CN103495385A - Modified activated carbon for processing dye waste water and its preparation method - Google Patents
Modified activated carbon for processing dye waste water and its preparation method Download PDFInfo
- Publication number
- CN103495385A CN103495385A CN201310387358.XA CN201310387358A CN103495385A CN 103495385 A CN103495385 A CN 103495385A CN 201310387358 A CN201310387358 A CN 201310387358A CN 103495385 A CN103495385 A CN 103495385A
- Authority
- CN
- China
- Prior art keywords
- activated carbon
- modified
- modified activated
- water
- attapulgite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
Modified activated carbon for processing dye waste water is characterized by being prepared from the following raw materials: by weight, 100-200 parts of activated carbon, 20-24 parts of straw, 3-4 parts of expanded graphite, 30-35 parts of expanded perlite, 8-9 parts of modified attapulgite and a moderate amount of water. The modified activated carbon for processing the dye waste water uses the activated carbon as a main material, a certain amount of the expanded perlite and other porous raw materials with large specific surface area are added into the modified activated carbon, the straw is also added to use as an auxiliary material, the modified activated carbon material which is strong in adsorption effect and capable of absorbing various pollutants is prepared through processing of high temperature calcining, spray drying and other steps, and at the same time, the modified activated carbon material comprises desulfurization components, has good adsorption effect on printing and dyeing waste water, is simple to prepare, and is low in cost.
Description
Technical field
The present invention relates to a kind of method of modifying of nonmetallic ore, relate in particular to a kind of dye wastewater treatment using modified activated carbon and preparation method thereof.
Background technology
Along with scientific and technological development, the progressively construction of modernization industry, various chemicals are exploited, and have brought facility to people's life, simultaneously because chemicals has produced environment and the harmful material of human body, the problem that has also become people to have to face.
Current airborne pollutant is mainly the toxic and harmful produced in the gas that produces of industrial fuel burning, vehicle exhaust, production.It is mainly to contain a large amount of noxious materials in the sewage of industrial production discharge that water pollutes, and also has the sewage in people's life to produce a lot of harmful substances.Also have and many times need to remove toxin in people life, such as air conditioning filter has a lot of bacteriums, toxin on the net, newly-decorated has the harmful substance such as formaldehyde, all needs to remove toxin.All remove at present toxin and often use adsorbent, mainly contain silica gel, activated alumina, active carbon, molecular sieve etc., the sorbing material of developing for certain compositional selecting absorption in addition in addition.But the most adsorption capacity of these adsorbents is limited, need to study different adsorbents for different requirements, bring into play best effect.Simultaneously, find new raw material, to strengthen adsorption effect, cost-saving.
Summary of the invention
The object of the present invention is to provide a kind of dye wastewater treatment using modified activated carbon and preparation method thereof.
Technical scheme of the present invention is as follows:
A kind of dye wastewater treatment using modified activated carbon is characterized in that being made by the raw material of following weight portion: active carbon 100-120, stalk 20-24, expanded graphite 3-4, expanded perlite 30-35, attapulgite modified 8-9, water are appropriate; The described attapulgite modified raw material by following weight portion is made: attapulgite 120-130, silver nitrate 1-2, alum 5-6, iron ore ground-slag 1-2, polytetrafluoroethylene (PTFE) 4-5, titanium sulfate 14-18, jade powder 12-14, zinc sulfate 1-2, chromium oxide 3-4, morpholine 1-2, N-2-(aminoethyl)-3-aminopropyl trimethoxysilane 2-3, water are appropriate; Attapulgite, iron ore ground-slag are sent in calcining furnace, and under 950-990 ℃, calcining 3-4 hour, take out, and spills the N-2-(aminoethyl)-the 3-aminopropyl trimethoxysilane
,put into suitable quantity of water again and grind, regulating the lapping liquid pH value is 4-5, grinds 1-2 hour, obtains 100-150 order slurry, then regulates the lapping liquid pH value for neutral, adds other residual components, continues to grind, and obtains 200-300 order slurry, and spray-drying, obtain.
