CN103566896A - Bentonite-based copolymerized compound adsorbent and preparation method thereof - Google Patents
Bentonite-based copolymerized compound adsorbent and preparation method thereof Download PDFInfo
- Publication number
- CN103566896A CN103566896A CN201310442165.XA CN201310442165A CN103566896A CN 103566896 A CN103566896 A CN 103566896A CN 201310442165 A CN201310442165 A CN 201310442165A CN 103566896 A CN103566896 A CN 103566896A
- Authority
- CN
- China
- Prior art keywords
- bentonite
- parts
- based copolymerized
- copolymerized compound
- water
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bentonite-based copolymerized compound adsorbent. The bentonite-based copolymerized compound adsorbent is characterized by being prepared from the following raw materials in parts by weight: 120-130 parts of bentonite, 7-9 parts of crylic acid, 8-10 parts of vinyl acetate, 5-7 parts of maleic anhydride, 10-13 parts of calcium chloride, 8-10 parts of iron dihydrogen phosphate, 4-5 parts of modified diatomite and a suitable amount of water. By utilizing high chelation capability of a high-molecular chelating agent, the chelation capability of calcium chloride and iron dihydrogen phosphate and the high adsorption capability of bentonite, the bentonite-based copolymerized compound adsorbent disclosed by the invention has the characteristics of high adsorption capability, large adsorption capacity, high decolourization ratio to heavy metal ions and organic cationic dyes in wastewater, and the like. The bentonite-based copolymerized compound adsorbent can be used for adsorbing and removing the organic cationic dyes such as heavy metal ions and methylene blue in wastewater. By virtue of detection, the bentonite-based copolymerized compound disclosed by the invention has the advantages that the removal rate of silver ions in wastewater is 95.1% and the removal rate of methylene blue is 96.9%.
Description
Technical field
The present invention relates to a kind of modified function Material Field, relate in particular to copolymerized thing adsorbent of a kind of bentonite base and preparation method thereof.
Background technology
Along with industrial expansion, water pollutes day by day serious, is related to the future great cause of people's livelihood safety and motherland.Water treatment agent is varied, but much there is no specific aim, and cost is higher, needs further research adsorbent more targetedly, reduces costs, and reduces secondary pollution.
Summary of the invention
The object of the present invention is to provide copolymerized thing adsorbent of a kind of bentonite base and preparation method thereof.
Technical scheme of the present invention is as follows:
A copolymerized thing adsorbent, is characterized in that being made by the raw material of following weight portion: bentonite 120-130, acrylic acid 7-9, vinyl acetate 8-10, maleic anhydride 5-7, calcium chloride 10-13, primary iron phosphate 8-10, modification infusorial earth 4-5, water are appropriate;
Described modification infusorial earth is made by the raw material of following weight portion: diatomite 140-150, alum 10-12, nano-sized carbon 1-2, coix seed oil 1-2, ascorbic acid 2-3, citric acid 1-2, sodium phosphate trimer 2-3, ginseng pulverate 2-3; Preparation method puts into calcining furnace by diatomite to calcine 3-4 hour at 540-560 ℃, takes out, and the hydrochloric acid solution of putting into 12-15% soaks 4-5 hour, filter and take out, use clear water cyclic washing, dry, be added to the water, simultaneously, add nano-sized carbon, ascorbic acid, citric acid, alum, grind and obtain slurry, spraying is dry, other residual components is mixed with dried powder, and grinding distribution evenly and get final product.
The preparation method of the copolymerized thing adsorbent of described bentonite base, it is characterized in that comprising the following steps: bentonite is pulverized, send in retort, when 2-3 is processed in charing at 650-750 ℃, take out, add furnishing mud shape in suitable quantity of water together with acrylic acid, vinyl acetate, maleic anhydride, calcium chloride, primary iron phosphate, be heated to 75-85 ℃, grind 2-3 hour to obtain 200-300 order slurry, it is neutral with clear water, washing to pH value, dries; Mix and be uniformly dispersed and get final product with other surplus stocks.
