CN103508706A - 一种提高混凝土管桩轴向承载力的配方 - Google Patents

一种提高混凝土管桩轴向承载力的配方 Download PDF

Info

Publication number
CN103508706A
CN103508706A CN201310404592.9A CN201310404592A CN103508706A CN 103508706 A CN103508706 A CN 103508706A CN 201310404592 A CN201310404592 A CN 201310404592A CN 103508706 A CN103508706 A CN 103508706A
Authority
CN
China
Prior art keywords
formula
tubular pile
concrete tubular
bearing capacity
axial bearing
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Pending
Application number
CN201310404592.9A
Other languages
English (en)
Inventor
胡德云
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Anhui Pile Tube Branch Co Of Rich And Powerful Concrete Co Ltd
Original Assignee
Anhui Pile Tube Branch Co Of Rich And Powerful Concrete Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Anhui Pile Tube Branch Co Of Rich And Powerful Concrete Co Ltd filed Critical Anhui Pile Tube Branch Co Of Rich And Powerful Concrete Co Ltd
Priority to CN201310404592.9A priority Critical patent/CN103508706A/zh
Publication of CN103508706A publication Critical patent/CN103508706A/zh
Pending legal-status Critical Current

Abstract

本发明涉及一种提高混凝土管桩轴向承载力的配方，该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：铝酸钠5%～8%、砂30%～35%、石25%～30%、陶粒10%～15%、木质素磺酸钙4%～8%、水泥12%～20%、水3%～7%。本发明具有材料搭配合理、方便制造和制造成本低等优点，能提高混凝土管桩轴向承载力进而缩小管桩体积，节省了生产制造的成本，为混凝土管桩的运输以及施工提供了方便。

Description

一种提高混凝土管桩轴向承载力的配方
技术领域
本发明涉及管桩制造技术领域，具体的说是一种提高混凝土管桩轴向承载力的配方。
背景技术
在当今的大城市里，经常会看到造型独特的建筑。这些建筑本身对于其地基的牢固程度要求较高，如有的要求有高的抗裂弯矩，有的要求能够承受较高的轴向压力，有的要求有效预应力要达到一定值等等，尤其是对于轴向压力要求较高的混凝土管桩，致使混凝土管桩的体积不得不随着要求的提高而变大，这样给管桩的运输以及施工都带来了极大的麻烦。
发明内容
本发明所要解决的技术问题在于提供一种材料搭配合理的、方便制造的、制造成本低的，能提高混凝土管桩轴向承载力进而缩小管桩体积的配方，即一种提高混凝土管桩轴向承载力的配方。
本发明所要解决的技术问题采用以下技术方案来实现：
一种提高混凝土管桩轴向承载力的配方，该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：
所述各组分所占的最佳质量百分比如下：
Figure BDA0000378893280000021
相关组分的性能及作用如下：
铝酸钠：性质：白色、无臭、无味，呈强碱性的固体，高温熔融产物为白色粉末，溶于水，不溶于乙醇，在空气中易吸收水份和二氧化碳，水中溶解后易析出氢氧化铝沉淀，氢氧化铝溶于氢氧化钠溶液也生成偏铝酸钠溶液。用作纺织品的媒染剂、纸的填料、水的净化剂等。可用氧化铝与固态氢氧化钠或碳酸钠共熔制得。主要用于土木工程方面，本品与水玻璃混合用于施工中的堵漏；造纸行业，本品与硫酸铝混合使用是一种良好的填充剂；水处理方面，可做净水剂助剂，可做为水泥速凝剂；在石油化工、制药、橡胶、印染、纺织、催化剂生产中也有较广泛的应用。
陶粒：具有密度小、质轻、保温、隔热、耐火性优异、抗震性好、抗渗性优异等特性，能够提高混凝土管桩的结构强度，起到隔震、抗震的作用，对混凝土管桩起到保护作用。
木质素磺酸钙：溶于水，微酸性，稳定性良好。有以下用途：1、用作混凝土减水剂：掺水泥量的0.25～0.3%，可以减少用水量10～14以上，改善混凝土和易性，提高工程质量，夏季使用，可抑制坍落度损失，一般都与高效减水剂复配使用；2、用作矿粘结剂：冶炼业，用木质素磺酸钙与矿粉混合，制成矿粉球，干燥后放入窑中，可大幅度提高冶炼回收率；3、耐火材料：制造耐火材料砖瓦时，使用木质素磺酸钙做分散剂和粘合剂，能显著改善操作性能，并有减水、增强、防止龟裂等良好效果；4、陶瓷：木质素磺酸钙用于陶瓷制品，可以降低碳含量增加生坯强度，减少塑性粘土用量，泥浆流动性好，提高成品率70-90%，烧结速度由70分钟减少为40分钟；5、用作饲料粘合剂，可提高家畜和家禽的喜食性，颗粒强度好，减少饲料的微粉量，减少粉料反回率，降低成本。模的损失减少，生产能力提高10-20%，美国与加拿大在饲料中允许掺量为4.0%；6、其它：木质素磺酸钙还可用于精炼助剂、铸造、农药可湿性粉剂加工、型煤压制、采矿、选矿业的选矿剂，道路、土壤、粉尘的控制、制革鞣革填料、炭黑造粒等方面。
本发明的有益效果是：本发明具有材料搭配合理、方便制造和制造成本低等优点，能提高混凝土管桩轴向承载力进而缩小管桩体积，节省了生产制造的成本，为混凝土管桩的运输以及施工提供了方便。
具体实施方式
为了使本发明实现的技术手段、创作特征、达成目的与功效易于明白了解，下面对本发明进一步阐述。
实施例一：
一种提高混凝土管桩轴向承载力的配方，该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：
Figure BDA0000378893280000031
实施例二：
一种提高混凝土管桩轴向承载力的配方，该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：
Figure BDA0000378893280000032
实施例三：
一种提高混凝土管桩轴向承载力的配方，该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：
Figure BDA0000378893280000042
以上显示和描述了本发明的基本原理、主要特征和本发明的优点。本行业的技术人员应该了解，本发明不受上述实施例的限制，上述实施例和说明书中描述的只是本发明的原理，在不脱离本发明精神和范围的前提下，本发明还会有各种变化和改进，这些变化和改进都落入要求保护的本发明范围内。本发明要求保护范围由所附的权利要求书及其等效物界定。

Claims (2)

1.一种提高混凝土管桩轴向承载力的配方，其特征在于：该配方包括铝酸钠、砂、石、陶粒、木质素磺酸钙、水泥和水，各组分所占质量百分比如下：
Figure FDA0000378893270000011
2.根据权利要求1所述的一种提高混凝土管桩轴向承载力的配方，其特征在于：所述各组分所占的最佳质量百分比如下：
Figure FDA0000378893270000012
CN201310404592.9A 2013-09-08 2013-09-08 一种提高混凝土管桩轴向承载力的配方 Pending CN103508706A (zh)