CN103522654B - A kind of transparency protected Rotating fields of the coat of metal and process thereof - Google Patents
A kind of transparency protected Rotating fields of the coat of metal and process thereof Download PDFInfo
- Publication number
- CN103522654B CN103522654B CN201310469310.3A CN201310469310A CN103522654B CN 103522654 B CN103522654 B CN 103522654B CN 201310469310 A CN201310469310 A CN 201310469310A CN 103522654 B CN103522654 B CN 103522654B
- Authority
- CN
- China
- Prior art keywords
- layer
- salt
- acrylic acid
- water soluble
- soluble polymer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
The present invention provides a kind of transparency protected Rotating fields of the coat of metal and process thereof; coat of metal protective clear layer is made up of oil-soluble macromolecule protective clear layer, water soluble polymer protective clear layer and the coat of metal coated from top to down; the protective layer structure of the present invention is made up of two-layer protective clear layer; the water soluble polymer hyaline membrane contacted with metal coating surface forms ground floor, it covers again oil-soluble macromolecule hyaline membrane and forms the second layer.Wherein the effect of ground floor is to prevent other organic or inorganic reagent to the erosion of the coat of metal, discoloration; the effect of the second layer is the transparent and extraneous vapor water of exclusion of water soluble macromolecular and the contacting of liquid water; improve the stability of ground floor, give wear-resisting, the decay resistance of whole protective layer simultaneously.
Description
Technical field
The present invention relates to a kind of transparency protected Rotating fields of the coat of metal and process thereof.
Background technology
In recent years, along with automobile, household electrical appliance and corresponding decoration industrial expansion and people are to beautifying the raising day by day of life requirement, the dicoration of product and decay resistance etc. are required to improve the most further by industrial operation person.Surface metallization technology is to utilize that the marginality new technique of the subjects such as modern physics, metallography and electrochemistry interpenetrates, crossing one another changes the organizational structure of product surface or deposit one or more layers metal film on original surface, to reach property as obtained the process with metal finishing outward appearance etc. of workpiece.Surface coating technique is the important component part of Surface Engineering and Rebuilding engineering, currently mainly includes Vacuum Deposition, chemical plating, plating and Brush Plating etc..
Due to the coat of metal the most relatively thin (0.05 μm~5.0 μm), cause the surface of part metals ripple the most alive metal such as aluminum, silvering to be vulnerable to external influence such as light, oxygen, soda acid, scratch and occur variable color, aoxidize, the phenomenon such as rotten and damage.In order to improve the colour stability of coating, corrosion resistance and the character such as wear-resisting; dealer would generally take chemical passivation, electrochemical passivation or plate the method such as alloy of the noble metals such as a layer of chemically stable gold, palladium, rhodium, indium or noble metal again, but these methods all exist complex process, improve limitation and high in cost of production shortcoming limits its application.By simple dipping, spraying or electrophoresis process coating surface formed one layer of fine and close organic polymer transparent lamina just can effectively mask erosion medium, improve surface abrasion resistance, prevent variable color.But the organic solvent in most of macromolecular solutions, monomer, firming agent etc. can occur serious variable color even to destroy the phenomenons such as coating after contacting with coating particularly Vacuum Deposition, chemical plating metal coating in actual mechanical process.Although the most a small amount of water soluble polymer clear solution will not occur the phenomenon such as coating color, damage after contacting with the coat of metal; but owing to being exposed in air after this kind of macromolecule filming; the moisture in air can be adsorbed; causing protective layer character to be deteriorated, affecting matrix particularly has the stability of ferrous components matrix.
The most how to find one the easiest, the most do not destroy coating and cost but also low transparent protective layer technology, there is important practical significance.
Summary of the invention
It is an object of the invention to; overcome existing coat of metal protective clear layer technological deficiency; there is provided a kind of new metal coating surface to form transparent protective layer preparation method and protective layer structure, meet wear-resisting to the coat of metal, the corrosion-resistant and requirement of the performance such as metallic luster, texture decoration.Specific embodiments of the present invention are:
A kind of transparency protected Rotating fields of the coat of metal, described coat of metal protective clear layer is made up of oil-soluble macromolecule protective clear layer, water soluble polymer protective clear layer and the coat of metal coated from top to down.
