CN103570322A - 一种掺高量矿粉的水下桩砼 - Google Patents
一种掺高量矿粉的水下桩砼 Download PDFInfo
- Publication number
- CN103570322A CN103570322A CN201310560016.3A CN201310560016A CN103570322A CN 103570322 A CN103570322 A CN 103570322A CN 201310560016 A CN201310560016 A CN 201310560016A CN 103570322 A CN103570322 A CN 103570322A
- Authority
- CN
- China
- Prior art keywords
- kilograms
- concrete
- water
- cement
- mineral powder
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
本发明公开一种掺高量矿粉的水下桩砼,包括水泥、砂、碎石、水、粉煤灰、矿粉、减水剂,各组按重量配比为,水泥240~268千克∶砂663~695千克∶碎石1080~1090千克∶水179~190千克∶粉煤灰60~61千克∶矿粉75~83千克∶减水剂7.1~7.9千克。掺加高量矿粉,取代水泥,减少水泥用量,在坍落度、抗压强度具有明显的提高。同时大掺量矿粉的混凝土可以有效降低水化热,可以减少混凝土收缩,对减少混凝土裂缝非常有利。
Description
技术领域
本发明涉及一种建筑材料,特别涉及一种掺高量矿粉的水下桩砼。
背景技术
随着城市基础建设,工业民用建设的大力发展。混凝土,特别是商品混凝土的需求量也越来越大。中国是混凝土生产第一大国,而作为混凝土中的最主要材料--水泥。中国也是水泥生产第一大国,水泥生产是一种严重污染环境的工业,在生产过程中要排出大量粉尘和有害气体,是室温气体CO2排放源之一。作为一种技术或者产品,节约资源、能源,减少环境污染也是为了自身能够存在和持续发展。C30、C35水下桩砼是一种商品混凝土,传统主要由水泥、水、砂、碎石按一定的配合比构成。如要随便减少水泥用量或增加水、砂、碎石就会造成坍落度、抗压强度不达标。
发明内容
针对上述现有技术的不足,本发明提供一种掺高量矿粉的水下桩砼,具有减少水泥用量,不会造成坍落度、抗压强度不达标的特点。
为了实现上述目的,本发明一种掺高量矿粉的水下桩砼采用如下技术方案:(1)掺加高效减水剂,减少用水量,减少水泥用量;(2)掺加磨细掺和料,取代水泥,减少水泥用量;(3)按最佳的原料配合比构成水下桩砼。
混凝土掺加的磨细掺和料主要有(1)粉煤灰;(2)粒化高炉矿渣粉(以下简称矿粉);(3)硅粉;(4)沸石粉。应用技术比较成熟的有粉煤灰和矿粉。
粉煤灰:粉煤灰是由火力发电厂煤粉炉排出的烟气中收集到的灰白色颗粒粉末,表面光滑呈球型,主要以玻璃体状态存在。粉煤灰的活性,主要取决于玻璃体的含量,以及无定形的氧化铝和氧化硅的含量,而粉煤灰的细度、需水量比也是影响活性的两个主要物理因素。
粒化高炉矿渣是铁矿石在冶炼过程中与石灰石等溶剂化合所得以硅酸钙与铝硅酸钙为主要成分的熔融物,经急速与水淬冷后形成的玻璃状颗粒物质。其主要化学成分是CaO、SiO2、Al2O3,三者的总量一般占90%以上。经加工后成矿粉,其活性较高,是混凝土生产中常用的掺和料。
掺高量矿粉的水下桩砼,包括水泥、砂、碎石、水、粉煤灰、矿粉、减水剂,各组按重量配比为,水泥240~268千克∶砂663~695千克∶碎石1080~1090千克∶水179~190千克∶粉煤灰60~61千克∶矿粉75~83千克∶减水剂7.1~7.9千克。
