CN103554705A - Renewable mid-sole material of PVC plastic floor - Google Patents
Renewable mid-sole material of PVC plastic floor Download PDFInfo
- Publication number
- CN103554705A CN103554705A CN201310380450.3A CN201310380450A CN103554705A CN 103554705 A CN103554705 A CN 103554705A CN 201310380450 A CN201310380450 A CN 201310380450A CN 103554705 A CN103554705 A CN 103554705A
- Authority
- CN
- China
- Prior art keywords
- plastic floor
- parts
- renewable
- pvc plastic
- pvc
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a renewable mid-sole material of a PVC plastic floor. The renewable mid-sole material comprises 38-42 parts of PVC mixed powder, 135-145 parts of calcium carbonate powder, 0.4-0.6 parts of a stabilizer, 0.1-0.3 parts of paraffin, 0.3-0.5 parts of rosin and 0.4-0.6 parts of carbon powder. A preparation method of the renewable mid-sole material comprises the following steps: mixing the PVC mixed powder, the calcium carbonate powder, the stabilizer, the paraffin, the rosin and the carbon powder by using an internal mixer, calendering, cooling, cutting, and molding. The renewable mid-sole material of a PVC plastic floor has the advantages of scientific and reasonable composition, simple and scientific production process, high product quality and high production efficiency.
Description
Technical field
The present invention relates to floor production technical field, particularly the renewable middle bed material of a kind of PVC plastic floor.
Background technology
In prior art, the application of PVC plastic floor is more and more extensive, but in prior art conventionally technician with PVC plastic cement reworked material, produce in during bed material, because not knowing the moiety of concrete material, knowledge is produced with sensation, so the material of producing is made after finished product, because existing the change of feed back to make product performance have the factors of instability, therefore, after the component content that needs in prior art to use relevant test set to detect each material, thereby the increase and decrease of carrying out as requested again respective material makes product reach unified standard, complex process, stability is not high, affect the raising of quality product and production efficiency.
Summary of the invention
The present invention proposes the renewable middle bed material of a kind of PVC plastic floor, its component is scientific and reasonable, the simple science of production technique, quality product and production efficiency high.The technical solution adopted in the present invention is specifically achieved in that
The invention provides the renewable middle bed material of a kind of PVC plastic floor, it comprises: the PVC powder mix of 38-42 part, the Paris white of 135-145 part, the stablizer of 0.4-0.6 part, the rosin of the paraffin of 0.1-0.3 part, 0.3-0.5 part and the carbon dust of 0.4-0.6 part, described PVC powder mix, described Paris white, described stablizer, described paraffin, described rosin and described carbon dust are after Banbury mixer refining, then process is rolled, cooling and cut-parts aftershaping.
In the specific embodiment of the invention, comprise the PVC powder mix of 40 parts, the Paris white of 140 parts, the stablizer of 0.5 part, the paraffin of 0.2 part, the rosin of 0.4 part and the carbon dust of 0.5 part.
In the specific embodiment of the invention, described Banbury mixer refining temperature is 135 ℃.
In the specific embodiment of the invention, be 35 minutes described cooling time.
In the specific embodiment of the invention, described stablizer adopts one or more in lead salts, metal soap, organic tin, phosphorous acid lipid, rare-earth stabilizer.
The renewable middle bed material of PVC plastic floor of the present invention, its component is scientific and reasonable, the simple science of production technique, quality product and production efficiency high.
Embodiment
For above-mentioned purpose of the present invention, feature and advantage can be become apparent more, below the specific embodiment of the present invention is described in detail, it will be more clear making above-mentioned and other object of the present invention, Characteristics and advantages.
The invention provides the renewable middle bed material of a kind of PVC plastic floor, it comprises: the PVC powder mix of 38-42 part, the Paris white of 135-145 part, the stablizer of 0.4-0.6 part, the rosin of the paraffin of 0.1-0.3 part, 0.3-0.5 part and the carbon dust of 0.4-0.6 part, described PVC powder mix, described Paris white, described stablizer, described paraffin, described rosin and described carbon dust are after Banbury mixer refining, then process is rolled, cooling and cut-parts aftershaping.
