CN103571107A - 一种高抗冲树脂抑菌薄膜及其制备方法 - Google Patents
一种高抗冲树脂抑菌薄膜及其制备方法 Download PDFInfo
- Publication number
- CN103571107A CN103571107A CN201310548790.2A CN201310548790A CN103571107A CN 103571107 A CN103571107 A CN 103571107A CN 201310548790 A CN201310548790 A CN 201310548790A CN 103571107 A CN103571107 A CN 103571107A
- Authority
- CN
- China
- Prior art keywords
- resin
- parts
- thermo
- toughner
- stabilizer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明涉及一种高抗冲树脂抑菌薄膜及其制备方法,包括:聚氯乙烯、聚酰胺树脂,增韧剂、抗氧化剂、填充剂、热稳定剂、紫外线吸收剂,其中各组分按重量配比为:聚氯乙烯30-50份、聚酰胺树脂15-25份,增韧剂5-15份、抗氧化剂1-5份、抑菌复合物5-10份、热稳定剂1-5份、紫外线吸收剂10-15份;本发明强度好、使用寿命长,可广泛应用于建筑、运输等行业。
Description
技术领域
本发明涉及一种共聚树脂,特别涉及一种高抗冲树脂抑菌薄膜及其制备方法。
背景技术
目前,塑料已经被广泛的应用于工业、农业生产的各个领域。塑料因为其优良的可塑性和易加工性能,在很多领域代替了钢材、木材以及石材等。但是强度低、抗冲击力差是塑料的一个致命的弱点。塑料生产后在搬运、安装、使用的过程中很容易受到碰撞和冲击,造成制品外观损坏,甚至严重影响正常使用;特别是一些搬运、装卸设备、工具上使用的塑料,高强度和好的抗冲击力更是安全的保证。为了使塑料具有高抗冲击力,现有技术在韧性上进行研究,人们开发了橡胶改性的塑料,通过将橡胶加入塑料基材中,可生产出具有不同性能的各种品级的高抗冲击塑料。这种塑料的强度有了明显的提高,但是,这种塑料在耐热性、氧渗透性、抗老化等方面的性能有一定的不足,致使这种塑料制品的高抗冲性能不能持久,使用寿命短。
发明内容
本发明要解决的技术问题是提供一种强度好、使用寿命长的高抗冲树脂抑菌薄膜及其制备方法。
为解决上述技术问题,本发明的高抗冲树脂抑菌薄膜,包括:聚氯乙烯、聚酰胺树脂,增韧剂、抗氧化剂、填充剂、热稳定剂、紫外线吸收剂,其中各组分按重量配比为:聚氯乙烯30-50份、聚酰胺树脂15-25份,增韧剂5-15份、抗氧化剂1-5份、填充剂5-10份、热稳定剂1-5份、紫外线吸收剂10-15份;
所述增韧剂为苯乙烯-丁二烯热塑性弹性体(SBS)和氯化聚乙烯弹性体(CM)的混合物,两者的重量份数比为2:1;
所述热稳定剂为硬脂酸锌、硬脂酸钙、硬脂酸钡或硬脂酸铬中的至少一种;
所述抗氧剂为苯二胺、双酚、多酚、对苯二酚中的至少一种;
所述填充剂为纳米碳酸钙或者纳米二氧化硅,可以用来增加树脂的整体密度,从而提高强度;
所述紫外线吸收剂为2-羟基-4-正辛氧基二苯甲酮、2-(2'-羟基 -3'-叔丁基-5'-甲基苯基)-5-氯代苯并***中的至少一种;
进一步改进,所述树脂包括:聚氯乙烯15-25份、聚酰胺树脂30-50份,增韧剂5-15份、抗氧化剂1-5份、抑菌复合物5-10份、热稳定剂1-5份、紫外线吸收剂10-15份;
进一步改进,所述树脂包括:聚氯乙烯15-25份、聚酰胺树脂30-50份,增韧剂10-20份、抗氧化剂1-5份、抑菌复合物15-20份、热稳定剂1-5份、紫外线吸收剂5-10份;
进一步改进,所述树脂还包括2-5份的分散剂。
本发明还提供了一种高抗冲树脂抑菌薄膜的制备方法,其步骤为:
称重,将各成分按照比例称量好;
搅拌,把上述聚氯乙烯、聚酰胺树脂放入真空搅拌机中,在50℃-80℃下真空搅拌10-30分钟;加入增韧剂、抗氧化剂、填充剂、热稳定剂、紫外线吸收剂,在50℃-80℃下真空搅拌10-30分钟;
