CN103509485A - 一种植物基热熔胶 - Google Patents

一种植物基热熔胶 Download PDF

Info

Publication number
CN103509485A
CN103509485A CN201310401054.4A CN201310401054A CN103509485A CN 103509485 A CN103509485 A CN 103509485A CN 201310401054 A CN201310401054 A CN 201310401054A CN 103509485 A CN103509485 A CN 103509485A
Authority
CN
China
Prior art keywords
parts
hot melt
melt adhesive
raw material
resin
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310401054.4A
Other languages
English (en)
Inventor
吴顺保
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Wuhu City Zheng Tong Electric Appliance Equipment Co Ltd
Original Assignee
Wuhu City Zheng Tong Electric Appliance Equipment Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Wuhu City Zheng Tong Electric Appliance Equipment Co Ltd filed Critical Wuhu City Zheng Tong Electric Appliance Equipment Co Ltd
Priority to CN201310401054.4A priority Critical patent/CN103509485A/zh
Publication of CN103509485A publication Critical patent/CN103509485A/zh
Pending legal-status Critical Current

Abstract

本发明公开了一种植物基热熔胶，它是由下述重量份的原料组成的：小麦改性淀粉50-60、聚氨酯10-12、油酸酰胺2-3、聚丙烯酸丁酯2-3、氢化松香甘油酯10-20、聚碳酸酯2-3、EVA树脂7-10、二甲基二巯基乙酸异辛酯锡1-2、棉纤维0.4-0.6、乙撑基双硬脂酰胺1-2、增粘剂6-8；本发明制备的热熔胶成本低，对环境污染小，可部分降解，本发明的热熔胶硬度高、易低温粘合、耐油脂、耐水洗性强。

Description

一种植物基热熔胶
技术领域
    本发明主要涉及一种热熔胶粉末，尤其涉及一种植物基热熔胶。
背景技术
    热熔胶是一种可塑性的粘合剂，在一定温度范围内其物理状态随温度改变而改变，而化学特性不变，其无毒无味，属环保型化学产品。
发明内容
本发明目的就是提供一种植物基热熔胶。
本发明是通过以下技术方案实现的：
一种植物基热熔胶，它是由下述重量份的原料组成的：
小麦改性淀粉50-60、聚氨酯10-12、油酸酰胺2-3、聚丙烯酸丁酯2-3、氢化松香甘油酯10-20、聚碳酸酯2-3、EVA树脂7-10、二甲基二巯基乙酸异辛酯锡1-2、棉纤维0.4-0.6、乙撑基双硬脂酰胺1-2、增粘剂6-8；
所述的增粘剂是由下述重量份的原料组成的：
萜烯树脂30-40、C5石油树脂20-30、氟硅酸钠3-5、硅烷偶联剂KH-5501-2、吡啶硫酮锌0.2-0.3、聚乳酸2-3、聚四氢呋喃醚二醇1-2；
将上述萜烯树脂与C5石油树脂混合加热到100-150℃，加入氟硅酸钠，保温搅拌10-15分钟，降低温度为70-75℃，加入吡啶硫酮锌，充分混合，降低温度为60-65℃，加入硅烷偶联剂KH-550，600-800转/分搅拌分散4-6分钟，加入剩余各原料，充分混合后干燥脱水，即得所述增粘剂。
一种植物基热熔胶的制备方法，包括以下步骤：
（1）将上述聚丙烯酸丁酯、氢化松香甘油酯、聚碳酸酯、EVA树脂与棉纤维混合，在130-150℃下熔融混合30-50 分钟，再加入上述聚氨酯、二甲基二巯基乙酸异辛酯锡，搅拌混合20-30 分钟后，冷却挤出，造粒；
（2）将上述处理后的各原料与剩余各原料混合，送入双螺杆挤出机，挤出造粒，即得所述植物基热熔胶。
本发明的优点是：
    本发明制备的热熔胶成本低，对环境污染小，可部分降解，本发明的热熔胶硬度高、易低温粘合、耐油脂、耐水洗性强。
具体实施方式
实施例1
一种植物基热熔胶，它是由下述重量份（公斤）的原料组成的：
小麦改性淀粉60、聚氨酯12、油酸酰胺3、聚丙烯酸丁酯2、氢化松香甘油酯20、聚碳酸酯2、EVA树脂10、二甲基二巯基乙酸异辛酯锡1、棉纤维0.6、乙撑基双硬脂酰胺1、增粘剂6；
所述的增粘剂是由下述重量份的原料组成的：
萜烯树脂40、C5石油树脂30、氟硅酸钠3、硅烷偶联剂KH-5501、吡啶硫酮锌0.2、聚乳酸2、聚四氢呋喃醚二醇2；
将上述萜烯树脂与C5石油树脂混合加热到130℃，加入氟硅酸钠，保温搅拌15分钟，降低温度为75℃，加入吡啶硫酮锌，充分混合，降低温度为65℃，加入硅烷偶联剂KH-550，800转/分搅拌分散6分钟，加入剩余各原料，充分混合后干燥脱水，即得所述增粘剂。
一种植物基热熔胶的制备方法，包括以下步骤：
（1）将上述聚丙烯酸丁酯、氢化松香甘油酯、聚碳酸酯、EVA树脂与棉纤维混合，在150℃下熔融混合50 分钟，再加入上述聚氨酯、二甲基二巯基乙酸异辛酯锡，搅拌混合30 分钟后，冷却挤出，造粒；
（2）将上述处理后的各原料与剩余各原料混合，送入双螺杆挤出机，挤出造粒，即得所述植物基热熔胶。
性能测试：
180℃熔融粘度 mpa.s：60000-75000；
T 剥离强度测试N/2.5cm ：35-50。

Claims (2)

1.一种植物基热熔胶，其特征在于它是由下述重量份的原料组成的：
小麦改性淀粉50-60、聚氨酯10-12、油酸酰胺2-3、聚丙烯酸丁酯2-3、氢化松香甘油酯10-20、聚碳酸酯2-3、EVA树脂7-10、二甲基二巯基乙酸异辛酯锡1-2、棉纤维0.4-0.6、乙撑基双硬脂酰胺1-2、增粘剂6-8；
所述的增粘剂是由下述重量份的原料组成的：
萜烯树脂30-40、C5石油树脂20-30、氟硅酸钠3-5、硅烷偶联剂KH-5501-2、吡啶硫酮锌0.2-0.3、聚乳酸2-3、聚四氢呋喃醚二醇1-2；
将上述萜烯树脂与C5石油树脂混合加热到100-150℃，加入氟硅酸钠，保温搅拌10-15分钟，降低温度为70-75℃，加入吡啶硫酮锌，充分混合，降低温度为60-65℃，加入硅烷偶联剂KH-550，600-800转/分搅拌分散4-6分钟，加入剩余各原料，充分混合后干燥脱水，即得所述增粘剂。
2.一种如权利要求1所述的植物基热熔胶的制备方法，其特征在于包括以下步骤：
（1）将上述聚丙烯酸丁酯、氢化松香甘油酯、聚碳酸酯、EVA树脂与棉纤维混合，在130-150℃下熔融混合30-50 分钟，再加入上述聚氨酯、二甲基二巯基乙酸异辛酯锡，搅拌混合20-30 分钟后，冷却挤出，造粒；
（2）将上述处理后的各原料与剩余各原料混合，送入双螺杆挤出机，挤出造粒，即得所述植物基热熔胶。
CN201310401054.4A 2013-09-06 2013-09-06 一种植物基热熔胶 Pending CN103509485A (zh)