CN103482929A - Cement-based dry powder coating - Google Patents
Cement-based dry powder coating Download PDFInfo
- Publication number
- CN103482929A CN103482929A CN201310409368.9A CN201310409368A CN103482929A CN 103482929 A CN103482929 A CN 103482929A CN 201310409368 A CN201310409368 A CN 201310409368A CN 103482929 A CN103482929 A CN 103482929A
- Authority
- CN
- China
- Prior art keywords
- cement
- powder coating
- water
- color
- diameter
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention relates to a preparation method of a cement-based dry powder coating. The preparation method is characterized by comprising the following steps: preparing 60-100g of white cement, 20-30g of SiO2 with the diameter of 5-30nm, 5-10g of water-soluble fluoride resin, 2-4g of defoaming agent, 20-30g of CaCO3 and 2-3g of color, uniformly stirring through a stirring machine, packaging according to set dosage and warehousing. In construction, water and the well prepared dry powder coating are mixed on site, wherein the ratio of the water to the coating is 8-9: 4-6; and the mixture is further sprayed or coated on a cement-based exterior wall body. A coat formed by the coating does not crack, hardly peel off, has good waterproofness and resistance to corrosion of acid, alkali and the like, and particularly has good fireproofness and strong decoration rendering performance.
Description
Technical field
The present invention relates to a kind of coating, particularly relate to a kind of cement-based powder coating for skin.
Background technology
Along with the high speed development of national economy and the raising day by day of living standards of the people, the requirement clean and tidy to the appearance of the city is also more and more higher.For beautifying of the attractive in appearance and city of building, on the exterior wall of a lot of buildingss, be coated with versicolor coating.But the known coatings cohesiveness of using at present is poor, the special cohesive force with cement basic layer is poor, easy to crack and come off, and particularly for the brushing of clear-water concrete basic unit or to spray cohesive force all poor, and cost is high.
Summary of the invention
Purpose of the present invention, be to provide a kind of cement based powder coating, and water resistance is good, spray or be applied on the cement based exterior wall do not come off, fire-resistant, corrosion-resistant.Water resistance is good.
The technical scheme adopted for achieving the above object is:
A kind of cement-based powder coating is the SiO that is 5-30nm by white cement 60-100g, diameter
2the CaCO that 20-30g, water soluble fluoridized resin 5-10g, defoamer 2-4g, diameter are 5-30nm
320-30g and color 2-3g are mixed with.
Add water during use and stir, spraying or brushing are on the cement based exterior wall.
Water and coating ratio=8-9:4-6.
The pigment added should be selected according to actual needs, take that to reach attractive in appearance and generous be purpose.
Preparation method of the present invention is:
The SiO that to get white cement 60-100g, diameter be 5-30nm
220-30g, water soluble fluoridized resin 5-10g, defoamer 2-4g, CaCO
320-30g and color 2-3g, with stirrer, stir, by setting metering packing, warehouse-in, get final product.
During construction, the dry powder paint scene prepared is added to water and mix, water sprays or is coated on the cement based exterior wall with coating ratio=8-9:4-6..
The invention has the advantages that: this paint coatings does not ftracture, difficult drop-off, water resistance are good, and it is good to have acidproof, alkaline-resisting etc. corrosive nature, particularly fire line, and decorating a surname's metachromia can be strong.
Embodiment
Embodiment mono-
A kind of cement-based powder coating is the SiO that is 30nm by white cement 100g, diameter
230g, water soluble fluoridized resin 10g, defoamer 4g, CaCO
330g and color 3g are mixed with.
Embodiment bis-
A kind of cement-based powder coating is the SiO that is 5nm by white cement 60g, diameter
220-30g, water soluble fluoridized resin 5g, defoamer 2g, CaC O
320g and color 2g are mixed with.
Embodiment tri-
A kind of cement-based powder coating is the SiO that is 15nm by white cement 80g, diameter
215g, water soluble fluoridized resin 6g, defoamer 3g, CaC O
315g and color 1.5g are mixed with.
Embodiment tetra-
A kind of preparation method of cement-based powder coating is characterized in that: the SiO that to get white cement 60-100g, diameter be 5-30nm
220-30g, water soluble fluoridized resin 5-10g, defoamer 2-4g, CaCO
320-30g and color 2-3g, with stirrer, stir, by setting metering packing, warehouse-in, get final product;
During construction, the dry powder paint scene prepared is added to water and mix, water sprays or is coated on the cement based exterior wall with coating ratio=8-9:4-6..
Claims (4)
1. a cement-based powder coating, is characterized in that: the SiO that is 30nm by white cement 100g, diameter
230g, water soluble fluoridized resin 10g, defoamer 4g, CaCO
330g and color 3g are mixed with.
2. a kind of cement-based powder coating according to claim 1, is characterized in that: the SiO that is 5nm by white cement 60g, diameter
220-30g, water soluble fluoridized resin 5g, defoamer 2g, CaC O
320g and color 2g are mixed with.
3. a kind of cement-based powder coating according to claim 1, is characterized in that: the SiO that is 15nm by white cement 80g, diameter
215g, water soluble fluoridized resin 6g, defoamer 3g, CaC O
315g and color 1.5g are mixed with.
4. the preparation method of a cement-based powder coating is characterized in that: the SiO that to get white cement 60-100g, diameter be 5-30nm
220-30g, water soluble fluoridized resin 5-10g, defoamer 2-4g, CaCO
320-30g and color 2-3g, with stirrer, stir, by setting metering packing, warehouse-in, get final product;
During construction, the dry powder paint scene prepared is added to water and mix, water sprays or is coated on the cement based exterior wall with coating ratio=8-9:4-6..