CN103613332A - 一种集料掺镍渣的高强混凝土 - Google Patents
一种集料掺镍渣的高强混凝土 Download PDFInfo
- Publication number
- CN103613332A CN103613332A CN201310568834.8A CN201310568834A CN103613332A CN 103613332 A CN103613332 A CN 103613332A CN 201310568834 A CN201310568834 A CN 201310568834A CN 103613332 A CN103613332 A CN 103613332A
- Authority
- CN
- China
- Prior art keywords
- concrete
- nickel slag
- aggregate
- strength
- quality
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明提供一种集料掺镍渣的高强混凝土,它含有胶凝材料和集料;胶凝材料含有水泥、矿粉及粉煤灰;集料含有黄砂、石子及镍渣;每立方米混凝土中,水泥的质量为365~405kg;矿粉的质量为68~100kg;粉煤灰的质量为35~55kg;黄砂的质量为320~425kg;石子的质量为950~1100kg;镍渣的质量为320~420kg。本发明采用镍渣作为集料的一部分,该组分配比中的镍渣能充分改善集料的级配问题,提高集料的密实程度,改善混凝土拌合物性能,从而提高混凝土的强度。又配合使用聚羧酸系的高性能减水剂,该减水剂具有减水率高的特点,能充分分散水泥颗粒,减少坍塌度的损失,改善C60高强混凝土在施工中存在的粘稠、结底板结等问题,同样也提高了混凝土的强度及耐久性。
Description
技术领域
本发明涉及一种集料掺镍渣的高强混凝土,这种高强混凝土特别是标号为C60的混凝土。
背景技术
混凝土是指由胶凝材料将集料胶结成整体的工程复合材料的统称。通常是指用水泥作胶凝材料,砂、石子作集料,与水(加或不加外加剂和掺合料)按一定比例配合,经搅拌、成型、养护而得的水泥混凝土。
混凝土按标准抗压强度(以边长为150mm的立方体为标准试件,在标准养护条件下养护28天,按照标准试验方法测得的具有95%保证率的立方体抗压强度)划分的强度等级,称为标号,用C表示。通常分为C10、C15、C20、C25、C30、C35、C40、C45、C50、C55、C60等。C60混凝土指的是这种混凝土的抗压强度是60Mpa。
随着国民经济的高速发展,高强高性能混凝土在建筑、道路、桥梁、港口、海洋、大跨度及预应力结构、高耸建筑物等工程中的应用将越来越广泛,高强高性能混凝土作为***推广应用的十大新技术之一,是建设工程发展的必然趋势。混凝土强度等级也将不断提高,C60~C80的混凝土将普遍得到应用。
而随着C60高强混凝土的普遍应用,C60混凝土的各方面性能要求也越来越高,选择使用好的原材料就显得尤为关键。目前市场上的好质量的集料越来越紧张,价格也越来越高。而随着经济的高速发展,工矿企业生产的工业废渣——镍渣也越来越多,如何能因地制宜合理地将此工业废料加以利用,使这种工业废渣能应用到混凝土的集料中去,并不改变混凝土的强度、工作性和耐久性能性能,是本发明要研究的内容。
发明内容
本发明提供一种集料掺镍渣的的高强混凝土。
为达到上述目的,本发明采用的技术方案是:一种集料掺镍渣的高强混凝土,它含有胶凝材料和集料;所述胶凝材料含有水泥、矿粉及粉煤灰;所述集料含有黄砂、石子及镍渣;每立方米混凝土中,所述水泥的质量为365~405kg;所述矿粉的质量为68~100kg;所述粉煤灰的质量为35~55kg;所述黄砂的质量为320~425kg;所述石子的质量为950~1100kg;所述镍渣的质量为320~420kg。
