CN103623934A - 一种碳化硅提纯分离药剂及其制备方法 - Google Patents
一种碳化硅提纯分离药剂及其制备方法 Download PDFInfo
- Publication number
- CN103623934A CN103623934A CN201310615015.4A CN201310615015A CN103623934A CN 103623934 A CN103623934 A CN 103623934A CN 201310615015 A CN201310615015 A CN 201310615015A CN 103623934 A CN103623934 A CN 103623934A
- Authority
- CN
- China
- Prior art keywords
- parts
- silicon carbide
- acid
- silicon
- separation agent
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
一种碳化硅提纯分离药剂,由下列重量份的原料制成:2-萘磺酸钠3-4、焦磷酸4-6、二聚酸2-3、邻苯二甲酸酯5-8、油酸3-5、松醇油12-14、柠檬酸1-2、O-烷基-N-烷基硫逐氨基甲酸酯7-9、硬脂酸聚氧乙烯酯1-2、甲醇40-45、柴油35-40、助剂4-5、水40-45。本发明使用多种溶剂和水,在表面活性剂的作用下,形成稳定的乳化体系,改变硅和碳化硅的界面张力,将其二者分离,通过使用本发明的助剂,使得硅和碳化硅的分离更彻底,得到的碳化硅纯度更高,成品纯度能够达到96%,大大提高了回收产品的质量。
Description
技术领域
本发明涉及硅片线锯工艺产生的砂浆中的硅与碳化硅的粉体分离技术领域,尤其涉及一种碳化硅提纯分离药剂及其制备方法。
背景技术
各种硅片,包括单晶硅和多晶硅太阳能电池片、微电子产业用的硅晶圆,普遍采用钢丝线锯配合碳化硅磨料浆切割生产,一下简称砂浆。硅片厚度一般为0.22mm,目前还没有减薄的发展趋势,线锯缝宽度一般为0.18-0.30mm,这意味着将有20-60%的高纯硅料成为锯屑进入砂浆,其提取回收等于开辟一种新的规模可观的高纯硅原料来源。
虽然回收高纯硅的效益可观,但是硅和碳化硅的物化性质较为接近,目前为止关于该项目的研究成果还很少,也没有实际生产成功的案例,需要进一步研究可行的用于实际生产的分离药剂和方法。
发明内容
本发明的目的在于提供一种碳化硅提纯分离药剂及其制备方法,使用该药剂碳化硅回收率高,碳化硅纯度高。
本发明的技术方案如下:
一种碳化硅提纯分离药剂,其特征在于由下列重量份的原料制成:2-萘磺酸钠3-4、焦磷酸4-6、二聚酸2-3、邻苯二甲酸酯5-8、油酸3-5、松醇油12-14、柠檬酸1-2、O-烷基-N-烷基硫逐氨基甲酸酯7-9、硬脂酸聚氧乙烯酯1-2、甲醇40-45、柴油35-40、助剂4-5、水40-45。所述的助剂由下列重量份的原料混合而成:12-15%盐酸溶液20-24、乙醇40-45、扩散剂MF 3-4、水100。
所述的碳化硅提纯分离药剂的制备方法,其特征在于包括以下步骤:将水、2-萘磺酸钠、焦磷酸、甲醇混合,加热至35-45℃,加入邻苯二甲酸酯、油酸、松醇油、柠檬酸、O-烷基-N-烷基硫逐氨基甲酸酯、二聚酸、硬脂酸聚氧乙烯酯、柴油,搅拌均匀,加热至60-70℃,加入其他剩余成分,搅拌10-15分钟,即得。
使用该浮选剂时,浮选剂与砂浆重量比为1:2-3;将砂浆与浮选剂混合,以1000-1200rad/min 的转速搅拌4-6min,静置时体系分层,上层为碳化硅、中间为液体层、下层为硅,刮取上层碳化硅,收集下层硅而实现分离。
本发明的有益效果
本发明使用多种溶剂和水,在表面活性剂的作用下,形成稳定的乳化体系,改变硅和碳化硅的界面张力,将其二者分离,通过使用本发明的助剂,使得硅和碳化硅的分离更彻底,得到的碳化硅纯度更高,成品纯度能够达到96%,大大提高了回收产品的质量。
具体实施方式
一种碳化硅提纯分离药剂,由下列重量份(公斤)的原料制成:2-萘磺酸钠3.5、焦磷酸5、二聚酸2.5、邻苯二甲酸酯6、油酸4、松醇油13、柠檬酸1.5、O-烷基-N-烷基硫逐氨基甲酸酯8、硬脂酸聚氧乙烯酯1.5、甲醇43、柴油38、助剂4.5、水43。所述的助剂由下列重量份(公斤)的原料混合而成:12-15%盐酸溶液20、乙醇40、扩散剂MF 4、水100。
所述的碳化硅提纯分离药剂的制备方法,包括以下步骤:将水、2-萘磺酸钠、焦磷酸、甲醇混合,加热至40℃,加入邻苯二甲酸酯、油酸、松醇油、柠檬酸、O-烷基-N-烷基硫逐氨基甲酸酯、二聚酸、硬脂酸聚氧乙烯酯、柴油,搅拌均匀,加热至65℃,加入其他剩余成分,搅拌14分钟,即得。
使用该浮选剂时,浮选剂与砂浆重量比为1:2.5;将砂浆与浮选剂混合,以1100rad/min 的转速搅拌5min,静置时体系分层,上层为碳化硅、中间为液体层、下层为硅,刮取上层碳化硅,收集下层硅而实现分离。
该实施例收集的碳化中残存的硅少于4%wt,砂浆中残存的碳化硅少于6%wt。
Claims (2)
1.一种碳化硅提纯分离药剂,其特征在于由下列重量份的原料制成:2-萘磺酸钠3-4、焦磷酸4-6、二聚酸2-3、邻苯二甲酸酯5-8、油酸3-5、松醇油12-14、柠檬酸1-2、O-烷基-N-烷基硫逐氨基甲酸酯7-9、硬脂酸聚氧乙烯酯1-2、甲醇40-45、柴油35-40、助剂4-5、水40-45;所述的助剂由下列重量份的原料混合而成:12-15%盐酸溶液20-24、乙醇40-45、扩散剂MF 3-4、水100。
2.根据权利要求1所述的碳化硅提纯分离药剂的制备方法,其特征在于包括以下步骤:将水、2-萘磺酸钠、焦磷酸、甲醇混合,加热至35-45℃,加入邻苯二甲酸酯、油酸、松醇油、柠檬酸、O-烷基-N-烷基硫逐氨基甲酸酯、二聚酸、硬脂酸聚氧乙烯酯、柴油,搅拌均匀,加热至60-70℃,加入其他剩余成分,搅拌10-15分钟,即得。