CN103525009B - 一种抗老化阻燃塑料 - Google Patents
一种抗老化阻燃塑料 Download PDFInfo
- Publication number
- CN103525009B CN103525009B CN201310440542.6A CN201310440542A CN103525009B CN 103525009 B CN103525009 B CN 103525009B CN 201310440542 A CN201310440542 A CN 201310440542A CN 103525009 B CN103525009 B CN 103525009B
- Authority
- CN
- China
- Prior art keywords
- mass parts
- aging
- plastics
- resistant flame
- parts
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
本发明公开了一种抗老化阻燃塑料，由下述重量份组分组成：80-95质量份环氧树脂、50-55质量份硝化棉树酯、10-14质量份铝粉、10-15质量份氧化铍、10-15质量份三乙烯四胺、10-13质量份硅酸锆、5-9质量份玉米粉、10-18质量份甲醇和4-8质量份环氧硬脂酸辛酯。本发明制得的塑料具有良好的抗老化和阻燃功能；并且不影响塑料的机械强度；同时同树脂的相容性要好，在塑料制品中不迁移、不析出、不被萃取。
Description
技术领域
本发明属于高分子材料领域，具体涉及一种抗老化阻燃塑料。
技术背景
近年来，电子电器、建筑、航空与汽车行业的快速发展对塑料的性能提出的更高的要求。其中，阻燃型的塑料不易燃烧，火焰传播速率小，质量损失速率及释热速率较低，而且具有一定的自熄性。但是，目前使用的阻燃塑料性能不能满足要求，并且多采用卤素阻燃剂，燃烧过程会放出卤化氢对人体造成严重的危害。
同时为了适应不同的工作环境和使用需求，所以会对塑料进行改进性性能，而只具有单一的功能的塑料在现在竞争越来越激烈的市场中，越来越出来劣势。所以需要对塑料进行改性，使其具有不止一种特性，从而增强在市场的竞争力。
然而市面上的改性塑料的质量不稳定，抗老化性能并不佳，还是容易老化，发生龟裂，降低使用寿命。
发明内容
针对现有技术中存在的上述不足，本发明目的是提供一种抗老化阻燃塑料。
本发明的目的是通过以下技术方案实现的：一种抗老化阻燃塑料，由下述重量份组分组成：80-95质量份环氧树脂、50-55质量份硝化棉树酯、10-14质量份铝粉、10-15质量份氧化铍、10-15质量份三乙烯四胺、10-13质量份硅酸锆、5-9质量份玉米粉、10-18质量份甲醇和4-8质量份环氧硬脂酸辛酯。
一种抗老化阻燃塑料，由下述重量份组分组成：95质量份环氧树脂、54质量份硝化棉树酯、13质量份铝粉、14质量份氧化铍、14质量份三乙烯四胺、13质量份硅酸锆、8质量份玉米粉、17质量份甲醇和6质量份环氧硬脂酸辛酯。
一种抗老化阻燃塑料，由下述重量份组分组成：83质量份环氧树脂、51质量份硝化棉树酯、11质量份铝粉、11质量份氧化铍、11质量份三乙烯四胺、12质量份硅酸锆、8质量份玉米粉、11质量份甲醇和6质量份环氧硬脂酸辛酯。
本发明具有的有益效果：本发明制得的塑料具有良好的抗老化和阻燃功能；并且不影响塑料的机械强度；同时同树脂的相容性要好，在塑料制品中不迁移、不析出、不被萃取。
具体实施方式
实施例1
抗老化阻燃塑料的制备：将80-95质量份环氧树脂、50-55质量份硝化棉树酯、10-14质量份铝粉、10-15质量份氧化铍、10-15质量份三乙烯四胺、10-13质量份硅酸锆、5-9质量份玉米粉、10-18质量份甲醇和4-8质量份环氧硬脂酸辛酯混合放入搅拌机，搅拌均匀后放入密炼机密炼，密练温度为170-175℃、转速为900-950rpm；然后将密炼后的混合物经造粒机造粒，得到颗粒，将颗粒放入水槽冷却，然后在常温下干燥；本实施例制备出的材料的主要性能如下：拉伸强度 MPa（GB/T1040-2006）：35-39，冲击强度 kJ/m2（GB/T1043-2008）：3-4.9；氧指数%（GB/T2406-2008）:3，垂直燃烧级别UL-94：V0；500h光老化冲击强度保持率：100%。
实施例2
抗老化阻燃塑料的制备：将95质量份环氧树脂、54质量份硝化棉树酯、13质量份铝粉、14质量份氧化铍、14质量份三乙烯四胺、13质量份硅酸锆、8质量份玉米粉、17质量份甲醇和6质量份环氧硬脂酸辛酯混合放入搅拌机，搅拌均匀后放入密炼机密炼，密练温度为170-175℃、转速为900-950rpm；然后将密炼后的混合物经造粒机造粒，得到颗粒，将颗粒放入水槽冷却，然后在常温下干燥。
实施例3
抗老化阻燃塑料的制备：将83质量份环氧树脂、51质量份硝化棉树酯、11质量份铝粉、11质量份氧化铍、11质量份三乙烯四胺、12质量份硅酸锆、8质量份玉米粉、11质量份甲醇和6质量份环氧硬脂酸辛酯混合放入搅拌机，搅拌均匀后放入密炼机密炼，密练温度为170-175℃、转速为900-950rpm；然后将密炼后的混合物经造粒机造粒，得到颗粒，将颗粒放入水槽冷却，然后在常温下干燥。
Claims (3)
1.一种抗老化阻燃塑料，其特征在于由下述重量份组分组成：80-95质量份环氧树脂、50-55质量份硝化棉树酯、10-14质量份铝粉、10-15质量份氧化铍、10-15质量份三乙烯四胺、10-13质量份硅酸锆、5-9质量份玉米粉、10-18质量份甲醇和4-8质量份环氧硬脂酸辛酯。
2.根据权利要求1所述的一种抗老化阻燃塑料，其特征在于由下述重量份组分组成：95质量份环氧树脂、54质量份硝化棉树酯、13质量份铝粉、14质量份氧化铍、14质量份三乙烯四胺、13质量份硅酸锆、8质量份玉米粉、17质量份甲醇和6质量份环氧硬脂酸辛酯。
3.根据权利要求1所述的一种抗老化阻燃塑料，其特征在于由下述重量份组分组成：83质量份环氧树脂、51质量份硝化棉树酯、11质量份铝粉、11质量份氧化铍、11质量份三乙烯四胺、12质量份硅酸锆、8质量份玉米粉、11质量份甲醇和6质量份环氧硬脂酸辛酯。