CN103601442B - Waterproof slurry with sterilization function for toilet bath room decoration surfaces - Google Patents

Waterproof slurry with sterilization function for toilet bath room decoration surfaces Download PDF

Info

Publication number
CN103601442B
CN103601442B CN201310532446.4A CN201310532446A CN103601442B CN 103601442 B CN103601442 B CN 103601442B CN 201310532446 A CN201310532446 A CN 201310532446A CN 103601442 B CN103601442 B CN 103601442B
Authority
CN
China
Prior art keywords
component
bath
facing
waterproofing slurry
sterilizing function
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310532446.4A
Other languages
Chinese (zh)
Other versions
CN103601442A (en
Inventor
邓德安
董峰亮
方楚燕
吴海明
刘少严
刘建农
阿那
梁至柔
胡程
周碧平
丁天华
吴斌
严昌俊
万德刚
薛静
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Sikadegao Shanghai Building Materials Co Ltd
Original Assignee
Chengdu Parex Davco Building Material Co ltd
Parex Davco Shanghai Construction Materials Co ltd
Davco Guangzhou Building Material Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Chengdu Parex Davco Building Material Co ltd, Parex Davco Shanghai Construction Materials Co ltd, Davco Guangzhou Building Material Co Ltd filed Critical Chengdu Parex Davco Building Material Co ltd
Priority to CN201310532446.4A priority Critical patent/CN103601442B/en
Publication of CN103601442A publication Critical patent/CN103601442A/en
Priority to PCT/CN2014/084133 priority patent/WO2015062332A1/en
Application granted granted Critical
Publication of CN103601442B publication Critical patent/CN103601442B/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

The invention relates to waterproof slurry with a sterilization function for toilet bath room decoration surfaces. The waterproof slurry is composed of A and B double components, the A component comprises white portland cement, quartz sand, cellulose ether, a water reducing agent, slag, titanium dioxide, ferric chloride, calcium ascorbate, attapulgite, sepiolite, diatomite, tourmaline and zinc oxide, the B component comprises acrylic emulsion, a defoaming agent, color paste, a composite antibacterial agent, natural essential oil and water. The waterproof slurry uses cement-class inorganic components as main materials, also has decorative effects and a waterproof function, and can be used as decoration surface layers in a toilet, a bathroom, a rest room, and other long-term watery and moist environment, is good in decorative effect, and is scrub resistant; by adding of the composite antibacterial agent prepared according to the environment characteristics of the toilet, the bathroom and the rest room, growth of bacteria and mold can be effectively inhibited; through the use of a composite deodorizing technology of a combination of minerals and the natural essential oil, undesirable odor of the toilet, the bathroom and the rest room can be controlled.

Description

The waterproofing slurry with sterilizing function of facing between the bath of a kind of lavatory
Technical field
The present invention relates to a kind of water-proof material, particularly the waterproofing slurry with sterilizing function of facing between the bath of a kind of lavatory, belongs to the water-proof material technical field in building trade.
Background technology
Waterproofing slurry is a kind of two-pack water-proof material for buildings waterproof, by powder part and liquid material part by a certain percentage proportioning form.Powder is made up of the cement fine sand of high-quality and the active substance of uniqueness, and liquid material is then formed by high molecular polymer and auxiliary agent fusion, is painted on cement basal plane and reaches waterproof effect after two groups of material mixing.
Waterproofing slurry mainly contains universal waterproofing slurry and the large class of flexible waterproofing slurry two, active ingredient in universal waterproofing slurry can infiltrate pore in base material, tiny crack produce chemical reaction and form the xln intercepting water and pass through, and combines together with ground and play waterproof action; After powder in flexible waterproofing slurry mixes with additive, series of physical chemical reaction occurs, slurry infiltrates the pore of ground, forms firmly permanent bond with ground.Form the tough and tensile elastic water-proof film of one deck after construction, prevent the seepage of water.Universal water-proof material adherence force is strong, can direct paving ceramic tile and painting on waterproof layer, and waterproof layer fastness to rubbing is high.The snappiness that its tool is certain simultaneously, can cover cracklin, resists slight concussion distortion, is mainly used in house decoration and indoor waterproof.As the ground and metope etc. of kitchen, lavatory, balcony, underground garage; Flexible waterproofing slurry has better tensile strength while retaining good water resistance and adherence force, wider crack and concussion distortion can be covered, can be applicable to house decoration waterproof, building roof waterproof etc., more obvious especially for its advantage during mouth of pipe waterproof.