上述技术方案中的有关内容解释如下:
1、上述方案中,所述胶凝材料还含有外加剂,所述外加剂为聚羧酸系高性能减水剂。
2、上述方案中,所述聚羧酸系高性能减水剂占所述胶凝材料总质量的1.2%~1.5%。
3、上述方案中,所述镍渣是冶炼镍铁合金产生的固体废渣,是工矿企业生产的废渣,镍铁合金主要被用作不锈钢生产,因此镍渣也被称为不锈钢渣或镍铁渣。
4、上述方案中,所述镍渣作为集料的一部分,按一定比例添加在集料中,其他组分基本不变。
由于上述技术方案运用,本发明与现有技术相比具有下列优点:
由于本发明采用镍渣作为集料的一部分,则该组分中的镍渣能充分改善集料的级配问题,提高集料的密实程度,改善混凝土拌合物性能,从而提高混凝土的强度。又配合使用聚羧酸系的高性能减水剂,该减水剂具有减水率高的特点,能充分分散水泥颗粒,减少坍塌度的损失,改善C60高强混凝土在施工中存在的粘稠、结底板结等问题,同样也提高了混凝土的强度及耐久性,弹性模量也一并得到了提高。
具体实施方式
下面结合实施例对本发明作进一步描述:
实施例:
一种集料掺镍渣的高强混凝土,它含有胶凝材料和集料;所述胶凝材料含有水泥、矿粉及粉煤灰;所述集料含有黄砂、石子及镍渣;每立方米混凝土中,所述水泥的质量为365~405kg;所述矿粉的质量为68~100kg;所述粉煤灰的质量为35~55kg;所述黄砂的质量为320~425kg;所述石子的质量为950~1100kg;所述镍渣的质量为320~420kg。
所述胶凝材料还含有外加剂,所述外加剂为聚羧酸系高性能减水剂。
所述聚羧酸系高性能减水剂占所述胶凝材料总质量的1.2%~1.5%。
所述镍渣是冶炼镍铁合金产生的固体废渣,是工矿企业生产的废渣,镍铁合金主要被用作不锈钢生产,因此镍渣也被称为不锈钢渣或镍铁渣。
所述镍渣作为集料的一部分,按一定比例添加在集料中,其他组分基本不变。可以使掺了镍渣的C60高强混凝土的设计强度可以达到70Mpa。同时,掺用了镍渣的C60高强混凝土的和易性、流动性都较好,基本不泌水,能保持优异的工作性能。混凝土的混凝土的坍塌度设计值达到220mm以上,扩展径60mm以上。混凝土的坍塌度1h损失值小于20mm。
采用镍渣作为集料的一部分,则该组分中的镍渣能充分改善集料的级配问题,提高集料的密实程度,改善混凝土拌合物性能,从而提高混凝土的强度。又配合使用聚羧酸系的高性能减水剂,该减水剂具有减水率高的特点,能充分分散水泥颗粒,减少坍塌度的损失,改善C60高强混凝土在施工中存在的粘稠、结底板结等问题,同样也提高了混凝土的强度及耐久性,弹性模量也一并得到了提高。
上述实施例只为说明本发明的技术构思及特点,其目的在于让熟悉此项技术的人士能够了解本发明的内容并据以实施,并不能以此限制本发明的保护范围。凡根据本发明精神实质所作的等效变化或修饰,都应涵盖在本发明的保护范围之内。
Claims (3)
1.一种集料掺镍渣的高强混凝土,其特征在于:它含有胶凝材料和集料;所述胶凝材料含有水泥、矿粉及粉煤灰;所述集料含有黄砂、石子及镍渣;每立方米混凝土中,所述水泥的质量为365~405kg;所述矿粉的质量为68~100kg;所述粉煤灰的质量为35~55kg;所述黄砂的质量为320~425kg;所述石子的质量为950~1100kg;所述镍渣的质量为320~420kg。
2.根据权利要求1所述的集料掺镍渣的高强混凝土,其特征在于:所述胶凝材料还含有外加剂,所述外加剂为聚羧酸系高性能减水剂。
3.根据权利要求2所述的集料掺镍渣的高强混凝土,其特征在于:所述聚羧酸系高性能减水剂占所述胶凝材料总质量的1.2%~1.5%。