Beneficial effect of the present invention
The present invention utilizes the sequestering power of strong sequestering power, calcium chloride and the primary iron phosphate of high-molecular chelating agent, bentonitic strong adsorption capacity, heavy metal ion in waste water and organic cation dye are had to attached ability is strong, adsorption capacity large, percent of decolourization high, can be used for the organic cation dyes such as heavy metal ion in adsorbing and removing waste water and methylene blue.After testing, the copolymerized thing of bentonite base of the present invention reaches 95.1% to the clearance of silver in waste ion, and the clearance of methylene blue is reached to 96.9%.
The specific embodiment
A copolymerized thing adsorbent, by following weight portion (kilogram) raw material make: bentonite 125, acrylic acid 8, vinyl acetate 9, maleic anhydride 6, calcium chloride 12, primary iron phosphate 9, modification infusorial earth 4, water are appropriate;
Described modification infusorial earth by following weight portion (kilogram) raw material make: diatomite 145, alum 11, nano-sized carbon 1.5, coix seed oil 1.5, ascorbic acid 2.5, citric acid 1.6, sodium phosphate trimer 2.4, ginseng pulverate 2.4; Preparation method puts into calcining furnace by diatomite at 550 ℃, to calcine 3.6 hours, takes out, and puts into 13% hydrochloric acid solution and soaks 4.5 hours, filter and take out, use clear water cyclic washing, dry, be added to the water, simultaneously, add nano-sized carbon, ascorbic acid, citric acid, alum, grind and obtain slurry, spraying is dry, other residual components is mixed with dried powder, and grinding distribution evenly and get final product.
The preparation method of the copolymerized thing adsorbent of described bentonite base, comprise the following steps: bentonite is pulverized, send in retort, at 700 ℃, charing is processed 2.5 o'clock, takes out, and adds furnishing mud shape in suitable quantity of water together with acrylic acid, vinyl acetate, maleic anhydride, calcium chloride, primary iron phosphate, be heated to 80 ℃, grind 2 hours to obtain 200 order slurries, it is neutral with clear water, washing to pH value, dries; Mix and be uniformly dispersed and get final product with other surplus stocks.
After measured, its iodine number 1579mg/g, methylene blue adsorption value 29.3mL/0.1g.
Claims (2)
1. the copolymerized thing adsorbent of bentonite base, is characterized in that being made by the raw material of following weight portion: bentonite 120-130, acrylic acid 7-9, vinyl acetate 8-10, maleic anhydride 5-7, calcium chloride 10-13, primary iron phosphate 8-10, modification infusorial earth 4-5, water are appropriate;
Described modification infusorial earth is made by the raw material of following weight portion: diatomite 140-150, alum 10-12, nano-sized carbon 1-2, coix seed oil 1-2, ascorbic acid 2-3, citric acid 1-2, sodium phosphate trimer 2-3, ginseng pulverate 2-3; Preparation method puts into calcining furnace by diatomite to calcine 3-4 hour at 540-560 ℃, takes out, and the hydrochloric acid solution of putting into 12-15% soaks 4-5 hour, filter and take out, use clear water cyclic washing, dry, be added to the water, simultaneously, add nano-sized carbon, ascorbic acid, citric acid, alum, grind and obtain slurry, spraying is dry, other residual components is mixed with dried powder, and grinding distribution evenly and get final product.
2. the preparation method of the copolymerized thing adsorbent of bentonite base according to claim 1, it is characterized in that comprising the following steps: bentonite is pulverized, send in retort, when 2-3 is processed in charing at 650-750 ℃, take out, add furnishing mud shape in suitable quantity of water together with acrylic acid, vinyl acetate, maleic anhydride, calcium chloride, primary iron phosphate, be heated to 75-85 ℃, grind 2-3 hour to obtain 200-300 order slurry, it is neutral with clear water, washing to pH value, dries; Mix and be uniformly dispersed and get final product with other surplus stocks.