CN103525144B - 一种高温防烧粘涂料 - Google Patents

一种高温防烧粘涂料 Download PDF

Info

Publication number
CN103525144B
CN103525144B CN201310419062.1A CN201310419062A CN103525144B CN 103525144 B CN103525144 B CN 103525144B CN 201310419062 A CN201310419062 A CN 201310419062A CN 103525144 B CN103525144 B CN 103525144B
Authority
CN
China
Prior art keywords
add
raw material
preventing coating
adhesive aid
sticking preventing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
CN201310419062.1A
Other languages
English (en)
Other versions
CN103525144A (zh
Inventor
任振州
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Guangdong Teflon Ceramic Technology Research And Development Co ltd
Original Assignee
Individual
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Individual filed Critical Individual
Priority to CN201310419062.1A priority Critical patent/CN103525144B/zh
Publication of CN103525144A publication Critical patent/CN103525144A/zh
Application granted granted Critical
Publication of CN103525144B publication Critical patent/CN103525144B/zh
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Abstract

本发明公开了一种高温防烧粘涂料，它是由下述重量份的原料组成的：硅丙乳液10-15、二硫化钼1-2、超细硫酸钡3-5、三氧化二锑1-2、四氟化铈0.1-0.2、氧化铝4-6、氢氧化镁2-3、焦磷酸钾0.1-0.2、硅酸钙4-5、丙烯酸乙酯2-3、粘结助剂5-8、去离子水40-60；本发明的涂料层对金属底材具有良好的粘结力、耐侯性、优异的防烧粘功能和防护功能，而且涂层在室温下能快速自干，使用操作方便。

Description

一种高温防烧粘涂料
技术领域
本发明主要涉及一种涂料，尤其涉及一种高温防烧粘涂料。
背景技术
涂料应该具有防腐、防水、防油、耐化学品、耐光、耐温等，物件暴露在大气之中，受到氧气、水分等的侵蚀，造成金属锈蚀、木材腐朽、水泥风化等破坏现象。在物件表面涂以涂料，形成一层保护膜，能够阻止或延迟这些破坏现象的发生和发展，使各种材料的使用寿命延长。所以，保护作用是涂料的一个主要作用，提高传统涂料的保护作用，才能进一步提高涂料的品质。
发明内容
本发明目的就是为了提供一种高温防烧粘涂料。
本发明是通过以下技术方案实现的：
一种高温防烧粘涂料，它是由下述重量份的原料组成的：
硅丙乳液10-15、二硫化钼1-2、超细硫酸钡3-5、三氧化二锑1-2、四氟化铈0.1-0.2、氧化铝4-6、氢氧化镁2-3、焦磷酸钾0.1-0.2、硅酸钙4-5、丙烯酸乙酯2-3、粘结助剂5-8、去离子水40-60；
所述的粘结助剂是由下述重量份的原料组成的：
苯丙乳液60-70、黄蓍胶6-8、吡啶硫酮锌1-2、硅铝酸钠4-6、聚丙烯酸丁酯1-2、羟乙基纤维素2-4、2,6-二叔丁基对甲酚0.1-0.3、水适量；
将上述重量黄蓍胶的10-20%加入到10-15倍水中，加入羟乙基纤维素和2,6-二叔丁基对甲酚，在400-600转/分的速度下搅拌分散10-15分钟，升高温度为60-80℃，加入吡啶硫酮锌、硅铝酸钠、聚丙烯酸丁酯，充分混合后，加入剩余各原料，搅拌均匀后过80-100℃的蒸汽加热，使得体系固含量为60-65%，冷却至常温，即得所述粘结助剂。
一种高温防烧粘涂料的制备方法，包括以下步骤：
将上述二硫化钼、超细硫酸钡、三氧化二锑、四氟化铈、氧化铝、氢氧化镁、焦磷酸钾、硅酸钙、丙烯酸乙酯混合，放入球磨罐中，加入上述重量去离子水的40-50%，充分研磨，加入粘结助剂，60-80℃下保温搅拌1-2小时，冷却，加入剩余各原料，搅拌均匀，即得所述高温防烧粘涂料。
本发明的优点是：
本发明的涂料层对金属底材具有良好的粘结力、耐侯性、优异的防烧粘功能和防护功能，而且涂层在室温下能快速自干，使用操作方便。
具体实施方式
实施例1
一种高温防烧粘涂料，它是由下述重量份（公斤）的原料组成的：
硅丙乳液15、二硫化钼1、超细硫酸钡5、三氧化二锑2、四氟化铈0.2、氧化铝4、氢氧化镁2、焦磷酸钾0.2、硅酸钙5、丙烯酸乙酯3、粘结助剂8、去离子水60；
所述的粘结助剂是由下述重量份的原料组成的：
苯丙乳液70、黄蓍胶8、吡啶硫酮锌1、硅铝酸钠6、聚丙烯酸丁酯1、羟乙基纤维素4、2,6-二叔丁基对甲酚0.3、水适量；
将上述重量黄蓍胶的20%加入到15倍水中，加入羟乙基纤维素和2,6-二叔丁基对甲酚，在600转/分的速度下搅拌分散15分钟，升高温度为80℃，加入吡啶硫酮锌、硅铝酸钠、聚丙烯酸丁酯，充分混合后，加入剩余各原料，搅拌均匀后过100℃的蒸汽加热，使得体系固含量为65%，冷却至常温，即得所述粘结助剂。
一种高温防烧粘涂料的制备方法，包括以下步骤：
将上述二硫化钼、超细硫酸钡、三氧化二锑、四氟化铈、氧化铝、氢氧化镁、焦磷酸钾、硅酸钙、丙烯酸乙酯混合，放入球磨罐中，加入上述重量去离子水的50%，充分研磨，加入粘结助剂，80℃下保温搅拌2小时，冷却，加入剩余各原料，搅拌均匀，即得所述高温防烧粘涂料。
性能测试：
涂层附着力1级；
储存稳定性：1年。

