CN103553038A - 一种龙眼核改性活性炭及其制备方法 - Google Patents

一种龙眼核改性活性炭及其制备方法 Download PDF

Info

Publication number
CN103553038A
CN103553038A CN201310440764.8A CN201310440764A CN103553038A CN 103553038 A CN103553038 A CN 103553038A CN 201310440764 A CN201310440764 A CN 201310440764A CN 103553038 A CN103553038 A CN 103553038A
Authority
CN
China
Prior art keywords
parts
longan
pit
seed
active carbon
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310440764.8A
Other languages
English (en)
Inventor
孙夕雨
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
BENGBU DEMO FILTRATION TECHNOLOGY Co Ltd
Original Assignee
BENGBU DEMO FILTRATION TECHNOLOGY Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by BENGBU DEMO FILTRATION TECHNOLOGY Co Ltd filed Critical BENGBU DEMO FILTRATION TECHNOLOGY Co Ltd
Priority to CN201310440764.8A priority Critical patent/CN103553038A/zh
Publication of CN103553038A publication Critical patent/CN103553038A/zh
Pending legal-status Critical Current

Abstract

一种龙眼核改性活性炭，由下列重量份的原料制成：龙眼核80-100、淀粉6-8、聚乙烯醇5-7、粘土8-10、聚乙烯5-7、稻壳30-40、氧化钙10-15、松香酸钠4-5、环氧氯丙烷2-3、N，N-二甲基甲酰胺3-4、改性硅藻土4-5、水适量。本发明使用龙眼核作为原料生产的活性炭质地均匀、微孔孔隙发达；配合稻壳使用，形成的空隙不同，吸附不同的有害物质；通过使用聚乙烯醇等聚合物，形成粘合剂，使活性炭不易崩解，抗压强度提高，落粉率减少；同时添加氧化钙，能够高效脱硫及其他酸性物质；有效利用其制备环保型活性炭，不仅有助于解决焚烧或丢弃时带来的环境污染问题，而且大大降低了制造成本，可期工业化生产。

