CN103590192B - 分散蓝2bln/聚丙烯腈基有色纳米纤维膜制备方法 - Google Patents

分散蓝2bln/聚丙烯腈基有色纳米纤维膜制备方法 Download PDF

Info

Publication number
CN103590192B
CN103590192B CN201310483552.8A CN201310483552A CN103590192B CN 103590192 B CN103590192 B CN 103590192B CN 201310483552 A CN201310483552 A CN 201310483552A CN 103590192 B CN103590192 B CN 103590192B
Authority
CN
China
Prior art keywords
polyacrylonitrile
electrostatic spinning
blue
coloured
disperse blue
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310483552.8A
Other languages
English (en)
Other versions
CN103590192A (zh
Inventor
胡毅
张声诚
丁云法
陈文祥
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Wanfang weaving & Dyeing Co. Ltd
Original Assignee
Zhejiang Sanzhi Textile Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Zhejiang Sanzhi Textile Co Ltd filed Critical Zhejiang Sanzhi Textile Co Ltd
Priority to CN201310483552.8A priority Critical patent/CN103590192B/zh
Publication of CN103590192A publication Critical patent/CN103590192A/zh
Application granted granted Critical
Publication of CN103590192B publication Critical patent/CN103590192B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种分散蓝2BLN/聚丙烯腈基有色纳米纤维膜制备方法，依次包括a)蓝色静电纺丝溶液制备：称取一定质量比的聚丙烯腈（PAN）、分散蓝2BLN染料，混合溶于N-N二甲基甲酰胺（DMF），搅拌后得到分散均匀的蓝色静电纺丝溶液；b)静电纺丝：设定喷丝头与接收板距离为11～19cm，调整蓝色静电纺丝溶液的流速为0.3～1.1ml/h，喷丝头直径为0.3～0.55mm，稳定挤出时，施加9～17KV的高压静电进行静电纺丝；c)铝箔纸接收：通过铝箔纸接收板接收喷丝头上挤出的丝，得到蓝色纳米纤维膜等步骤。本发明制备方法简单，制备出的有色纳米纤维膜色泽匀染性较好，制备过程中无水介质，无污染，无染废料产生，耗能低，对环境污染小。