Claims (2)

1.一种高温防烧粘涂料，其特征在于它是由下述重量份的原料组成的：
硅丙乳液10-15、二硫化钼1-2、超细硫酸钡3-5、三氧化二锑1-2、四氟化铈0.1-0.2、氧化铝4-6、氢氧化镁2-3、焦磷酸钾0.1-0.2、硅酸钙4-5、丙烯酸乙酯2-3、粘结助剂5-8、去离子水40-60；
所述的粘结助剂是由下述重量份的原料组成的：
苯丙乳液60-70、黄蓍胶6-8、吡啶硫酮锌1-2、硅铝酸钠4-6、聚丙烯酸丁酯1-2、羟乙基纤维素2-4、2,6-二叔丁基对甲酚0.1-0.3、水适量；
将上述重量黄蓍胶的10-20%加入到10-15倍水中，加入羟乙基纤维素和2,6-二叔丁基对甲酚，在400-600转/分的速度下搅拌分散10-15分钟，升高温度为60-80℃，加入吡啶硫酮锌、硅铝酸钠、聚丙烯酸丁酯，充分混合后，加入剩余各原料，搅拌均匀后过80-100℃的蒸汽加热，使得体系固含量为60-65%，冷却至常温，即得所述粘结助剂。
2.一种如权利要求1所述的高温防烧粘涂料的制备方法，其特征在于包括以下步骤：
将上述二硫化钼、超细硫酸钡、三氧化二锑、四氟化铈、氧化铝、氢氧化镁、焦磷酸钾、硅酸钙、丙烯酸乙酯混合，放入球磨罐中，加入上述重量去离子水的40-50%，充分研磨，加入粘结助剂，60-80℃下保温搅拌1-2小时，冷却，加入剩余各原料，搅拌均匀，即得所述高温防烧粘涂料。
CN201310419062.1A 2013-09-13 2013-09-13 一种高温防烧粘涂料 Active CN103525144B (zh)