The preparation method of described dye wastewater treatment using modified activated carbon is characterized in that comprising the following steps: by crushed stalk, add water with expanded perlite and mix, practice into the mud shape, granulate, send into calcining 2-3 hour in 620-650 ℃ of calcining furnace, take out, with active carbon, expanded graphite, attapulgite modified merging, add suitable quantity of water, grind to form 200-300 order slurry, spray-drying, obtain powder, sends in 340-380 ℃ of heat-treatment furnace, heat treatment 2-3 hour, take out cooling and get final product.
Divide the beneficial effect of the invention
It is major ingredient that the present invention adopts active carbon, add that the specific area such as a certain amount of expanded perlite is large, the raw material of porous has also added stalk as auxiliary material, through step process such as high-temperature calcination, spray-dryings, formed suction-operated strong, the modified active Carbon Materials of absorption multiple pollutant, dyeing waste water is had to good adsorption effect, and preparation is simple, cost is low.
The specific embodiment
A kind of dye wastewater treatment using modified activated carbon, by the raw material of following weight portion (kilogram), made: active carbon 100, stalk 20, expanded graphite 3, expanded perlite 30, attapulgite modified 8, water is appropriate;
The described attapulgite modified raw material by following weight portion (kilogram) is made: attapulgite 110, silver nitrate 1.5, alum 5, iron ore ground-slag 1, polytetrafluoroethylene (PTFE) 4, titanium sulfate 16, jade powder 13, zinc sulfate 1, chromium oxide 3, morpholine 1, N-2-(aminoethyl)-3-aminopropyl trimethoxysilane 2, water are appropriate; Attapulgite, iron ore ground-slag are sent in calcining furnace, and under 970 ℃, calcining is 3 hours, takes out, and spills the N-2-(aminoethyl)-the 3-aminopropyl trimethoxysilane
,put into suitable quantity of water again and grind, regulating the lapping liquid pH value is 4, grinds 1 hour, obtains 100 order slurries, then regulates the lapping liquid pH value for neutral, adds other residual components, continues to grind, and obtains 200 order slurries, and spray-drying, obtain.
The preparation method of described dye wastewater treatment using modified activated carbon comprises the following steps: by crushed stalk, add water with expanded perlite and mix, practice into the mud shape, granulate, send in 630 ℃ of calcining furnaces and calcine 2 hours, take out, with active carbon, expanded graphite, attapulgite modified merging, add suitable quantity of water, grind to form 200 order slurries, spray-drying, obtain powder, sends in 360 ℃ of heat-treatment furnaces, heat treatment 2 hours, take out cooling and get final product.
After measured, its iodine number 1578mg/g, methylene blue adsorption value 23.4mL/0.1g.
Claims (2)
1. a dye wastewater treatment using modified activated carbon is characterized in that being made by the raw material of following weight portion: active carbon 100-120, stalk 20-24, expanded graphite 3-4, expanded perlite 30-35, attapulgite modified 8-9, water are appropriate; The described attapulgite modified raw material by following weight portion is made: attapulgite 120-130, silver nitrate 1-2, alum 5-6, iron ore ground-slag 1-2, polytetrafluoroethylene (PTFE) 4-5, titanium sulfate 14-18, jade powder 12-14, zinc sulfate 1-2, chromium oxide 3-4, morpholine 1-2, N-2-(aminoethyl)-3-aminopropyl trimethoxysilane 2-3, water are appropriate; Attapulgite, iron ore ground-slag are sent in calcining furnace, and under 950-990 ℃, calcining 3-4 hour, take out, and spills the N-2-(aminoethyl)-the 3-aminopropyl trimethoxysilane
,put into suitable quantity of water again and grind, regulating the lapping liquid pH value is 4-5, grinds 1-2 hour, obtains 100-150 order slurry, then regulates the lapping liquid pH value for neutral, adds other residual components, continues to grind, and obtains 200-300 order slurry, and spray-drying, obtain.
2. the preparation method of dye wastewater treatment using modified activated carbon according to claim 1, is characterized in that comprising the following steps: by crushed stalk, add water with expanded perlite and mix, practice into the mud shape, granulate, send into calcining 2-3 hour in 620-650 ℃ of calcining furnace, take out, with active carbon, expanded graphite, attapulgite modified merging, add suitable quantity of water, grind to form 200-300 order slurry, spray-drying, obtain powder, sends in 340-380 ℃ of heat-treatment furnace, heat treatment 2-3 hour, take out cooling and get final product.