CN103485419A - 复合防水卷材配方及其制备方法 - Google Patents
复合防水卷材配方及其制备方法 Download PDFInfo
- Publication number
- CN103485419A CN103485419A CN201210195536.4A CN201210195536A CN103485419A CN 103485419 A CN103485419 A CN 103485419A CN 201210195536 A CN201210195536 A CN 201210195536A CN 103485419 A CN103485419 A CN 103485419A
- Authority
- CN
- China
- Prior art keywords
- jin
- polyethylene
- preparation
- roll material
- waterproof roll
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
复合防水卷材配方及其制备方法,它涉及一种复合防水卷材。它的配方组成为:聚乙烯35-49.4斤、网格布5-14斤、无纺布14-28斤、色母0.1-0.5斤、抗老化剂0.02-0.1斤;它的制备工艺为:1、将聚乙烯、网格布、无纺布、色母、抗老化剂按照配比进行搅拌混合;2、将两台聚乙烯流延膜挤出机械经模头定量挤出;3、模头上方备有专用纤维网格布摆放展平架均匀输送纤维网格布;4、将双面无纺布复合定型,使其五层合一;5、牵引,收卷;6、成品经检验合格后包装;本发明自然与纤维网格布非织造布通过自然热量压延而成,且无脱层现象使其容为一体,无需任何粘合剂;不仅能起到防水的作用,而且能延长使用寿命。
Description
技术领域:
本发明涉及一种复合防水卷材,具体涉及一种复合防水卷材配方及其制备方法。
背景技术:
防水卷材产品主要有沥青防水卷材和高分子防水卷材。沥青防水卷材是用原纸、纤维毡等胎体材料浸涂沥青,表面撒布粉状、粒状或片状材料制成可卷曲的片状防水材料。沥青防水卷材分为有胎卷材和无胎卷材。凡是用厚纸或玻璃丝布、石棉布、棉麻织品等胎料浸渍石油沥青制成的卷状材料,称为有胎卷材;将石棉、橡胶粉等掺入沥青材料中,经碾压制成的卷状材料称为辊压卷材即无胎卷材。高分子防水卷材是以合成橡胶、合成树脂或二者的共混体为基料,加入适量的化学助剂和填充剂等,采用密炼、挤出或压延等橡胶或塑料的加工工艺所制成的可卷曲片状防水材料。一般采用单层防水体系,适合于一些防水等级要求较高、维修施工不便的防水工程。
目前使用的高分子防水卷材存在粘结性差,施工技术要求高,与基层完全粘结困难;搭接缝多,易产生接缝粘结不善产生渗漏的问题,宜与涂料复合使用,以增强防水层的整体性,提高防水可靠度。后期收缩大大多数合成高分子防水卷材的热收缩和后期收缩均较大,常使卷材防水层产生较大内应力加速老化,或产生防水层被拉裂、搭接缝拉脱翘边等缺陷。
发明内容:
本发明的目的是提供复合防水卷材配方及其制备方法,它在达到熔点后,自然产生180-200摄氏度热量,其自然与纤维网格布非织造布通过自然热量压延而成,且无脱层现象使其容为一体,无需任何粘合剂;不仅能起到防水的作用,而且能延长使用寿命。
为了解决背景技术所存在的问题,本发明是采用以下技术方案:它的配方组成为:聚乙烯35-49.4斤、网格布5-14斤、无纺布14-28斤、色母0.1-0.5斤、抗老化剂0.02-0.1斤。
它的制备工艺为:1、将聚乙烯、网格布、无纺布、色母、抗老化剂按照配比进行搅拌混合;2、将两台聚乙烯流延膜挤出机械经模头定量挤出;3、模头上方备有专用纤维网格布摆放展平架均匀输送纤维网格布;4、将双面无纺布复合定型,使其五层合一;5牵引,收卷;6、成品经检验合格后包装。
所述的工艺步骤3中纤维网格布融入在双层聚乙烯流延膜中间,使其三层复合。
本发明具有以下有益效果:在达到熔点后,自然产生180-200摄氏度热量,其自然与纤维网格布非织造布通过自然热量压延而成,且无脱层现象使其容为一体,无需任何粘合剂;不仅能起到防水的作用,而且能延长使用寿命。
具体实施方式:
具体实施方式一:本具体实施方式采用以下技术方案:它的配方组成为:聚乙烯35斤、网格布5斤、无纺布14斤、色母0.1斤、抗老化剂0.02斤。
它的制备工艺为:1、将聚乙烯、网格布、无纺布、色母、抗老化剂按照配比进行搅拌混合;2、将两台聚乙烯流延膜挤出机械经模头定量挤出;3、模头上方备有专用纤维网格布摆放展平架均匀输送纤维网格布;4、将双面无纺布复合定型,使其五层合一;5牵引,收卷;6、成品经检验合格后包装。
所述的工艺步骤3中纤维网格布融入在双层聚乙烯流延膜中间,使其三层复合。
具体实施方式二:本具体实施方式与具体实施方式一不同之处在于它的配方组成为:聚乙烯40斤、网格布8斤、无纺布18斤、色母0.3斤、抗老化剂0.05斤;其制备工艺均与具体实施方式一相同。
具体实施方式三:本具体实施方式与具体实施方式一不同之处在于它的配方组成为:聚乙烯49.4斤、网格布14斤、无纺布28斤、色母0.5斤、抗老化剂0.1斤;其制备工艺均与具体实施方式一相同。
Claims (5)
1.复合防水卷材配方及其制备方法,其特征在于它的配方组成为:聚乙烯35-49.4斤、网格布5-14斤、无纺布14-28斤、色母0.1-0.5斤、抗老化剂0.02-0.1斤;它的制备工艺为:1、将聚乙烯、网格布、无纺布、色母、抗老化剂按照配比进行搅拌混合;2、将两台聚乙烯流延膜挤出机械经模头定量挤出;3、模头上方备有专用纤维网格布摆放展平架均匀输送纤维网格布;4、将双面无纺布复合定型,使其五层合一;5牵引,收卷;6、成品经检验合格后包装。
2.根据权利要求1所述的复合防水卷材配方及其制备方法,其特征在于所述的工艺步骤3中纤维网格布融入在双层聚乙烯流延膜中间,使其三层复合。
3.根据权利要求1所述的复合防水卷材配方及其制备方法,其特征在于它的配方组成为:聚乙烯35斤、网格布5斤、无纺布14斤、色母0.1斤、抗老化剂0.02斤。
4.根据权利要求1所述的复合防水卷材配方及其制备方法,其特征在于它的配方组成为:聚乙烯40斤、网格布8斤、无纺布18斤、色母0.3斤、抗老化剂0.05斤。
5.根据权利要求1所述的复合防水卷材配方及其制备方法,其特征在于它的配方组成为:聚乙烯49.4斤、网格布14斤、无纺布28斤、色母0.5斤、抗老化剂0.1斤。