Along with people require more and more higher to the environmental protection of modern house ornamentation, attractive in appearance, personalized etc., people are more prone to some and more emphasize functional, individual character, waterproofing slurry with strong points.
Toilet, bathroom etc. because being in water, moist environment for a long time, easy mould growth, and the generation causing peculiar smell.Wall decoration between existing domestic lavatory bath is liked selecting ceramic tile, and ceramic tile has easily arranges easy cleaning, the long-term feature keeping original facing function.But tile laying technics comparing is complicated, easily produces hollowing, dangerous, and easy retaining forms aqueous stratum at the position of hollowing, thus causes waterproof failure.Moisture prolonged stay, in ceramic tile, causes mouldy smelly in enclosed space environment, and smell is abnormal, affects the quality of the life of people.The position of wall decoration between the bath of external lavatory usually only below 1.5 meters uses ceramic tile, and the position of more than 1.5 meters uses color decorative coating.This decorative paint take organism as main component, construction is simple, there is not hollowing layer, but there is water resistance difference, weather resistance is bad, not scrubbing resistance, easily and basic unit the defect such as to peel, and its organic composition easily becomes bacterium, mould grows " organic food ".
The features such as common waterproofing slurry is a kind of based on inorganic componentss such as cement, adds the water-proof material of a small amount of organics modifications, has construction simple, good endurance, and water resistance is excellent, are commonly used to the waterproof construction between the bath of lavatory now.But common waterproofing slurry only forms one deck waterproof layer, as hidden layer, still need carry out the facings such as ceramic tile on waterproof layer, attractive in appearance, generous decorative effect cannot be provided, use as finish coat separately.
The existing published waterproof paint that can be used for toilet or bathroom, be more for reaching impervious, the effect of waterproof and designing, and fail comprehensively to consider aforesaid wall decoration, tile laying, peculiar smell produce existing for problem; And such waterproof paint is not environmental quality for toilet, bathroom and designs, specific aim is not strong.As patent CN 101891432 B discloses a kind of penetration crystallization type water proofing paint, be made up of silicate cement, quartz sand, filler, ionic calcium cpd, crystalline deposit agent, complexing auxiliary agent, film coalescence aid, complexing agent, water reducer, methylcellulose gum, mainly by growing insoluble crystal in concrete surface pore and crackle, by pore passageway and crackle blocking, thus the object playing waterproofing and leakage-stopping is widely used in the impervious waterproof construction of vault, toilet; Patent CN 1952030B discloses a kind of environment-friendly type high performance polyurethane water-proof paint and production technique, and this product is also applicable to the waterproof in toilet, bathroom, but does not possess facing function.
Some add the waterproof paint of sterilant or sanitas, as patent ZL201110332094.9 discloses a kind of soft polymer cement waterproof mortar, containing sterilant in its formula, there is water resistance and also have sterilization effect simultaneously, but when it is applied to toilet or bathroom, also cannot realize good finishing effect and sterilizing deodoring effect with strong points, and there is the problems such as the inevitable accumulation of salt in the surface soil, aberration for facing in mortar.Patent CN101429401A discloses a kind of high-performance waterproof coating material of cement based polymer, and its formula is also containing sterilant, but its relevant sterilization effect not mentioned, and for the service condition in this kind of wet environment in toilet or bathroom.
Also report is had about the waterproof paint with decorative effect, such as, patent CN 102329112B discloses a kind of colored polymer cement underwater paint be made up of powder and liquid material, powder comprises: inert inorganic powder 1-4 part, pigment 0.001-0.01 part, containing aqueous solution 0.5-1 part of polymer emulsion 10%-20%, cement 1-7 part, dispersion agent 0.002-0.01 part, liquid material comprises: polymer emulsion 0.5-0.9 part, water 0.1-0.5 part, defoamer 0.01-0.003 part, achieves polymer cement waterproof material colorize.Be directly used in the facing mortar of construction wall surface decoration due to its decorative effect uniqueness naturally, various texture can be processed into, the advantages such as ventilative cracking resistance obtain application gradually, make people outside coating, ceramic tile, have another kind of selection, such as, patent CN 102424554 B discloses the two-pack facing mortar that a kind of dry component comprising the additive such as cement, latex powder, dicalcium powder, quartz sand, pigment and thickening material, hydrophober and defoamer composition and the wet component be made up of polymer micro-emulsion and water form.But usually there is the problems such as the accumulation of salt in the surface soil, aberration, cracking or constructional difficulties in facing mortar.Patent CN 1045457C discloses a kind of chromatic waterproofing paint, also be the waterproof that can be used for toilet, but this patent and above-mentioned these two kinds have the waterproof paint of decorative effect, except having facing, water-proof function, also do not possess for biocidal efficacies when toilet, bathroom.