作为优选,各组按重量配比为,水泥242千克∶砂693千克∶碎石1083千克∶水189千克∶粉煤灰60千克∶矿粉76千克∶减水剂7.2千克。
作为优选,各组按重量配比为为,水泥266千克∶砂666千克∶碎石1087千克∶水180千克∶粉煤灰61千克∶矿粉82千克∶减水剂7.8千克。
上述配比原料中,采用P.O42.5级水泥,II级粉煤灰,S95磨细矿粉,高效泵送减水剂(减水率19%),天然中砂细度模数2.6,碎石5~31.5mm。
本发明一种掺高量矿粉的水下桩砼有益效果:根据以上原材料与配比与传统的C30、C35水下桩砼配比进行比较,见下表:
C30桩砼: 单位:千克
水泥 | 砂 | 碎石 | 水 | 粉煤灰 | 矿粉 | 减水剂 | |
原有配比 | 333 | 710 | 1021 | 205 | 59 | -- | 7.1 |
现有配比 | 242 | 693 | 1083 | 189 | 60 | 76 | 7.2 |
C35桩砼: 单位:千克
水泥 | 砂 | 碎石 | 水 | 粉煤灰 | 矿粉 | 减水剂 | |
原有配比 | 375 | 643 | 1050 | 200 | 65 | -- | 8.3 |
现有配比 | 266 | 666 | 1087 | 180 | 61 | 82 | 7.8 |
其性能指标如下:
上表结果明显的减少了水泥用量,在坍落度、抗压强度具有明显的提高。同时大掺量矿粉的混凝土可以有效降低水化热,可以减少混凝土收缩,对减少混凝土裂缝非常有利。
具体实施方式:
下面结合实例C30、C35水下桩砼,对一种掺高量矿粉的水下桩砼作进一步详细说明。
1、选用湖州南方P.O42.5级水泥,其物理性能见下表。
2、选用长兴电厂II级粉煤灰,细度经0.045mm筛余17.0%,需水比101%。
3、选用无锡金希达S95磨细矿粉,细度经0.045mm筛余1.5%,比表面积410m2/kg,28天活性指数比100%。
4、选用德清五龙III型高效泵送减水剂(减水率19%)。
5、黄砂用天然中砂,细度模数2.6,含泥量小于1.0%。石子用湖州新纪元5~31.5mm连续级配碎石,压碎指标7%,含泥量小于1.0%。
C30水下桩砼:用以上原料,按重量经计量后配比,水泥242千克∶砂693千克∶碎石1083千克∶水189千克∶粉煤灰60千克∶矿粉76千克∶减水剂7.2千克。配比好后先将减水剂放入水中混合,再将全部原料送到制强搅拌机内搅拌40秒,然后放入搅拌车内供使用。
C35水下桩砼:用以上原料,按重量经计量后配比,水泥266千克∶砂666千克∶碎石1087千克∶水180千克∶粉煤灰61千克∶矿粉82千克∶减水剂7.8千克,配比好后先将减水剂放入水中混合,再将全部原料送到制强搅拌机内搅拌40秒,然后放入搅拌车内供使用。
Claims (3)
1.一种掺高量矿粉的水下桩砼,包括水泥、砂、碎石、水、粉煤灰、矿粉、减水剂,其特征在于:各组按重量配比为,水泥240~268千克∶砂663~695千克∶碎石1080~1090千克∶水179~190千克∶粉煤灰60~61千克∶矿粉75~83千克∶减水剂7.1~7.9千克。
2.根据权利要求1所述的一种掺高量矿粉的水下桩砼,其特征在于:各组按重量配比为,水泥242千克∶砂693千克∶碎石1083千克∶水189千克∶粉煤灰60千克∶矿粉76千克∶减水剂7.2千克。
3.根据权利要求1所述的一种掺高量矿粉的水下桩砼,其特征在于:各组按重量配比为,水泥266千克∶砂666千克∶碎石1087千克∶水180千克∶粉煤灰61千克∶矿粉82千克∶减水剂7.8千克。