Further, the transparency protected layer thickness of described water soluble polymer is 0.02 μm~100.0 μm.
Further, the described transparency protected layer thickness of oil-soluble macromolecule is 0.05 μm~500.0 μm.
Present invention additionally comprises a kind of coat of metal protective clear layer process, it is characterised in that comprise the following steps:
(1) dipping, spraying, electrostatic spraying or brushing method is utilized to prepare one layer of uniform water soluble polymer transparent membrane at metal or alloy coating surface;
(2) treat that water soluble polymer hyaline membrane is completely dried formation water soluble polymer protective clear layer;
(3) dipping, spraying, electrostatic spraying or brushing method is utilized to prepare one layer of oil-soluble macromolecule transparent membrane on the water soluble polymer clear layer that step (2) is formed;
(4) wait to be fully cured or form oil-soluble macromolecule protective clear layer after drying.
nullFurther,Described water soluble polymer transparent membrane component at least contains acrylic acid、Methacrylic acid、Acrylic acid sodium salt、Sodium salt of methacrylic acid、Acrylic acid potassium salt、Metering system acid potassium salt、Acrylic acid lithium salts、Methacrylic acid lithium salts、Acrylic acid calcium salt、Metering system acid calcium salt、Acrylic acid magnesium salt、Methacrylic acid magnesium salt、Acrylic acid zinc salt、Methacrylic acid zinc salt、Acrylic acid barium salt、Methacrylic acid barium salt、Acrylic acid ammonium salt、Methacrylic acid ammonium salt、Acrylamide、Methacrylamide、Hydrolyzed polyacrylamide、Acrylic acid glycol ester、Acrylic acid glycerine ester、Diethylene glycol、Bisphenol A-type diacrylate、Bisphenol-f type diacrylate、Vinylpyrrolidone、Quaternary amine、Aminoacid、Glucose、Ethylene glycol、Arabic gum、Algin sodium、Bone meal、Gelatin、Casein、Silicon alkoxide、Maleic anhydride、Vinyl alcohol、Starch derivatives、Carboxymethyl cellulose、Methylcellulose、Ethyl cellulose、One of hydroxyethyl cellulose.
Further, oil-soluble macromolecule transparent membrane component at least contains one of polyurethane transparent paint, transparent epoxy resin paint, acrylic clear paint, the NC Nitroncellulose colored varnish, the alkyd resin colored varnish, UV cured transparent resin.
Compared with prior art; the method have the advantages that the protective layer structure of the present invention is made up of two-layer protective clear layer; water soluble polymer hyaline membrane in metal coating surface coating forms ground floor, it covers again oil-soluble macromolecule hyaline membrane and forms the second layer.Wherein the effect of ground floor is to prevent other organic or inorganic reagent to the erosion of the coat of metal, discoloration; the effect of the second layer is the transparent and extraneous vapor water of exclusion of water soluble macromolecular and the contacting of liquid water; improve the stability of ground floor, give wear-resisting, the decay resistance of whole protective layer simultaneously.
Accompanying drawing explanation
Fig. 1 is the structural representation of existing silver-plated iron craftworks.
Fig. 2 is that the present invention is in iron craftworks silver-plated surface protective clear layer example schematic.
Fig. 3 is existing plastic toy aluminium plated surface schematic diagram.
Fig. 4 is that the present invention is in plastic toy aluminium plated surface protective clear layer example schematic.
In figure: 10-Iron skeleton, 20-Epoxy resin layer, 30-Silvering, 40-Water soluble polymer protective clear layer, 50-Oil-soluble macromolecule protective clear layer, 60-Plastic substrate, 70-Aluminium coat.
Detailed description of the invention
The present invention will be further described in detail with detailed description of the invention below in conjunction with the accompanying drawings.
A kind of transparency protected Rotating fields of the coat of metal, it is characterised in that described coat of metal protective clear layer is constituted by by the oil-soluble macromolecule protective clear layer 50 coated from top to down, water soluble polymer protective clear layer 40 and the coat of metal 30 (70).
