CN103602267A - Texture paint and preparation method thereof - Google Patents
Texture paint and preparation method thereof Download PDFInfo
- Publication number
- CN103602267A CN103602267A CN201310629378.3A CN201310629378A CN103602267A CN 103602267 A CN103602267 A CN 103602267A CN 201310629378 A CN201310629378 A CN 201310629378A CN 103602267 A CN103602267 A CN 103602267A
- Authority
- CN
- China
- Prior art keywords
- texture paint
- cellulose
- emulsion
- texture
- property
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Provided texture paint is aqueous texture paint employing macromolecular synthetic resin emulsion and additives. By employing a strong-thixotropy alkali-swelling type thickener and cellulose ether for cooperative use, the texture paint is reasonable in thixotropy and relatively good in thickening property, storage property and construction property, and has no influence on water whitening resistance of the emulsion. After a high-viscosity auxiliary agent with water-retaining property replaces part of cellulose ether, the texture paint is high in viscosity, good in water-retaining property, no sand falls off during construction, the opening time is long, the scraping and the levelling are facilitated, and the use amount of the paint is substantially reduced. The addition of a thixotropy lubricant helps to improve the lubrication viscosity-reducing property, reduce construction resistance, improve sagging resistance, improve construction performances, prevent knife-adhering phenomenon from generating and prolong construction time.
Description
Technical field
The present invention relates to a kind of coating, especially a kind of texture paint.
Background technology
Decorative paint is of a great variety at present, and the true mineral varnish of artificial granite is rich in the strength of character intension of natural granite, and the noble grade of quite aobvious grouan, be the novel upgrading kind of traditional natural real stone paint, but its effect is not true to nature.Texture coating, with the individual character collocation of its with countless changes three-dimensional texture, more options, represents unique visual angle, space, abundant and lively, makes us fresh and new.Texture coating is radiationless, and from heavy and light, effect is true to nature, and by different construction technologies, gimmick and skill, create infinite special decorative effect.But texture coating is filmed thicker, more strict to the requirement of open hour, when constructing summer, temperature is high, fast drying, the actual open hour are short, are easy to occur lapping defect, and the main thickening material in current texture coating is Natvosol, there is poor water retention property, the open hour are short, cohesiveness is not high shortcoming in currently available products, can cause batch to scrape easily fall sand, dry soon in summer, and unit surface is surged by paint amount, the increase of not only constructional difficulties, and cost is very large.
Summary of the invention
For the problems referred to above, the invention provides a kind of texture paint, adopt the water-based texture coating of speciality polymer synthetic resin emulsion and additive, by different service tools and gimmick, mould the metope effect of various solids, concavo-convex texture.
The present invention is that the technical scheme that technical solution problem adopts is:
A texture paint, its component and quality percentage composition are:
Preferably, Antisepticize and mildew preventive is two or three of ROHM AND HAAS mould inhibitor-363, Kathon LEX sterilant and carbendazim original powder.
Preferably, dispersion agent is sodium polyacrylate dipersant; Film coalescence aid is lauryl alcohol ester; Defoamer is A203E type defoamer.
Preferably, emulsion is AC-261 emulsion and D-68 emulsion.
Preferably, titanium dioxide is R-258 titanium dioxide; Aggregate is one or both in 325 order extra white stone flours and 30-60 order snowflake white sand.
Preferably, ether of cellulose is one or more in Vltra tears, Natvosol, hydroxyethylmethyl-cellulose.
Preferably, also comprise thickening material, wherein thickening material is the thickening material of alkali swelling type.
Preferably, also comprise solubility promoter, wherein solubility promoter is ethylene glycol.
Preferably, in the present invention, the thickening material of alkali swelling type is that liquid thickener TT-615 is or/and ASE-60.
A method of preparing above-mentioned texture paint, comprises the steps:
(1) drop into Antisepticize and mildew preventive, defoamer add water in cylinder after; Startup anchor formula is stirred under 300-500RPM rotating speed and stirs 1-2 minute;
(2) throw in emulsion, start the stirring of anchor formula, helical stir; Start and disperse axle and be adjusted to 500-800RPM;
(3) by order from fine to coarse, at the uniform velocity throw in aggregate, aggregate is thrown in complete, dispersion axle is adjusted to 1000-1500RPM and guarantees slurry high speed dispersion 3-5 minute in cylinder;
(4) film coalescence aid poured into large glue bucket, then slowly poured into ether of cellulose and stir evenly wettingly, then slowly cellulose ether mixture is entered in cylinder and carried out high speed dispersion 10-15 minute until cellulose-less ether particle.