Summary of the invention
The object of the invention is to for above-mentioned deficiency, there is provided a kind of lavatory, bathroom, toilet wall decoration use and there is the waterproofing slurry of sterilizing function, this waterproofing slurry is based on cement class inorganic components, possess decorative effect and water-proof function simultaneously, can separately as finish coat be used for lavatory, bathroom, toilet and other have in the environment of water and humidity for a long time, good decorating effect, scrubbing resistance; Long-acting complex antimicrobials technology is have employed, the growth of the complex antimicrobials prepared by the environmental quality added for lavatory, bathroom, toilet anti-bacteria, mould effectively in this waterproofing slurry formula; The compound taste removal technology adopting mineral substance and natural fragrant essence to combine in formula realizes generation to lavatory, bathroom, peculiar smell in toilet and control.
For solving the problem, the technical solution adopted in the present invention is as follows: the waterproofing slurry with sterilizing function of facing between the bath of a kind of lavatory, is made up of A, B two-component, and in A, B component, the parts by weight of each material are as follows respectively:
Component A:
B component:
Described long-acting complex antimicrobials is that chlormethylisothiazo,ine ketone, methylisothiazolinone, BIT, derosal, octylisothiazolinone and Diuron Tech obtain in 1:1:1:1:1:1 ratio is composite; Described component A, B component are according to component A: the powder liquor ratio of B component=1:0.3 prepares the waterproofing slurry with sterilizing function of facing between the bath of lavatory.
The grade of described white portland cement is 42.5 or 42.5R or 52.5.
Described quartz sand preferable particle size is the quartz sand of 40-200 object oyster white or semi-transparent clear shape.
Described ether of cellulose is any one in hydroxypropyl methyl cellulose ether, methyl cellulose ether, hydroxyethyl ether cellulose, and the viscosity of described ether of cellulose is 500-25000mPas.
Described water reducer is the one of polycarboxylic acid salt's water reducer or melamine high efficiency water reducing agent.
Described slag preferable particle size is 40-200 object slag.
The coating titanium dioxide that the preferred content of titanium dioxide of described titanium dioxide is greater than 90%.
Described iron(ic) chloride selects iron(ic) chloride powder.
The crystalline powder product of described calcium ascorbate preferred white.
Described attapulgite is a kind of clay mineral of moisture zeopan.
Described sepiolite is a kind of fibrous silicate clay mineral of rich magnesium, the sepiolite of preferred white of the present invention.
The siliceous rock of described diatomite to be a kind of with silicon-dioxide be main component, the diatomite that the preferred dioxide-containing silica of the present invention is greater than 80%.
Described tourmalinite is a kind of Silicate Rocks mineral.
Described zinc oxide preferred white hexagonal crystal or powdery product.
Described ACRYLIC EMULSION is preferably the shallow white translucent ACRYLIC EMULSION of following performance index: viscosity (CP25 DEG C), 300-2000, solid content 48-57%, pH value 7-9.
Described defoamer preferred liquid silicone antifoam agent or dimethyl siloxane defoamer.
Described mill base is water-based organic or inorganic dispersible pigment color paste.
Described natural aromatic oil preferably lemon flavour also can be extract the perfume oil essence from natural phant.
Between the bath of lavatory of the present invention, the waterproofing slurry with sterilizing function of facing is prepared according to the following steps: by each composition of formula precise, and hand operated mixing mixing in advance, forms uniform component A powder system and B component liquid material system.By component A: the powder liquor ratio of B component=1:0.3, first B component is put into cement mortar mixer, then add component A, stirring at low speed, stir 5-10 minute, until mix.