Water soluble polymer protective clear layer 40 thickness is 0.02 μm~100.0 μm.
Oil-soluble macromolecule protective clear layer 50 thickness is 0.05 μm~500.0 μm.
Embodiment 1: iron craftworks protective clear layer embodiment.
Fig. 1 is the structural representation of existing silver-plated iron craftworks, and iron craftworks iron skeleton 10 has epoxy resin protective layer 20, then passes through Vacuum Deposition, chemical plating, plating or Brush Plating and forms one layer of silvering 30.
As in figure 2 it is shown, the described transparency protected Rotating fields of iron silver-plated surface includes from top to down: oil-soluble macromolecule protective clear layer 50, water soluble polymer protective clear layer 40, silvering 30、Epoxy resin layer 20, iron skeleton 10.
Preparation method:
nullThe present invention uses dipping at metal coating surface、The methods such as spraying or brushing prepare one layer of uniform water soluble polymer transparent membrane,Wherein at least contain acrylic acid in water soluble polymer transparent configuration or in synthon、Methacrylic acid、Acrylic acid sodium salt、Sodium salt of methacrylic acid、Acrylic acid potassium salt、Metering system acid potassium salt、Acrylic acid lithium salts、Methacrylic acid lithium salts、Acrylic acid calcium salt、Metering system acid calcium salt、Acrylic acid magnesium salt、Methacrylic acid magnesium salt、Acrylic acid zinc salt、Methacrylic acid zinc salt、Acrylic acid barium salt、Methacrylic acid barium salt、Acrylic acid ammonium salt、Methacrylic acid ammonium salt、Acrylamide、Methacrylamide、Hydrolyzed polyacrylamide、Acrylic acid glycol ester、Acrylic acid glycerine ester、Diethylene glycol、Bisphenol A-type diacrylate、Bisphenol-f type diacrylate、Vinylpyrrolidone、Quaternary amine、Aminoacid、Glucose、Ethylene glycol、Arabic gum、Algin sodium、Bone meal、Gelatin、Casein、Silicon alkoxide、Maleic anhydride、Vinyl alcohol、Starch derivatives、Carboxymethyl cellulose、Methylcellulose、Ethyl cellulose、One of hydroxyethyl cellulose.Water soluble polymer transparent membrane thickness, between 0.02 μm~100.0 μm, enters next procedure after drying completely.
After water soluble polymer transparent membrane is completely dried, uses dipping again, sprays or the method such as brushing prepares one layer of oil-soluble macromolecule transparent membrane in the above, wait to be fully cured or formed after drying wear-resisting, corrosion-resistant and transparent coat of metal protective layer.Its oil-soluble macromolecule is transparent at least contains one of polyurethane transparent paint, transparent epoxy resin paint, acrylic clear paint, the NC Nitroncellulose colored varnish, the alkyd resin colored varnish, UV cured transparent resin.The dried thickness of oil-soluble macromolecule transparent membrane is preferable between 0.05 μm~500.0 μm.
Embodiment 2: plastic toy goods aluminium plated surface protective clear layer example
Fig. 3 is the structural representation of existing aluminized plastic toy, and plastic substrate 60 surface forms one layer of aluminium coat 70 by Vacuum Deposition.
Fig. 4 is that the present invention is in plastic toy aluminium plated surface protective clear layer example schematic.Described iron craftworks includes from top to down: oil-soluble macromolecule protective clear layer 50, water soluble polymer protective clear layer 40, silver aluminium lamination 70、Plastic substrate 60.