Description

一种龙眼核改性活性炭及其制备方法
技术领域
本发明涉及一种改性功能材料领域，尤其涉及一种龙眼核改性活性炭及其制备方法。
背景技术
活性炭被广泛用于吸附有害物质，活性炭的原料是含炭为主的物质，包括木质、兽骨、血、煤炭、石油等矿物质，经高温碳化和活化制得。
龙眼核，其味微苦、涩，平；内用于胃痛、疝气痛；外用治外伤出血、用于止血止痛、烧烫伤、刀伤出血等。龙眼核为无患子科植物龙眼的种子，质地坚硬，含炭量高，适合做活性炭。
发明内容
本发明的目的在于提供一种龙眼核改性活性炭及其制备方法。
本发明的技术方案如下：
   一种龙眼核改性活性炭，其特征在于由下列重量份的原料制成：龙眼核80-100、淀粉6-8、聚乙烯醇5-7、粘土8-10、聚乙烯5-7、稻壳30-40、氧化钙10-15、松香酸钠4-5、环氧氯丙烷2-3、N，N-二甲基甲酰胺3-4、改性硅藻土4-5、水适量；
    所述改性硅藻土由下列重量份的原料制成：硅藻土100-110、麦饭石30-34、纳米碳1-2、抗坏血酸1-2、薏仁油1-2、十二烷基苯磺酸钠1-2、葡萄糖酸锌2-3、蒲公英粉2-3；制备方法是将硅藻土、麦饭石放入煅烧炉中在540-560℃下煅烧3-4小时，取出，放入12-15%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干，加入水中，同时，加入纳米碳、抗坏血酸、葡萄糖酸锌，研磨得到浆料，喷雾干燥，将其它剩余成分与干燥粉末混合，研磨分散均匀即得。
所述龙眼核改性活性炭的制备方法，其特征在于包括以下步骤：将龙眼核、稻壳粉碎，与淀粉、粘土一起送入炭化炉中，在600-720℃下炭化处理3-4小时，取出，与聚乙烯醇、聚乙烯、氧化钙、松香酸钠、环氧氯丙烷、N，N-二甲基甲酰胺一起加入适量水中调成泥状，加热至80-90℃，研磨2-3小时得200-300目浆料，用清水洗涤至PH值为中性，烘干；与其他剩余原料混合分散均匀即得。
本发明的有益效果
本发明使用龙眼核作为原料生产的活性炭质地均匀、微孔孔隙发达；配合稻壳使用，形成的空隙不同，吸附不同的有害物质；通过使用聚乙烯醇等聚合物，形成粘合剂，使活性炭不易崩解，抗压强度提高，落粉率减少；同时添加氧化钙，能够高效脱硫及其他酸性物质；有效利用其制备环保型活性炭，不仅有助于解决焚烧或丢弃时带来的环境污染问题，而且大大降低了活性炭的制造成本，可期工业化生产。
具体实施方式
一种龙眼核改性活性炭，由下列重量份（公斤）的原料制成：龙眼核90、淀粉7、聚乙烯醇6、粘土9、聚乙烯6、稻壳36、氧化钙14、松香酸钠4、环氧氯丙烷2、N，N-二甲基甲酰胺3、改性硅藻土4、水适量；
    所述改性硅藻土由下列重量份(公斤)的原料制成：硅藻土106、麦饭石33、纳米碳1.4、抗坏血酸1.5、薏仁油1.6、十二烷基苯磺酸钠1.5、葡萄糖酸锌2.5、蒲公英粉2.4；制备方法是将硅藻土、麦饭石放入煅烧炉中在550℃下煅烧3.4小时，取出，放入15%的盐酸溶液中浸泡4小时，过滤取出，用清水反复洗涤，烘干，加入水中，同时，加入纳米碳、抗坏血酸、葡萄糖酸锌，研磨得到浆料，喷雾干燥，将其它剩余成分与干燥粉末混合，研磨分散均匀即得。
所述龙眼核改性活性炭的制备方法，包括以下步骤：将龙眼核、稻壳粉碎，与淀粉、粘土一起送入炭化炉中，在680℃下炭化处理3小时，取出，与聚乙烯醇、聚乙烯、氧化钙、松香酸钠、环氧氯丙烷、N，N-二甲基甲酰胺一起加入适量水中调成泥状，加热至85℃，研磨2.6小时得250目浆料，用清水洗涤至PH值为中性，烘干；与其他剩余原料混合分散均匀即得。
经测定，其碘值1531mg/g，亚甲基蓝吸附值25.7mL/0.1g。

Claims (2)

1.一种龙眼核改性活性炭，其特征在于由下列重量份的原料制成：龙眼核80-100、淀粉6-8、聚乙烯醇5-7、粘土8-10、聚乙烯5-7、稻壳30-40、氧化钙10-15、松香酸钠4-5、环氧氯丙烷2-3、N，N-二甲基甲酰胺3-4、改性硅藻土4-5、水适量；
所述改性硅藻土由下列重量份的原料制成：硅藻土100-110、麦饭石30-34、纳米碳1-2、抗坏血酸1-2、薏仁油1-2、十二烷基苯磺酸钠1-2、葡萄糖酸锌2-3、蒲公英粉2-3；制备方法是将硅藻土、麦饭石放入煅烧炉中在540-560℃下煅烧3-4小时，取出，放入12-15%的盐酸溶液中浸泡4-5小时，过滤取出，用清水反复洗涤，烘干，加入水中，同时，加入纳米碳、抗坏血酸、葡萄糖酸锌，研磨得到浆料，喷雾干燥，将其它剩余成分与干燥粉末混合，研磨分散均匀即得。
2.根据权利要求1所述龙眼核改性活性炭的制备方法，其特征在于包括以下步骤：将龙眼核、稻壳粉碎，与淀粉、粘土一起送入炭化炉中，在600-720℃下炭化处理3-4小时，取出，与聚乙烯醇、聚乙烯、氧化钙、松香酸钠、环氧氯丙烷、N，N-二甲基甲酰胺一起加入适量水中调成泥状，加热至80-90℃，研磨2-3小时得200-300目浆料，用清水洗涤至PH值为中性，烘干；与其他剩余原料混合分散均匀即得。
CN201310440764.8A 2013-09-25 2013-09-25 一种龙眼核改性活性炭及其制备方法 Pending CN103553038A (zh)