Description

分散蓝2BLN/聚丙烯腈基有色纳米纤维膜制备方法
【技术领域】
本发明涉及原液着色和静电纺丝法相结合制备分散蓝2BLN/聚丙烯腈基有色纳米纤维膜，属于功能性纳米纤维的制备技术领域。
【背景技术】
静电纺丝技术是基于高压电场下导电流体产生高速喷射原理，在毛细喷丝头和接地极间瞬时产生一个电位差，使毛细管内溶液或者熔融体克服自身的表面张力和粘弹性力，在喷丝头末端呈现半球状液滴。随着电场强度增加，液滴被拉成圆锥状即Taylor锥。当电场强度超过某一临界值后，将克服液滴表面张力形成射流，在电场中进一步加速，直径减小，拉伸成一直线至一定距离后弯曲，进行循环或者循螺旋形路径行走，伴随溶剂挥发或熔融体冷却固化，终落在收集板上形成纤维。
通过静电纺丝可将天然或化学聚合物纺制出微米至纳米级各类纤维，是一独特的纳米纤维制备方法，工序简单、设备廉价、广泛运用于光电子器件、传感器技术、催化、过滤以及医学等领域，如：静电纺材料能很好模拟细胞外基质(ECM)结构，提供潜在的组织工程支架。
原液着色是指在聚合加工过程中或过程后，在纺丝前加入着色剂制得有色纤维的生产方法。经过九十多年的发展，原液染色技术目前在欧美和日本已广泛用于合成纤维。其中已工业化生产的原液染色纤维包括：聚酰胺、聚酯、聚丙烯、聚乙烯、聚丙烯腈等。原液染色效果优越、工艺简单、污染小、节约能源，尤其适用于按标准色号进行大规模生产的织物，它在一切需要高度染色均匀度和坚牢度的应用领域中占据稳固地位，具有广阔的发展前景。
本发明将静电纺丝技术和原液着色技术相结合制备有色纳米纤维膜，制备方法简单，得到的蓝色纳米纤维膜匀染性好，制备过程中无水介质，无污染，无染废料产生，耗能低，对环境污染小，属于一种环境友好型制备有色纳米纤维的方法。
【发明内容】
本发明的目的就是解决现有技术中的问题，提出一种分散蓝2BLN/聚丙烯腈基有色纳米纤维膜制备方法，能够制备方法简单，得到的蓝色纳米纤维膜匀染性好，制备过程中无水介质，无污染，无染废料产生，耗能低，对环境污染小。
为实现上述目的，本发明提出了分散蓝2BLN/聚丙烯腈基有色纳米纤维膜制备方法，依次包括以下步骤：
a)蓝色静电纺丝溶液制备：称取一定质量比的聚丙烯腈(PAN)、分散蓝2BLN染料置于20ml的样品瓶中，聚丙烯腈(PAN)的浓度为6～10wt％，分散蓝2BLN染料与聚丙烯腈(PAN)的质量比例为1：10～30，利用移液管移取15ml的N-N二甲基甲酰胺(DMF)，样品瓶用生料带密封，加热到60℃搅拌24小时，搅拌后得到分散均匀的蓝色静电纺丝溶液；
b)静电纺丝：设定喷丝头与接收板距离为11～19cm，调整蓝色静电纺丝溶液的流速为0.3～1.1ml/h，喷丝头直径为0.3～0.55mm，稳定挤出时，施加9～17KV的高压静电进行静电纺丝；
c)铝箔纸接收：通过铝箔纸接收板接收喷丝头上挤出的丝，得到蓝色纳米纤维膜。
作为优选，所述a)步骤中的聚丙烯腈(PAN)的分子量Mw＝130000～170000g/mol；聚丙烯腈(PAN)的链状结构为：
作为优选，所述a)步骤中的分散蓝2BLN染料的结构式为：
本发明的有益效果：
(1)本发明制备方法简单，制备出的有色纳米纤维膜色泽匀染性较好；
(2)静电纺丝和原液着色相结合制备有色纳米纤维膜，属于一种环境友好型制备有色纳米纤维的方法，制备过程中无水介质，无污染，无染废料产生，耗能低，对环境污染小。
【具体实施方式】
以下通过具体实施例来进一步说明本发明，但实施例仅用于说明，并不能限制本发明的范围。此外应了解，在阅读本发明讲述内容后，本领域技术人员课对本发明做各种改动或修改，这些等价形式同样落于本申请所附权利要求书所先限定要求。
实施例1：
分散蓝2BLN/聚丙烯腈基有色纳米纤维膜制备方法，依次包括以下步骤：
(1)用电子天平称取一定量分散蓝2BLN和PAN粉末(其中分散蓝2BLN、PAN质量比为1:10，且PAN质量分数为8％)置于20ml的样品瓶中，利用移液管移取15ml的N-N二甲基甲酰胺(DMF)，样品瓶用生料带密封，加热到60℃搅拌24小时，最终制得PAN分散比较均匀的溶液。
(2)裁出面积为40cm×40cm的锡箔纸紧贴于平板收集器上，取5ml纺丝溶液样品放入注射针管中，将高压发生器正极与喷丝口相连，负极与平板接收器相连，调节注射泵溶液流速0.7ml/h，设定喷丝头与接收板距离15cm，喷丝头直径0.43mm，待其稳定挤出时开启高压发生器至设定电压15KV。
(3)通过铝箔纸接收板得到分散蓝2BLN/聚丙烯腈基有色纳米纤维膜。
该制备方法简单，制备出的有色纳米纤维膜色泽匀染性较好，静电纺丝和原液着色相结合制备有色纳米纤维膜，属于一种环境友好型制备有色纳米纤维的方法，制备过程中无水介质，无污染，无染废料产生，耗能低，对环境污染小。
上面以举例方式对本发明进行了说明，但本发明不限于上述具体实施例，凡基于本发明所做的任何改动或变型均属于本发明要求保护的范围。

Claims (3)

1.分散蓝2BLN/聚丙烯腈基有色纳米纤维膜制备方法，其特征在于：依次包括以下步骤：
a)蓝色静电纺丝溶液制备：称取一定质量比的聚丙烯腈(PAN)、分散蓝2BLN染料置于20ml的样品瓶中，聚丙烯腈(PAN)的浓度为6～10wt％，分散蓝2BLN染料与聚丙烯腈(PAN)的质量比例为1：10～30，利用移液管移取15ml的N-N二甲基甲酰胺(DMF)，样品瓶用生料带密封，加热到60℃搅拌24小时，搅拌后得到分散均匀的蓝色静电纺丝溶液；
b)静电纺丝：设定喷丝头与接收板距离为11～19cm，调整蓝色静电纺丝溶液的流速为0.3～1.1ml/h，喷丝头直径为0.3～0.55mm，稳定挤出时，施加9～17KV的高压静电进行静电纺丝；
c)铝箔纸接收：通过铝箔纸接收板接收喷丝头上挤出的丝，得到蓝色纳米纤维膜。
2.如权利要求1所述的分散蓝2BLN/聚丙烯腈基有色纳米纤维膜制备方法，其特征在于：所述a)步骤中的聚丙烯腈(PAN)的分子量Mw＝130000～170000g/mol；聚丙烯腈(PAN)的链状结构为：
3.如权利要求1所述的分散蓝2BLN/聚丙烯腈基有色纳米纤维膜制备方法，其特征在于：所述a)步骤中的分散蓝2BLN染料的结构式为：
CN201310483552.8A 2013-10-15 2013-10-15 分散蓝2bln/聚丙烯腈基有色纳米纤维膜制备方法 Active CN103590192B (zh)