When between the bath of lavatory of the present invention, the waterproofing slurry with sterilizing function of facing is for constructing, flow process is as follows:
(1) all basal planes structurally must be firm, dry, clean and without movement, oils, grease, paraffin and other fouling productss; Paint basal plane must expose more than at least 75% clean basal plane;
(2) according to proportioning, powder and liquid material are mixed, by electric blender, waterproofing slurry is stirred well to evenly without caking pulp-like;
(3) waterproofing slurry after stirring is left standstill about 5 minutes, again stir 1-2 minute, can use;
(4) by waterproofing slurry uniform crossover brush, batch scrape or be sprayed at the ground handled well on, note avoiding slurry gather blocked up somewhere or leak brush;
(5) according to the finishing effect that oneself needs, with suitable brush, spatula, notched scraper or other surface roughening tools on waterproofing slurry, many textures sgraffito is carried out;
(6) after waterproofing slurry is constructed 1 day, can use, the concrete time appropriately adjusts depending on weather, execution conditions difference.
The present invention is as follows relative to the beneficial effect of prior art:
(1) formula of the present invention takes into full account cooperation and the consistency of wherein inorganic materials, organic materials, adopt the present invention's obtained waterproofing slurry of filling a prescription to possess good water resistance, meet the JC/T2090-2011 polymer cement waterproof slurry standard of up-to-date release;
(2) waterproofing slurry of the present invention is based on cement class inorganic components, there is polychromy effect and water-proof function simultaneously, this waterproofing slurry can separately as finish coat be used for lavatory, bathroom, toilet and other have the environment of water and humidity, good decorating effect, scrubbing resistance for a long time;
(3) apply long-acting composite antibacterial technology in the present invention and can effectively suppress the growth of bacterium, mould in lavatory, bathroom, toilet: the long-acting complex antimicrobials in formula is formed in 1:1:1:1:1:1 ratio is composite by chlormethylisothiazo,ine ketone, methylisothiazolinone, BIT, derosal, octylisothiazolinone and Diuron Tech, effectively can extend the quality guaranteed period of waterproofing slurry, effectively suppress the growth of bacterium, mould in lavatory, bathroom, toilet; Carry out anti-fungal property mensuration by ASTM G21-96 (2002) synthetic polymeric material mildew-resistant (resistance to fungi) performance test standard, mildew-resistant grade is 0 grade;
(4) the present invention's application compound taste removal technology can effectively suppress the stink from toilet, floor drain in lavatory, bathroom, toilet: between the bath of lavatory, the main component of stink is ammonia and hydrogen sulfide, iron(ic) chloride in formula inhibited oxidation together with calcium ascorbate, reacts with smell substances such as ammonia and makes it to become free from extraneous odour material; Zinc oxide and hydrogen sulfide generation on-catalytic gas-particle two-phase react, and can remove the hydrogen sulfide in air; Use the sorbent material based on attapulgite and sepiolite simultaneously, by adding diatomite, tourmalinite natural mineral matter, there is light current, there is the feature of the obnoxious flavoures such as Preferential adsorption formaldehyde, ammonia, reach the effect of air between the bath of purification lavatory; Use natural aromatic oil lemon flavour as sheltering deodovization agent, the peculiar smell of removal, to the generation of fungi, mould, has natural restraining effect.
Embodiment
Be described in further details the present invention below by embodiment, these embodiments are only used for the present invention is described, do not limit the scope of the invention.
Embodiment 1 is by the waterproofing slurry with sterilizing function of facing between following formula preparation lavatory of the present invention bath:
(1) fill a prescription as shown in the table:
(2) prepare:
By each composition of formula precise, hand operated mixing mixing in advance, forms uniform component A system and B component system.By component A: the powder liquor ratio of B component=1:0.3, first B component is put into cement mortar mixer, then add component A, stirring at low speed, stir 5 minutes, until mix.
Detect the waterproofing slurry that can be used for colored finish of above-mentioned preparation, indices is as shown in the table all meets JC/T2090-2011 polymer cement waterproof slurry standard.
Embodiment 2 is by the waterproofing slurry with sterilizing function of facing between following formula preparation lavatory of the present invention bath:
(1) fill a prescription as shown in the table:
(2) prepare: by each composition of formula precise, hand operated mixing mixing in advance, forms uniform component A system and B component system.By component A: the powder liquor ratio of B component=1:0.3, first B component is put into cement mortar mixer, then add component A, stirring at low speed, stir 10 minutes, until mix.
