CN103525279A - Iron oxide red antirust primer - Google Patents
Iron oxide red antirust primer Download PDFInfo
- Publication number
- CN103525279A CN103525279A CN201310466751.8A CN201310466751A CN103525279A CN 103525279 A CN103525279 A CN 103525279A CN 201310466751 A CN201310466751 A CN 201310466751A CN 103525279 A CN103525279 A CN 103525279A
- Authority
- CN
- China
- Prior art keywords
- parts
- iron oxide
- oxide red
- proofing primer
- red rust
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to the paint field, and particularly relates to an iron oxide red antirust primer. The primer comprises following components by weight: 25-35 parts of a modified alkyd resin, 20-30 parts of cellulose acetate, 5-8 parts of tannic acid, 20-25 parts of iron oxide red, 3-5 parts of talcum powder, 3-6 parts of mica powder, 2-5 parts of gallotannic acid, 0.5-1.5 parts of a leveling agent, 0.2-1.2 parts of an antifoaming agent, 20-30 parts of butanol, 15-20 parts of cyclohexanone and 10-15 parts of isopropanol. Beneficial effects adopting the technical scheme by the invention are that: the iron oxide red antirust primer has good adhesive force, good chemical properties, salt mist resistance, water proofness and oil proofness; the iron oxide red antirust primer has good mechanical performances and fallibility, and is especially suitable for antirust priming of various metal products, vehicle machinery, ships, and the like; application processes are pollution-free, safe and environmental-friendly; and producing processes are simple without the need of special equipment, and has a high cost performance ratio.
Description
Technical field
The present invention relates to paint field, particularly a kind of iron oxide red rust-proofing primer.
Background technology
Iron oxide red anticorrosive paint is a kind of chemistry that metallic surface avoids atmosphere, seawater etc. or coating of galvanic corrosion protected.By modified alkyd resin, rust-stabilising pigment, pigment extender, siccative, the compositions such as organic solvent.
The antirust function of rust-proofing primer mainly plays a role by rust-stabilising pigment, therefore conventionally with effect and the name class of rust-stabilising pigment, names.Rust inhibition mechanism with rust-stabilising pigment, roughly be summarized as Four types: physical action rust-proofing primer, chemical action rust-proofing primer, electrochemical action rust-proofing primer and comprehensive action rust-proofing primer, wherein chemical action rust-proofing primer is generally chemical rust proof paint, phosphatization primary coat and on rust paint.Be combined with effect and can be divided into again common rust-inhibiting paint and extraordinary rust-inhibiting paint, common rust-inhibiting paint is divided into physics and general chemical rust proof paint, and extraordinary rust-inhibiting paint is divided into: wash primer, zinc rich primer and rust coating materials.
Tradition anticorrosive paint, though there is its advantage, need to take welding as cost, obtains self benefit.As red lead paint, although antirust mass ratio is better, because lead content is high, when constructing and root out old red lead paint and welding, easily produce poisonous substance, workmen is injured greatly, and be difficult to cure.By the lower red lead paint of shovel or the unrestrained red lead paint on the ground of ejection, infiltration in the ground or flow to meeting polluted water in rivers, and in evil case to people.
Summary of the invention
The object of the invention is: overcome and in prior art, in rust-proofing primer, contain the objectionable impuritiess such as plumbous, the technical deficiency that human body and environment are impacted, provides that a kind of cost is low, the iron oxide red rust-proofing primer of safety non-pollution.
For realizing object of the present invention, the technical solution used in the present invention is as follows:
A rust-proofing primer, its mass parts consists of: 25～35 parts of modified alkyd resins, 20～30 parts of cellulose acetates, 5～8 parts, Weibull, 20～25 parts of iron oxide reds, 3～5 parts of talcum powder, 3～6 parts of mica powders, 2～5 parts of tannic acids, 0.5～1.5 part of flow agent, 0.2～1.2 part of defoamer, 20～30 parts, butanols, 15～20 parts of pimelinketone, 10～15 parts of Virahols.
Further, described modified alkyd resin is selected from: at least one in rosin modified alkyd resin, styrene alkyd resin, benzoic acid modified Synolac.
Further, described flow agent is selected from: slipping and leveling agent, quick foam-killing agent, at least one in deaerating agent of solvent based coating.
Further, described defoamer is selected from: at least one in silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and polyoxypropylene.
Further, described defoamer is the fatty acid ester compounded things of higher alcohols.
Further, a rust-proofing primer, its mass parts consists of: 30 parts of modified alkyd resins, 25 parts of cellulose acetates, 6 parts, Weibull, 22 parts of iron oxide reds, 4 parts of talcum powder, 4 parts of mica powders, 3.5 parts of tannic acids, 1 part of flow agent, 0.7 part of defoamer, 25 parts, butanols, 17 parts of pimelinketone, 12 parts of Virahols.
The object that the present invention adds the fatty acid ester compounded thing of higher alcohols is: non-corrosiveness, nonflammable, non-explosive, non-volatile, stable in properties, 1% aqueous solution pH is 8～9, relative density 0.78～0.88, easily flows under room temperature and while heating, and in the time of-25～-30 ℃, viscosity increases, poor fluidity, safe and reliable as defoamer.