混合,将上述混合好的各成分在双辊开炼机上熔融混合,温度为120-160℃;
成型,在开炼机上反复混合均匀后,将混合好的成分输送入挤出造粒机,经过造粒成型备用。
有益效果:本发明聚氯乙烯、聚酰胺、增韧剂、填充剂共混改性,大大提高了树脂的机械性能,使之具有高抗冲击的力学性能;热稳定剂、紫外线吸收剂合理的组份搭配,使树脂的氧渗透性、抗老化性能优良,延长了使用寿命。具有杀菌效果的薄膜材料、绿色环保并且具有抑菌效果;对人、畜无害。另外,本发明配方合理,制备方法简单。
具体实施方式
下面结合具体实施方式对本发明作进一步详细的描述:
实施例1、
一种高抗冲树脂抑菌薄膜,包括:聚氯乙烯、聚酰胺树脂,增韧剂、抗氧化剂、填充剂、热稳定剂、紫外线吸收剂,其特征在于:其中各组分按重量配比为:聚氯乙烯30 份、聚酰胺树脂15 份,增韧剂5 份、抗氧化剂1 份、热稳定剂1 份、紫外线吸收剂10 份、抑菌复合物 20 份;
所述的抑菌复合物的制备方法为:
将啤酒花、飞机草、五爪金龙、百里香、高良姜、大蒜、艾叶、水按照15-20:10-15:10-15 :12-15:8-10:8-10: 5-7:15-20的质量份数配比混合,加入(8份的活力单位为100U)的纤维素酶进行酶解,酶解反应温度为25℃,酶解反应时间为1小时,过滤得到中草药液;去渣后再加入浓度为70%的乙醇水溶液,再将固液混合物超声波辅助提取,超声波提取条件:超声温度为50℃、超声频率为30kHz、超声提取时间为2个小时,然后将固液混合物在35kPa真空条件下抽滤,取滤液在30kPa真空、55℃条件下减压蒸馏得植物源抑菌物。
所述增韧剂为苯乙烯-丁二烯热塑性弹性体(SBS)和氯化聚乙烯弹性体(CM)的混合物,两者的重量份数比为2:1;
所述热稳定剂为硬脂酸锌、硬脂酸钙、硬脂酸钡或硬脂酸铬中的至少一种;
所述抗氧剂为苯二胺、双酚、多酚、对苯二酚中的至少一种;
所述填充剂为纳米碳酸钙或者纳米二氧化硅,可以用来增加树脂的整体密度,从而提高强度;
所述紫外线吸收剂为2-羟基-4-正辛氧基二苯甲酮、2-(2'-羟基 -3'-叔丁基-5'-甲基苯基)-5-氯代苯并***中的至少一种;
一种高抗冲树脂抑菌薄膜的制备方法,其步骤为:
称重,将各成分按照比例称量好;
搅拌,把上述聚氯乙烯、聚酰胺树脂放入真空搅拌机中,在50℃-80℃下真空搅拌10-30分钟;加入增韧剂、抗氧化剂、抑菌复合物、热稳定剂、紫外线吸收剂,在50℃-80℃下真空搅拌10-30分钟;
将上述混合好的各成分在双辊开炼机上熔融混合,温度为150℃; 成型,采用塑料吹膜机挤出吹膜,即得产品;所述的吹膜机料筒后段温度分四段控制,分别控制在150℃,料筒前段温度分四段控制,分别控制在200℃,机头温度分两段控制,分别控制在210℃,吹胀比为3.0,螺杆转速20~40r/min,牵引速度10~50m/min。
实施例2、一种高抗冲树脂抑菌薄膜,包括:聚氯乙烯、聚酰胺树脂,增韧剂、抗氧化剂、填充剂、热稳定剂、紫外线吸收剂,其特征在于:其中各组分按重量配比为:聚氯乙烯 50份、聚酰胺树脂 25份,增韧剂 15份、抗氧化剂 5份、热稳定剂 5份、紫外线吸收剂 15份、抑菌复合物 25份;
所述的抑菌复合物的制备方法为:
将啤酒花、飞机草、五爪金龙、百里香、高良姜、大蒜、艾叶、水按照15-20:10-15:10-15 :12-15:8-10:8-10: 5-7:15-20的质量份数配比混合,加入(8份的活力单位为100U)的纤维素酶进行酶解,酶解反应温度为25℃,酶解反应时间为1小时,过滤得到中草药液;去渣后再加入浓度为70%的乙醇水溶液,再将固液混合物超声波辅助提取,超声波提取条件:超声温度为50℃、超声频率为30kHz、超声提取时间为2个小时,然后将固液混合物在35kPa真空条件下抽滤,取滤液在30kPa真空、55℃条件下减压蒸馏得植物源抑菌物。
所述增韧剂为苯乙烯-丁二烯热塑性弹性体(SBS)和氯化聚乙烯弹性体(CM)的混合物,两者的重量份数比为2:1;
