1350～1550 kg；水泥183～337 kg；粉煤灰32～60 kg；粉煤灰蒸压砖砌筑专用砂浆外加剂2.15～7.15kg；水215～250 kg。
2.根据权利要求1所述的一种粉煤灰蒸压砖砌筑专用砂浆，其特征在于：所述天然砂的细度模数是中砂。
3.根据权利要求1所述的一种粉煤灰蒸压砖砌筑专用砂浆，其特征在于：所述水泥为强度等级是32.5级的复合硅酸盐水泥或强度等级是32.5级矿渣硅酸盐水泥或普通硅酸盐水泥。
4.根据权利要求1所述的一种粉煤灰蒸压砖砌筑专用砂浆，其特征在于：所述粉煤灰为Ⅰ级或Ⅱ级粉煤灰。
5.根据权利要求1所述的一种粉煤灰蒸压砖砌筑专用砂浆，其特征在于：所述外加剂为粉煤灰蒸压砖砌筑专用砂浆外加剂。
6.一种是粉煤灰蒸压砖砌筑专用砂浆的制备方法，其特征在于：该方法包括以下步骤：①将天然砂1350～1550kg；水泥183～337 kg；粉煤灰32～60 kg；粉煤灰蒸压砖砌筑专用砂浆外加剂2.15kg～7.15Kg；水215～250 kg按重量比通过机械均匀混合；②将步骤①混合好的砂浆用机械搅拌3min。
CN201210302053.XA 2012-08-23 2012-08-23 粉煤灰蒸压砖砌筑专用砂浆及制备方法 Pending CN103626442A (zh)