CN103484866B - A kind of polishing anti-corrosive pulp - Google Patents
A kind of polishing anti-corrosive pulp Download PDFInfo
- Publication number
- CN103484866B CN103484866B CN201310434345.3A CN201310434345A CN103484866B CN 103484866 B CN103484866 B CN 103484866B CN 201310434345 A CN201310434345 A CN 201310434345A CN 103484866 B CN103484866 B CN 103484866B
- Authority
- CN
- China
- Prior art keywords
- polishing
- kilogram
- metal surface
- corrosive pulp
- present
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Abstract
A kind of polishing anti-corrosive pulp of the present invention, the aluminum oxide polishing powder that this slurry contains 10～30wt%, the 3-TSL 8330 of 1～5wt%, the stearic acid of 0.1～3wt%, the glycerine of 1～2wt%, the phosphoric acid of 0.1～1wt%, the manganese dioxide of 0.1～1wt%, 0.1～0.5wt% surfactant, surplus is water. Adopt polishing anti-corrosive pulp of the present invention in completing metal surface polishing, form layer protecting film in metal surface and prevent ambient oxidizable metal surface.
Description
Technical field
The present invention relates to a kind of slurry for metal surface polishing.
Background technology
Metal with the Long Term Contact process of air in unavoidably can occur to be to a certain degree oxidized, make metal lose metallic luster, for this reason, be before use, although existing polishing agent can be removed the oxide layer of metal surface, but the metal after polishing is if do not carried out preservative treatment, very soon can be oxidized and lose metallic luster in the metal surface after polishing.
Summary of the invention
The object of this invention is to provide a kind of polishing anti-corrosive pulp.
To achieve these goals, the invention provides following technical scheme:
A kind of polishing anti-corrosive pulp, the aluminum oxide polishing powder that contains 10～30wt%, the 3-TSL 8330 of 1～5wt%, the stearic acid of 0.1～3wt%, the glycerine of 1～2wt%, the phosphoric acid of 0.1～1wt%, the manganese dioxide of 0.1～1wt%, 0.1～0.5wt% surfactant, surplus is water.
Further, the particle diameter of described aluminum oxide polishing powder is 4～50 μ m.
Further, described surfactant is dodecyl sodium sulfate or NPE NP-10.
Adopt polishing anti-corrosive pulp of the present invention in completing metal surface polishing, can form layer protecting film in metal surface and prevent ambient oxidizable metal surface, thereby play the effect that prevents metal erosion.
Detailed description of the invention
Below the preferred embodiments of the present invention are described, should be appreciated that preferred embodiment described herein, only for description and interpretation the present invention, is not intended to limit the present invention.
Embodiment 1
A kind of polishing anti-corrosive pulp, by 1 kilogram of aluminum oxide polishing powder, (particle diameter is α-Al of 4～15 μ m2O3), the 3-TSL 8330 (CAS:13822-56-5) of 0.1 kilogram, the stearic acid of 0.2 kilogram, the glycerine of 0.1 kilogram, the phosphoric acid of 0.01 kilogram, the manganese dioxide of 0.01 kilogram, the water of the dodecyl sodium sulfate of 0.01 kilogram and 8.57 kilograms, ground and mixed obtains after evenly.
Embodiment 2
A kind of polishing anti-corrosive pulp, by 2 kilograms of aluminum oxide polishing powders, (particle diameter is α-Al of 10～25 μ m2O3), the 3-TSL 8330 of 0.3 kilogram, the stearic acid of 0.3 kilogram, the glycerine of 0.1 kilogram, the phosphoric acid of 0.1 kilogram, the manganese dioxide of 0.1 kilogram, the water of the dodecyl sodium sulfate of 0.05 kilogram and 7.05 kilograms, ground and mixed obtains after evenly.
Embodiment 3
A kind of polishing anti-corrosive pulp, by 3 kilograms of aluminum oxide polishing powders, (particle diameter is α-Al of 25～50 μ m2O3), the 3-TSL 8330 of 0.5 kilogram, the stearic acid of 0.01 kilogram, the glycerine of 0.2 kilogram, the phosphoric acid of 0.05 kilogram, the manganese dioxide of 0.05 kilogram, the NPE NP-10 of 0.03 kilogram and the water of 6.16 kilograms, obtain after ground and mixed is even.
The use of this polishing anti-corrosive pulp: use spray gun that slurry is sprayed pending aluminum ironware, show after metallic luster to utensil, places 10～20 minutes, then water flushing.
The foregoing is only the preferred embodiments of the present invention, be not limited to the present invention, although the present invention is had been described in detail with reference to previous embodiment, for a person skilled in the art, its technical scheme that still can record aforementioned each embodiment is modified, or part technical characterictic is wherein equal to replacement. Within the spirit and principles in the present invention all, any amendment of doing, be equal to replacement, improvement etc., within all should being included in protection scope of the present invention.
Claims (2)
1. a polishing anti-corrosive pulp, the aluminum oxide polishing powder that contains 10～30wt%, the 3-TSL 8330 of 1～5wt%, the stearic acid of 0.1～3wt%, the glycerine of 1～2wt%, the phosphoric acid of 0.1～1wt%, the manganese dioxide of 0.1～1wt%, 0.1～0.5wt% surfactant, surplus is water; Described surfactant is dodecyl sodium sulfate or NPE NP-10.
2. polishing anti-corrosive pulp according to claim 1, is characterized in that, the particle diameter of described aluminum oxide polishing powder is 4～50 μ m.