Adopt the beneficial effect of technical scheme of the present invention to be: iron oxide red rust-proofing primer of the present invention has good sticking power, has good chemical quality, salt spray resistance, water tolerance, oil-proofness are better.And its good mechanical property, fillibility are strong, are particularly useful for the antirust bottoming such as all kinds of metal productss, vehicle mechanical, boats and ships, construction process is pollution-free, safety and environmental protection, and production process is simple, need not specific installation, cost performance is high.
Embodiment
Below in conjunction with specific embodiment, the present invention will be further described.
Embodiment 1
A rust-proofing primer, its mass parts consists of: 25 parts of rosin modified alkyd resin, benzoic acid modified Synolac, 20 parts of cellulose acetates, 5 parts, Weibull, 20 parts of iron oxide reds, 3 parts of talcum powder, 3 parts of mica powders, 2 parts of tannic acids, 0.5 part of slipping and leveling agent, silicone emulsion, 0.2 part of the fatty acid ester compounded thing of higher alcohols, 20 parts, butanols, 15 parts of pimelinketone, 10 parts of Virahols.
Embodiment 2
A rust-proofing primer, its mass parts consists of: 30 parts of rosin modified alkyd resin, styrene alkyd resins, 25 parts of cellulose acetates, 6 parts, Weibull, 22 parts of iron oxide reds, 4 parts of talcum powder, 4 parts of mica powders, 3.5 parts of tannic acids, 1 part of slipping and leveling agent, quick foam-killing agent, 0.7 part of the fatty acid ester compounded thing of higher alcohols, 25 parts, butanols, 17 parts of pimelinketone, 12 parts of Virahols.
Embodiment 3
A rust-proofing primer, its mass parts consists of: 35 parts of benzoic acid modified Synolac, 30 parts of cellulose acetates, 8 parts, Weibull, 25 parts of iron oxide reds, 5 parts of talcum powder, 6 parts of mica powders, 5 parts of tannic acids, 1.5 parts of deaerating agents for solvent based coating, 1.2 parts of polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and polyoxypropylenes, 30 parts, butanols, 20 parts of pimelinketone, 15 parts of Virahols.
The object that the present invention adds the fatty acid ester compounded thing of higher alcohols is: non-corrosiveness, nonflammable, non-explosive, non-volatile, stable in properties, 1% aqueous solution pH is 8～9, relative density 0.78～0.88, easily flows under room temperature and while heating, and in the time of-25～-30 ℃, viscosity increases, poor fluidity, safe and reliable as defoamer.
The present invention adopts the object of benzoic acid modified Synolac: benzoic acid modified Synolac is the modified alkyd resin that replaces partial fatty acid to make with phenylformic acid or p-tert-butyl benzoic acid.Phenylformic acid is monoprotic acid, molecular weight, and have a benzene ring structure, introduce in Structure Detemination of Alkyd Resins and can make paint film quick-drying, good luster, hardness is large, water tolerance, salt fog resistance, gloss retention, weathering resistance are all good, and solvent resistance is better than phenylethene modified Synolac, is not afraid of and has stung; But more crisp, shock-resistance is poorer than unmodified person with bendability, also fine with the compatibility of other Synolac or aminoresin, can be used together.
Although above-described embodiment describes in detail technical scheme of the present invention, but technical scheme of the present invention is not limited to above embodiment, in the situation that not departing from thought of the present invention and aim, any change that technical scheme of the present invention is done all will fall into claims limited range of the present invention.
Claims (6)
1. an iron oxide red rust-proofing primer, it is characterized in that, its mass parts consists of: 25～35 parts of modified alkyd resins, 20～30 parts of cellulose acetates, 5～8 parts, Weibull, 20～25 parts of iron oxide reds, 3～5 parts of talcum powder, 3～6 parts of mica powders, 2～5 parts of tannic acids, 0.5～1.5 part of flow agent, 0.2～1.2 part of defoamer, 20～30 parts, butanols, 15～20 parts of pimelinketone, 10～15 parts of Virahols.
2. a kind of iron oxide red rust-proofing primer according to claim 1, is characterized in that, described modified alkyd resin is selected from: at least one in rosin modified alkyd resin, styrene alkyd resin, benzoic acid modified Synolac.
3. a kind of iron oxide red rust-proofing primer according to claim 1, is characterized in that, described flow agent is selected from: slipping and leveling agent, quick foam-killing agent, at least one in deaerating agent of solvent based coating.
4. a kind of iron oxide red rust-proofing primer according to claim 1, it is characterized in that, described defoamer is selected from: at least one in silicone emulsion, the fatty acid ester compounded thing of higher alcohols, polyoxyethylene polyoxypropylene tetramethylolmethane ether, polyoxyethylene polyoxy propyl alcohol amidogen ether, polypropylene glycerol aether and polyoxypropylene.
5. a kind of iron oxide red rust-proofing primer according to claim 1, is characterized in that, described defoamer is the fatty acid ester compounded things of higher alcohols.
6. a kind of iron oxide red rust-proofing primer according to claim 1, it is characterized in that, its mass parts consists of: 30 parts of modified alkyd resins, 25 parts of cellulose acetates, 6 parts, Weibull, 22 parts of iron oxide reds, 4 parts of talcum powder, 4 parts of mica powders, 3.5 parts of tannic acids, 1 part of flow agent, 0.7 part of defoamer, 25 parts, butanols, 17 parts of pimelinketone, 12 parts of Virahols.