nullThe present invention uses dipping at metal coating surface、The methods such as spraying or brushing prepare one layer of uniform water soluble polymer transparent membrane,Wherein at least contain acrylic acid in water soluble polymer transparent configuration or in synthon、Methacrylic acid、Acrylic acid sodium salt、Sodium salt of methacrylic acid、Acrylic acid potassium salt、Metering system acid potassium salt、Acrylic acid lithium salts、Methacrylic acid lithium salts、Acrylic acid calcium salt、Metering system acid calcium salt、Acrylic acid magnesium salt、Methacrylic acid magnesium salt、Acrylic acid zinc salt、Methacrylic acid zinc salt、Acrylic acid barium salt、Methacrylic acid barium salt、Acrylic acid ammonium salt、Methacrylic acid ammonium salt、Acrylamide、Methacrylamide、Hydrolyzed polyacrylamide、Acrylic acid glycol ester、Acrylic acid glycerine ester、Diethylene glycol、Bisphenol A-type diacrylate、Bisphenol-f type diacrylate、Vinylpyrrolidone、Quaternary amine、Aminoacid、Glucose、Ethylene glycol、Arabic gum、Algin sodium、Bone meal、Gelatin、Casein、Silicon alkoxide、Maleic anhydride、Vinyl alcohol、Starch derivatives、Carboxymethyl cellulose、Methylcellulose、Ethyl cellulose、One of hydroxyethyl cellulose.Water soluble polymer transparent membrane thickness, between 0.02 μm~100.0 μm, enters next procedure after drying completely.
After water soluble polymer transparent membrane is completely dried, uses dipping again, sprays or the method such as brushing prepares one layer of oil-soluble macromolecule transparent membrane in the above, wait to be fully cured or formed after drying wear-resisting, corrosion-resistant and transparent coat of metal protective layer.Its oil-soluble macromolecule is transparent at least contains one of polyurethane transparent paint, transparent epoxy resin paint, acrylic clear paint, the NC Nitroncellulose colored varnish, the alkyd resin colored varnish, UV cured transparent resin.The dried thickness of oil-soluble macromolecule transparent membrane is preferable between 0.05 μm~500.0 μm.
Different colours material can also be selected additionally, water soluble polymer of the present invention is transparent, oil-soluble macromolecule is transparent or adds the composition of different colours to reach special metallic mirror surface effect, meeting different demands.
The coat of metal protective clear layer technology of the present invention can be widely applied to artware, toy, stationery, decorate, fit up, electronic device housing, household appliances shell, packing box, the field such as packaging bag.
The foregoing is only presently preferred embodiments of the present invention, all impartial changes done according to scope of the present invention patent and modification, all should belong to the covering scope of the present invention.
Claims (1)
1. the process preparing coat of metal protective clear layer, it is characterised in that comprise the following steps:
(1) dipping, spraying or brushing method is utilized to prepare one layer of uniform water soluble polymer transparent membrane at metal coating surface;
null(2) treat that water soluble polymer transparent membrane is completely dried formation water soluble polymer protective clear layer,Described water soluble polymer transparent membrane component at least contains acrylic acid、Methacrylic acid、Acrylic acid sodium salt、Sodium salt of methacrylic acid、Acrylic acid potassium salt、Metering system acid potassium salt、Acrylic acid lithium salts、Methacrylic acid lithium salts、Acrylic acid calcium salt、Metering system acid calcium salt、Acrylic acid magnesium salt、Methacrylic acid magnesium salt、Acrylic acid zinc salt、Methacrylic acid zinc salt、Acrylic acid barium salt、Methacrylic acid barium salt、Acrylic acid ammonium salt、Methacrylic acid ammonium salt、Acrylamide、Methacrylamide、Hydrolyzed polyacrylamide、Diethylene glycol、Vinylpyrrolidone、Quaternary amine、Aminoacid、Glucose、Ethylene glycol、Arabic gum、Algin sodium、Bone meal、Gelatin、Silicon alkoxide、Maleic anhydride、Vinyl alcohol、Starch derivatives、Carboxymethyl cellulose、Methylcellulose、One of hydroxyethyl cellulose,The thickness of described water soluble polymer protective clear layer is 0.02 μm~100.0 μm;
(3) utilize dipping, spraying or brushing method to prepare one layer of oil-soluble macromolecule transparent membrane on the water soluble polymer protective clear layer that step (2) is formed, component at least contains one of polyurethane transparent paint, transparent epoxy resin paint, acrylic clear paint, the NC Nitroncellulose colored varnish, the alkyd resin colored varnish, UV cured transparent resin;
(4) waiting to be fully cured or form oil-soluble macromolecule protective clear layer after drying, the described transparency protected layer thickness of oil-soluble macromolecule is 0.05 μm~500.0 μm.