In the specific embodiment of the invention, comprise the PVC powder mix of 40 parts, the Paris white of 140 parts, the stablizer of 0.5 part, the paraffin of 0.2 part, the rosin of 0.4 part and the carbon dust of 0.5 part.Banbury mixer refining temperature is 135 ℃.Be 35 minutes cooling time.Stablizer adopts one or more in lead salts, metal soap, organic tin, phosphorous acid lipid, rare-earth stabilizer, for example, can adopt lead sulfate tribasic, dibasic lead phosphite and dibasic lead stearate in lead salts; Also can adopt the unsaturated fatty acidss such as calcium in metal soap, barium, cadmium, zinc, magnesium, oleic acid; Can also adopt sulfur-bearing organic tin in organic tin etc.
Particularly, the renewable middle bed material of the PVC plastic floor of the specific embodiment of the invention, it comprises the PVC powder mix of 40 kilograms, the Paris white of 140 kilograms, the stablizer of 0.5 kilogram, the paraffin of 0.2 kilogram, the rosin of 0.4 kilogram and the carbon dust of 0.5 kilogram.Component to improve quality, after mixing machine mixes, is put into Banbury mixer and refined, put into afterwards rolling press and roll, carry out again afterwards cooling process, in addition put into afterwards slitter and carry out cut-parts processing, obtain bed material in the PVC plastic floor of moulding.In this treatment step, for example, Banbury mixer refining temperature is 135 ℃, and be 35 minutes described cooling time, but be not limited to this, can also be other temperature or cooling time.
The renewable middle bed material of PVC plastic floor of the present invention, its component is scientific and reasonable, the simple science of production technique, quality product and production efficiency high.
In above description, a lot of details have been set forth so that fully understand the present invention.But above description is only preferred embodiment of the present invention, the present invention can implement to be much different from alternate manner described here, so the present invention is not subject to the restriction of disclosed concrete enforcement above.Any skilled personnel are not departing from technical solution of the present invention scope situation simultaneously, all can utilize method and the technology contents of above-mentioned announcement to make many possible changes and modification to technical solution of the present invention, or be revised as the equivalent embodiment of equivalent variations.Every content that does not depart from technical solution of the present invention,, all still belongs in the scope of technical solution of the present invention protection any simple modification made for any of the above embodiments, equivalent variations and modification according to technical spirit of the present invention.
Claims (5)
1. the renewable middle bed material of PVC plastic floor, it is characterized in that, comprise: the PVC powder mix of 38-42 part, the Paris white of 135-145 part, the stablizer of 0.4-0.6 part, the rosin of the paraffin of 0.1-0.3 part, 0.3-0.5 part and the carbon dust of 0.4-0.6 part, described PVC powder mix, described Paris white, described stablizer, described paraffin, described rosin and described carbon dust are after Banbury mixer refining, then process is rolled, cooling and cut-parts aftershaping.
2. the renewable middle bed material of PVC plastic floor according to claim 1, is characterized in that, comprises the PVC powder mix of 40 parts, the Paris white of 140 parts, the stablizer of 0.5 part, the paraffin of 0.2 part, the rosin of 0.4 part and the carbon dust of 0.5 part.
3. the renewable middle bed material of PVC plastic floor according to claim 1, is characterized in that, described Banbury mixer refining temperature is 135 ℃.
4. the renewable middle bed material of PVC plastic floor according to claim 1, is characterized in that, be 35 minutes described cooling time.
5. the renewable middle bed material of PVC plastic floor according to claim 1, is characterized in that, described stablizer adopts one or more in lead salts, metal soap, organic tin, phosphorous acid lipid, rare-earth stabilizer.