所述热稳定剂为硬脂酸锌、硬脂酸钙、硬脂酸钡或硬脂酸铬中的至少一种;
所述抗氧剂为苯二胺、双酚、多酚、对苯二酚中的至少一种;
所述填充剂为纳米碳酸钙或者纳米二氧化硅,可以用来增加树脂的整体密度,从而提高强度;
所述紫外线吸收剂为2-羟基-4-正辛氧基二苯甲酮、2-(2'-羟基 -3'-叔丁基-5'-甲基苯基)-5-氯代苯并***中的至少一种;
一种高抗冲树脂抑菌薄膜的制备方法,其步骤为:
称重,将各成分按照比例称量好;
搅拌,把上述聚氯乙烯、聚酰胺树脂放入真空搅拌机中,在50℃-80℃下真空搅拌10-30分钟;加入增韧剂、抗氧化剂、抑菌复合物、热稳定剂、紫外线吸收剂,在50℃-80℃下真空搅拌10-30分钟;
将上述混合好的各成分在双辊开炼机上熔融混合,温度为150℃; 成型,采用塑料吹膜机挤出吹膜,即得产品;所述的吹膜机料筒后段温度分四段控制,分别控制在150℃,料筒前段温度分四段控制,分别控制在200℃,机头温度分两段控制,分别控制在210℃,吹胀比为3.0,螺杆转速20~40r/min,牵引速度10~50m/min。
以上显示和描述了本发明的基本原理和主要特征和本发明的优点。本行业的技术人员应该了解,本发明不受上述实施例的限制,上述实施例和说明书中描述的只是说明本发明的原理,在不脱离本发明精神和范围的前提下,本发明还会有各种变化和改进,这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。
Claims (7)
1.一种高抗冲树脂抑菌薄膜,包括:聚氯乙烯、聚酰胺树脂,增韧剂、抗氧化剂、填充剂、热稳定剂、紫外线吸收剂,其特征在于:其中各组分按重量配比为:聚氯乙烯30-50份、聚酰胺树脂15-25份,增韧剂5-15份、抗氧化剂1-5份、热稳定剂1-5份、紫外线吸收剂10-15份、抑菌复合物 20-25份;
所述的抑菌复合物的制备方法为:
将啤酒花、飞机草、五爪金龙、百里香、高良姜、大蒜、艾叶、水按照15-20:10-15:10-15 :12-15:8-10:8-10: 5-7:15-20的质量份数配比混合,加入(8份的活力单位为100U)的纤维素酶进行酶解,酶解反应温度为25℃,酶解反应时间为1小时,过滤得到中草药液;去渣后再加入浓度为70%的乙醇水溶液,再将固液混合物超声波辅助提取,超声波提取条件:超声温度为50℃、超声频率为30kHz、超声提取时间为2个小时,然后将固液混合物在35kPa真空条件下抽滤,取滤液在30kPa真空、55℃条件下减压蒸馏得植物源抑菌物。
2.根据权利要求1所述的高抗冲树脂抑菌薄膜,其特征在于:所述增韧剂为苯乙烯-丁二烯热塑性弹性体(SBS)和氯化聚乙烯弹性体(CM)的混合物,两者的重量份数比为2:1。
3.根据权利要求2所述的高抗冲树脂抑菌薄膜,其特征在于:所述热稳定剂为硬脂酸锌、硬脂酸钙、硬脂酸钡或硬脂酸铬中的至少一种。
4.根据权利要求3所述的高抗冲树脂抑菌薄膜,其特征在于:所述抗氧剂为苯二胺、双酚、多酚、对苯二酚中的至少一种。
5.根据权利要求5所述的高抗冲树脂抑菌薄膜,其特征在于:所述紫外线吸收剂为2-羟基-4-正辛氧基二苯甲酮、2-(2'-羟基-3'-叔丁基-5'-甲基苯基)-5-氯代苯并***中的至少一种。
6.根据权利要求6所述的高抗冲树脂抑菌薄膜,其特征在于:所述树脂还包括2-5份的分散剂。
7.根据权利要求1所述的一种制备高抗冲树脂抑菌薄膜的方法,其特征在于:一种高抗冲树脂抑菌薄膜的制备方法,其步骤为:
称重,将各成分按照比例称量好;
搅拌,把上述聚氯乙烯、聚酰胺树脂放入真空搅拌机中,在50℃-80℃下真空搅拌10-30分钟;加入增韧剂、抗氧化剂、抑菌复合物、热稳定剂、紫外线吸收剂,在50℃-80℃下真空搅拌10-30分钟;
将上述混合好的各成分在双辊开炼机上熔融混合,温度为150℃; 成型,采用塑料吹膜机挤出吹膜,即得产品;所述的吹膜机料筒后段温度分四段控制,分别控制在150℃,料筒前段温度分四段控制,分别控制在200℃,机头温度分两段控制,分别控制在210℃,吹胀比为3.0,螺杆转速20~40r/min,牵引速度10~50m/min。