Preferably, after being dispersed to cellulose-less particle, add ammoniacal liquor or 25% sodium hydroxide solution, then liquid thickener TT-615 is watered by the mass ratio of 1:1 by the mass ratio of 1:3 or by ASE-60, stir and slowly drop into liquid thickener after dilution in cylinder, and continuing high speed dispersion 5-10 clock.
Preferably, utilize described ammoniacal liquor or 25% sodium hydroxide solution to regulate pH to 8.0-9.0, utilize thickening material adjusting viscosity to 40000-50000cps/25 ℃, proportion: 1.60-1.70.
The present invention with respect to the beneficial effect of prior art is: select alkali swelling type thickening material and the ether of cellulose that thixotropy is strong to be used in conjunction with, thixotropy is reasonable, and thickening, storage, workability are all better, and does not affect the water-whitening resistance of emulsion.Adopt high viscosity and water-retentivity auxiliary agent to replace after part ether of cellulose, cohesiveness is high, good water-retaining property, so can not fall sand in construction, the open hour are long, is convenient to criticize scrape levelling, has greatly reduced with paint and has measured.Add thixotroping lubricant and can improve lubricated viscosity-reducing performance, reduce construction resistance, improve sag resistance, improve workability, prevent that sticky cutter phenomenon from producing, and extends the engineering time.Texture coating is contained on body of wall through selecting different instruments and construction gimmick to be coated with; formation has the texture texture coating of certain thickness, snappiness and hardness; can bridging crack; make crack not arrive surface layer; than common flat painting or elastic coating, have more cracking resistance advantage, improve the artistic feeling of buildings, extend buildings work-ing life; play decoration, protection and enhancement, and effectively solve site operation quality problems.
Embodiment
Embodiment 1
A texture paint, its component and quality percentage composition are:
AC-261 emulsion and D-68 emulsion: 20%;
325 order extra white stone flours: 60%;
Titanium dioxide: 6%;
Lauryl alcohol ester: 1.5%;
A203E type defoamer: 0.25%;
Sodium polyacrylate dipersant: 0.20%;
ROHM AND HAAS mould inhibitor-363 and Kathon LEX fungicide mixture: 0.8%;
Vltra tears: 0.20%;
Thickening material TT-615:0.60%;
Surplus is water;
Wherein, the mass ratio of AC-261 emulsion and D-68 emulsion is: 2:1; In ROHM AND HAAS mould inhibitor-363 and Kathon LEX fungicide mixture, the mass ratio of two kinds of compositions is 3:2.
A method of preparing above-mentioned texture paint, comprises the steps:
(1) drop into Antisepticize and mildew preventive, defoamer add water in cylinder after; Startup anchor formula is stirred under 300-500RPM rotating speed and stirs 1-2 minute;
(2) throw in emulsion, start the stirring of anchor formula, helical stir; Start and disperse axle and be adjusted to 500-800RPM;
(3) by order from fine to coarse, at the uniform velocity throw in aggregate, aggregate is thrown in complete, dispersion axle is adjusted to 1000-1500RPM and guarantees slurry high speed dispersion 3-5 minute in cylinder;
(4) film coalescence aid poured into large glue bucket, then slowly poured into ether of cellulose and stir evenly wetting, then slowly cellulose ether mixture is entered in cylinder and carried out high speed dispersion 10-15 minute until cellulose-less ether particle, add ammoniacal liquor to regulate pH to 8.0-9.0, then liquid thickener TT-615 is watered by the mass ratio of 1:3, stir and slowly drop into liquid thickener after dilution in cylinder, and continuing high speed dispersion 5-10 clock.
