CN103614802A - Filament for thermal insulating plastic woven bags - Google Patents
Filament for thermal insulating plastic woven bags Download PDFInfo
- Publication number
- CN103614802A CN103614802A CN201310616046.1A CN201310616046A CN103614802A CN 103614802 A CN103614802 A CN 103614802A CN 201310616046 A CN201310616046 A CN 201310616046A CN 103614802 A CN103614802 A CN 103614802A
- Authority
- CN
- China
- Prior art keywords
- parts
- filament
- woven bag
- plastic woven
- powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention discloses a filament for thermal insulating plastic woven bags. The filament is characterized by being prepared from the following raw materials in parts by weight through the processes of compounding, melting, filtrating, film forming by extrusion, water-cooling, filament separating, filament drawing, rolling, and the like: 100 parts of polypropylene, 14-17 parts of medium-density polyethylene, 1-1.2 parts of ammonium polyphosphate, 2-2.4 parts of pentaerythritol, 0.4-0.6 parts of dibutyl phthalate, 12-15 parts of ABS high glue powder, 0.8-1.0 parts of microcrystalline wax, 1-2 parts of 2-methyl methacrylate, 1-2 parts of crosslinking agent TAC, 2-3 parts of menthyl acetate, and 3-3.5 parts of additives. The filament disclosed by the invention is reasonable in formula and low in cost; a prepared plastic woven bag has good heat preservation and thermal insulation effects, and is large in volume, novel in structure, sturdy and durable, skidproof, and unbreakable, therefor, the plastic woven bag is especially suitable for long-distance transportation and export, and belongs to a novel woven bag for material storage and transportation.
Description
Technical field
The present invention relates to chemical technology field, particularly silk for a kind of heatpiston's woven bag.
Background technology
Polywoven Bag forms and is divided into Polypropylene Bag, Polythene Bag by main material; By method of sewing, be divided into bag at the bottom of the seam end bag, tape edge.A kind of packaging material that are widely used at present the article such as fertilizer, chemical products.Its main production is that to utilize plastic raw materials be flat filament through extrusion film, cutting, simple tension, through obtaining product through knitting device, is commonly referred to as woven bag.The packaging bag of the polypropylene flat-filament establishment that conventional art is produced, weatherability is poor, at north of china in winter, easily occur hardening, the problem such as embrittlement, demoulding, peeling, fracture, in south because summer temperature is high, illumination is strong, ultraviolet penetration power is strong, easily cause that woven bag is aging, the problem such as burn into poor toughness, intensity low service life is short, not only wasted resource but also contaminated environment.
Summary of the invention
The object of this invention is to provide silk for a kind of heatpiston's woven bag.
In order to realize object of the present invention, the present invention passes through following scheme implementation:
Silk for a kind of heatpiston's woven bag, is made by operations such as batching, melting, filtration, extruding membrane, water-cooled, sub-wire, wire drawing, rollings by the raw material of following weight portion: polypropylene 100, medium density polyethylene 14-17, APP 1-1.2, pentaerythrite 2-2.4, dibutyl phthalate 0.4-0.6, ABS high glue powder 12-15, microwax 0.8-1.0,2-methyl methacrylate 1-2, crosslinking agent TAC 1-2, menthyl acetate 2-3, auxiliary agent 3-3.5;
Described auxiliary agent is made by the raw material of following weight portion: clay 20-24, alum 5-6, altax 2-3, crosslinking agent TAC 2-3, antioxidant 1010 1-2, actinolite 3-4, ferrocene 2-3, morpholine 1-2,1,6 hexanediyl ester 5-7, phthalic acid ester 35-40, n-propyl gallate 3-4, green tea powder 1-2, coix seed oil 2-3, vanadium diboride 2-3, epicatechin 1-2; Preparation method sends into clay, actinolite in calcining furnace and calcine 2-3 hour at 720-740 ℃, then, takes out, and sends in the hydrochloric acid solution of 10-15% and soaks 2-3 hour, filters, and obtains filter residue, with clear water, cleans, and dries, grinds to form 400-600 order powder; Gained powder mixes with other residual components, is heated to 60-70 ℃, and stirring reaction 40-50 minute is cooling, grinds to form slurry, obtains.
Excellent effect of the present invention is: the present invention fills a prescription rationally, and cost is low, and the Polywoven Bag of making has good heat insulating effect, volume is large, and novel structure is durable, anti-skidding, bale broken not, suitable especially long distance transportation and outlet, belong to that novel material is stored and the woven bag of transportation use.
The specific embodiment
Below by instantiation, the present invention is described in detail.
Silk for a kind of heatpiston's woven bag, by following weight portion (kilogram) raw material by operations such as batching, melting, filtration, extruding membrane, water-cooled, sub-wire, wire drawing, rollings, make: polypropylene 100, medium density polyethylene 14, APP 1, pentaerythrite 2, dibutyl phthalate 0.4, ABS high glue powder 12, microwax 0.8,2-methyl methacrylate 1, crosslinking agent TAC 1, menthyl acetate 2, auxiliary agent 3;
Described auxiliary agent by following weight portion (kilogram) raw material make: described auxiliary agent by following weight portion (kilogram) raw material make: clay 20, alum 5, altax 3, crosslinking agent TAC 2, antioxidant 1010 1, actinolite 3, ferrocene 2, morpholine 1,1,6 hexanediyl ester 5, phthalic acid ester 35, n-propyl gallate 3, green tea powder 1, coix seed oil 2, vanadium diboride 3, epicatechin 1; Preparation method sends into clay, actinolite in calcining furnace and calcine 2-3 hour at 720-740 ℃, then, takes out, and sends in the hydrochloric acid solution of 10-15% and soaks 2-3 hour, filters, and obtains filter residue, with clear water, cleans, and dries, grinds to form 400-600 order powder; Gained powder mixes with other residual components, is heated to 60-70 ℃, and stirring reaction 40-50 minute is cooling, grinds to form slurry, obtains.
After tested, the flat filament that the present invention produces radially pull-off force and broadwise pull-off force is all greater than 760N/50mm, has greatly improved the TENSILE STRENGTH of flat filament, has stopped the fracture of wire problem in braiding process.
Claims (1)
1. silk for heatpiston's woven bag, it is characterized in that, by the raw material of following weight portion, by operations such as batching, melting, filtration, extruding membrane, water-cooled, sub-wire, wire drawing, rollings, made: polypropylene 100, medium density polyethylene 14-17, APP 1-1.2, pentaerythrite 2-2.4, dibutyl phthalate 0.4-0.6, ABS high glue powder 12-15, microwax 0.8-1.0,2-methyl methacrylate 1-2, crosslinking agent TAC 1-2, menthyl acetate 2-3, auxiliary agent 3-3.5;
Described auxiliary agent is made by the raw material of following weight portion: clay 20-24, alum 5-6, altax 2-3, crosslinking agent TAC 2-3, antioxidant 1010 1-2, actinolite 3-4, ferrocene 2-3, morpholine 1-2,1,6 hexanediyl ester 5-7, phthalic acid ester 35-40, n-propyl gallate 3-4, green tea powder 1-2, coix seed oil 2-3, vanadium diboride 2-3, epicatechin 1-2; Preparation method sends into clay, actinolite in calcining furnace and calcine 2-3 hour at 720-740 ℃, then, takes out, and sends in the hydrochloric acid solution of 10-15% and soaks 2-3 hour, filters, and obtains filter residue, with clear water, cleans, and dries, grinds to form 400-600 order powder; Gained powder mixes with other residual components, is heated to 60-70 ℃, and stirring reaction 40-50 minute is cooling, grinds to form slurry, obtains.