Embodiment 3 is by the waterproofing slurry with sterilizing function of facing between following formula preparation lavatory of the present invention bath:
(1) fill a prescription as shown in the table:
(2) prepare: by each composition of formula precise, hand operated mixing mixing in advance, forms uniform component A system and B component system.By component A: the powder liquor ratio of B component=1:0.3, first B component is put into cement mortar mixer, then add component A, stirring at low speed, stir 5 minutes, until mix.
Embodiment 4 is by the waterproofing slurry with sterilizing function of facing between following formula preparation lavatory of the present invention bath:
(1) fill a prescription as shown in the table:
(2) prepare: by each composition of formula precise, hand operated mixing mixing in advance, forms uniform component A system and B component system.By component A: the powder liquor ratio of B component=1:0.3, first B component is put into cement mortar mixer, then add component A, stirring at low speed, stir 10 minutes, until mix.
Embodiment 5 is by the waterproofing slurry with sterilizing function of facing between following formula preparation lavatory of the present invention bath:
(1) fill a prescription as shown in the table:
(2) prepare: by each composition of formula precise, hand operated mixing mixing in advance, forms uniform component A system and B component system.By component A: the powder liquor ratio of B component=1:0.3, first B component is put into cement mortar mixer, then add component A, stirring at low speed, stir 5 minutes, until mix.

Claims (9)

1. the waterproofing slurry with sterilizing function of facing between the bath of lavatory, is characterized in that: be made up of A, B two-component, and in A, B component, the parts by weight of each material are as follows respectively:
Component A:
White portland cement 300-700 part
Quartz sand 200-600 part
Ether of cellulose 0.01-5 part
Water reducer 0.5-4 part
Slag 10-200 part
Titanium dioxide 5-50 part
Iron(ic) chloride 1-50 part
Calcium ascorbate 1-50 part
Attapulgite 1-100 part
Sepiolite 1-100 part
Diatomite 1-50 part
Tourmalinite 1-50 part
Zinc oxide 1-50 part,
B component:
ACRYLIC EMULSION 100-600 part
Defoamer 0.5-10 part
Mill base 1-30 part
Long-acting complex antimicrobials 0.5-10 part
Natural aromatic oil 1-10 part
Water 100-500 part,
Described long-acting complex antimicrobials is that chlormethylisothiazo,ine ketone, methylisothiazolinone, BIT, derosal, octylisothiazolinone and Diuron Tech obtain in 1:1:1:1:1:1 ratio is composite; Described component A, B component are according to component A: the powder liquor ratio of B component=1:0.3 prepares the waterproofing slurry with sterilizing function of facing between the bath of lavatory.
2. the waterproofing slurry with sterilizing function of facing between the bath of lavatory according to claim 1, is characterized in that: described natural aromatic oil is for extracting the mixture of one or more essence in the perfume oil essence of natural phant.
3. the waterproofing slurry with sterilizing function of facing between the bath of lavatory according to claim 1, is characterized in that: described slag particle diameter is 40-200 order.
4. the waterproofing slurry with sterilizing function of facing between the bath of lavatory according to claim 1, is characterized in that: described titanium dioxide is the coating titanium dioxide that content of titanium dioxide is greater than 90%.
5. the waterproofing slurry with sterilizing function of facing between the bath of lavatory according to claim 1, is characterized in that: the grade of described white portland cement is 42.5 or 42.5R or 52.5.
6. the waterproofing slurry with sterilizing function of facing between the bath of lavatory according to claim 1, is characterized in that: described quartz sand is the quartz sand of 40-200 object oyster white or semi-transparent clear shape.
7. the waterproofing slurry with sterilizing function of facing between the bath of lavatory according to claim 1, it is characterized in that: described ether of cellulose is any one in hydroxypropyl methyl cellulose ether, methyl cellulose ether, hydroxyethyl ether cellulose, the viscosity of described ether of cellulose is 500-25000mPas.
8. the waterproofing slurry with sterilizing function of facing between the bath of lavatory according to claim 1, it is characterized in that: described ACRYLIC EMULSION is the shallow white translucent ACRYLIC EMULSION of following performance index: viscosity (CP25 DEG C) 300-2000, solid content 48-57%, pH value 7-9.
9. the waterproofing slurry with sterilizing function of facing between the bath of lavatory according to claim 1, is characterized in that: described defoamer is liquid silicone defoamer or dimethyl siloxane defoamer.
CN201310532446.4A 2013-10-31 2013-10-31 Waterproof slurry with sterilization function for toilet bath room decoration surfaces Active CN103601442B (en)