Embodiment 2
A texture paint, its component and quality percentage composition are:
AC-261 emulsion and D-68 emulsion: 15%;
60 order snowflake white sands: 70%;
R-258 titanium dioxide: 5%;
Lauryl alcohol ester: 1.5%;
A203E type defoamer: 0.15%;
Sodium polyacrylate dipersant: 0.20%;
The mixture of ROHM AND HAAS mould inhibitor-363, Kathon LEX sterilant and carbendazim original powder: 0.5%;
Hydroxyethylmethyl-cellulose: 0.15%;
Surplus is water;
Wherein, the mass ratio of AC-261 emulsion and D-68 emulsion is: 1.5:1; In the mixture of ROHM AND HAAS mould inhibitor-363, Kathon LEX sterilant and carbendazim original powder, the mass ratio of three kinds of compositions is: ROHM AND HAAS mould inhibitor-363:Kathon LEX sterilant: carbendazim original powder=4:3:3.
A method of preparing above-mentioned texture paint, comprises the steps:
(1) drop into Antisepticize and mildew preventive, defoamer add water in cylinder after; Startup anchor formula is stirred under 300-500RPM rotating speed and stirs 1-2 minute;
(2) throw in emulsion, start the stirring of anchor formula, helical stir; Start and disperse axle and be adjusted to 500-800RPM;
(3) by order from fine to coarse, at the uniform velocity throw in aggregate, aggregate is thrown in complete, dispersion axle is adjusted to 1000-1500RPM and guarantees slurry high speed dispersion 3-5 minute in cylinder;
(4) film coalescence aid poured into large glue bucket, then slowly poured into ether of cellulose and stir evenly wettingly, then slowly cellulose ether mixture is entered in cylinder and carried out high speed dispersion 10-15 minute until cellulose-less ether particle.Add 25% sodium hydroxide solution to regulate pH to 8.0-9.0, then thickening material ASE-60 is watered by the mass ratio of 1:1, stir and slowly drop into liquid thickener after dilution in cylinder, and continuing high speed dispersion 5-10 clock.
Claims (10)
1. a texture paint, its component and quality percentage composition are:
2. texture paint according to claim 1, is characterized in that, Antisepticize and mildew preventive is two or three of ROHM AND HAAS mould inhibitor-363, Kathon LEX sterilant and carbendazim original powder.
3. texture paint according to claim 1, is characterized in that, dispersion agent is sodium polyacrylate dipersant; Film coalescence aid is lauryl alcohol ester; Defoamer is A203E type defoamer.
4. texture paint according to claim 1, is characterized in that, emulsion is AC-261 emulsion and D-68 emulsion.
5. texture paint according to claim 1, is characterized in that, titanium dioxide is R-258 titanium dioxide; Aggregate is one or both in 325 order extra white stone flours and 30-60 order snowflake white sand.
6. texture paint according to claim 1, is characterized in that, ether of cellulose is one or more in Vltra tears, Natvosol, hydroxyethylmethyl-cellulose.
7. according to the texture paint described in any one in claim 1-6, it is characterized in that, also comprise thickening material, wherein thickening material is the thickening material of alkali swelling type.
8. prepare according to a method for the texture paint described in any one in claim 1-7, comprise the steps:
(1) drop into Antisepticize and mildew preventive, defoamer add water in cylinder after; Startup anchor formula is stirred under 300-500RPM rotating speed and stirs 1-2 minute;
(2) throw in emulsion, start the stirring of anchor formula, helical stir; Start and disperse axle and be adjusted to 500-800RPM;
(3) by order from fine to coarse, at the uniform velocity throw in aggregate, aggregate is thrown in complete, dispersion axle is adjusted to 1000-1500RPM and guarantees slurry high speed dispersion 3-5 minute in cylinder;
(4) film coalescence aid poured into large glue bucket, then slowly poured into ether of cellulose and stir evenly wettingly, then slowly cellulose ether mixture is entered in cylinder and carried out high speed dispersion 10-15 minute until cellulose-less ether particle.
9. method according to claim 8, it is characterized in that, after being dispersed to cellulose-less particle, add ammoniacal liquor or 25% sodium hydroxide solution, then liquid thickener TT-615 is watered by the mass ratio of 1:1 by the mass ratio of 1:3 or by ASE-60, stir and slowly drop into liquid thickener after dilution in cylinder, and continuing high speed dispersion 5-10 clock.
10. method according to claim 9, is characterized in that, utilizes described ammoniacal liquor or 25% sodium hydroxide solution to regulate pH to 8.0-9.0, utilizes thickening material adjusting viscosity to 40000-50000cps/25 ℃, proportion: 1.60-1.70.